Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled price 1493 per MT

Physical Properties
Density
8.25 g/cc

Mechanical Properties
Tensile Strength, Ultimate
664 MPa @Temperature 871 °C
Tensile Strength, Ultimate
924 MPa @Temperature 760 °C
Tensile Strength, Ultimate
1047 MPa @Temperature 649 °C
Tensile Strength, Yield
506 MPa @Strain 0.200 %, Temperature 871 °C
Tensile Strength, Yield
785 MPa @Strain 0.200 %, Temperature 760 °C
Tensile Strength, Yield
847 MPa @Strain 0.200 %, Temperature 649 °C
Elongation at Break
2.0 % @Temperature 871 °C
Elongation at Break
4.0 % @Temperature 760 °C
Elongation at Break
7.0 % @Temperature 649 °C
Modulus of Elasticity
185 GPa
Modulus of Elasticity
110 GPa @Temperature 871 °C
Modulus of Elasticity
163 GPa @Temperature 760 °C
Modulus of Elasticity
185 GPa @Temperature 649 °C
Poissons Ratio
0.31
Poissons Ratio
0.31 @Temperature 149 °C
Poissons Ratio
0.32 @Temperature 482 °C
Poissons Ratio
0.32 @Temperature 371 °C
Poissons Ratio
0.32 @Temperature 260 °C
Poissons Ratio
0.33 @Temperature 760 °C
Poissons Ratio
0.33 @Temperature 677 °C
Poissons Ratio
0.33 @Temperature 649 °C
Poissons Ratio
0.34 @Temperature 843 °C
Poissons Ratio
0.35 @Temperature 927 °C
Shear Modulus
83.0 GPa
Shear Modulus
55.0 GPa @Temperature 927 °C
Shear Modulus
61.0 GPa @Temperature 843 °C
Shear Modulus
64.0 GPa @Temperature 760 °C
Shear Modulus
67.0 GPa @Temperature 677 °C
Shear Modulus
69.0 GPa @Temperature 593 °C
Shear Modulus
72.0 GPa @Temperature 482 °C
Shear Modulus
75.0 GPa @Temperature 371 °C
Shear Modulus
77.0 GPa @Temperature 260 °C
Shear Modulus
81.0 GPa @Temperature 149 °C

Thermal Properties
CTE, linear
13.5 µm/m-°C @Temperature 21.0 - 538 °C
CTE, linear
14.0 µm/m-°C @Temperature 21.0 - 649 °C
CTE, linear
14.8 µm/m-°C @Temperature 21.0 - 760 °C
CTE, linear
15.2 µm/m-°C @Temperature 21.0 - 871 °C
CTE, linear
16.3 µm/m-°C @Temperature 21.0 - 927 °C
CTE, linear
16.8 µm/m-°C @Temperature 21.0 - 982 °C
Specific Heat Capacity
0.452 J/g-°C @Temperature 21.0 °C
Thermal Conductivity
11.5 W/m-K @Temperature 149 °C
Thermal Conductivity
12.5 W/m-K @Temperature 204 °C
Thermal Conductivity
13.6 W/m-K @Temperature 260 °C
Thermal Conductivity
14.7 W/m-K @Temperature 316 °C
Thermal Conductivity
16.8 W/m-K @Temperature 427 °C
Thermal Conductivity
18.8 W/m-K @Temperature 538 °C
Thermal Conductivity
20.0 W/m-K @Temperature 593 °C
Thermal Conductivity
21.0 W/m-K @Temperature 644 °C
Thermal Conductivity
22.0 W/m-K @Temperature 704 °C
Thermal Conductivity
23.1 W/m-K @Temperature 760 °C
Thermal Conductivity
24.1 W/m-K @Temperature 816 °C
Thermal Conductivity
25.1 W/m-K @Temperature 871 °C
Melting Point
1310 - 1345 °C
Solidus
1310 °C
Liquidus
1335 °C

Component Elements Properties
Aluminum, Al
1.4 - 1.6 %
Boron, B
0.0030 - 0.010 %
Carbon, C
0.050 - 0.12 %
Chromium, Cr
18 - 20 %
Cobalt, Co
10 - 12 %
Iron, Fe
<= 5.0 %
Manganese, Mn
<= 0.10 %
Molybdenum, Mo
9.0 - 10.5 %
Nickel, Ni
53 %
Silicon, Si
<= 0.50 %
Sulfur, S
<= 0.015 %
Titanium, Ti
3.0 - 3.3 %

Electrical Properties
Magnetic Permeability
<= 1.002 @Temperature 21.0 °C

Alternative products

Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1400°F (760°C) accurate 77%

$ 1481/MT

Density: 8.44 g/cc
Hardness, Rockwell B: 96
Tensile Strength, Ultimate: 1012 MPa
Tensile Strength, Yield: 609 MPa @Strain 0.200 %
Elongation at Break: 36 %

Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work accurate 77%

$ 2115/MT

Density: 8.44 g/cc
Tensile Strength, Ultimate: 972 MPa
Tensile Strength, Yield: 529 MPa @Strain 0.200 %
Elongation at Break: 42 %
Modulus of Elasticity: 208 GPa

Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work accurate 77%

$ 2384/MT

Density: 8.44 g/cc
Tensile Strength, Ultimate: 951 MPa
Tensile Strength, Yield: 563 MPa @Strain 0.200 %
Elongation at Break: 46 %
Modulus of Elasticity: 208 GPa

Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1200°F (650°C) accurate 77%

$ 1746/MT

Density: 8.44 g/cc
Hardness, Rockwell B: 100
Tensile Strength, Ultimate: 1040 MPa
Tensile Strength, Yield: 835.6 MPa @Strain 0.200 %
Elongation at Break: 31 %

Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) accurate 77%

$ 1465/MT

Density: 8.44 g/cc
Hardness, Rockwell B: 96
Tensile Strength, Ultimate: 957.0 MPa
Tensile Strength, Yield: 535 MPa @Strain 0.200 %
Elongation at Break: 45 %

Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) accurate 77%

$ 1458/MT

Density: 8.44 g/cc
Hardness, Rockwell B: 84
Tensile Strength, Ultimate: 769.5 MPa
Tensile Strength, Yield: 319 MPa @Strain 0.200 %
Elongation at Break: 63 %

Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work accurate 77%

$ 1774/MT

Density: 8.44 g/cc
Tensile Strength, Ultimate: 973.5 MPa
Tensile Strength, Yield: 527 MPa @Strain 0.200 %
Elongation at Break: 42 %
Modulus of Elasticity: 208 GPa

Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C) accurate 77%

$ 1894/MT

Density: 8.44 g/cc
Hardness, Rockwell B: 95
Tensile Strength, Ultimate: 836.3 MPa
Tensile Strength, Yield: 390 MPa @Strain 0.200 %
Elongation at Break: 50 %

ATI Allegheny Ludlum AL 625HP™ Stainless Steel accurate 99%

$ 1468/MT

Density: 8.44 g/cc
Tensile Strength, Ultimate: 940 MPa
Tensile Strength, Yield: 485 MPa
Elongation at Break: 46 %
Modulus of Elasticity: 205 GPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship cargo for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

6 prices for Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled

Seller from Shenyang – 2021-08-03:

Seller from Shenyang work with company: 3M, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2139 per MT

Seller from Tehran – 2021-07-19:

Seller from Tehran work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1493 per MT

Seller from Delhi – 2021-06-04:

Seller from Delhi work with company: Solvay, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2593 per MT

Seller from Tehran – 2021-05-30:

Seller from Tehran work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1999 per MT

Seller from Hechi – 2021-06-14:

Seller from Hechi work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2105 per MT

Seller from Saint Petersburg – 2021-07-11:

Seller from Saint Petersburg work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1870 per MT

Would you like to sell Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled?