Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C)

Seller in Toronto price: $2521 per MT

Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) in Nickel Alloy

  • Physical Properties
  • Density
  • 8.37 g/cc
  • Mechanical Properties
  • Tensile Strength, Ultimate
  • 66.0 MPa @Temperature 980 °C
  • Tensile Strength, Ultimate
  • 286 MPa @Temperature 760 °C
  • Tensile Strength, Ultimate
  • 439 MPa @Temperature 870 °C
  • Tensile Strength, Ultimate
  • 473 MPa @Temperature 650 °C
  • Tensile Strength, Ultimate
  • 726 MPa @Temperature 540 °C
  • Tensile Strength, Ultimate
  • 792 MPa @Temperature 25.0 °C
  • Tensile Strength, Yield
  • 31.0 MPa @Strain 0.200 %, Temperature 980 °C
  • Tensile Strength, Yield
  • 68.0 MPa @Strain 0.200 %, Temperature 870 °C
  • Tensile Strength, Yield
  • 152 MPa @Strain 0.200 %, Temperature 760 °C
  • Tensile Strength, Yield
  • 275 MPa @Strain 0.200 %, Temperature 650 °C
  • Tensile Strength, Yield
  • 363 MPa @Strain 0.200 %, Temperature 540 °C
  • Tensile Strength, Yield
  • 407 MPa @Strain 0.200 %, Temperature 25.0 °C
  • Elongation at Break
  • 27 % @Temperature 540 °C
  • Elongation at Break
  • 31 % @Temperature 25.0 °C
  • Elongation at Break
  • 32 % @Temperature 650 °C
  • Elongation at Break
  • 75 % @Temperature 760 °C
  • Elongation at Break
  • 90 % @Temperature 870 °C
  • Elongation at Break
  • 91 % @Temperature 980 °C
  • Rupture Strength
  • 8.30 MPa @Temperature 870 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 14.0 MPa @Temperature 870 °C, Time 360000 sec
  • Rupture Strength
  • 15.0 MPa @Temperature 815 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 25.0 MPa @Temperature 870 °C, Time 36000 sec
  • Rupture Strength
  • 26.0 MPa @Temperature 815 °C, Time 360000 sec
  • Rupture Strength
  • 26.0 MPa @Temperature 760 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 40.0 MPa @Temperature 815 °C, Time 36000 sec
  • Rupture Strength
  • 41.0 MPa @Temperature 760 °C, Time 360000 sec
  • Rupture Strength
  • 47.0 MPa @Temperature 705 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 66.0 MPa @Temperature 760 °C, Time 36000 sec
  • Rupture Strength
  • 70.0 MPa @Temperature 705 °C, Time 360000 sec
  • Rupture Strength
  • 83.0 MPa @Temperature 650 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 110 MPa @Temperature 705 °C, Time 36000 sec
  • Rupture Strength
  • 130 MPa @Temperature 650 °C, Time 360000 sec
  • Rupture Strength
  • 185 MPa @Temperature 650 °C, Time 36000 sec
  • Modulus of Elasticity
  • 140 GPa @Temperature 1000 °C
  • Modulus of Elasticity
  • 153 GPa @Temperature 900 °C
  • Modulus of Elasticity
  • 165 GPa @Temperature 800 °C
  • Modulus of Elasticity
  • 173 GPa @Temperature 700 °C
  • Modulus of Elasticity
  • 181 GPa @Temperature 600 °C
  • Modulus of Elasticity
  • 197 GPa @Temperature 400 °C
  • Modulus of Elasticity
  • 210 GPa @Temperature 200 °C
  • Modulus of Elasticity
  • 221 GPa @Temperature 20.0 °C
  • Thermal Properties
  • CTE, linear
  • 14.3 µm/m-°C @Temperature 20.0 - 500 °C
  • CTE, linear
  • 15.0 µm/m-°C @Temperature 20.0 - 600 °C
  • CTE, linear
  • 15.4 µm/m-°C @Temperature 20.0 - 700 °C
  • CTE, linear
  • 16.5 µm/m-°C @Temperature 20.0 - 800 °C
  • CTE, linear
  • 17.1 µm/m-°C @Temperature 20.0 - 900 °C
  • CTE, linear
  • 18.2 µm/m-°C @Temperature 20.0 - 1000 °C
  • Thermal Conductivity
  • 18.6 W/m-K @Temperature 400 °C
  • Thermal Conductivity
  • 22.7 W/m-K @Temperature 600 °C
  • Thermal Conductivity
  • 24.7 W/m-K @Temperature 700 °C
  • Thermal Conductivity
  • 26.5 W/m-K @Temperature 800 °C
  • Thermal Conductivity
  • 28.4 W/m-K @Temperature 900 °C
  • Thermal Conductivity
  • 30.1 W/m-K @Temperature 1000 °C
  • Melting Point
  • 1340 - 1380 °C
  • Solidus
  • 1340 °C
  • Liquidus
  • 1380 °C
  • Electrical Properties
  • Electrical Resistivity
  • 0.000112 ohm-cm @Temperature 200 °C
  • Electrical Resistivity
  • 0.000115 ohm-cm @Temperature 600 °C
  • Electrical Resistivity
  • 0.000115 ohm-cm @Temperature 700 °C
  • Electrical Resistivity
  • 0.000115 ohm-cm @Temperature 800 °C
  • Electrical Resistivity
  • 0.000115 ohm-cm @Temperature 900 °C
  • Electrical Resistivity
  • 0.000116 ohm-cm @Temperature 1000 °C
  • Electrical Resistivity
  • 0.000117 ohm-cm @Temperature 400 °C
  • Processing Properties
  • Annealing Temperature
  • 1052 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C)

Seller from Toronto – 2021-06-29:

Seller from Toronto work with company: Solvay, Dow Corning, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2521 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit