Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) price 1478 per MT

Physical Properties
Density
8.25 g/cc

Mechanical Properties
Tensile Strength, Ultimate
1047 MPa
Tensile Strength, Ultimate
179 MPa @Temperature 982 °C
Tensile Strength, Ultimate
677 MPa @Temperature 871 °C
Tensile Strength, Ultimate
858 MPa @Temperature 760 °C
Tensile Strength, Ultimate
958 MPa @Temperature 538 °C
Tensile Strength, Ultimate
970 MPa @Temperature 649 °C
Tensile Strength, Yield
799 MPa @Strain 0.200 %
Tensile Strength, Yield
80.0 MPa @Strain 0.200 %, Temperature 982 °C
Tensile Strength, Yield
450 MPa @Strain 0.200 %, Temperature 871 °C
Tensile Strength, Yield
535 MPa @Strain 0.200 %, Temperature 760 °C
Tensile Strength, Yield
746 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
748 MPa @Strain 0.200 %, Temperature 649 °C
Modulus of Elasticity
150 GPa @Temperature 927 °C
Modulus of Elasticity
160 GPa @Temperature 871 °C
Modulus of Elasticity
163 GPa @Temperature 843 °C
Modulus of Elasticity
166 GPa @Temperature 816 °C
Modulus of Elasticity
171 GPa @Temperature 760 °C
Modulus of Elasticity
178 GPa @Temperature 677 °C
Modulus of Elasticity
179 GPa @Temperature 649 °C
Modulus of Elasticity
182 GPa @Temperature 593 °C
Modulus of Elasticity
188 GPa @Temperature 538 °C
Modulus of Elasticity
190 GPa @Temperature 482 °C
Modulus of Elasticity
198 GPa @Temperature 371 °C
Modulus of Elasticity
204 GPa @Temperature 260 °C
Modulus of Elasticity
213 GPa @Temperature 149 °C
Modulus of Elasticity
218 GPa @Temperature 25.0 °C
Poissons Ratio
0.31
Poissons Ratio
0.31 @Temperature 149 °C
Poissons Ratio
0.32 @Temperature 482 °C
Poissons Ratio
0.32 @Temperature 371 °C
Poissons Ratio
0.32 @Temperature 260 °C
Poissons Ratio
0.33 @Temperature 760 °C
Poissons Ratio
0.33 @Temperature 677 °C
Poissons Ratio
0.33 @Temperature 649 °C
Poissons Ratio
0.34 @Temperature 843 °C
Poissons Ratio
0.35 @Temperature 927 °C
Shear Modulus
83.0 GPa
Shear Modulus
55.0 GPa @Temperature 927 °C
Shear Modulus
61.0 GPa @Temperature 843 °C
Shear Modulus
64.0 GPa @Temperature 760 °C
Shear Modulus
67.0 GPa @Temperature 677 °C
Shear Modulus
69.0 GPa @Temperature 593 °C
Shear Modulus
72.0 GPa @Temperature 482 °C
Shear Modulus
75.0 GPa @Temperature 371 °C
Shear Modulus
77.0 GPa @Temperature 260 °C
Shear Modulus
81.0 GPa @Temperature 149 °C

Thermal Properties
CTE, linear
13.5 µm/m-°C @Temperature 21.0 - 538 °C
CTE, linear
14.0 µm/m-°C @Temperature 21.0 - 649 °C
CTE, linear
14.8 µm/m-°C @Temperature 21.0 - 760 °C
CTE, linear
15.2 µm/m-°C @Temperature 21.0 - 871 °C
CTE, linear
16.3 µm/m-°C @Temperature 21.0 - 927 °C
CTE, linear
16.8 µm/m-°C @Temperature 21.0 - 982 °C
Specific Heat Capacity
0.452 J/g-°C @Temperature 21.0 °C
Thermal Conductivity
11.5 W/m-K @Temperature 149 °C
Thermal Conductivity
12.5 W/m-K @Temperature 204 °C
Thermal Conductivity
13.6 W/m-K @Temperature 260 °C
Thermal Conductivity
14.7 W/m-K @Temperature 316 °C
Thermal Conductivity
16.8 W/m-K @Temperature 427 °C
Thermal Conductivity
18.8 W/m-K @Temperature 538 °C
Thermal Conductivity
20.0 W/m-K @Temperature 593 °C
Thermal Conductivity
21.0 W/m-K @Temperature 644 °C
Thermal Conductivity
22.0 W/m-K @Temperature 704 °C
Thermal Conductivity
23.1 W/m-K @Temperature 760 °C
Thermal Conductivity
24.1 W/m-K @Temperature 816 °C
Thermal Conductivity
25.1 W/m-K @Temperature 871 °C
Melting Point
1310 - 1345 °C
Solidus
1310 °C

Electrical Properties
Magnetic Permeability
<= 1.002 @Temperature 21.0 °C

Alternative products

Hexcel® Redux® 810 Two-Part Epoxy Paste Adhesive accurate 99%

$ 2584/MT

Density: 1.02 g/cc @Temperature 25.0 °C
Density: 1.11 g/cc @Temperature 25.0 °C
Density: 1.15 g/cc @Temperature 25.0 °C
Viscosity: 4000 - 8000 cP @Temperature 25.0 °C
Viscosity: 80000 - 90000 cP @Temperature 25.0 °C

DuPont Teijin Films Mylar® A Polyester Film, 1200 Gauge accurate 99%

$ 1518/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Tensile Modulus: 3.50 GPa
Poissons Ratio: 0.38
Poissons Ratio: 0.58

DuPont Teijin Films Mylar® A Polyester Film, 200 Gauge accurate 99%

$ 1476/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Film Elongation at Break, MD: 135 %
Film Elongation at Break, TD: 110 %
Tensile Modulus: 3.50 GPa

DuPont Teijin Films Mylar® A Polyester Film, 500 Gauge accurate 99%

$ 2436/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Film Elongation at Break, MD: 140 %
Film Elongation at Break, TD: 115 %
Tensile Modulus: 3.50 GPa

Ampco Metal AMPCO® 15 Aluminum Bronze, Extruded Rod, 25.4 - 50.8 mm. accurate 99%

$ 2351/MT

Specific Gravity: 7.65 g/cc
Density: 7.64 g/cc
Hardness, Brinell: 170
Hardness, Rockwell B: 87
Tensile Strength, Ultimate: >= 586 MPa

Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched accurate 99%

$ 1603/MT

Density: 8.20 g/cc
Hardness, Brinell: 190
Hardness, Knoop: 211
Hardness, Vickers: 199
Tensile Strength, Ultimate: 767 MPa

Haynes Multimet® alloy, GTAW, 6.35 mm plate accurate 99%

$ 1486/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 768 MPa
Elongation at Break: 21 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction accurate 99%

$ 1593/MT

Density: 8.20 g/cc
Hardness, Brinell: 342
Hardness, Knoop: 371
Hardness, Rockwell C: 37
Hardness, Vickers: 358

Haynes Multimet® alloy, SMAW, 9.5 mm plate accurate 99%

$ 1589/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 724 MPa
Elongation at Break: 28 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled accurate 99%

$ 1517/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F)

Seller from Hāora – 2021-04-04:

Seller from Hāora work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1490 per MT

Seller from Rangoon – 2021-05-14:

Seller from Rangoon work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2012 per MT

Seller from Monterrey – 2021-08-10:

Seller from Monterrey work with company: 3M, Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1867 per MT

Seller from Cairo – 2021-07-22:

Seller from Cairo work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1495 per MT

Seller from Kinshasa – 2021-07-24:

Seller from Kinshasa work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1478 per MT

Would you like to sell Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F)?