Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed price 2133 per MT

Physical Properties
Density
8.83 g/cc

Mechanical Properties
Tensile Strength, Ultimate
683 MPa @Thickness 19.1 mm, Temperature 427 °C
Tensile Strength, Ultimate
688 MPa @Thickness 19.1 mm, Temperature 371 °C
Tensile Strength, Ultimate
692 MPa @Thickness 19.1 mm, Temperature 316 °C
Tensile Strength, Ultimate
706 MPa @Thickness 19.1 mm, Temperature 260 °C
Tensile Strength, Ultimate
723 MPa @Thickness 19.1 mm, Temperature 204 °C
Tensile Strength, Ultimate
749 MPa @Thickness 19.1 mm, Temperature 149 °C
Tensile Strength, Ultimate
778 MPa @Thickness 19.1 mm, Temperature 93.0 °C
Tensile Strength, Ultimate
809 MPa @Thickness 19.1 mm, Temperature 25.0 °C
Tensile Strength, Yield
225 MPa @Thickness 19.1 mm, Temperature 427 °C
Tensile Strength, Yield
240 MPa @Thickness 19.1 mm, Temperature 371 °C
Tensile Strength, Yield
245 MPa @Thickness 19.1 mm, Temperature 316 °C
Tensile Strength, Yield
246 MPa @Thickness 19.1 mm, Temperature 260 °C
Tensile Strength, Yield
268 MPa @Thickness 19.1 mm, Temperature 204 °C
Tensile Strength, Yield
294 MPa @Thickness 19.1 mm, Temperature 149 °C
Tensile Strength, Yield
327 MPa @Thickness 19.1 mm, Temperature 93.0 °C
Tensile Strength, Yield
362 MPa @Thickness 19.1 mm, Temperature 25.0 °C
Elongation at Break
70.5 % @Thickness 19.1 mm, Temperature 25.0 °C
Elongation at Break
71.1 % @Thickness 19.1 mm, Temperature 316 °C
Elongation at Break
74 % @Thickness 19.1 mm, Temperature 371 °C
Elongation at Break
74.6 % @Thickness 19.1 mm, Temperature 204 °C
Elongation at Break
74.7 % @Thickness 19.1 mm, Temperature 260 °C
Elongation at Break
74.8 % @Thickness 19.1 mm, Temperature 93.0 °C
Elongation at Break
74.8 % @Thickness 19.1 mm, Temperature 149 °C
Elongation at Break
76.3 % @Thickness 19.1 mm, Temperature 427 °C
Modulus of Elasticity
188 GPa @Temperature 600 °C
Modulus of Elasticity
191 GPa @Temperature 500 °C
Modulus of Elasticity
197 GPa @Temperature 400 °C
Modulus of Elasticity
200 GPa @Temperature 300 °C
Modulus of Elasticity
205 GPa @Temperature 200 °C
Modulus of Elasticity
211 GPa @Temperature 100 °C
Modulus of Elasticity
217 GPa @Temperature 25.0 °C
Charpy Impact
347 J @Temperature -196 °C
Charpy Impact
>= 358 J @Temperature 25.0 °C
Charpy Impact
>= 358 J @Temperature 25.0 °C
Charpy Impact
>= 358 J @Temperature -196 °C

Thermal Properties
CTE, linear
11.5 µm/m-°C @Temperature 25.0 - 100 °C
CTE, linear
11.9 µm/m-°C @Temperature 25.0 - 200 °C
CTE, linear
12.2 µm/m-°C @Temperature 25.0 - 300 °C
CTE, linear
12.5 µm/m-°C @Temperature 25.0 - 400 °C
CTE, linear
12.7 µm/m-°C @Temperature 25.0 - 500 °C
CTE, linear
12.7 µm/m-°C @Temperature 25.0 - 600 °C
Specific Heat Capacity
0.403 J/g-°C @Temperature 25.0 °C
Specific Heat Capacity
0.416 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.429 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.439 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.449 J/g-°C @Temperature 400 °C
Specific Heat Capacity
0.457 J/g-°C @Temperature 600 °C
Specific Heat Capacity
0.461 J/g-°C @Temperature 500 °C
Thermal Conductivity
9.30 W/m-K @Temperature 25.0 °C
Thermal Conductivity
10.5 W/m-K @Temperature 100 °C
Thermal Conductivity
11.9 W/m-K @Temperature 200 °C
Thermal Conductivity
13.5 W/m-K @Temperature 300 °C
Thermal Conductivity
14.9 W/m-K @Temperature 400 °C
Thermal Conductivity
16.4 W/m-K @Temperature 500 °C
Thermal Conductivity
17.5 W/m-K @Temperature 600 °C
Maximum Service Temperature, Air
427 °C

Component Elements Properties
Aluminum, Al
<= 0.50 %
Carbon, C
<= 0.010 %
Chromium, Cr
15 %
Iron, Fe
<= 1.25 %

Electrical Properties
Electrical Resistivity
0.000126 ohm-cm @Temperature 25.0 °C
Electrical Resistivity
0.000127 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.000127 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.000128 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000128 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000129 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000131 ohm-cm @Temperature 600 °C

Alternative products

Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed accurate 99%

$ 1570/MT

Density: 8.83 g/cc
Tensile Strength, Ultimate: 745 MPa @Thickness 3.20 mm, Temperature 316 °C
Tensile Strength, Ultimate: 747 MPa @Thickness 3.20 mm, Temperature 371 °C
Tensile Strength, Ultimate: 754 MPa @Thickness 3.20 mm, Temperature 260 °C
Tensile Strength, Ultimate: 763 MPa @Thickness 3.20 mm, Temperature 204 °C

Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed accurate 99%

$ 1656/MT

Density: 8.83 g/cc
Tensile Strength, Ultimate: 705 MPa @Thickness 25.4 mm, Temperature 427 °C
Tensile Strength, Ultimate: 712 MPa @Thickness 25.4 mm, Temperature 371 °C
Tensile Strength, Ultimate: 714 MPa @Thickness 25.4 mm, Temperature 316 °C
Tensile Strength, Ultimate: 725 MPa @Thickness 25.4 mm, Temperature 260 °C

Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform accurate 99%

$ 1545/MT

Density: 8.83 g/cc
Tensile Strength, Ultimate: 613 MPa @Diameter 12.7 mm, Temperature 427 °C
Tensile Strength, Ultimate: 632 MPa @Diameter 12.7 mm, Temperature 371 °C
Tensile Strength, Ultimate: 647 MPa @Diameter 12.7 mm, Temperature 260 °C
Tensile Strength, Ultimate: 651 MPa @Diameter 12.7 mm, Temperature 316 °C

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed accurate 99%

$ 1888/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Hardness, Rockwell B: 90
Tensile Strength, Ultimate: 665 MPa @Temperature 600 °C
Tensile Strength, Ultimate: 691 MPa @Temperature 500 °C

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform accurate 99%

$ 1817/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Tensile Strength, Ultimate: 724 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Ultimate: 1054 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Yield: 455 MPa @Diameter 12.7 mm

Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate accurate 99%

$ 1909/MT

Density: 8.83 g/cc
Tensile Strength, Ultimate: 681 MPa @Thickness 12.7 mm, Temperature 260 °C
Tensile Strength, Ultimate: 684 MPa @Thickness 12.7 mm, Temperature 427 °C
Tensile Strength, Ultimate: 687 MPa @Thickness 12.7 mm, Temperature 371 °C
Tensile Strength, Ultimate: 709 MPa @Thickness 12.7 mm, Temperature 316 °C

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 99%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform accurate 99%

$ 1617/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Tensile Strength, Ultimate: 708 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Ultimate: 1062 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Yield: 458 MPa @Diameter 12.7 mm

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet accurate 99%

$ 1643/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Tensile Strength, Ultimate: 799 MPa @Thickness 3.20 mm, Temperature 25.0 °C
Tensile Strength, Ultimate: 1088 MPa @Thickness 3.20 mm, Temperature 25.0 °C
Tensile Strength, Yield: 451 MPa @Strain 0.200 %, Thickness 3.20 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, tanker vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed

Seller from Shanghai – 2021-05-17:

Seller from Shanghai work with company: Solvay, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2133 per MT