Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled price 1517 per MT

Physical Properties
Density
8.20 g/cc

Mechanical Properties
Hardness, Brinell
159
Hardness, Knoop
176
Hardness, Rockwell B
92
Hardness, Vickers
201
Tensile Strength, Ultimate
800 MPa
Tensile Strength, Ultimate
69.0 MPa @Temperature 1038 °C
Tensile Strength, Ultimate
137 MPa @Temperature 927 °C
Tensile Strength, Ultimate
505 MPa @Temperature 649 °C
Tensile Strength, Yield
393 MPa @Strain 0.200 %
Elongation at Break
43 %
Elongation at Break
34 % @Temperature 1038 °C
Elongation at Break
35 % @Temperature 649 °C
Elongation at Break
39 % @Temperature 927 °C
Poissons Ratio
0.298
Poissons Ratio
0.315 @Temperature 426 °C
Poissons Ratio
0.319 @Temperature -78.0 °C
Poissons Ratio
0.325 @Temperature 650 °C
Poissons Ratio
0.339 @Temperature 816 °C

Thermal Properties
CTE, linear
15.3 µm/m-°C @Temperature 23.0 - 300 °C
CTE, linear
15.6 µm/m-°C @Temperature 23.0 - 400 °C
CTE, linear
16.0 µm/m-°C @Temperature 23.0 - 500 °C
CTE, linear
16.7 µm/m-°C @Temperature 23.0 - 600 °C
CTE, linear
17.2 µm/m-°C @Temperature 23.0 - 700 °C
CTE, linear
17.5 µm/m-°C @Temperature 23.0 - 800 °C
CTE, linear
17.8 µm/m-°C @Temperature 23.0 - 900 °C
CTE, linear
17.8 µm/m-°C @Temperature 23.0 - 1000 °C
CTE, linear
18.4 µm/m-°C @Temperature 23.0 - 1100 °C
Specific Heat Capacity
0.435 J/g-°C @Temperature >=100 °C
Thermal Conductivity
15.9 W/m-K @Temperature 300 °C
Thermal Conductivity
17.3 W/m-K @Temperature 400 °C
Thermal Conductivity
18.6 W/m-K @Temperature 500 °C
Thermal Conductivity
20.0 W/m-K @Temperature 600 °C
Thermal Conductivity
20.0 W/m-K @Temperature 200 °C
Melting Point
1288 - 1354 °C
Solidus
1288 °C
Liquidus
1354 °C

Optical Properties
Emissivity (0-1)
0.88 @Temperature 1090 °C

Component Elements Properties
Carbon, C
0.080 - 0.16 %
Cb + Ta
0.75 - 1.25 %
Chromium, Cr
20 - 22.5 %
Cobalt, Co
18.5 - 21 %
Iron, Fe
33 %
Manganese, Mn
1.0 - 2.0 %
Molybdenum, Mo
2.5 - 3.5 %
Nickel, Ni
19 - 21 %
Nitrogen, N
0.10 - 0.20 %
Silicon, Si
<= 1.0 %
Tungsten, W
2.0 - 3.0 %

Electrical Properties
Electrical Resistivity
0.0000930 ohm-cm @Temperature 22.0 °C

Alternative products

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction accurate 61%

$ 1518/MT

Density: 8.20 g/cc
Hardness, Brinell: 318
Hardness, Knoop: 343
Hardness, Rockwell C: 34
Hardness, Vickers: 332

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled accurate 68%

$ 1534/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched accurate 68%

$ 1589/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction accurate 61%

$ 1593/MT

Density: 8.20 g/cc
Hardness, Brinell: 342
Hardness, Knoop: 371
Hardness, Rockwell C: 37
Hardness, Vickers: 358

Haynes Multimet® alloy, SMAW, 9.5 mm plate accurate 61%

$ 1589/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 724 MPa
Elongation at Break: 28 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction accurate 61%

$ 2073/MT

Density: 8.20 g/cc
Hardness, Brinell: 369
Hardness, Knoop: 403
Hardness, Rockwell C: 40
Hardness, Vickers: 388

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction accurate 68%

$ 1909/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

Haynes Multimet® alloy, SMAW, 3.2 mm sheet accurate 61%

$ 1984/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 800 MPa
Elongation at Break: 27 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled accurate 61%

$ 2005/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 811 MPa
Tensile Strength, Ultimate: 572 MPa @Temperature 649 °C
Tensile Strength, Yield: 493 MPa @Strain 0.200 %
Tensile Strength, Yield: 338 MPa @Strain 0.200 %, Temperature 649 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships forsale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled

Seller from Los Angeles – 2021-06-30:

Seller from Los Angeles work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1564 per MT

Seller from Sūrat – 2021-03-21:

Seller from Sūrat work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2539 per MT

Seller from Melbourne – 2021-07-05:

Seller from Melbourne work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1517 per MT

Seller from Barcelona – 2021-04-04:

Seller from Barcelona work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2193 per MT

Seller from Montréal – 2021-05-15:

Seller from Montréal work with company: Hexcel, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1790 per MT