Haynes Hastelloy® G-30® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire price 1838 per MT

Physical Properties
Density
8.22 g/cc

Mechanical Properties
Tensile Strength, Ultimate
717 MPa
Tensile Strength, Ultimate
510 MPa @Temperature 538 °C
Tensile Strength, Ultimate
572 MPa @Temperature 260 °C
Tensile Strength, Yield
462 MPa @Strain 0.200 %
Tensile Strength, Yield
324 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
345 MPa @Strain 0.200 %, Temperature 260 °C
Elongation at Break
43 %
Elongation at Break
40 % @Temperature 260 °C
Elongation at Break
44 % @Temperature 538 °C
Reduction of Area
40 %
Reduction of Area
36 % @Temperature 260 °C
Reduction of Area
39 % @Temperature 538 °C
Modulus of Elasticity
202 GPa
Modulus of Elasticity
184 GPa @Temperature 538 °C
Modulus of Elasticity
192 GPa @Temperature 427 °C
Modulus of Elasticity
194 GPa @Temperature 316 °C
Modulus of Elasticity
196 GPa @Temperature 204 °C

Thermal Properties
CTE, linear
14.4 µm/m-°C @Temperature 30.0 - 316 °C
CTE, linear
14.9 µm/m-°C @Temperature 30.0 - 427 °C
CTE, linear
15.5 µm/m-°C @Temperature 30.0 - 538 °C
CTE, linear
16.0 µm/m-°C @Temperature 30.0 - 760 °C
CTE, linear
16.0 µm/m-°C @Temperature 30.0 - 649 °C
Thermal Conductivity
10.2 W/m-K @Temperature 24.0 °C
Thermal Conductivity
11.9 W/m-K @Temperature 100 °C
Thermal Conductivity
14.4 W/m-K @Temperature 200 °C
Thermal Conductivity
16.7 W/m-K @Temperature 300 °C
Thermal Conductivity
18.7 W/m-K @Temperature 400 °C
Thermal Conductivity
20.3 W/m-K @Temperature 500 °C
Thermal Conductivity
21.4 W/m-K @Temperature 600 °C

Component Elements Properties
Carbon, C
<= 0.030 %
Chromium, Cr
28 - 31.5 %
Cobalt, Co
<= 5.0 %
Copper, Cu
1.0 - 2.4 %
Iron, Fe
13 - 17 %
Manganese, Mn
<= 1.5 %
Molybdenum, Mo
4.0 - 6.0 %
Nb + Ta
0.30 - 1.5 %
Nickel, Ni
43 %
Phosphorous, P
<= 0.040 %
Silicon, Si
0.80 %
Sulfur, S
<= 0.020 %
Tungsten, W
1.5 - 4.0 %

Electrical Properties
Electrical Resistivity
0.000116 ohm-cm @Temperature 24.0 °C
Electrical Resistivity
0.000117 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.000119 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.000119 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000123 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000124 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000125 ohm-cm @Temperature 600 °C

Alternative products

Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld accurate 61%

$ 1735/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 676 MPa
Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
Tensile Strength, Yield: 331 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld accurate 61%

$ 1510/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 676 MPa
Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
Tensile Strength, Yield: 331 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld accurate 61%

$ 1672/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 676 MPa
Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
Tensile Strength, Yield: 331 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld accurate 61%

$ 1532/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 676 MPa
Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
Tensile Strength, Yield: 331 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, 31.8 mm thick plate accurate 61%

$ 1477/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 683 MPa
Tensile Strength, Yield: 310 MPa @Strain 0.200 %
Elongation at Break: 60 %
Modulus of Elasticity: 202 GPa

Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet accurate 61%

$ 1918/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 690 MPa
Tensile Strength, Yield: 352 MPa @Strain 0.200 %
Elongation at Break: 56 %
Modulus of Elasticity: 202 GPa

Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire accurate 61%

$ 1540/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 696 MPa
Tensile Strength, Ultimate: 372 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 503 MPa @Temperature 538 °C
Tensile Strength, Yield: 365 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate accurate 61%

$ 1453/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 690 MPa
Tensile Strength, Yield: 317 MPa @Strain 0.200 %
Elongation at Break: 64 %
Reduction of Area: 77 %

Haynes Hastelloy® G-30® alloy, 9.5 mm thick plate accurate 61%

$ 1454/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 690 MPa
Tensile Strength, Yield: 310 MPa @Strain 0.200 %
Elongation at Break: 65 %
Reduction of Area: 68 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes Hastelloy® G-30® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire

Seller from Hanoi – 2021-04-23:

Seller from Hanoi work with company: RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1838 per MT