Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed

Seller in Mexico City price: $1656 per MT

Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed in Nickel Alloy

  • Physical Properties
  • Density
  • 8.83 g/cc
  • Mechanical Properties
  • Tensile Strength, Ultimate
  • 705 MPa @Thickness 25.4 mm, Temperature 427 °C
  • Tensile Strength, Ultimate
  • 712 MPa @Thickness 25.4 mm, Temperature 371 °C
  • Tensile Strength, Ultimate
  • 714 MPa @Thickness 25.4 mm, Temperature 316 °C
  • Tensile Strength, Ultimate
  • 725 MPa @Thickness 25.4 mm, Temperature 260 °C
  • Tensile Strength, Ultimate
  • 743 MPa @Thickness 25.4 mm, Temperature 204 °C
  • Tensile Strength, Ultimate
  • 769 MPa @Thickness 25.4 mm, Temperature 149 °C
  • Tensile Strength, Ultimate
  • 798 MPa @Thickness 25.4 mm, Temperature 93.0 °C
  • Tensile Strength, Ultimate
  • 832 MPa @Thickness 25.4 mm, Temperature 25.0 °C
  • Tensile Strength, Yield
  • 252 MPa @Thickness 25.4 mm, Temperature 371 °C
  • Tensile Strength, Yield
  • 256 MPa @Thickness 25.4 mm, Temperature 316 °C
  • Tensile Strength, Yield
  • 256 MPa @Thickness 25.4 mm, Temperature 427 °C
  • Tensile Strength, Yield
  • 273 MPa @Thickness 25.4 mm, Temperature 260 °C
  • Tensile Strength, Yield
  • 289 MPa @Thickness 25.4 mm, Temperature 204 °C
  • Tensile Strength, Yield
  • 311 MPa @Thickness 25.4 mm, Temperature 149 °C
  • Tensile Strength, Yield
  • 347 MPa @Thickness 25.4 mm, Temperature 93.0 °C
  • Tensile Strength, Yield
  • 385 MPa @Thickness 25.4 mm, Temperature 25.0 °C
  • Elongation at Break
  • 63 % @Thickness 25.4 mm, Temperature 25.0 °C
  • Elongation at Break
  • 72 % @Thickness 25.4 mm, Temperature 316 °C
  • Elongation at Break
  • 72 % @Thickness 25.4 mm, Temperature 371 °C
  • Elongation at Break
  • 72.1 % @Thickness 25.4 mm, Temperature 204 °C
  • Elongation at Break
  • 72.7 % @Thickness 25.4 mm, Temperature 260 °C
  • Elongation at Break
  • 72.8 % @Thickness 25.4 mm, Temperature 149 °C
  • Elongation at Break
  • 73.6 % @Thickness 25.4 mm, Temperature 93.0 °C
  • Elongation at Break
  • 74.1 % @Thickness 25.4 mm, Temperature 427 °C
  • Modulus of Elasticity
  • 188 GPa @Temperature 600 °C
  • Modulus of Elasticity
  • 191 GPa @Temperature 500 °C
  • Modulus of Elasticity
  • 197 GPa @Temperature 400 °C
  • Modulus of Elasticity
  • 200 GPa @Temperature 300 °C
  • Modulus of Elasticity
  • 205 GPa @Temperature 200 °C
  • Modulus of Elasticity
  • 211 GPa @Temperature 100 °C
  • Modulus of Elasticity
  • 217 GPa @Temperature 25.0 °C
  • Thermal Properties
  • CTE, linear
  • 11.5 µm/m-°C @Temperature 25.0 - 100 °C
  • CTE, linear
  • 11.9 µm/m-°C @Temperature 25.0 - 200 °C
  • CTE, linear
  • 12.2 µm/m-°C @Temperature 25.0 - 300 °C
  • CTE, linear
  • 12.5 µm/m-°C @Temperature 25.0 - 400 °C
  • CTE, linear
  • 12.7 µm/m-°C @Temperature 25.0 - 500 °C
  • CTE, linear
  • 12.7 µm/m-°C @Temperature 25.0 - 600 °C
  • Specific Heat Capacity
  • 0.403 J/g-°C @Temperature 25.0 °C
  • Specific Heat Capacity
  • 0.416 J/g-°C @Temperature 100 °C
  • Specific Heat Capacity
  • 0.429 J/g-°C @Temperature 200 °C
  • Specific Heat Capacity
  • 0.439 J/g-°C @Temperature 300 °C
  • Specific Heat Capacity
  • 0.449 J/g-°C @Temperature 400 °C
  • Specific Heat Capacity
  • 0.457 J/g-°C @Temperature 600 °C
  • Specific Heat Capacity
  • 0.461 J/g-°C @Temperature 500 °C
  • Thermal Conductivity
  • 9.30 W/m-K @Temperature 25.0 °C
  • Thermal Conductivity
  • 10.5 W/m-K @Temperature 100 °C
  • Thermal Conductivity
  • 11.9 W/m-K @Temperature 200 °C
  • Thermal Conductivity
  • 13.5 W/m-K @Temperature 300 °C
  • Thermal Conductivity
  • 14.9 W/m-K @Temperature 400 °C
  • Thermal Conductivity
  • 16.4 W/m-K @Temperature 500 °C
  • Thermal Conductivity
  • 17.5 W/m-K @Temperature 600 °C
  • Maximum Service Temperature, Air
  • 427 °C
  • Component Elements Properties
  • Aluminum, Al
  • <= 0.50 %
  • Carbon, C
  • <= 0.010 %
  • Chromium, Cr
  • 15 %
  • Iron, Fe
  • <= 1.25 %
  • Manganese, Mn
  • 0.25 %
  • Molybdenum, Mo
  • 22 %
  • Nickel, Ni
  • 60.91 %
  • Silicon, Si
  • <= 0.080 %
  • Electrical Properties
  • Electrical Resistivity
  • 0.000126 ohm-cm @Temperature 25.0 °C
  • Electrical Resistivity
  • 0.000127 ohm-cm @Temperature 100 °C
  • Electrical Resistivity
  • 0.000127 ohm-cm @Temperature 200 °C
  • Electrical Resistivity
  • 0.000128 ohm-cm @Temperature 300 °C
  • Electrical Resistivity
  • 0.000128 ohm-cm @Temperature 400 °C
  • Electrical Resistivity
  • 0.000129 ohm-cm @Temperature 500 °C
  • Electrical Resistivity
  • 0.000131 ohm-cm @Temperature 600 °C
  • Descriptive Properties
  • Thermal Diffusivity
  • 0.0264 cm/s
  • Thermal Diffusivity
  • 0.0291 cm/s
  • Thermal Diffusivity
  • 0.0319 cm/s
  • Thermal Diffusivity
  • 0.0352 cm/s
  • Thermal Diffusivity
  • 0.0382 cm/s
  • Thermal Diffusivity
  • 0.0412 cm/s

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, general cargo for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed

Seller from Mexico City – 2021-08-15:

Seller from Mexico City work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1656 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Lexus dealer in Singapore open-nearme.com