Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened

Seller in Hyderabad price: $2165 per MT
Seller in Dhaka price: $2138 per MT

Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened in Nickel Alloy

  • Physical Properties
  • Density
  • 8.27 g/cc
  • Density
  • 8.29 g/cc
  • Mechanical Properties
  • Hardness, Rockwell C
  • 30
  • Tensile Strength, Ultimate
  • 115 MPa @Temperature 1000 °C
  • Tensile Strength, Ultimate
  • 447 MPa @Temperature 900 °C
  • Tensile Strength, Ultimate
  • 730 MPa @Temperature 800 °C
  • Tensile Strength, Ultimate
  • 945 MPa @Temperature 700 °C
  • Tensile Strength, Ultimate
  • 980 MPa @Temperature 600 °C
  • Tensile Strength, Ultimate
  • 1132 MPa @Temperature 25.0 °C
  • Tensile Strength, Yield
  • 75.0 MPa @Strain 0.200 %, Temperature 1000 °C
  • Tensile Strength, Yield
  • 396 MPa @Strain 0.200 %, Temperature 900 °C
  • Tensile Strength, Yield
  • 580 MPa @Strain 0.200 %, Temperature 800 °C
  • Tensile Strength, Yield
  • 625 MPa @Strain 0.200 %, Temperature 700 °C
  • Tensile Strength, Yield
  • 631 MPa @Strain 0.200 %, Temperature 600 °C
  • Tensile Strength, Yield
  • 699 MPa @Strain 0.200 %, Temperature 25.0 °C
  • Elongation at Break
  • 23 % @Temperature 800 °C
  • Elongation at Break
  • 24 % @Temperature 700 °C
  • Elongation at Break
  • 30.0 % @Temperature 25.0 °C
  • Elongation at Break
  • 31 % @Temperature 600 °C
  • Elongation at Break
  • 34 % @Temperature 900 °C
  • Elongation at Break
  • 64 % @Temperature 1000 °C
  • Creep Strength
  • 12.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
  • Creep Strength
  • 25.0 MPa @Temperature 982 °C, Time 360000 sec
  • Creep Strength
  • 29.0 MPa @Temperature 927 °C, Time 3.60e+6 sec
  • Creep Strength
  • 57.0 MPa @Temperature 927 °C, Time 360000 sec
  • Creep Strength
  • 62.0 MPa @Temperature 871 °C, Time 3.60e+6 sec
  • Creep Strength
  • 117 MPa @Temperature 871 °C, Time 360000 sec
  • Creep Strength
  • 124 MPa @Temperature 816 °C, Time 3.60e+6 sec
  • Creep Strength
  • 207 MPa @Temperature 816 °C, Time 360000 sec
  • Creep Strength
  • 228 MPa @Temperature 760 °C, Time 3.60e+6 sec
  • Creep Strength
  • 317 MPa @Temperature 760 °C, Time 360000 sec
  • Creep Strength
  • 352 MPa @Temperature 704 °C, Time 3.60e+6 sec
  • Creep Strength
  • 483 MPa @Temperature 704 °C, Time 360000 sec
  • Creep Strength
  • 538 MPa @Temperature 649 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 17.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 38.0 MPa @Temperature 982 °C, Time 360000 sec
  • Rupture Strength
  • 41.0 MPa @Temperature 927 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 83.0 MPa @Temperature 871 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 83.0 MPa @Temperature 927 °C, Time 360000 sec
  • Rupture Strength
  • 152 MPa @Temperature 871 °C, Time 360000 sec
  • Rupture Strength
  • 159 MPa @Temperature 816 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 225 MPa @Temperature 816 °C, Time 360000 sec
  • Rupture Strength
  • 262 MPa @Temperature 760 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 386 MPa @Temperature 704 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 386 MPa @Temperature 760 °C, Time 360000 sec
  • Rupture Strength
  • 517 MPa @Temperature 704 °C, Time 360000 sec
  • Rupture Strength
  • 552 MPa @Temperature 649 °C, Time 3.60e+6 sec
  • Modulus of Elasticity
  • 140 GPa @Temperature 1000 °C
  • Modulus of Elasticity
  • 154 GPa @Temperature 900 °C
  • Modulus of Elasticity
  • 166 GPa @Temperature 800 °C
  • Modulus of Elasticity
  • 175 GPa @Temperature 700 °C
  • Modulus of Elasticity
  • 183 GPa @Temperature 600 °C
  • Modulus of Elasticity
  • 190 GPa @Temperature 500 °C
  • Modulus of Elasticity
  • 196 GPa @Temperature 400 °C
  • Modulus of Elasticity
  • 202 GPa @Temperature 300 °C
  • Modulus of Elasticity
  • 209 GPa @Temperature 200 °C
  • Modulus of Elasticity
  • 213 GPa @Temperature 100 °C
  • Modulus of Elasticity
  • 217 GPa @Temperature 25.0 °C
  • Poissons Ratio
  • 0.319 @Temperature 25.0 °C
  • Poissons Ratio
  • 0.326 @Temperature 100 °C
  • Poissons Ratio
  • 0.335 @Temperature 200 °C
  • Poissons Ratio
  • 0.335 @Temperature 300 °C
  • Poissons Ratio
  • 0.337 @Temperature 400 °C
  • Poissons Ratio
  • 0.341 @Temperature 500 °C
  • Poissons Ratio
  • 0.346 @Temperature 600 °C
  • Poissons Ratio
  • 0.352 @Temperature 700 °C
  • Poissons Ratio
  • 0.355 @Temperature 800 °C
  • Poissons Ratio
  • 0.357 @Temperature 900 °C
  • Poissons Ratio
  • 0.363 @Temperature 1000 °C
  • Shear Modulus
  • 51.0 GPa @Temperature 1000 °C
  • Shear Modulus
  • 57.0 GPa @Temperature 900 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, bulk cargo ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened

Seller from Hyderabad – 2021-03-01:

Seller from Hyderabad work with company: 3M, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2165 per MT

Seller from Dhaka – 2021-03-23:

Seller from Dhaka work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2138 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Basketball court in Singapore open-nearme.com