Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C price 1595 per MT

Physical Properties
Density
8.69 g/cc

Mechanical Properties
Hardness, Rockwell B
93 @Temperature 23.0 °C
Hardness, Rockwell B
95 @Temperature 23.0 °C
Tensile Strength, Ultimate
1420 MPa
Tensile Strength, Yield
1331 MPa @Strain 0.200 %
Elongation at Break
15 %
Modulus of Elasticity
206 GPa
Modulus of Elasticity
145 GPa @Temperature 982 °C
Modulus of Elasticity
154 GPa @Temperature 871 °C
Modulus of Elasticity
163 GPa @Temperature 760 °C
Modulus of Elasticity
171 GPa @Temperature 649 °C
Modulus of Elasticity
177 GPa @Temperature 538 °C
Modulus of Elasticity
183 GPa @Temperature 427 °C
Modulus of Elasticity
190 GPa @Temperature 316 °C
Modulus of Elasticity
196 GPa @Temperature 204 °C
Modulus of Elasticity
203 GPa @Temperature 93.0 °C

Thermal Properties
CTE, linear
12.4 µm/m-°C @Temperature 24.0 - 93.0 °C
CTE, linear
12.4 µm/m-°C @Temperature 24.0 - 204 °C
CTE, linear
12.6 µm/m-°C @Temperature 24.0 - 316 °C
CTE, linear
13.3 µm/m-°C @Temperature 24.0 - 427 °C
CTE, linear
13.9 µm/m-°C @Temperature 24.0 - 538 °C
CTE, linear
14.6 µm/m-°C @Temperature 24.0 - 649 °C
CTE, linear
15.3 µm/m-°C @Temperature 24.0 - 760 °C
CTE, linear
15.8 µm/m-°C @Temperature 24.0 - 871 °C
CTE, linear
16.2 µm/m-°C @Temperature 24.0 - 982 °C
Specific Heat Capacity
0.414 J/g-°C @Temperature 52.0 °C
Specific Heat Capacity
0.423 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.444 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.460 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.476 J/g-°C @Temperature 400 °C
Specific Heat Capacity
0.489 J/g-°C @Temperature 500 °C
Specific Heat Capacity
0.514 J/g-°C @Temperature 600 °C
Thermal Conductivity
10.1 W/m-K @Temperature 48.0 °C
Thermal Conductivity
11.1 W/m-K @Temperature 100 °C
Thermal Conductivity
13.4 W/m-K @Temperature 200 °C
Thermal Conductivity
15.5 W/m-K @Temperature 300 °C
Thermal Conductivity
17.5 W/m-K @Temperature 400 °C
Thermal Conductivity
19.5 W/m-K @Temperature 500 °C
Thermal Conductivity
21.3 W/m-K @Temperature 600 °C
Melting Point
1357 - 1399 °C
Solidus
1357 °C
Liquidus
1399 °C

Component Elements Properties
Carbon, C
<= 0.010 %
Chromium, Cr
22 %
Cobalt, Co
<= 2.5 %
Iron, Fe
3.0 %
Manganese, Mn
<= 0.50 %
Molybdenum, Mo
13 %
Nickel, Ni
56 %
Silicon, Si
<= 0.080 %
Tungsten, W
3.0 %
Vanadium, V
<= 0.35 %

Electrical Properties
Electrical Resistivity
0.000114 ohm-cm @Temperature 24.0 °C
Electrical Resistivity
0.000123 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.000124 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.000125 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000126 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000127 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000128 ohm-cm @Temperature 600 °C

Alternative products

Haynes Hastelloy® C-22® alloy, 0% cold worked sheet accurate 93%

$ 1477/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 800 MPa
Tensile Strength, Yield: 407 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C accurate 93%

$ 2312/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 1138 MPa
Tensile Strength, Yield: 972 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched accurate 93%

$ 2334/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 1034 MPa
Tensile Strength, Yield: 593 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, 30% cold worked sheet accurate 93%

$ 1788/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 1172 MPa
Tensile Strength, Yield: 1041 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, GTAW, as welded, notched accurate 93%

$ 2475/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 1014 MPa
Tensile Strength, Yield: 579 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal accurate 93%

$ 1913/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 779 MPa
Tensile Strength, Yield: 510 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, all-weld metal, GMAW short arc accurate 93%

$ 2135/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 779 MPa
Tensile Strength, Ultimate: 579 MPa @Temperature 538 °C

Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched accurate 93%

$ 2344/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 786 MPa
Tensile Strength, Yield: 407 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, 10% cold worked sheet accurate 93%

$ 1675/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 896 MPa
Tensile Strength, Yield: 641 MPa @Strain 0.200 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, commercial ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: a.kutuzov@plastic-price.com

Work with plastics from August, 2015

2 prices for Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C

Seller from Shenzhen – 2021-07-23:

Seller from Shenzhen work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1595 per MT

Seller from Kolkata – 2021-05-17:

Seller from Kolkata work with company: Exxon Chemical, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $1857 per MT