Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform price 1681 per MT

Physical Properties
Density
8.22 g/cc

Mechanical Properties
Tensile Strength, Ultimate
441 MPa @Diameter 12.7 mm, Temperature 538 °C
Tensile Strength, Ultimate
538 MPa @Diameter 12.7 mm, Temperature 260 °C
Tensile Strength, Ultimate
696 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Yield
302 MPa @Diameter 12.7 mm, Temperature 538 °C
Tensile Strength, Yield
336 MPa @Diameter 12.7 mm, Temperature 260 °C
Tensile Strength, Yield
486 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Elongation at Break
42 % @Diameter 12.7 mm, Temperature 538 °C
Elongation at Break
43 % @Diameter 12.7 mm, Temperature 25.0 °C
Elongation at Break
46 % @Diameter 12.7 mm, Temperature 260 °C
Modulus of Elasticity
170 GPa @Temperature 649 °C
Modulus of Elasticity
177 GPa @Temperature 538 °C
Modulus of Elasticity
183 GPa @Temperature 427 °C
Modulus of Elasticity
189 GPa @Temperature 316 °C
Modulus of Elasticity
204 GPa @Temperature 25.0 °C

Thermal Properties
CTE, linear
12.3 µm/m-°C @Temperature 21.0 - 100 °C
CTE, linear
12.6 µm/m-°C @Temperature 21.0 - 200 °C
CTE, linear
13.2 µm/m-°C @Temperature 21.0 - 300 °C
CTE, linear
13.4 µm/m-°C @Temperature 21.0 - 400 °C
CTE, linear
13.6 µm/m-°C @Temperature 21.0 - 500 °C
CTE, linear
14.4 µm/m-°C @Temperature 21.0 - 600 °C
Specific Heat Capacity
0.450 J/g-°C @Temperature 25.0 °C
Specific Heat Capacity
0.470 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.490 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.510 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.530 J/g-°C @Temperature 400 °C
Specific Heat Capacity
0.530 J/g-°C @Temperature 500 °C
Specific Heat Capacity
0.600 J/g-°C @Temperature 600 °C
Thermal Conductivity
10.0 W/m-K @Temperature 25.0 °C
Thermal Conductivity
12.0 W/m-K @Temperature 100 °C
Thermal Conductivity
14.0 W/m-K @Temperature 200 °C
Thermal Conductivity
16.0 W/m-K @Temperature 300 °C
Thermal Conductivity
18.0 W/m-K @Temperature 400 °C
Thermal Conductivity
19.0 W/m-K @Temperature 500 °C
Thermal Conductivity
23.0 W/m-K @Temperature 600 °C
Melting Point
1332 - 1361 °C
Solidus
1332 °C
Liquidus
1361 °C

Component Elements Properties
Aluminum, Al
<= 0.40 %
Carbon, C
<= 0.050 %
Chromium, Cr
33 %
Iron, Fe
<= 2.0 %
Manganese, Mn
<= 0.50 %
Molybdenum, Mo
8.0 %
Nickel, Ni
55.5 %
Silicon, Si
<= 0.60 %

Electrical Properties
Electrical Resistivity
0.000118 ohm-cm @Temperature 25.0 °C
Electrical Resistivity
0.000119 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.000120 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.000121 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000122 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000124 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000125 ohm-cm @Temperature 600 °C

Processing Properties
Annealing Temperature
1120 °C

Descriptive Properties
Thermal Diffusivity
0.028 cm/s
Thermal Diffusivity
0.031 cm/s
Thermal Diffusivity
0.034 cm/s
Thermal Diffusivity
0.038 cm/s
Thermal Diffusivity
0.042 cm/s
Thermal Diffusivity
0.045 cm/s
Thermal Diffusivity
0.048 cm/s

Alternative products

Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed accurate 74%

$ 1570/MT

Density: 8.83 g/cc
Tensile Strength, Ultimate: 745 MPa @Thickness 3.20 mm, Temperature 316 °C
Tensile Strength, Ultimate: 747 MPa @Thickness 3.20 mm, Temperature 371 °C
Tensile Strength, Ultimate: 754 MPa @Thickness 3.20 mm, Temperature 260 °C
Tensile Strength, Ultimate: 763 MPa @Thickness 3.20 mm, Temperature 204 °C

Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate accurate 74%

$ 2310/MT

Density: 8.22 g/cc
Tensile Strength, Ultimate: 501 MPa @Thickness 12.7 mm, Temperature 538 °C
Tensile Strength, Ultimate: 555 MPa @Thickness 12.7 mm, Temperature 260 °C
Tensile Strength, Ultimate: 724 MPa @Thickness 12.7 mm, Temperature 25.0 °C
Tensile Strength, Yield: 246 MPa @Thickness 12.7 mm, Temperature 538 °C

Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform accurate 74%

$ 1545/MT

Density: 8.83 g/cc
Tensile Strength, Ultimate: 613 MPa @Diameter 12.7 mm, Temperature 427 °C
Tensile Strength, Ultimate: 632 MPa @Diameter 12.7 mm, Temperature 371 °C
Tensile Strength, Ultimate: 647 MPa @Diameter 12.7 mm, Temperature 260 °C
Tensile Strength, Ultimate: 651 MPa @Diameter 12.7 mm, Temperature 316 °C

Osprey Metals 430L Stainless Steel Powder (Grade 90% - 22) accurate 74%

$ 1750/MT

Particle Size: 10 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.030 %
Chromium, Cr: 16 - 18 %
Iron, Fe: 81.79 %

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform accurate 87%

$ 1817/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Tensile Strength, Ultimate: 724 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Ultimate: 1054 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Yield: 455 MPa @Diameter 12.7 mm

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 99%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) accurate 74%

$ 1482/MT

Density: 8.22 g/cc
Modulus of Elasticity: 170 GPa @Temperature 649 °C
Modulus of Elasticity: 177 GPa @Temperature 538 °C
Modulus of Elasticity: 183 GPa @Temperature 427 °C
Modulus of Elasticity: 189 GPa @Temperature 316 °C

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform accurate 87%

$ 1617/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Tensile Strength, Ultimate: 708 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Ultimate: 1062 MPa @Diameter 12.7 mm, Temperature 25.0 °C
Tensile Strength, Yield: 458 MPa @Diameter 12.7 mm

Osprey Metals Co212-e Cobalt Alloy Powder (Grade 80% - 22) accurate 74%

$ 2148/MT

Particle Size: 12 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.20 %
Chromium, Cr: 27 - 30 %
Cobalt, Co: 62.85 %

Haynes Hastelloy® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet accurate 87%

$ 1643/MT

Density: 8.60 g/cc
Density: 8.64 g/cc
Tensile Strength, Ultimate: 799 MPa @Thickness 3.20 mm, Temperature 25.0 °C
Tensile Strength, Ultimate: 1088 MPa @Thickness 3.20 mm, Temperature 25.0 °C
Tensile Strength, Yield: 451 MPa @Strain 0.200 %, Thickness 3.20 mm

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform

Seller from Guangzhou – 2021-06-28:

Seller from Guangzhou work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1798 per MT

Seller from Atlanta – 2021-06-01:

Seller from Atlanta work with company: Solvay, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $2227 per MT

Seller from Buenos Aires – 2021-05-27:

Seller from Buenos Aires work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2512 per MT

Seller from Khartoum – 2021-07-28:

Seller from Khartoum work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1681 per MT

Seller from Xi’an – 2021-08-10:

Seller from Xi’an work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1869 per MT