Haynes Hastelloy® B-3® alloy, 10% cold work price 1527 per MT

Physical Properties
Density
9.22 g/cc

Mechanical Properties
Hardness, Brinell
290
Hardness, Knoop
311
Hardness, Rockwell C
30
Hardness, Vickers
301
Tensile Strength, Ultimate
965 MPa
Tensile Strength, Yield
690 MPa @Strain 0.200 %
Elongation at Break
40 %
Modulus of Elasticity
216 GPa
Modulus of Elasticity
147 GPa @Temperature 1000 °C
Modulus of Elasticity
157 GPa @Temperature 900 °C
Modulus of Elasticity
168 GPa @Temperature 800 °C
Modulus of Elasticity
178 GPa @Temperature 700 °C
Modulus of Elasticity
185 GPa @Temperature 600 °C
Modulus of Elasticity
190 GPa @Temperature 500 °C
Modulus of Elasticity
197 GPa @Temperature 400 °C
Modulus of Elasticity
202 GPa @Temperature 300 °C
Modulus of Elasticity
208 GPa @Temperature 200 °C
Modulus of Elasticity
213 GPa @Temperature 100 °C

Thermal Properties
CTE, linear
11.4 µm/m-°C @Temperature 25.0 - 300 °C
CTE, linear
11.6 µm/m-°C @Temperature 25.0 - 400 °C
CTE, linear
11.8 µm/m-°C @Temperature 25.0 - 600 °C
CTE, linear
11.8 µm/m-°C @Temperature 25.0 - 500 °C
CTE, linear
12.2 µm/m-°C @Temperature 25.0 - 700 °C
CTE, linear
13.1 µm/m-°C @Temperature 25.0 - 800 °C
CTE, linear
13.9 µm/m-°C @Temperature 25.0 - 900 °C
CTE, linear
14.4 µm/m-°C @Temperature 25.0 - 1000 °C
Specific Heat Capacity
0.373 J/g-°C
Specific Heat Capacity
0.382 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.409 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.421 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.431 J/g-°C @Temperature 400 °C
Specific Heat Capacity
0.434 J/g-°C @Temperature 600 °C
Specific Heat Capacity
0.436 J/g-°C @Temperature 500 °C
Specific Heat Capacity
0.575 J/g-°C @Temperature 1000 °C
Specific Heat Capacity
0.577 J/g-°C @Temperature 900 °C
Specific Heat Capacity
0.589 J/g-°C @Temperature 800 °C
Specific Heat Capacity
0.595 J/g-°C @Temperature 700 °C
Thermal Conductivity
11.2 W/m-K
Thermal Conductivity
12.1 W/m-K @Temperature 100 °C
Thermal Conductivity
13.4 W/m-K @Temperature 200 °C
Thermal Conductivity
14.8 W/m-K @Temperature 300 °C
Thermal Conductivity
16.3 W/m-K @Temperature 400 °C
Thermal Conductivity
17.9 W/m-K @Temperature 500 °C
Thermal Conductivity
19.6 W/m-K @Temperature 600 °C
Thermal Conductivity
21.4 W/m-K @Temperature 700 °C
Thermal Conductivity
21.4 W/m-K @Temperature 800 °C
Thermal Conductivity
23.3 W/m-K @Temperature 900 °C
Thermal Conductivity
27.5 W/m-K @Temperature 1000 °C
Melting Point
1370 - 1418 °C
Solidus
1370 °C
Liquidus
1418 °C

Component Elements Properties
Aluminum, Al
<= 0.50 %
Carbon, C
<= 0.010 %
Chromium, Cr
1.5 %
Cobalt, Co
<= 3.0 %
Iron, Fe
1.5 %
Manganese, Mn
<= 3.0 %
Molybdenum, Mo
28.5 %
Nickel, Ni
>= 65 %

Electrical Properties
Electrical Resistivity
0.000137 ohm-cm
Electrical Resistivity
0.000130 ohm-cm @Temperature 1000 °C
Electrical Resistivity
0.000132 ohm-cm @Temperature 900 °C
Electrical Resistivity
0.000137 ohm-cm @Temperature 800 °C
Electrical Resistivity
0.000137 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.000137 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.000138 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000138 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000140 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000142 ohm-cm @Temperature 700 °C
Electrical Resistivity
0.000143 ohm-cm @Temperature 600 °C

Alternative products

Osprey Metals Co 400 Cobalt Thermal Spray Powder accurate 79%

$ 1667/MT

Hardness, Rockwell C: 51 - 58
Carbon, C: 0.080 %
Carbon, C: <= 0.10 %
Chromium, Cr: 7.0 - 9.0 %
Cobalt, Co: 57.32 %

Osprey Metals HTN 2 Brazing Powder accurate 59%

$ 1550/MT

Melting Point: 970 - 1000 °C
Solidus: 970 °C
Liquidus: 1000 °C
Aluminum, Al: <= 0.050 %
Boron, B: 2.75 - 3.15 %

Osprey Metals HTN 4 Brazing Powder accurate 59%

$ 1492/MT

Melting Point: 980 - 1070 °C
Solidus: 980 °C
Liquidus: 1070 °C
Aluminum, Al: <= 0.050 %
Boron, B: 1.5 - 2.2 %

Crucible Compaction Metals P/M 625 Corrosion Resistant Alloy accurate 79%

$ 1926/MT

Environmental Stress Crack Resistance: 336 hour
Environmental Stress Crack Resistance: 720 hour
Environmental Stress Crack Resistance: 4320 hour
Tensile Strength, Ultimate: 850 MPa
Tensile Strength, Ultimate: 1010 MPa

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed accurate 59%

$ 1888/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Hardness, Rockwell B: 90
Tensile Strength, Ultimate: 665 MPa @Temperature 600 °C
Tensile Strength, Ultimate: 691 MPa @Temperature 500 °C

Special Metals NIMONIC® Alloy 81 accurate 99%

$ 1911/MT

Density: 8.06 g/cc
Tensile Strength, Ultimate: 830 MPa @Temperature 650 °C
Tensile Strength, Ultimate: 1050 MPa @Temperature 23.0 °C
Tensile Strength, Yield: 600 MPa @Strain 0.200 %
Tensile Strength, Yield: 520 MPa @Strain 0.200 %, Temperature 650 °C

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 79%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

Latrobe LSSâ„¢ 135M Nitriding Steel (ASTM A355 Class A) accurate 99%

$ 1566/MT

Specific Gravity: 7.86 g/cc
Density: 7.86 g/cc
Hardness, Rockwell C: 22
Hardness, Rockwell C: 27
Hardness, Rockwell C: 30

ATI Allegheny Ludlum Altemp® A286 Iron-Base Superalloy, UNS S66286 accurate 59%

$ 1686/MT

Density: 7.92 g/cc
Hardness, Rockwell B: 85
Tensile Strength, Ultimate: 620 MPa
Tensile Strength, Yield: 275 MPa
Elongation at Break: 40 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale nl. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Haynes Hastelloy® B-3® alloy, 10% cold work

Seller from Dallas – 2021-04-28:

Seller from Dallas work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1527 per MT

Seller from Toronto – 2021-05-08:

Seller from Toronto work with company: Solvay, SABIC Innovative Plastics (GE Plastics), Dow Chemical, ALIMEX GmbH

Price: $1565 per MT

Seller from Baghdad – 2021-08-02:

Seller from Baghdad work with company: RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1821 per MT

Seller from Barcelona – 2021-06-05:

Seller from Barcelona work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1535 per MT