Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched

Seller in Shenyang price: $1483 per MT

Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched in Nickel Alloy, Superalloy

  • Physical Properties
  • Density
  • 8.64 g/cc
  • Mechanical Properties
  • Tensile Strength, Ultimate
  • 483 MPa @Thickness 9.50 mm, Temperature 760 °C
  • Tensile Strength, Ultimate
  • 584 MPa @Thickness 9.50 mm, Temperature 649 °C
  • Tensile Strength, Ultimate
  • 635 MPa @Thickness 12.7 mm, Temperature 538 °C
  • Tensile Strength, Ultimate
  • 643 MPa @Thickness 9.50 mm, Temperature 538 °C
  • Tensile Strength, Ultimate
  • 657 MPa @Thickness 9.50 mm, Temperature 427 °C
  • Tensile Strength, Ultimate
  • 683 MPa @Thickness 6.30 mm, Temperature 427 °C
  • Tensile Strength, Ultimate
  • 688 MPa @Thickness 12.7 mm, Temperature 427 °C
  • Tensile Strength, Ultimate
  • 704 MPa @Thickness 9.50 mm, Temperature 316 °C
  • Tensile Strength, Ultimate
  • 707 MPa @Thickness 12.7 mm, Temperature 316 °C
  • Tensile Strength, Ultimate
  • 712 MPa @Thickness 6.30 mm, Temperature 316 °C
  • Tensile Strength, Ultimate
  • 717 MPa @Thickness 6.30 mm, Temperature 204 °C
  • Tensile Strength, Ultimate
  • 725 MPa @Thickness 12.7 mm, Temperature 204 °C
  • Tensile Strength, Ultimate
  • 727 MPa @Thickness 9.50 mm, Temperature 204 °C
  • Tensile Strength, Ultimate
  • 765 MPa @Thickness 12.7 mm, Temperature 93.0 °C
  • Tensile Strength, Ultimate
  • 767 MPa @Thickness 6.30 mm, Temperature 20.0 °C
  • Tensile Strength, Ultimate
  • 791 MPa @Thickness 9.50 mm, Temperature 20.0 °C
  • Tensile Strength, Ultimate
  • 805 MPa @Thickness 12.7 mm, Temperature 20.0 °C
  • Tensile Strength, Yield
  • 205 MPa @Thickness 12.7 mm, Temperature 538 °C
  • Tensile Strength, Yield
  • 211 MPa @Thickness 9.50 mm, Temperature 760 °C
  • Tensile Strength, Yield
  • 217 MPa @Thickness 9.50 mm, Temperature 649 °C
  • Tensile Strength, Yield
  • 228 MPa @Thickness 9.50 mm, Temperature 538 °C
  • Tensile Strength, Yield
  • 236 MPa @Thickness 12.7 mm, Temperature 427 °C
  • Tensile Strength, Yield
  • 247 MPa @Thickness 12.7 mm, Temperature 316 °C
  • Tensile Strength, Yield
  • 255 MPa @Thickness 6.30 mm, Temperature 427 °C
  • Tensile Strength, Yield
  • 258 MPa @Thickness 9.50 mm, Temperature 427 °C
  • Tensile Strength, Yield
  • 264 MPa @Thickness 12.7 mm, Temperature 204 °C
  • Tensile Strength, Yield
  • 270 MPa @Thickness 9.50 mm, Temperature 316 °C
  • Tensile Strength, Yield
  • 281 MPa @Thickness 6.30 mm, Temperature 316 °C
  • Tensile Strength, Yield
  • 295 MPa @Thickness 6.30 mm, Temperature 204 °C
  • Tensile Strength, Yield
  • 301 MPa @Thickness 9.50 mm, Temperature 204 °C
  • Tensile Strength, Yield
  • 301 MPa @Thickness 12.7 mm, Temperature 93.0 °C
  • Tensile Strength, Yield
  • 335 MPa @Thickness 12.7 mm, Temperature 20.0 °C
  • Tensile Strength, Yield
  • 336 MPa @Thickness 6.30 mm, Temperature 20.0 °C
  • Tensile Strength, Yield
  • 356 MPa @Thickness 9.50 mm, Temperature 20.0 °C
  • Elongation at Break
  • 52 % @Thickness 9.50 mm, Temperature 538 °C
  • Elongation at Break
  • 52 % @Thickness 9.50 mm, Temperature 649 °C
  • Elongation at Break
  • 54 % @Thickness 6.30 mm, Temperature 204 °C
  • Elongation at Break
  • 55 % @Thickness 6.30 mm, Temperature 316 °C
  • Elongation at Break
  • 56 % @Thickness 9.50 mm, Temperature 204 °C
  • Elongation at Break
  • 58 % @Thickness 6.30 mm, Temperature 20.0 °C
  • Elongation at Break
  • 59 % @Thickness 9.50 mm, Temperature 20.0 °C
  • Elongation at Break
  • 59 % @Thickness 9.50 mm, Temperature 316 °C
  • Elongation at Break
  • 60 % @Thickness 6.30 mm, Temperature 427 °C
  • Elongation at Break
  • 61 % @Thickness 12.7 mm, Temperature 204 °C
  • Elongation at Break
  • 62 % @Thickness 9.50 mm, Temperature 427 °C
  • Elongation at Break
  • 63 % @Thickness 12.7 mm, Temperature 20.0 °C
  • Elongation at Break
  • 63 % @Thickness 9.50 mm, Temperature 760 °C
  • Elongation at Break
  • 65 % @Thickness 12.7 mm, Temperature 316 °C
  • Elongation at Break
  • 66 % @Thickness 12.7 mm, Temperature 427 °C
  • Elongation at Break
  • 70 % @Thickness 12.7 mm, Temperature 93.0 °C
  • Elongation at Break
  • 71 % @Thickness 12.7 mm, Temperature 538 °C
  • Modulus of Elasticity
  • 211 GPa
  • Modulus of Elasticity
  • 141 GPa @Temperature 982 °C
  • Modulus of Elasticity
  • 152 GPa @Temperature 871 °C
  • Modulus of Elasticity
  • 162 GPa @Temperature 760 °C
  • Modulus of Elasticity
  • 171 GPa @Temperature 649 °C
  • Modulus of Elasticity
  • 179 GPa @Temperature 538 °C
  • Modulus of Elasticity
  • 187 GPa @Temperature 427 °C
  • Modulus of Elasticity
  • 194 GPa @Temperature 316 °C
  • Modulus of Elasticity
  • 201 GPa @Temperature 204 °C
  • Modulus of Elasticity
  • 207 GPa @Temperature 93.0 °C
  • Electrical Properties
  • Electrical Resistivity
  • 0.000125 ohm-cm @Temperature 100 °C
  • Electrical Resistivity
  • 0.000125 ohm-cm @Temperature 23.0 °C
  • Electrical Resistivity
  • 0.000126 ohm-cm @Temperature 200 °C
  • Electrical Resistivity
  • 0.000127 ohm-cm @Temperature 300 °C
  • Electrical Resistivity
  • 0.000128 ohm-cm @Temperature 400 °C
  • Electrical Resistivity
  • 0.000129 ohm-cm @Temperature 500 °C
  • Electrical Resistivity
  • 0.000132 ohm-cm @Temperature 600 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched

Seller from Shenyang – 2021-05-21:

Seller from Shenyang work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1483 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Towing equipment provider in Singapore open-nearme.com