Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled price 1742 per MT

Physical Properties
Density
8.22 g/cc

Mechanical Properties
Tensile Strength, Ultimate
1324 MPa
Tensile Strength, Yield
1158 MPa @Strain 0.200 %
Elongation at Break
8.0 %
Reduction of Area
14 %
Modulus of Elasticity
202 GPa
Modulus of Elasticity
184 GPa @Temperature 538 °C
Modulus of Elasticity
192 GPa @Temperature 427 °C
Modulus of Elasticity
194 GPa @Temperature 316 °C
Modulus of Elasticity
196 GPa @Temperature 204 °C
Charpy Impact
15.0 J

Thermal Properties
CTE, linear
14.4 µm/m-°C @Temperature 30.0 - 316 °C
CTE, linear
14.9 µm/m-°C @Temperature 30.0 - 427 °C
CTE, linear
15.5 µm/m-°C @Temperature 30.0 - 538 °C
CTE, linear
16.0 µm/m-°C @Temperature 30.0 - 760 °C
CTE, linear
16.0 µm/m-°C @Temperature 30.0 - 649 °C
Thermal Conductivity
10.2 W/m-K @Temperature 24.0 °C
Thermal Conductivity
11.9 W/m-K @Temperature 100 °C
Thermal Conductivity
14.4 W/m-K @Temperature 200 °C
Thermal Conductivity
16.7 W/m-K @Temperature 300 °C
Thermal Conductivity
18.7 W/m-K @Temperature 400 °C
Thermal Conductivity
20.3 W/m-K @Temperature 500 °C
Thermal Conductivity
21.4 W/m-K @Temperature 600 °C

Component Elements Properties
Carbon, C
<= 0.030 %
Chromium, Cr
28 - 31.5 %
Cobalt, Co
<= 5.0 %
Copper, Cu
1.0 - 2.4 %
Iron, Fe
13 - 17 %
Manganese, Mn
<= 1.5 %
Molybdenum, Mo
4.0 - 6.0 %
Nb + Ta
0.30 - 1.5 %
Nickel, Ni
43 %
Phosphorous, P
<= 0.040 %
Silicon, Si
0.80 %
Sulfur, S
<= 0.020 %
Tungsten, W
1.5 - 4.0 %

Electrical Properties
Electrical Resistivity
0.000116 ohm-cm @Temperature 24.0 °C
Electrical Resistivity
0.000117 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.000119 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.000119 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000123 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000124 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000125 ohm-cm @Temperature 600 °C

Alternative products

Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled accurate 86%

$ 1517/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 1241 MPa
Tensile Strength, Yield: 1110 MPa @Strain 0.200 %
Elongation at Break: 12 %
Reduction of Area: 45 %

Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire accurate 86%

$ 1540/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 696 MPa
Tensile Strength, Ultimate: 372 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 503 MPa @Temperature 538 °C
Tensile Strength, Yield: 365 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, 19.1 mm thick plate accurate 86%

$ 1796/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 676 MPa
Tensile Strength, Yield: 324 MPa @Strain 0.200 %
Elongation at Break: 65 %
Reduction of Area: 67 %

Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire accurate 86%

$ 2049/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 696 MPa
Tensile Strength, Ultimate: 379 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
Tensile Strength, Yield: 379 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire accurate 86%

$ 1662/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 710 MPa
Tensile Strength, Ultimate: 372 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 490 MPa @Temperature 538 °C
Tensile Strength, Yield: 393 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, plate and bar accurate 86%

$ 1934/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 710 MPa
Tensile Strength, Ultimate: 524 MPa @Temperature 538 °C
Tensile Strength, Ultimate: 552 MPa @Temperature 427 °C
Tensile Strength, Ultimate: 572 MPa @Temperature 316 °C

Haynes Hastelloy® G-30® alloy, 10% cold rolled accurate 86%

$ 1728/MT

Density: 8.22 g/cc
Hardness, Brinell: 139
Hardness, Knoop: 186
Hardness, Rockwell B: 98
Hardness, Vickers: 241

Haynes Hastelloy® G-30® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire accurate 86%

$ 1838/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 717 MPa
Tensile Strength, Ultimate: 510 MPa @Temperature 538 °C
Tensile Strength, Ultimate: 572 MPa @Temperature 260 °C
Tensile Strength, Yield: 462 MPa @Strain 0.200 %

Haynes Hastelloy® G-30® alloy, mill annealed accurate 86%

$ 1524/MT

Density: 8.22 g/cc
Hardness, Brinell: 128
Hardness, Knoop: 172
Hardness, Rockwell B: 90
Hardness, Vickers: 191

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cruise ship sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled

Seller from Karachi – 2021-05-24:

Seller from Karachi work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1876 per MT

Seller from Shenzhen – 2021-06-23:

Seller from Shenzhen work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2264 per MT

Seller from Hechi – 2021-06-24:

Seller from Hechi work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1742 per MT

Seller from Rangoon – 2021-05-13:

Seller from Rangoon work with company: 3M, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2221 per MT