Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) price 1801 per MT

Physical Properties
Density
8.50 g/cc

Mechanical Properties
Tensile Strength, Ultimate
554 MPa @Temperature 649 °C
Tensile Strength, Ultimate
585 MPa @Temperature 482 °C
Tensile Strength, Ultimate
586 MPa @Temperature 538 °C
Tensile Strength, Ultimate
605 MPa @Temperature 371 °C
Tensile Strength, Ultimate
609 MPa @Temperature 427 °C
Tensile Strength, Ultimate
616 MPa @Temperature 316 °C
Tensile Strength, Ultimate
641 MPa @Temperature 260 °C
Tensile Strength, Ultimate
676 MPa @Temperature 204 °C
Tensile Strength, Ultimate
684 MPa @Temperature 149 °C
Tensile Strength, Ultimate
724 MPa @Temperature 93.0 °C
Tensile Strength, Ultimate
724 MPa @Diameter 50.8 mm, Temperature 25.0 °C
Tensile Strength, Ultimate
738 MPa @Diameter 88.9 mm, Temperature 25.0 °C
Tensile Strength, Ultimate
738 MPa @Diameter 19.1 mm, Temperature 25.0 °C
Tensile Strength, Ultimate
745 MPa @Diameter 9.70 mm, Temperature 25.0 °C
Tensile Strength, Ultimate
758 MPa @Diameter 25.4 mm, Temperature 25.0 °C
Tensile Strength, Yield
331 MPa @Diameter 9.70 mm, Temperature 25.0 °C
Tensile Strength, Yield
345 MPa @Diameter 19.1 mm, Temperature 25.0 °C
Tensile Strength, Yield
379 MPa @Diameter 25.4 mm, Temperature 25.0 °C
Tensile Strength, Yield
379 MPa @Diameter 50.8 mm, Temperature 25.0 °C
Tensile Strength, Yield
386 MPa @Diameter 88.9 mm, Temperature 25.0 °C
Tensile Strength, Yield
209 MPa @Strain 0.200 %, Temperature 649 °C
Tensile Strength, Yield
214 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
216 MPa @Strain 0.200 %, Temperature 427 °C
Tensile Strength, Yield
223 MPa @Strain 0.200 %, Temperature 482 °C
Tensile Strength, Yield
234 MPa @Strain 0.200 %, Temperature 371 °C
Tensile Strength, Yield
243 MPa @Strain 0.200 %, Temperature 316 °C
Tensile Strength, Yield
260 MPa @Strain 0.200 %, Temperature 260 °C
Tensile Strength, Yield
283 MPa @Strain 0.200 %, Temperature 204 °C
Tensile Strength, Yield
308 MPa @Strain 0.200 %, Temperature 149 °C
Tensile Strength, Yield
319 MPa @Strain 0.200 %, Temperature 93.0 °C
Elongation at Break
67.9 % @Temperature 260 °C
Elongation at Break
68.8 % @Temperature 149 °C
Elongation at Break
69.3 % @Temperature 204 °C
Elongation at Break
69.8 % @Temperature 371 °C
Elongation at Break
70.3 % @Temperature 93.0 °C
Elongation at Break
70.7 % @Temperature 649 °C
Elongation at Break
72.6 % @Temperature 482 °C
Elongation at Break
72.7 % @Temperature 316 °C
Elongation at Break
73 % @Temperature 427 °C
Elongation at Break
75.3 % @Temperature 538 °C
Elongation at Break
67 % @Diameter 9.70 mm, Temperature 25.0 °C
Elongation at Break
68 % @Diameter 25.4 mm, Temperature 25.0 °C
Elongation at Break
69 % @Diameter 19.1 mm, Temperature 25.0 °C
Elongation at Break
71 % @Diameter 50.8 mm, Temperature 25.0 °C
Elongation at Break
71 % @Diameter 88.9 mm, Temperature 25.0 °C
Modulus of Elasticity
162 GPa @Temperature 649 °C
Modulus of Elasticity
171 GPa @Temperature 538 °C
Modulus of Elasticity
177 GPa @Temperature 427 °C
Modulus of Elasticity
190 GPa @Temperature 316 °C
Modulus of Elasticity
207 GPa @Temperature 25.0 °C

Thermal Properties
CTE, linear
12.4 µm/m-°C @Temperature 25.0 - 100 °C
CTE, linear
12.4 µm/m-°C @Temperature 25.0 - 200 °C
CTE, linear
12.6 µm/m-°C @Temperature 25.0 - 300 °C
CTE, linear
12.9 µm/m-°C @Temperature 25.0 - 400 °C
CTE, linear
13.2 µm/m-°C @Temperature 25.0 - 500 °C
CTE, linear
13.3 µm/m-°C @Temperature 25.0 - 600 °C
Specific Heat Capacity
0.428 J/g-°C @Temperature 25.0 °C
Specific Heat Capacity
0.434 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.443 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.455 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.468 J/g-°C @Temperature 400 °C

Electrical Properties
Electrical Resistivity
0.000128 ohm-cm @Temperature 25.0 °C
Electrical Resistivity
0.000129 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.000130 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.000131 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000132 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000134 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000135 ohm-cm @Temperature 600 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C)

Seller from Hechi – 2021-07-14:

Seller from Hechi work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1801 per MT