$ 1481/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 818 MPa
- Tensile Strength, Yield: 411 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 211 GPa
$ 1801/MT
- Density: 8.50 g/cc
- Tensile Strength, Ultimate: 554 MPa @Temperature 649 °C
- Tensile Strength, Ultimate: 585 MPa @Temperature 482 °C
- Tensile Strength, Ultimate: 586 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 605 MPa @Temperature 371 °C
$ 1993/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 63 @Thickness 12.7 mm
- Hardness, Rockwell A: 66 @Thickness 1.45 mm
- Tensile Strength, Ultimate: 1207 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 1253 MPa @Thickness 1.45 mm
$ 2008/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1517/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 1241 MPa
- Tensile Strength, Yield: 1110 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Reduction of Area: 45 %
$ 1477/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Yield: 407 MPa @Strain 0.200 %
$ 1707/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 585 MPa @Strain 0.200 %
- Elongation at Break: 38 %
- Modulus of Elasticity: 218 GPa
$ 2267/MT
- Density: 8.64 g/cc
- Hardness, Brinell: 155 @Thickness 1.70 mm
- Hardness, Brinell: 159 @Thickness 3.20 mm
- Hardness, Knoop: 172 @Thickness 1.70 mm
- Hardness, Knoop: 176 @Thickness 3.20 mm
$ 1509/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 470 MPa @Strain 0.200 %
- Elongation at Break: 30 %
- Modulus of Elasticity: 208 GPa
$ 1630/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 794 MPa
- Tensile Strength, Ultimate: 234 MPa @Temperature 927 °C
- Tensile Strength, Ultimate: 385 MPa @Temperature 815 °C
- Tensile Strength, Ultimate: 480 MPa @Temperature 704 °C
$ 1478/MT
- Density: 8.25 g/cc
- Tensile Strength, Ultimate: 1047 MPa
- Tensile Strength, Ultimate: 179 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 677 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 858 MPa @Temperature 760 °C
$ 1628/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 64 @Thickness 12.7 mm
- Hardness, Rockwell A: 64 @Thickness 1.45 mm
- Tensile Strength, Ultimate: 996 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 1231 MPa @Thickness 1.45 mm
$ 1932/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 256
- Hardness, Knoop: 278
- Hardness, Rockwell C: 24
- Hardness, Vickers: 263
$ 1463/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 485 MPa @Strain 0.200 %
- Elongation at Break: 38.5 %
- Modulus of Elasticity: 211 GPa
$ 1795/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Ultimate: 33.0 MPa @Temperature 1204 °C
- Tensile Strength, Ultimate: 46.0 MPa @Temperature 1149 °C
- Tensile Strength, Ultimate: 68.0 MPa @Temperature 1093 °C
$ 1789/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Yield: 319 MPa @Strain 0.200 %
- Elongation at Break: 26 %
- Reduction of Area: 19 %
$ 2222/MT
- Density: 8.26 g/cc
- Tensile Strength, Ultimate: 115 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 360 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 650 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 990 MPa @Temperature 650 °C
$ 1459/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1420 MPa
- Tensile Strength, Yield: 1262 MPa @Strain 0.200 %
$ 2543/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 805 MPa
- Tensile Strength, Ultimate: 570 MPa @Temperature 649 °C
- Elongation at Break: 38.6 %
- Elongation at Break: 26.5 % @Temperature 649 °C
$ 1735/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %
$ 1510/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %
$ 1672/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %
$ 1532/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %
$ 1589/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 57
- Tensile Strength, Ultimate: 847 MPa
- Tensile Strength, Yield: 416 MPa @Strain 0.200 %
- Reduction of Area: 32 %
$ 1881/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1724 MPa
- Tensile Strength, Yield: 1682 MPa @Strain 0.200 %
$ 2190/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 495 MPa @Strain 0.200 %
- Elongation at Break: 39.1 %
- Modulus of Elasticity: 211 GPa
$ 2401/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 701 MPa
- Tensile Strength, Yield: 295 MPa @Strain 0.200 %
- Elongation at Break: 28 %
- Reduction of Area: 23 %
$ 1535/MT
- Density: 8.27 g/cc
- Density: 8.29 g/cc
- Tensile Strength, Ultimate: 181 MPa @Thickness 12.7 mm, Temperature 982 °C
- Tensile Strength, Ultimate: 575 MPa @Thickness 12.7 mm, Temperature 871 °C
- Tensile Strength, Ultimate: 867 MPa @Thickness 12.7 mm, Temperature 760 °C
$ 1819/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 342
- Hardness, Knoop: 371
- Hardness, Rockwell C: 37
- Hardness, Vickers: 358
$ 1556/MT
- Density: 8.75 g/cc
- Tensile Strength, Ultimate: 821 MPa
- Tensile Strength, Yield: 429 MPa @Strain 0.200 %
- Reduction of Area: 26 %
- Modulus of Elasticity: 132 GPa @Temperature 1093 °C
$ 2208/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 252
- Hardness, Knoop: 274
- Hardness, Rockwell C: 23.3
- Hardness, Vickers: 259
$ 1527/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 290
- Hardness, Knoop: 311
- Hardness, Rockwell C: 30
- Hardness, Vickers: 301
$ 1717/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 752 MPa
- Tensile Strength, Ultimate: 641 MPa @Temperature 400 °C
$ 1503/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 703 MPa
- Tensile Strength, Ultimate: 496 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 565 MPa @Temperature 260 °C
- Tensile Strength, Yield: 469 MPa @Strain 0.200 %
$ 1502/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 55 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 882 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 918 MPa @Thickness 1.45 mm
$ 1461/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 379
- Hardness, Knoop: 414
- Hardness, Rockwell C: 41
- Hardness, Vickers: 399
$ 1498/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 53 @Thickness 1.45 mm
- Hardness, Rockwell A: 56 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 879 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 904 MPa @Thickness 1.45 mm
$ 1898/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 995 MPa
- Tensile Strength, Ultimate: 30.0 MPa @Temperature 1205 °C
- Tensile Strength, Ultimate: 32.0 MPa @Temperature 1150 °C
- Tensile Strength, Ultimate: 58.0 MPa @Temperature 1095 °C
$ 1707/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 420 MPa @Strain 0.200 %
- Elongation at Break: 38 %
- Modulus of Elasticity: 211 GPa
$ 1537/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 786 MPa
- Tensile Strength, Ultimate: 524 MPa @Temperature 760 °C
$ 2348/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 785 MPa
- Tensile Strength, Ultimate: 310 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 610 MPa @Temperature 538 °C
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
$ 1577/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 774 MPa
- Tensile Strength, Yield: 321 MPa @Strain 0.200 %
- Elongation at Break: 66 %
- Reduction of Area: 73 %
$ 1657/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 277
- Hardness, Knoop: 301
- Hardness, Rockwell C: 27.9
- Hardness, Vickers: 287
$ 1711/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 765 MPa
- Tensile Strength, Ultimate: 496 MPa @Temperature 760 °C
$ 1584/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 890 MPa
- Tensile Strength, Yield: 395 MPa @Strain 0.200 %
- Elongation at Break: 34 %
- Modulus of Elasticity: 211 GPa
$ 1979/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 262
- Hardness, Knoop: 284
- Hardness, Rockwell C: 25.1
- Hardness, Vickers: 270
$ 1499/MT
- Density: 8.75 g/cc
- Tensile Strength, Ultimate: 964 MPa
- Tensile Strength, Yield: 678 MPa @Strain 0.200 %
- Elongation at Break: 25 %
- Reduction of Area: 24 %
$ 1486/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 838 MPa
- Tensile Strength, Yield: 354 MPa @Strain 0.200 %
- Elongation at Break: 38 %
- Reduction of Area: 31 %
$ 1828/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 786 MPa
- Tensile Strength, Yield: 400 MPa @Strain 0.200 %
$ 1742/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 1324 MPa
- Tensile Strength, Yield: 1158 MPa @Strain 0.200 %
- Elongation at Break: 8.0 %
- Reduction of Area: 14 %
$ 1480/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1700/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 411
- Hardness, Knoop: 451
- Hardness, Rockwell C: 44
- Hardness, Vickers: 434
$ 1479/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 500 MPa
- Tensile Strength, Yield: 415 MPa
- Elongation at Break: 14 %
- Reduction of Area: 50 %
$ 2404/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 279
- Hardness, Rockwell C: 24.3
- Hardness, Vickers: 265
$ 1790/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 970 MPa
- Tensile Strength, Yield: 665 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 208 GPa
$ 1747/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 830 MPa
- Tensile Strength, Ultimate: 295 MPa @Temperature 870 °C
- Tensile Strength, Yield: 555 MPa
- Tensile Strength, Yield: 275 MPa @Temperature 870 °C
$ 1665/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 902 MPa @Temperature 600 °C
- Tensile Strength, Ultimate: 964 MPa @Temperature 500 °C
- Tensile Strength, Ultimate: 1006 MPa @Temperature 400 °C
$ 1489/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 965 MPa
- Tensile Strength, Yield: 605 MPa @Strain 0.200 %
- Elongation at Break: 35.2 %
- Modulus of Elasticity: 218 GPa
$ 2342/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 820 MPa
- Tensile Strength, Ultimate: 300 MPa @Temperature 870 °C
- Tensile Strength, Yield: 475 MPa
- Tensile Strength, Yield: 240 MPa @Temperature 870 °C
$ 1526/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 731 MPa
- Tensile Strength, Yield: 372 MPa @Strain 0.200 %
$ 1499/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56
- Tensile Strength, Ultimate: 863 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 56 %
$ 1796/MT
- Density: 8.89 g/cc
- Hardness, Rockwell B: 87
- Hardness, Rockwell B: 90
- Tensile Strength, Ultimate: 601.2 MPa @Thickness 4.80 - 25.4 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 613 MPa @Thickness 1.60 - 4.70 mm, Temperature 538 °C
$ 1477/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 683 MPa
- Tensile Strength, Yield: 310 MPa @Strain 0.200 %
- Elongation at Break: 60 %
- Modulus of Elasticity: 202 GPa
$ 1459/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 985 MPa
- Tensile Strength, Yield: 670 MPa @Strain 0.200 %
- Elongation at Break: 13 %
- Modulus of Elasticity: 208 GPa
$ 2521/MT
- Density: 8.37 g/cc
- Tensile Strength, Ultimate: 66.0 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 286 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 439 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 473 MPa @Temperature 650 °C
$ 1505/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 324 MPa @Strain 0.200 %
- Elongation at Break: 56 %
- Modulus of Elasticity: 202 GPa
$ 1492/MT
- Density: 8.27 g/cc
- Hardness, Rockwell B: 93
- Hardness, Rockwell C: 15
- Tensile Strength, Ultimate: 816 MPa
- Tensile Strength, Ultimate: 830 MPa
$ 2044/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 79.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 155 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 286 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 483 MPa @Temperature 760 °C
$ 1778/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56
- Tensile Strength, Ultimate: 775 MPa
- Tensile Strength, Yield: 412 MPa @Strain 0.200 %
- Reduction of Area: 62 %
$ 2181/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 400
- Hardness, Knoop: 437
- Hardness, Rockwell C: 43
- Hardness, Vickers: 422
$ 2314/MT
- Density: 8.50 g/cc
- Tensile Strength, Ultimate: 528 MPa @Diameter 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 614 MPa @Diameter 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 733 MPa @Diameter 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 365 MPa @Diameter 12.7 mm, Temperature 538 °C
$ 1609/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 809 MPa
- Tensile Strength, Yield: 321 MPa @Strain 0.200 %
- Elongation at Break: 26 %
- Reduction of Area: 23 %
$ 1884/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 900 MPa
- Tensile Strength, Yield: 420 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- Modulus of Elasticity: 208 GPa
$ 2013/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 342
- Hardness, Knoop: 371
- Hardness, Rockwell C: 37
- Hardness, Vickers: 358
$ 1749/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1295 MPa
- Tensile Strength, Yield: 1105 MPa @Strain 0.200 %
- Elongation at Break: 9.7 %
- Modulus of Elasticity: 211 GPa
$ 1541/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 52
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 383 MPa @Strain 0.200 %
- Elongation at Break: 60 %
$ 1844/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 1130 MPa
- Tensile Strength, Yield: 815 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- Modulus of Elasticity: 208 GPa
$ 1953/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 990 MPa
- Tensile Strength, Yield: 555 MPa @Strain 0.200 %
- Elongation at Break: 36.3 %
- Modulus of Elasticity: 211 GPa
$ 2312/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1138 MPa
- Tensile Strength, Yield: 972 MPa @Strain 0.200 %
$ 2334/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1034 MPa
- Tensile Strength, Yield: 593 MPa @Strain 0.200 %
$ 1578/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 524 MPa @Temperature 760 °C
$ 2050/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 738 MPa
- Tensile Strength, Yield: 492 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 211 GPa
$ 1759/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 1055 MPa
- Tensile Strength, Ultimate: 565 MPa @Temperature 760 °C
- Tensile Strength, Yield: 755 MPa
- Tensile Strength, Yield: 400 MPa @Temperature 760 °C
$ 1918/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 352 MPa @Strain 0.200 %
- Elongation at Break: 56 %
- Modulus of Elasticity: 202 GPa
$ 1886/MT
- Density: 8.27 g/cc
- Density: 8.29 g/cc
- Tensile Strength, Ultimate: 185 MPa @Thickness 12.7 mm, Temperature 982 °C
- Tensile Strength, Ultimate: 565 MPa @Thickness 12.7 mm, Temperature 871 °C
- Tensile Strength, Ultimate: 852 MPa @Thickness 12.7 mm, Temperature 760 °C
$ 1654/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 975 MPa
- Tensile Strength, Yield: 575 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1548/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Yield: 560 MPa @Strain 0.200 %
- Elongation at Break: 32.3 %
- Modulus of Elasticity: 211 GPa
$ 1570/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 745 MPa @Thickness 3.20 mm, Temperature 316 °C
- Tensile Strength, Ultimate: 747 MPa @Thickness 3.20 mm, Temperature 371 °C
- Tensile Strength, Ultimate: 754 MPa @Thickness 3.20 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 763 MPa @Thickness 3.20 mm, Temperature 204 °C
$ 2475/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 256
- Hardness, Knoop: 278
- Hardness, Rockwell C: 24
- Hardness, Vickers: 263
$ 2048/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 935 MPa
- Tensile Strength, Yield: 450 MPa @Strain 0.200 %
- Elongation at Break: 39.2 %
- Modulus of Elasticity: 211 GPa
$ 1519/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 805 MPa
- Tensile Strength, Ultimate: 320 MPa @Temperature 870 °C
- Tensile Strength, Yield: 455 MPa
- Tensile Strength, Yield: 235 MPa @Temperature 870 °C
$ 1596/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 369
- Hardness, Knoop: 403
- Hardness, Rockwell C: 40
- Hardness, Vickers: 388
$ 1846/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 925 MPa
- Tensile Strength, Yield: 435 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 208 GPa
$ 1788/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1172 MPa
- Tensile Strength, Yield: 1041 MPa @Strain 0.200 %
$ 2475/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1014 MPa
- Tensile Strength, Yield: 579 MPa @Strain 0.200 %
$ 1557/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 910 MPa
- Tensile Strength, Yield: 420 MPa @Strain 0.200 %
- Elongation at Break: 33 %
- Modulus of Elasticity: 211 GPa
$ 1661/MT
- Density: 8.22 g/cc
- Hardness, Brinell: 334
- Hardness, Knoop: 362
- Hardness, Rockwell C: 36
- Hardness, Vickers: 349
$ 1731/MT
- Density: 8.27 g/cc
- Hardness, Rockwell C: 26
- Hardness, Rockwell C: 33
- Hardness, Rockwell C: 38
- Hardness, Rockwell C: 41
$ 1789/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 879 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 885 MPa @Thickness 1.45 mm
$ 1751/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1020 MPa
- Tensile Strength, Yield: 595 MPa @Strain 0.200 %
- Elongation at Break: 34.6 %
- Modulus of Elasticity: 211 GPa
$ 1585/MT
- Density: 8.27 g/cc
- Density: 8.29 g/cc
- Tensile Strength, Ultimate: 975 MPa @Treatment Temp. 871 °C, Time 3.60e+6 sec
- Tensile Strength, Ultimate: 1102 MPa @Treatment Temp. 816 °C, Time 3.60e+6 sec
- Tensile Strength, Ultimate: 1176 MPa @Treatment Temp. 760 °C, Time 3.60e+6 sec
$ 1564/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 919 MPa @Thickness 1.45 mm
- Tensile Strength, Yield: 370 MPa @Strain 0.200 %, Thickness 12.7 mm
$ 1536/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1472/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 57
- Tensile Strength, Ultimate: 867 MPa
- Tensile Strength, Yield: 385 MPa @Strain 0.200 %
- Elongation at Break: 60 %
$ 1615/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1130 MPa
- Tensile Strength, Yield: 920 MPa @Strain 0.200 %
- Elongation at Break: 16.8 %
- Modulus of Elasticity: 211 GPa
$ 1668/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 2244/MT
- Density: 8.25 g/cc
- Tensile Strength, Ultimate: 1285 MPa
- Tensile Strength, Ultimate: 75.0 MPa @Temperature 1093 °C
- Tensile Strength, Ultimate: 274 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 702 MPa @Temperature 871 °C
$ 1694/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 317
- Hardness, Knoop: 344
- Hardness, Rockwell C: 33.8
- Hardness, Vickers: 330
$ 1615/MT
- Density: 8.50 g/cc
- Tensile Strength, Ultimate: 752 MPa @Thickness 25.4 mm
- Tensile Strength, Ultimate: 752 MPa @Thickness 1.60 mm
- Tensile Strength, Ultimate: 758 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 765 MPa @Thickness 3.17 mm
$ 2042/MT
- Density: 8.50 g/cc
- Tensile Strength, Ultimate: 718 MPa @Thickness 25.4 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 364 MPa @Thickness 25.4 mm, Temperature 25.0 °C
- Elongation at Break: 58.1 % @Thickness 25.4 mm, Temperature 25.0 °C
- Modulus of Elasticity: 162 GPa @Temperature 649 °C
$ 1664/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 960 MPa
- Tensile Strength, Yield: 505 MPa @Strain 0.200 %
- Elongation at Break: 38.1 %
- Modulus of Elasticity: 211 GPa
$ 1606/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 789 MPa
- Tensile Strength, Ultimate: 426 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 482 MPa @Temperature 704 °C
- Tensile Strength, Ultimate: 568 MPa @Temperature 649 °C
$ 1446/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Hardness, Rockwell C: 30
- Hardness, Rockwell C: 35
- Hardness, Rockwell C: 40
$ 1605/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 880 MPa
- Tensile Strength, Yield: 455 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 208 GPa
$ 1761/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 960 MPa
- Tensile Strength, Ultimate: 34.0 MPa @Temperature 1205 °C
- Tensile Strength, Ultimate: 46.0 MPa @Temperature 1150 °C
- Tensile Strength, Ultimate: 62.0 MPa @Temperature 1095 °C
$ 1710/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 258
- Hardness, Knoop: 281
- Hardness, Rockwell C: 24.5
- Hardness, Vickers: 266
$ 1540/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 696 MPa
- Tensile Strength, Ultimate: 372 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 503 MPa @Temperature 538 °C
- Tensile Strength, Yield: 365 MPa @Strain 0.200 %
$ 1496/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 222
- Hardness, Knoop: 260
- Hardness, Rockwell A: 60
- Hardness, Rockwell B: 97
$ 1656/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 705 MPa @Thickness 25.4 mm, Temperature 427 °C
- Tensile Strength, Ultimate: 712 MPa @Thickness 25.4 mm, Temperature 371 °C
- Tensile Strength, Ultimate: 714 MPa @Thickness 25.4 mm, Temperature 316 °C
- Tensile Strength, Ultimate: 725 MPa @Thickness 25.4 mm, Temperature 260 °C
$ 1927/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 228
- Hardness, Knoop: 241
- Hardness, Rockwell C: 18
- Hardness, Vickers: 232
$ 2453/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 52
- Tensile Strength, Ultimate: 874 MPa
- Tensile Strength, Yield: 390 MPa @Strain 0.200 %
- Elongation at Break: 55 %
$ 1561/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 777 MPa
- Tensile Strength, Ultimate: 602 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 654 MPa @Temperature 260 °C
- Tensile Strength, Yield: 471 MPa @Strain 0.200 %
$ 2321/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 389
- Hardness, Knoop: 426
- Hardness, Rockwell C: 42
- Hardness, Vickers: 410
$ 1681/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 441 MPa @Diameter 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 538 MPa @Diameter 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 696 MPa @Diameter 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 302 MPa @Diameter 12.7 mm, Temperature 538 °C
$ 2400/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 825 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 58 %
- Modulus of Elasticity: 208 GPa
$ 1473/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1858/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 379 MPa @Strain 0.200 %
$ 1912/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 274
- Hardness, Knoop: 298
- Hardness, Rockwell C: 27.4
- Hardness, Vickers: 284
$ 2192/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Yield: 579 MPa @Strain 0.200 %
$ 1796/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Yield: 324 MPa @Strain 0.200 %
- Elongation at Break: 65 %
- Reduction of Area: 67 %
$ 1493/MT
- Density: 8.25 g/cc
- Tensile Strength, Ultimate: 664 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 924 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 1047 MPa @Temperature 649 °C
- Tensile Strength, Yield: 506 MPa @Strain 0.200 %, Temperature 871 °C
$ 1623/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 995 MPa
- Tensile Strength, Yield: 715 MPa @Strain 0.200 %
- Elongation at Break: 31.8 %
- Modulus of Elasticity: 211 GPa
$ 1913/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Yield: 510 MPa @Strain 0.200 %
$ 1484/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 985 MPa
- Tensile Strength, Yield: 660 MPa @Strain 0.200 %
- Elongation at Break: 17 %
- Modulus of Elasticity: 208 GPa
$ 1509/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 975 MPa
- Tensile Strength, Yield: 570 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1810/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 483 MPa @Temperature 649 °C
- Tensile Strength, Ultimate: 501 MPa @Temperature 593 °C
- Tensile Strength, Ultimate: 521 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 543 MPa @Temperature 482 °C
$ 2049/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 696 MPa
- Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 379 MPa @Strain 0.200 %
$ 1656/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 965 MPa
- Tensile Strength, Yield: 530 MPa @Strain 0.200 %
- Elongation at Break: 44 %
- Modulus of Elasticity: 208 GPa
$ 1760/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 41 %
- Modulus of Elasticity: 211 GPa
$ 1938/MT
- Density: 9.22 g/cc
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Ultimate: 675 MPa @Temperature 540 °C
- Tensile Strength, Ultimate: 705 MPa @Temperature 425 °C
- Tensile Strength, Ultimate: 715 MPa @Temperature 650 °C
$ 2080/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 965 MPa
- Tensile Strength, Yield: 565 MPa @Strain 0.200 %
- Elongation at Break: 35 %
- Modulus of Elasticity: 218 GPa
$ 2310/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 501 MPa @Thickness 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 555 MPa @Thickness 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 724 MPa @Thickness 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 246 MPa @Thickness 12.7 mm, Temperature 538 °C
$ 2254/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 507 MPa @Temperature 649 °C
- Elongation at Break: 39.3 %
- Elongation at Break: 18.1 % @Temperature 649 °C
$ 1545/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 613 MPa @Diameter 12.7 mm, Temperature 427 °C
- Tensile Strength, Ultimate: 632 MPa @Diameter 12.7 mm, Temperature 371 °C
- Tensile Strength, Ultimate: 647 MPa @Diameter 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 651 MPa @Diameter 12.7 mm, Temperature 316 °C
$ 1512/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 258
- Hardness, Knoop: 280
- Hardness, Rockwell C: 24.4
- Hardness, Vickers: 265
$ 1516/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Yield: 524 MPa @Strain 0.200 %
$ 1755/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Yield: 435 MPa @Strain 0.200 %
- Elongation at Break: 32 %
- Modulus of Elasticity: 208 GPa
$ 1651/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 290 MPa @Temperature 870 °C
- Tensile Strength, Yield: 425 MPa
- Tensile Strength, Yield: 215 MPa @Temperature 870 °C
$ 1577/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 261
- Hardness, Knoop: 283
- Hardness, Rockwell C: 24.9
- Hardness, Vickers: 268
$ 1684/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 975 MPa
- Tensile Strength, Yield: 560 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1814/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 385 MPa @Strain 0.200 %
- Elongation at Break: 43.7 %
- Modulus of Elasticity: 211 GPa
$ 1662/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 710 MPa
- Tensile Strength, Ultimate: 372 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
- Tensile Strength, Yield: 393 MPa @Strain 0.200 %
$ 1934/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 710 MPa
- Tensile Strength, Ultimate: 524 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 552 MPa @Temperature 427 °C
- Tensile Strength, Ultimate: 572 MPa @Temperature 316 °C
$ 1768/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 565 MPa @Temperature 649 °C
- Tensile Strength, Yield: 323 MPa @Strain 0.200 %
- Elongation at Break: 46 %
$ 2241/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Yield: 720 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 208 GPa
$ 1568/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 905 MPa
- Tensile Strength, Ultimate: 330 MPa @Temperature 870 °C
- Tensile Strength, Yield: 430 MPa
- Tensile Strength, Yield: 270 MPa @Temperature 870 °C
$ 1734/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Ultimate: 469 MPa @Temperature 760 °C
$ 2299/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 585 MPa @Strain 0.200 %
- Elongation at Break: 34.2 %
- Modulus of Elasticity: 218 GPa
$ 1728/MT
- Density: 8.22 g/cc
- Hardness, Brinell: 139
- Hardness, Knoop: 186
- Hardness, Rockwell B: 98
- Hardness, Vickers: 241
$ 1552/MT
- Density: 8.22 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1600/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 1100 MPa
- Tensile Strength, Ultimate: 580 MPa @Temperature 760 °C
- Tensile Strength, Yield: 795 MPa
- Tensile Strength, Yield: 445 MPa @Temperature 760 °C
$ 1945/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1451/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 66
- Tensile Strength, Ultimate: 1004 MPa
- Tensile Strength, Yield: 742 MPa @Strain 0.200 %
- Elongation at Break: 19 %
$ 2372/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 827 MPa
- Tensile Strength, Ultimate: 624 MPa @Temperature 593 °C
- Tensile Strength, Yield: 328 MPa @Strain 0.200 %
- Elongation at Break: 49 %
$ 1516/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1715/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1480 MPa
- Tensile Strength, Yield: 1275 MPa @Strain 0.200 %
- Elongation at Break: 6.0 %
- Modulus of Elasticity: 211 GPa
$ 2028/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 796 MPa
- Tensile Strength, Yield: 340 MPa @Strain 0.200 %
- Elongation at Break: 46.8 %
- Modulus of Elasticity: 122 GPa @Temperature 1049 °C
$ 1496/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 950 MPa
- Tensile Strength, Yield: 485 MPa @Strain 0.200 %
- Elongation at Break: 45 %
- Modulus of Elasticity: 208 GPa
$ 1585/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54
- Tensile Strength, Ultimate: 852 MPa
- Tensile Strength, Yield: 354 MPa @Strain 0.200 %
- Elongation at Break: 53 %
$ 2234/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 33 %
- Modulus of Elasticity: 211 GPa
$ 1503/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 620 MPa
- Tensile Strength, Yield: 330 MPa
- Elongation at Break: 62 %
- Reduction of Area: 69 %
$ 1506/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 767 MPa
- Tensile Strength, Ultimate: 30.0 MPa @Temperature 1204 °C
- Tensile Strength, Ultimate: 41.0 MPa @Temperature 1149.0 °C
- Tensile Strength, Ultimate: 74.0 MPa @Temperature 1093 °C
$ 1831/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 980 MPa
- Tensile Strength, Yield: 525 MPa @Strain 0.200 %
- Elongation at Break: 35.7 %
- Modulus of Elasticity: 211 GPa
$ 1453/MT
- Density: 9.22 g/cc
- Tensile Strength, Ultimate: 890 MPa
- Tensile Strength, Yield: 385 MPa @Strain 0.200 %
- Elongation at Break: 60.4 %
- Modulus of Elasticity: 216 GPa
$ 1453/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 317 MPa @Strain 0.200 %
- Elongation at Break: 64 %
- Reduction of Area: 77 %
$ 2368/MT
- Density: 8.50 g/cc
- Tensile Strength, Ultimate: 582 MPa @Thickness 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 654 MPa @Thickness 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 783 MPa @Thickness 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 301 MPa @Thickness 12.7 mm, Temperature 538 °C
$ 2239/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 980 MPa
- Tensile Strength, Yield: 555 MPa @Strain 0.200 %
- Elongation at Break: 35.6 %
- Modulus of Elasticity: 211 GPa
$ 1649/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Yield: 425 MPa @Strain 0.200 %
- Elongation at Break: 46.6 %
- Modulus of Elasticity: 211 GPa
$ 1901/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 870 MPa
- Tensile Strength, Yield: 370 MPa @Strain 0.200 %
- Elongation at Break: 37 %
- Modulus of Elasticity: 211 GPa
$ 1746/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 51 %
- Modulus of Elasticity: 211 GPa
$ 1694/MT
- Tensile Strength, Ultimate: 481 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 739 MPa @Temperature 25.0 °C
- Tensile Strength, Yield: 342 MPa @Strain 0.200 %, Temperature 25.0 °C
- Tensile Strength, Yield: 401 MPa @Strain 0.200 %, Temperature 760 °C
- Elongation at Break: 27 % @Temperature 760 °C
$ 1839/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 980 MPa
- Tensile Strength, Yield: 525 MPa @Strain 0.200 %
- Elongation at Break: 35.5 %
- Modulus of Elasticity: 211 GPa
$ 2053/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 250
- Hardness, Knoop: 272
- Hardness, Rockwell C: 22.9
- Hardness, Vickers: 257
$ 2369/MT
- Density: 8.44 g/cc
- Hardness, Brinell: 422
- Hardness, Knoop: 464
- Hardness, Rockwell C: 45
- Hardness, Vickers: 446
$ 1925/MT
- Density: 8.25 g/cc
- Hardness, Brinell: 360 @Temperature 760 °C
- Hardness, Knoop: 392 @Temperature 760 °C
- Hardness, Rockwell B: 86 @Temperature 760 °C
- Hardness, Rockwell C: 39 @Temperature 760 °C
$ 1531/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Ultimate: 400 MPa @Temperature 870 °C
- Tensile Strength, Yield: 505 MPa
- Tensile Strength, Yield: 350 MPa @Temperature 870 °C
$ 1510/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 440 MPa @Strain 0.200 %
- Elongation at Break: 43 %
- Modulus of Elasticity: 211 GPa
$ 1492/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 796 MPa
- Tensile Strength, Ultimate: 525 MPa @Temperature 704 °C
- Tensile Strength, Yield: 316 MPa @Strain 0.200 %
- Elongation at Break: 46 %
$ 1918/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 863 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 920 MPa @Thickness 1.45 mm
$ 1728/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 840 MPa
- Tensile Strength, Yield: 360 MPa @Strain 0.200 %
- Elongation at Break: 55 %
- Modulus of Elasticity: 208 GPa
$ 1575/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 375
- Hardness, Knoop: 410
- Hardness, Rockwell C: 40.6
- Hardness, Vickers: 394
$ 2083/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 1140 MPa
- Tensile Strength, Yield: 845 MPa @Strain 0.200 %
- Elongation at Break: 28 %
- Modulus of Elasticity: 208 GPa
$ 1888/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Hardness, Rockwell B: 90
- Tensile Strength, Ultimate: 665 MPa @Temperature 600 °C
- Tensile Strength, Ultimate: 691 MPa @Temperature 500 °C
$ 1838/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 717 MPa
- Tensile Strength, Ultimate: 510 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 572 MPa @Temperature 260 °C
- Tensile Strength, Yield: 462 MPa @Strain 0.200 %
$ 1629/MT
- Density: 8.75 g/cc
- Tensile Strength, Ultimate: 1073 MPa
- Tensile Strength, Yield: 439 MPa @Strain 0.200 %
- Reduction of Area: 25 %
- Modulus of Elasticity: 132 GPa @Temperature 1093 °C
$ 1595/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1420 MPa
- Tensile Strength, Yield: 1331 MPa @Strain 0.200 %
$ 2207/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 460 MPa @Strain 0.200 %
- Elongation at Break: 46 %
- Modulus of Elasticity: 208 GPa
$ 1900/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 972 MPa
- Tensile Strength, Yield: 758 MPa @Strain 0.200 %
$ 1572/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1637/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 279
- Hardness, Rockwell C: 24.3
- Hardness, Vickers: 265
$ 1524/MT
- Density: 8.22 g/cc
- Hardness, Brinell: 128
- Hardness, Knoop: 172
- Hardness, Rockwell B: 90
- Hardness, Vickers: 191
$ 1501/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 843 MPa
- Tensile Strength, Yield: 353 MPa @Strain 0.200 %
- Elongation at Break: 34 %
- Reduction of Area: 28 %
$ 1582/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 1090 MPa
- Tensile Strength, Yield: 715 MPa @Strain 0.200 %
- Elongation at Break: 26.1 %
- Modulus of Elasticity: 218 GPa
$ 1581/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 990 MPa
- Tensile Strength, Yield: 635 MPa @Strain 0.200 %
- Elongation at Break: 32.9 %
- Modulus of Elasticity: 211 GPa
$ 1817/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 724 MPa @Diameter 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Ultimate: 1054 MPa @Diameter 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 455 MPa @Diameter 12.7 mm
$ 1483/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 483 MPa @Thickness 9.50 mm, Temperature 760 °C
- Tensile Strength, Ultimate: 584 MPa @Thickness 9.50 mm, Temperature 649 °C
- Tensile Strength, Ultimate: 635 MPa @Thickness 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 643 MPa @Thickness 9.50 mm, Temperature 538 °C
$ 1476/MT
- Density: 8.36 g/cc
- Tensile Strength, Ultimate: 1050 MPa
- Tensile Strength, Ultimate: 88.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 170 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 350 MPa @Temperature 870 °C
$ 1959/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 880 MPa
- Tensile Strength, Yield: 405 MPa @Strain 0.200 %
- Elongation at Break: 50 %
- Modulus of Elasticity: 208 GPa
$ 1459/MT
- Density: 8.50 g/cc
- Tensile Strength, Ultimate: 552 MPa @Diameter 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 620 MPa @Diameter 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 740 MPa @Diameter 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 377 MPa @Diameter 12.7 mm, Temperature 538 °C
$ 2001/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 348 MPa @Strain 0.200 %
- Elongation at Break: 56 %
$ 2183/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 812 MPa
- Tensile Strength, Yield: 341 MPa @Strain 0.200 %
- Elongation at Break: 40 %
- Reduction of Area: 33 %
$ 1704/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 1080 MPa
- Tensile Strength, Yield: 680 MPa @Strain 0.200 %
- Elongation at Break: 27.1 %
- Modulus of Elasticity: 218 GPa
$ 1537/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 2120/MT
- Density: 8.20 g/cc
- Tensile Strength, Ultimate: 1335 MPa
- Tensile Strength, Ultimate: 83.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 220 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 545 MPa @Temperature 870 °C
$ 1851/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 840 MPa
- Tensile Strength, Yield: 365 MPa @Strain 0.200 %
- Elongation at Break: 56 %
- Modulus of Elasticity: 208 GPa
$ 1770/MT
- Density: 9.22 g/cc
- Hardness, Brinell: 434
- Hardness, Knoop: 478
- Hardness, Rockwell C: 46
- Hardness, Vickers: 459
$ 1475/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 935 MPa
- Tensile Strength, Yield: 530 MPa @Strain 0.200 %
- Elongation at Break: 35.1 %
- Modulus of Elasticity: 218 GPa
$ 1454/MT
- Density: 8.27 g/cc
- Density: 8.29 g/cc
- Tensile Strength, Ultimate: 1152 MPa
- Tensile Strength, Ultimate: 978 MPa @Treatment Temp. 871 °C, Time 5.76e+7 sec
- Tensile Strength, Ultimate: 1006 MPa @Treatment Temp. 871 °C, Time 2.88e+7 sec
$ 2138/MT
- Density: 8.27 g/cc
- Density: 8.29 g/cc
- Hardness, Rockwell C: 30
- Tensile Strength, Ultimate: 115 MPa @Temperature 1000 °C
- Tensile Strength, Ultimate: 447 MPa @Temperature 900 °C
$ 1706/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Ultimate: 535 MPa @Temperature 760 °C
- Tensile Strength, Yield: 745 MPa
- Tensile Strength, Yield: 390 MPa @Temperature 760 °C
$ 1491/MT
- Density: 8.27 g/cc
- Density: 8.29 g/cc
- Tensile Strength, Ultimate: 170 MPa @Thickness 3.20 mm, Temperature 982 °C
- Tensile Strength, Ultimate: 532 MPa @Thickness 3.20 mm, Temperature 871 °C
- Tensile Strength, Ultimate: 829 MPa @Thickness 3.20 mm, Temperature 760 °C
$ 2057/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 1390 MPa
- Tensile Strength, Yield: 1190 MPa @Strain 0.200 %
- Elongation at Break: 7.5 %
- Modulus of Elasticity: 211 GPa
$ 2022/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
$ 1550/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 248
- Hardness, Knoop: 270
- Hardness, Rockwell C: 22.5
- Hardness, Vickers: 255
$ 1464/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 43 %
- Modulus of Elasticity: 211 GPa
$ 1453/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 440 MPa @Strain 0.200 %
- Elongation at Break: 26 %
- Modulus of Elasticity: 208 GPa
$ 1968/MT
- Density: 9.22 g/cc
- Tensile Strength, Ultimate: 885 MPa
- Tensile Strength, Ultimate: 730 MPa @Temperature 540 °C
- Tensile Strength, Ultimate: 735 MPa @Temperature 650 °C
- Tensile Strength, Ultimate: 745 MPa @Temperature 425 °C
$ 1757/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 52 @Thickness 1.45 mm
- Hardness, Rockwell A: 57 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 110 MPa @Thickness 1.10 - 1.60 mm, Temperature 1093 °C
- Tensile Strength, Ultimate: 117 MPa @Thickness 9.50 - 25.4 mm, Temperature 1093 °C
$ 1454/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 780 MPa
- Tensile Strength, Ultimate: 290 MPa @Temperature 870 °C
- Tensile Strength, Yield: 395 MPa
- Tensile Strength, Yield: 230 MPa @Temperature 870 °C
$ 2266/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 765 MPa
- Tensile Strength, Ultimate: 97.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 175 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 310 MPa @Temperature 870 °C
$ 1581/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Ultimate: 55.0 MPa @Temperature 1204 °C
- Tensile Strength, Ultimate: 79.0 MPa @Temperature 1149 °C
- Tensile Strength, Ultimate: 120 MPa @Temperature 1093 °C
$ 1951/MT
- Density: 8.23 g/cc
- Tensile Strength, Ultimate: 1395 MPa
- Tensile Strength, Ultimate: 77.0 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 145 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 420 MPa @Temperature 870 °C
$ 1941/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 460 MPa @Strain 0.200 %
- Elongation at Break: 29 %
- Modulus of Elasticity: 208 GPa
$ 1909/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 681 MPa @Thickness 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 684 MPa @Thickness 12.7 mm, Temperature 427 °C
- Tensile Strength, Ultimate: 687 MPa @Thickness 12.7 mm, Temperature 371 °C
- Tensile Strength, Ultimate: 709 MPa @Thickness 12.7 mm, Temperature 316 °C
$ 1591/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 915 MPa
- Tensile Strength, Yield: 450 MPa @Strain 0.200 %
- Elongation at Break: 37 %
- Modulus of Elasticity: 211 GPa
$ 2181/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 490 MPa
- Tensile Strength, Yield: 355 MPa
- Elongation at Break: 17 %
- Reduction of Area: 51 %
$ 1482/MT
- Density: 8.22 g/cc
- Modulus of Elasticity: 170 GPa @Temperature 649 °C
- Modulus of Elasticity: 177 GPa @Temperature 538 °C
- Modulus of Elasticity: 183 GPa @Temperature 427 °C
- Modulus of Elasticity: 189 GPa @Temperature 316 °C
$ 1768/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 758 MPa
- Tensile Strength, Yield: 496 MPa @Strain 0.200 %
$ 1617/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 708 MPa @Diameter 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Ultimate: 1062 MPa @Diameter 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 458 MPa @Diameter 12.7 mm
$ 1689/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1496/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 812 MPa
- Tensile Strength, Ultimate: 674 MPa @Temperature 538 °C
- Tensile Strength, Yield: 311 MPa @Strain 0.200 %
- Elongation at Break: 50 %
$ 1830/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Ultimate: 359 MPa @Temperature 816 °C
- Tensile Strength, Ultimate: 438 MPa @Temperature 704 °C
- Tensile Strength, Ultimate: 493 MPa @Temperature 649 °C
$ 1852/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 800 MPa
- Tensile Strength, Yield: 427 MPa @Strain 0.200 %
$ 2344/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Hardness, Rockwell B: 88
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 628 MPa @Temperature 600 °C
$ 1940/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 745 MPa @Thickness 3.20 mm
- Tensile Strength, Yield: 348 MPa @Strain 0.200 %, Thickness 3.20 mm
- Elongation at Break: 59 % @Thickness 3.20 mm
- Modulus of Elasticity: 170 GPa @Temperature 649 °C
$ 2336/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 483 MPa @Temperature 649 °C
- Tensile Strength, Ultimate: 501 MPa @Temperature 593 °C
- Tensile Strength, Ultimate: 521 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 543 MPa @Temperature 482 °C
$ 1488/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 317 MPa @Strain 0.200 %
- Elongation at Break: 60 %
- Modulus of Elasticity: 202 GPa
$ 2156/MT
- Density: 8.75 g/cc
- Tensile Strength, Ultimate: 839 MPa
- Tensile Strength, Yield: 436 MPa @Strain 0.200 %
- Reduction of Area: 33 %
- Modulus of Elasticity: 132 GPa @Temperature 1093 °C
$ 2158/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 58
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Yield: 458 MPa @Strain 0.200 %
- Elongation at Break: 19 %
$ 1762/MT
- Density: 8.86 g/cc
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Ultimate: 453 MPa @Temperature 760 °C
- Tensile Strength, Yield: 301 MPa @Strain 0.200 %
- Elongation at Break: 40 %
$ 1538/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 54
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 348 MPa @Strain 0.200 %
- Elongation at Break: 56 %
$ 1812/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Hardness, Rockwell C: 30
- Tensile Strength, Ultimate: 1232 MPa
- Tensile Strength, Ultimate: 1227 MPa @Treatment Temp. 427 °C, Time 3.60e+6 sec
$ 1909/MT
- Density: 8.50 g/cc
- Tensile Strength, Ultimate: 565 MPa @Diameter 12.7 mm, Temperature 450 °C
- Tensile Strength, Ultimate: 744 MPa @Diameter 12.7 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 386 MPa @Diameter 12.7 mm, Temperature 450 °C
- Tensile Strength, Yield: 510 MPa @Diameter 12.7 mm, Temperature 25.0 °C
$ 2135/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Ultimate: 579 MPa @Temperature 538 °C
$ 1526/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56
- Tensile Strength, Ultimate: 867 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 58 %
$ 1771/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 960 MPa
- Tensile Strength, Yield: 555 MPa @Strain 0.200 %
- Elongation at Break: 36.5 %
- Modulus of Elasticity: 211 GPa
$ 1677/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 870 MPa
- Tensile Strength, Ultimate: 310 MPa @Temperature 870 °C
- Tensile Strength, Yield: 555 MPa
- Tensile Strength, Yield: 285 MPa @Temperature 870 °C
$ 2344/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 786 MPa
- Tensile Strength, Yield: 407 MPa @Strain 0.200 %
$ 1888/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 490 MPa @Thickness 12.7 mm, Temperature 760 °C
- Tensile Strength, Ultimate: 545 MPa @Thickness 3.17 mm, Temperature 538 °C
$ 1899/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 1140 MPa
- Tensile Strength, Yield: 815 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 208 GPa
$ 1955/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 915 MPa
- Tensile Strength, Yield: 495 MPa @Strain 0.200 %
- Elongation at Break: 39.9 %
- Modulus of Elasticity: 218 GPa
$ 2133/MT
- Density: 8.83 g/cc
- Tensile Strength, Ultimate: 683 MPa @Thickness 19.1 mm, Temperature 427 °C
- Tensile Strength, Ultimate: 688 MPa @Thickness 19.1 mm, Temperature 371 °C
- Tensile Strength, Ultimate: 692 MPa @Thickness 19.1 mm, Temperature 316 °C
- Tensile Strength, Ultimate: 706 MPa @Thickness 19.1 mm, Temperature 260 °C
$ 1848/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1531 MPa
- Tensile Strength, Yield: 1393 MPa @Strain 0.200 %
$ 2343/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 850 MPa
- Tensile Strength, Yield: 370 MPa @Strain 0.200 %
- Elongation at Break: 55 %
- Modulus of Elasticity: 208 GPa
$ 1766/MT
- Density: 8.25 g/cc
- Hardness, Brinell: 318 @Temperature 760 °C
- Hardness, Knoop: 343 @Temperature 760 °C
- Hardness, Rockwell B: 97 @Temperature 760 °C
- Hardness, Rockwell C: 34 @Temperature 760 °C
$ 2358/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Yield: 297 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- Reduction of Area: 20 %
$ 1539/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 970 MPa
- Tensile Strength, Yield: 565 MPa @Strain 0.200 %
- Elongation at Break: 42 %
- Modulus of Elasticity: 208 GPa
$ 1643/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 799 MPa @Thickness 3.20 mm, Temperature 25.0 °C
- Tensile Strength, Ultimate: 1088 MPa @Thickness 3.20 mm, Temperature 25.0 °C
- Tensile Strength, Yield: 451 MPa @Strain 0.200 %, Thickness 3.20 mm
$ 1626/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56 @Thickness 12.7 mm
- Hardness, Rockwell A: 56 @Thickness 1.45 mm
- Tensile Strength, Ultimate: 877 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 914 MPa @Thickness 1.45 mm
$ 2090/MT
- Density: 9.05 g/cc
- Hardness, Brinell: 257
- Hardness, Knoop: 286
- Hardness, Rockwell C: 19
- Hardness, Vickers: 78.0 @Temperature 870 °C
$ 1675/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 896 MPa
- Tensile Strength, Yield: 641 MPa @Strain 0.200 %
$ 2479/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Ultimate: 265 MPa @Temperature 870 °C
- Tensile Strength, Yield: 525 MPa
- Tensile Strength, Yield: 250 MPa @Temperature 870 °C
$ 2187/MT
- Density: 8.08 g/cc
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Yield: 320 MPa @Strain 0.200 %
- Elongation at Break: 36 %
- Reduction of Area: 28 %
$ 1675/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 57
- Tensile Strength, Ultimate: 705 MPa
- Tensile Strength, Yield: 425 MPa @Strain 0.200 %
- Elongation at Break: 21 %
$ 1607/MT
- Density: 8.05 g/cc
- Tensile Strength, Ultimate: 1085 MPa
- Tensile Strength, Yield: 720 MPa @Strain 0.200 %
- Elongation at Break: 27.6 %
- Modulus of Elasticity: 218 GPa
$ 1890/MT
- Density: 8.97 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 350 MPa @Strain 0.200 %
- Elongation at Break: 36 %
- Modulus of Elasticity: 211 GPa
$ 1727/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 765 MPa
- Tensile Strength, Yield: 386 MPa @Strain 0.200 %
$ 1996/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 875 MPa
- Tensile Strength, Yield: 400 MPa @Strain 0.200 %
- Elongation at Break: 52 %
- Modulus of Elasticity: 208 GPa
$ 1504/MT
- Density: 8.44 g/cc
- Tensile Strength, Ultimate: 840 MPa
- Tensile Strength, Yield: 360 MPa @Strain 0.200 %
- Elongation at Break: 55 %
- Modulus of Elasticity: 208 GPa
$ 1608/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 56
- Tensile Strength, Ultimate: 883 MPa
- Tensile Strength, Yield: 399 MPa @Strain 0.200 %
- Elongation at Break: 56 %
$ 1446/MT
- Density: 8.60 g/cc
- Density: 8.64 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 822 MPa
- Tensile Strength, Ultimate: 814 MPa @Treatment Temp. 427 °C, Time 2.88e+7 sec
$ 1454/MT
- Density: 8.22 g/cc
- Tensile Strength, Ultimate: 690 MPa
- Tensile Strength, Yield: 310 MPa @Strain 0.200 %
- Elongation at Break: 65 %
- Reduction of Area: 68 %
$ 1519/MT
- Density: 8.25 g/cc
- Hardness, Brinell: 369 @Temperature 760 °C
- Hardness, Knoop: 403 @Temperature 760 °C
- Hardness, Rockwell B: 97 @Temperature 760 °C
- Hardness, Rockwell C: 40 @Temperature 760 °C
$ 1981/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 65 @Thickness 1.45 mm
- Hardness, Rockwell A: 65 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 1247 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 1276 MPa @Thickness 1.45 mm
$ 1557/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 779 MPa
- Tensile Strength, Yield: 503 MPa @Strain 0.200 %
$ 1764/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 634 MPa @Thickness 23.4 mm, Temperature 400 °C
- Tensile Strength, Ultimate: 634 MPa @Thickness 46.1 mm, Temperature 400 °C
$ 1583/MT
- Density: 8.64 g/cc
- Tensile Strength, Ultimate: 784 MPa
- Tensile Strength, Yield: 429 MPa @Strain 0.200 %
- Elongation at Break: 48 %
- Modulus of Elasticity: 211 GPa
$ 2257/MT
- Density: 8.05 g/cc
- Hardness, Brinell: 348
- Hardness, Knoop: 378
- Hardness, Rockwell C: 37.6
- Hardness, Vickers: 364
$ 1453/MT
- Density: 8.75 g/cc
- Hardness, Rockwell A: 55 @Thickness 1.45 mm
- Hardness, Rockwell A: 55 @Thickness 12.7 mm
- Tensile Strength, Ultimate: 867 MPa @Thickness 12.7 mm
- Tensile Strength, Ultimate: 898 MPa @Thickness 1.45 mm
$ 1630/MT
- Density: 8.69 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Hardness, Rockwell B: 95 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1324 MPa
- Tensile Strength, Yield: 1200 MPa @Strain 0.200 %
$ 1559/MT
- Density: 9.00 g/cc
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Yield: 470 MPa
- Elongation at Break: 23 %
- Reduction of Area: 31 %
Delivery Nickel Alloy Haynes International, Inc.
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
ships for sale greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.