Haynes Hastelloy® X alloy, sheet price 2266 per MT

Physical Properties
Density
8.22 g/cc

Mechanical Properties
Tensile Strength, Ultimate
765 MPa
Tensile Strength, Ultimate
97.0 MPa @Temperature 1095 °C
Tensile Strength, Ultimate
175 MPa @Temperature 980 °C
Tensile Strength, Ultimate
310 MPa @Temperature 870 °C
Tensile Strength, Ultimate
465 MPa @Temperature 760 °C
Tensile Strength, Ultimate
570 MPa @Temperature 650 °C
Tensile Strength, Ultimate
615 MPa @Temperature 540 °C
Tensile Strength, Yield
380 MPa @Strain 0.200 %
Tensile Strength, Yield
44.0 MPa @Strain 0.200 %, Temperature 1095 °C
Tensile Strength, Yield
91.0 MPa @Strain 0.200 %, Temperature 980 °C
Tensile Strength, Yield
195 MPa @Strain 0.200 %, Temperature 870 °C
Tensile Strength, Yield
235 MPa @Strain 0.200 %, Temperature 760 °C
Tensile Strength, Yield
245 MPa @Strain 0.200 %, Temperature 540 °C
Tensile Strength, Yield
245 MPa @Strain 0.200 %, Temperature 650 °C
Elongation at Break
44.2 %
Elongation at Break
49.5 % @Temperature 540 °C
Elongation at Break
53.4 % @Temperature 760 °C
Elongation at Break
54 % @Temperature 650 °C
Elongation at Break
58.3 % @Temperature 870 °C
Elongation at Break
59.8 % @Temperature 1095 °C
Elongation at Break
65.1 % @Temperature 980 °C
Modulus of Elasticity
139 GPa @Temperature 1000 °C
Modulus of Elasticity
151 GPa @Temperature 900 °C
Modulus of Elasticity
158 GPa @Temperature 800 °C
Modulus of Elasticity
166 GPa @Temperature 700 °C
Modulus of Elasticity
174 GPa @Temperature 600 °C
Modulus of Elasticity
186 GPa @Temperature 400 °C
Modulus of Elasticity
197 GPa @Temperature 200 °C
Modulus of Elasticity
205 GPa @Temperature 20.0 °C

Thermal Properties
CTE, linear
15.0 µm/m-°C @Temperature 20.0 - 500 °C
CTE, linear
15.3 µm/m-°C @Temperature 20.0 - 600 °C
CTE, linear
15.6 µm/m-°C @Temperature 20.0 - 700 °C
CTE, linear
16.0 µm/m-°C @Temperature 20.0 - 800 °C
CTE, linear
16.3 µm/m-°C @Temperature 20.0 - 900 °C
CTE, linear
16.6 µm/m-°C @Temperature 20.0 - 1000 °C
Thermal Conductivity
16.9 W/m-K @Temperature 400 °C
Thermal Conductivity
20.9 W/m-K @Temperature 600 °C
Thermal Conductivity
22.8 W/m-K @Temperature 700 °C
Thermal Conductivity
24.8 W/m-K @Temperature 800 °C
Thermal Conductivity
26.7 W/m-K @Temperature 900 °C
Thermal Conductivity
28.7 W/m-K @Temperature 1000 °C
Melting Point
1260 - 1355 °C
Solidus
1260 °C
Liquidus
1355 °C
Maximum Service Temperature, Air
1095 °C

Component Elements Properties
Boron, B
<= 0.0080 %
Carbon, C
0.10 %
Chromium, Cr
22 %
Cobalt, Co
1.5 %
Iron, Fe
18 %
Manganese, Mn
<= 1.0 %
Molybdenum, Mo
9.0 %
Nickel, Ni
47 %
Silicon, Si
<= 1.0 %
Tungsten, W
0.60 %

Alternative products

HP Alloys Alloy X, 15% Cold Worked accurate 99%

$ 1452/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 945 MPa
Tensile Strength, Yield: 731 MPa
Elongation at Break: 20 %
Modulus of Elasticity: 205 GPa

Osprey Metals 434L Stainless Steel Powder (Grade 90% - 22) accurate 99%

$ 1815/MT

Particle Size: 10 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.12 %
Chromium, Cr: 16 - 18 %
Iron, Fe: 80.45 %

HP Alloys Alloy X, 5% Cold Worked accurate 99%

$ 1473/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 848 MPa
Tensile Strength, Yield: 565 MPa
Elongation at Break: 32 %
Modulus of Elasticity: 205 GPa

Osprey Metals Co212-e Cobalt Alloy Powder (Grade 90% - 22) accurate 99%

$ 1490/MT

Particle Size: 10 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.20 %
Chromium, Cr: 27 - 30 %
Cobalt, Co: 62.85 %

Osprey Metals 430L Stainless Steel Powder (Grade 80% - 22) accurate 99%

$ 1471/MT

Particle Size: 12 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.030 %
Chromium, Cr: 16 - 18 %
Iron, Fe: 81.79 %

Osprey Metals 430L Stainless Steel Powder (Grade 90% - 22) accurate 99%

$ 1750/MT

Particle Size: 10 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.030 %
Chromium, Cr: 16 - 18 %
Iron, Fe: 81.79 %

Osprey Metals 420 Stainless Steel Powder (Grade 90% - 22) accurate 99%

$ 2111/MT

Particle Size: 10 µm
Carbon, C: >= 0.15 %
Carbon, C: 0.50 %
Chromium, Cr: 12 - 14 %
Iron, Fe: 85 %

Osprey Metals Co212-e Cobalt Alloy Powder (Grade 95% - 16) accurate 99%

$ 2089/MT

Particle Size: 6.7 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.20 %
Chromium, Cr: 27 - 30 %
Cobalt, Co: 62.85 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 99%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-4 PH Stainless Steel Powder (Grade 90% - 16) accurate 99%

$ 1622/MT

Particle Size: 8.4 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.070 %
Chromium, Cr: 15.5 - 17.5 %
Copper, Cu: 3.0 - 5.0 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale vessel. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes Hastelloy® X alloy, sheet

Seller from Melbourne – 2021-07-04:

Seller from Melbourne work with company: PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2266 per MT

Seller from Xi’an – 2021-06-17:

Seller from Xi’an work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2557 per MT