Haynes Hastelloy® C-22® alloy, 0.71-3.2 mm thick sheet, solution heat treated price 1578 per MT

Physical Properties
Density
8.69 g/cc

Mechanical Properties
Hardness, Rockwell B
93 @Temperature 23.0 °C
Hardness, Rockwell B
95 @Temperature 23.0 °C
Tensile Strength, Ultimate
800 MPa
Tensile Strength, Ultimate
524 MPa @Temperature 760 °C
Tensile Strength, Ultimate
586 MPa @Temperature 649 °C
Tensile Strength, Ultimate
627 MPa @Temperature 538 °C
Tensile Strength, Ultimate
655 MPa @Temperature 427 °C
Tensile Strength, Ultimate
676 MPa @Temperature 316 °C
Tensile Strength, Ultimate
703 MPa @Temperature 204 °C
Tensile Strength, Ultimate
758 MPa @Temperature 93.0 °C
Tensile Strength, Yield
407 MPa @Strain 0.200 %
Tensile Strength, Yield
241 MPa @Strain 0.200 %, Temperature 760 °C
Tensile Strength, Yield
248 MPa @Strain 0.200 %, Temperature 649 °C
Tensile Strength, Yield
276 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
283 MPa @Strain 0.200 %, Temperature 427 °C
Tensile Strength, Yield
290 MPa @Strain 0.200 %, Temperature 316 °C
Tensile Strength, Yield
303 MPa @Strain 0.200 %, Temperature 204 °C
Tensile Strength, Yield
372 MPa @Strain 0.200 %, Temperature 93.0 °C
Elongation at Break
57 %
Elongation at Break
57 % @Temperature 204 °C
Elongation at Break
58 % @Temperature 93.0 °C
Elongation at Break
61 % @Temperature 538 °C
Elongation at Break
62 % @Temperature 316 °C
Elongation at Break
63 % @Temperature 760 °C
Elongation at Break
65 % @Temperature 649 °C
Elongation at Break
67 % @Temperature 427 °C
Modulus of Elasticity
206 GPa
Modulus of Elasticity
145 GPa @Temperature 982 °C
Modulus of Elasticity
154 GPa @Temperature 871 °C
Modulus of Elasticity
163 GPa @Temperature 760 °C
Modulus of Elasticity
171 GPa @Temperature 649 °C
Modulus of Elasticity
177 GPa @Temperature 538 °C
Modulus of Elasticity
183 GPa @Temperature 427 °C
Modulus of Elasticity
190 GPa @Temperature 316 °C
Modulus of Elasticity
196 GPa @Temperature 204 °C
Modulus of Elasticity
203 GPa @Temperature 93.0 °C
Charpy Impact
353 J
Charpy Impact
351 J @Temperature -196 °C

Thermal Properties
CTE, linear
12.4 µm/m-°C @Temperature 24.0 - 93.0 °C
CTE, linear
12.4 µm/m-°C @Temperature 24.0 - 204 °C
CTE, linear
12.6 µm/m-°C @Temperature 24.0 - 316 °C
CTE, linear
13.3 µm/m-°C @Temperature 24.0 - 427 °C
CTE, linear
13.9 µm/m-°C @Temperature 24.0 - 538 °C
CTE, linear
14.6 µm/m-°C @Temperature 24.0 - 649 °C
CTE, linear
15.3 µm/m-°C @Temperature 24.0 - 760 °C
CTE, linear
15.8 µm/m-°C @Temperature 24.0 - 871 °C
CTE, linear
16.2 µm/m-°C @Temperature 24.0 - 982 °C
Specific Heat Capacity
0.414 J/g-°C @Temperature 52.0 °C
Specific Heat Capacity
0.423 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.444 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.460 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.476 J/g-°C @Temperature 400 °C
Specific Heat Capacity
0.489 J/g-°C @Temperature 500 °C
Specific Heat Capacity
0.514 J/g-°C @Temperature 600 °C
Thermal Conductivity
10.1 W/m-K @Temperature 48.0 °C
Thermal Conductivity
11.1 W/m-K @Temperature 100 °C
Thermal Conductivity
13.4 W/m-K @Temperature 200 °C
Thermal Conductivity
15.5 W/m-K @Temperature 300 °C
Thermal Conductivity
17.5 W/m-K @Temperature 400 °C

Electrical Properties
Electrical Resistivity
0.000114 ohm-cm @Temperature 24.0 °C
Electrical Resistivity
0.000123 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.000124 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.000125 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000126 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000127 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000128 ohm-cm @Temperature 600 °C

Alternative products

Haynes Hastelloy® C-22® alloy, 0% cold worked sheet accurate 99%

$ 1477/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 800 MPa
Tensile Strength, Yield: 407 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, 50% cold worked sheet accurate 99%

$ 1459/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 1420 MPa
Tensile Strength, Yield: 1262 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched accurate 99%

$ 1526/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 731 MPa
Tensile Strength, Yield: 372 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate accurate 99%

$ 1734/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 758 MPa
Tensile Strength, Ultimate: 469 MPa @Temperature 760 °C

Haynes Hastelloy® C-22® alloy, SMAW weld, C-22 base metal, C-22 weld metal accurate 99%

$ 2022/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 779 MPa
Tensile Strength, Yield: 490 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C accurate 99%

$ 1852/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 800 MPa
Tensile Strength, Yield: 427 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched accurate 99%

$ 2344/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 786 MPa
Tensile Strength, Yield: 407 MPa @Strain 0.200 %

Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate accurate 99%

$ 1888/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 490 MPa @Thickness 12.7 mm, Temperature 760 °C
Tensile Strength, Ultimate: 545 MPa @Thickness 3.17 mm, Temperature 538 °C

Haynes Hastelloy® C-22® alloy, 60% cold worked sheet accurate 99%

$ 1848/MT

Density: 8.69 g/cc
Hardness, Rockwell B: 93 @Temperature 23.0 °C
Hardness, Rockwell B: 95 @Temperature 23.0 °C
Tensile Strength, Ultimate: 1531 MPa
Tensile Strength, Yield: 1393 MPa @Strain 0.200 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes Hastelloy® C-22® alloy, 0.71-3.2 mm thick sheet, solution heat treated

Seller from Nanjing – 2021-06-26:

Seller from Nanjing work with company: 3M, Exxon Chemical, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1578 per MT

Seller from Dallas – 2021-04-29:

Seller from Dallas work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1632 per MT