Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled price 1630 per MT

Physical Properties
Density
8.86 g/cc

Mechanical Properties
Tensile Strength, Ultimate
794 MPa
Tensile Strength, Ultimate
234 MPa @Temperature 927 °C
Tensile Strength, Ultimate
385 MPa @Temperature 815 °C
Tensile Strength, Ultimate
480 MPa @Temperature 704 °C
Tensile Strength, Ultimate
599 MPa @Temperature 593 °C
Tensile Strength, Yield
314 MPa @Strain 0.200 %
Tensile Strength, Yield
179 MPa @Strain 0.200 %, Temperature 927 °C
Tensile Strength, Yield
203 MPa @Strain 0.200 %, Temperature 815 °C
Tensile Strength, Yield
218 MPa @Strain 0.200 %, Temperature 704 °C
Tensile Strength, Yield
227 MPa @Strain 0.200 %, Temperature 593 °C
Elongation at Break
50.7 %
Elongation at Break
24.3 % @Temperature 815 °C
Elongation at Break
30 % @Temperature 927 °C
Elongation at Break
30 % @Temperature 704 °C
Elongation at Break
45.3 % @Temperature 593 °C
Modulus of Elasticity
122 GPa @Temperature 1049 °C
Modulus of Elasticity
136 GPa @Temperature 1000 °C
Modulus of Elasticity
143 GPa @Temperature 954 °C
Modulus of Elasticity
151 GPa @Temperature 904 °C
Modulus of Elasticity
157 GPa @Temperature 854 °C
Modulus of Elasticity
163 GPa @Temperature 800 °C
Modulus of Elasticity
171 GPa @Temperature 700 °C
Modulus of Elasticity
181 GPa @Temperature 577 °C
Modulus of Elasticity
181 GPa @Temperature 632 °C
Modulus of Elasticity
187 GPa @Temperature 500 °C
Modulus of Elasticity
192 GPa @Temperature 410 °C
Modulus of Elasticity
202 GPa @Temperature 221 °C
Modulus of Elasticity
219 GPa @Temperature 14.0 °C

Thermal Properties
CTE, linear
12.3 µm/m-°C @Temperature 21.0 - 316 °C
CTE, linear
12.7 µm/m-°C @Temperature 21.0 - 427 °C
CTE, linear
13.4 µm/m-°C @Temperature 21.0 - 538 °C
CTE, linear
14.0 µm/m-°C @Temperature 21.0 - 649 °C
CTE, linear
14.7 µm/m-°C @Temperature 21.0 - 760 °C
CTE, linear
15.3 µm/m-°C @Temperature 21.0 - 871 °C
CTE, linear
15.8 µm/m-°C @Temperature 21.0 - 982 °C
Specific Heat Capacity
0.419 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.440 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.456 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.469 J/g-°C @Temperature 400 °C
Specific Heat Capacity
0.477 J/g-°C @Temperature 480 °C
Specific Heat Capacity
0.485 J/g-°C @Temperature 540 °C
Specific Heat Capacity
0.523 J/g-°C @Temperature 570 °C
Specific Heat Capacity
0.565 J/g-°C @Temperature 590 °C
Specific Heat Capacity
0.578 J/g-°C @Temperature 680 °C
Specific Heat Capacity
0.578 J/g-°C @Temperature 700 °C
Specific Heat Capacity
0.582 J/g-°C @Temperature 660 °C
Specific Heat Capacity
0.586 J/g-°C @Temperature 620 °C
Thermal Conductivity
11.5 W/m-K
Thermal Conductivity
13.1 W/m-K @Temperature 100 °C
Thermal Conductivity
13.1 W/m-K @Temperature 200 °C
Thermal Conductivity
14.4 W/m-K @Temperature 300 °C
Thermal Conductivity
16.5 W/m-K @Temperature 400 °C
Thermal Conductivity
18.0 W/m-K @Temperature 500 °C
Thermal Conductivity
20.3 W/m-K @Temperature 600 °C
Thermal Conductivity
23.6 W/m-K @Temperature 700 °C
Melting Point
1300 - 1400 °C
Solidus
1300 °C
Liquidus
1400 °C

Component Elements Properties
Al + Ti
<= 0.50 %
Carbon, C
<= 0.080 %
Chromium, Cr
7.0 %
Cobalt, Co
<= 0.20 %
Copper, Cu
<= 0.35 %
Iron, Fe
<= 5.0 %
Manganese, Mn
<= 0.80 %
Molybdenum, Mo
16 %

Electrical Properties
Electrical Resistivity
0.000120 ohm-cm
Electrical Resistivity
0.000124 ohm-cm @Temperature 815 °C
Electrical Resistivity
0.000126 ohm-cm @Temperature 705 °C

Alternative products

Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) accurate 82%

$ 2543/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 805 MPa
Tensile Strength, Ultimate: 570 MPa @Temperature 649 °C
Elongation at Break: 38.6 %
Elongation at Break: 26.5 % @Temperature 649 °C

Haynes Hastelloy® N, weld metal as welded accurate 82%

$ 2254/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 800 MPa
Tensile Strength, Ultimate: 507 MPa @Temperature 649 °C
Elongation at Break: 39.3 %
Elongation at Break: 18.1 % @Temperature 649 °C

Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) accurate 82%

$ 1768/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 800 MPa
Tensile Strength, Ultimate: 565 MPa @Temperature 649 °C
Tensile Strength, Yield: 323 MPa @Strain 0.200 %
Elongation at Break: 46 %

Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) accurate 82%

$ 2028/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 796 MPa
Tensile Strength, Yield: 340 MPa @Strain 0.200 %
Elongation at Break: 46.8 %
Modulus of Elasticity: 122 GPa @Temperature 1049 °C

Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) accurate 82%

$ 1492/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 796 MPa
Tensile Strength, Ultimate: 525 MPa @Temperature 704 °C
Tensile Strength, Yield: 316 MPa @Strain 0.200 %
Elongation at Break: 46 %

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 99%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) accurate 82%

$ 1496/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 812 MPa
Tensile Strength, Ultimate: 674 MPa @Temperature 538 °C
Tensile Strength, Yield: 311 MPa @Strain 0.200 %
Elongation at Break: 50 %

Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded accurate 82%

$ 1830/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 800 MPa
Tensile Strength, Ultimate: 359 MPa @Temperature 816 °C
Tensile Strength, Ultimate: 438 MPa @Temperature 704 °C
Tensile Strength, Ultimate: 493 MPa @Temperature 649 °C

Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) accurate 82%

$ 1762/MT

Density: 8.86 g/cc
Tensile Strength, Ultimate: 793 MPa
Tensile Strength, Ultimate: 453 MPa @Temperature 760 °C
Tensile Strength, Yield: 301 MPa @Strain 0.200 %
Elongation at Break: 40 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, chemical tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled

Seller from Santiago – 2021-03-17:

Seller from Santiago work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2033 per MT

Seller from Mexico City – 2021-07-24:

Seller from Mexico City work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $1691 per MT

Seller from Los Angeles – 2021-07-07:

Seller from Los Angeles work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1630 per MT