Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C)

Seller in Hāora price: $2336 per MT

Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C) in Nickel Alloy

  • Physical Properties
  • Density
  • 8.22 g/cc
  • Mechanical Properties
  • Tensile Strength, Ultimate
  • 483 MPa @Temperature 649 °C
  • Tensile Strength, Ultimate
  • 501 MPa @Temperature 593 °C
  • Tensile Strength, Ultimate
  • 521 MPa @Temperature 538 °C
  • Tensile Strength, Ultimate
  • 543 MPa @Temperature 482 °C
  • Tensile Strength, Ultimate
  • 561 MPa @Temperature 427 °C
  • Tensile Strength, Ultimate
  • 570 MPa @Temperature 371 °C
  • Tensile Strength, Ultimate
  • 583 MPa @Temperature 316 °C
  • Tensile Strength, Ultimate
  • 600 MPa @Temperature 260 °C
  • Tensile Strength, Ultimate
  • 623 MPa @Temperature 204 °C
  • Tensile Strength, Ultimate
  • 656 MPa @Temperature 149 °C
  • Tensile Strength, Ultimate
  • 692 MPa @Temperature 93.0 °C
  • Tensile Strength, Ultimate
  • 689 MPa @Thickness 12.7 mm, Temperature 25.0 °C
  • Tensile Strength, Ultimate
  • 703 MPa @Thickness 6.40 mm, Temperature 25.0 °C
  • Tensile Strength, Yield
  • 318 MPa @Thickness 12.7 mm, Temperature 25.0 °C
  • Tensile Strength, Yield
  • 344 MPa @Thickness 6.40 mm, Temperature 25.0 °C
  • Tensile Strength, Yield
  • 184 MPa @Strain 0.200 %, Temperature 649 °C
  • Tensile Strength, Yield
  • 185 MPa @Strain 0.200 %, Temperature 593 °C
  • Tensile Strength, Yield
  • 194 MPa @Strain 0.200 %, Temperature 538 °C
  • Tensile Strength, Yield
  • 204 MPa @Strain 0.200 %, Temperature 482 °C
  • Tensile Strength, Yield
  • 215 MPa @Strain 0.200 %, Temperature 427 °C
  • Tensile Strength, Yield
  • 217 MPa @Strain 0.200 %, Temperature 371 °C
  • Tensile Strength, Yield
  • 219 MPa @Strain 0.200 %, Temperature 316 °C
  • Tensile Strength, Yield
  • 232 MPa @Strain 0.200 %, Temperature 260 °C
  • Tensile Strength, Yield
  • 248 MPa @Strain 0.200 %, Temperature 204 °C
  • Tensile Strength, Yield
  • 278 MPa @Strain 0.200 %, Temperature 149 °C
  • Tensile Strength, Yield
  • 313 MPa @Strain 0.200 %, Temperature 93.0 °C
  • Elongation at Break
  • 67.9 % @Temperature 260 °C
  • Elongation at Break
  • 68.2 % @Temperature 149 °C
  • Elongation at Break
  • 68.8 % @Temperature 316 °C
  • Elongation at Break
  • 69.3 % @Temperature 93.0 °C
  • Elongation at Break
  • 69.5 % @Temperature 204 °C
  • Elongation at Break
  • 70.2 % @Temperature 649 °C
  • Elongation at Break
  • 71 % @Temperature 482 °C
  • Elongation at Break
  • 72 % @Temperature 593 °C
  • Elongation at Break
  • 72.3 % @Temperature 371 °C
  • Elongation at Break
  • 72.7 % @Temperature 538 °C
  • Elongation at Break
  • 72.8 % @Temperature 427 °C
  • Elongation at Break
  • 66 % @Thickness 6.40 mm, Temperature 25.0 °C
  • Elongation at Break
  • 72 % @Thickness 12.7 mm, Temperature 25.0 °C
  • Modulus of Elasticity
  • 170 GPa @Temperature 649 °C
  • Modulus of Elasticity
  • 177 GPa @Temperature 538 °C
  • Modulus of Elasticity
  • 183 GPa @Temperature 427 °C
  • Modulus of Elasticity
  • 189 GPa @Temperature 316 °C
  • Modulus of Elasticity
  • 204 GPa @Temperature 25.0 °C
  • Thermal Properties
  • CTE, linear
  • 12.3 µm/m-°C @Temperature 21.0 - 100 °C
  • CTE, linear
  • 12.6 µm/m-°C @Temperature 21.0 - 200 °C
  • CTE, linear
  • 13.2 µm/m-°C @Temperature 21.0 - 300 °C
  • CTE, linear
  • 13.4 µm/m-°C @Temperature 21.0 - 400 °C
  • CTE, linear
  • 13.6 µm/m-°C @Temperature 21.0 - 500 °C
  • CTE, linear
  • 14.4 µm/m-°C @Temperature 21.0 - 600 °C
  • Specific Heat Capacity
  • 0.450 J/g-°C @Temperature 25.0 °C
  • Specific Heat Capacity
  • 0.470 J/g-°C @Temperature 100 °C
  • Specific Heat Capacity
  • 0.490 J/g-°C @Temperature 200 °C
  • Specific Heat Capacity
  • 0.510 J/g-°C @Temperature 300 °C
  • Specific Heat Capacity
  • 0.530 J/g-°C @Temperature 400 °C
  • Specific Heat Capacity
  • 0.530 J/g-°C @Temperature 500 °C
  • Specific Heat Capacity
  • 0.600 J/g-°C @Temperature 600 °C
  • Thermal Conductivity
  • 10.0 W/m-K @Temperature 25.0 °C
  • Thermal Conductivity
  • 12.0 W/m-K @Temperature 100 °C
  • Thermal Conductivity
  • 14.0 W/m-K @Temperature 200 °C
  • Electrical Properties
  • Electrical Resistivity
  • 0.000118 ohm-cm @Temperature 25.0 °C
  • Electrical Resistivity
  • 0.000119 ohm-cm @Temperature 100 °C
  • Electrical Resistivity
  • 0.000120 ohm-cm @Temperature 200 °C
  • Electrical Resistivity
  • 0.000121 ohm-cm @Temperature 300 °C
  • Electrical Resistivity
  • 0.000122 ohm-cm @Temperature 400 °C
  • Electrical Resistivity
  • 0.000124 ohm-cm @Temperature 500 °C
  • Electrical Resistivity
  • 0.000125 ohm-cm @Temperature 600 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale france. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C)

Seller from Hāora – 2021-08-16:

Seller from Hāora work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2336 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C)?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Awning supplier in Singapore open-nearme.com