Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure

Seller in Abidjan price: $1454 per MT

Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure in Nickel Alloy

  • Physical Properties
  • Density
  • 8.27 g/cc
  • Density
  • 8.29 g/cc
  • Mechanical Properties
  • Tensile Strength, Ultimate
  • 1152 MPa
  • Tensile Strength, Ultimate
  • 978 MPa @Treatment Temp. 871 °C, Time 5.76e+7 sec
  • Tensile Strength, Ultimate
  • 1006 MPa @Treatment Temp. 871 °C, Time 2.88e+7 sec
  • Tensile Strength, Ultimate
  • 1022 MPa @Treatment Temp. 871 °C, Time 1.44e+7 sec
  • Tensile Strength, Ultimate
  • 1065 MPa @Treatment Temp. 871 °C, Time 3.60e+6 sec
  • Tensile Strength, Ultimate
  • 1114 MPa @Treatment Temp. 871 °C, Time 360000 sec
  • Tensile Strength, Ultimate
  • 1161 MPa @Treatment Temp. 760 °C, Time 5.76e+7 sec
  • Tensile Strength, Ultimate
  • 1191 MPa @Treatment Temp. 760 °C, Time 2.88e+7 sec
  • Tensile Strength, Ultimate
  • 1205 MPa @Treatment Temp. 760 °C, Time 1.44e+7 sec
  • Tensile Strength, Ultimate
  • 1223 MPa @Treatment Temp. 760 °C, Time 360000 sec
  • Tensile Strength, Ultimate
  • 1226 MPa @Treatment Temp. 760 °C, Time 3.60e+6 sec
  • Tensile Strength, Ultimate
  • 1247 MPa @Treatment Temp. 649 °C, Time 360000 sec
  • Tensile Strength, Ultimate
  • 1248 MPa @Treatment Temp. 649 °C, Time 3.60e+6 sec
  • Tensile Strength, Ultimate
  • 1255 MPa @Treatment Temp. 649 °C, Time 1.44e+7 sec
  • Tensile Strength, Ultimate
  • 1260 MPa @Treatment Temp. 649 °C, Time 5.76e+7 sec
  • Tensile Strength, Ultimate
  • 1264 MPa @Treatment Temp. 649 °C, Time 2.88e+7 sec
  • Tensile Strength, Yield
  • 705 MPa
  • Tensile Strength, Yield
  • 452 MPa @Treatment Temp. 871 °C, Time 5.76e+7 sec
  • Tensile Strength, Yield
  • 473 MPa @Treatment Temp. 871 °C, Time 2.88e+7 sec
  • Tensile Strength, Yield
  • 487 MPa @Treatment Temp. 871 °C, Time 1.44e+7 sec
  • Tensile Strength, Yield
  • 533 MPa @Treatment Temp. 871 °C, Time 3.60e+6 sec
  • Tensile Strength, Yield
  • 618 MPa @Treatment Temp. 871 °C, Time 360000 sec
  • Tensile Strength, Yield
  • 658 MPa @Treatment Temp. 760 °C, Time 5.76e+7 sec
  • Tensile Strength, Yield
  • 690 MPa @Treatment Temp. 760 °C, Time 2.88e+7 sec
  • Tensile Strength, Yield
  • 707 MPa @Treatment Temp. 760 °C, Time 1.44e+7 sec
  • Tensile Strength, Yield
  • 742 MPa @Treatment Temp. 760 °C, Time 3.60e+6 sec
  • Tensile Strength, Yield
  • 759 MPa @Treatment Temp. 760 °C, Time 360000 sec
  • Tensile Strength, Yield
  • 798 MPa @Treatment Temp. 649 °C, Time 360000 sec
  • Tensile Strength, Yield
  • 814 MPa @Treatment Temp. 649 °C, Time 3.60e+6 sec
  • Tensile Strength, Yield
  • 816 MPa @Treatment Temp. 649 °C, Time 5.76e+7 sec
  • Tensile Strength, Yield
  • 819 MPa @Treatment Temp. 649 °C, Time 2.88e+7 sec
  • Tensile Strength, Yield
  • 830 MPa @Treatment Temp. 649 °C, Time 1.44e+7 sec
  • Elongation at Break
  • 30 %
  • Elongation at Break
  • 20 % @Treatment Temp. 760 °C, Time 2.88e+7 sec
  • Elongation at Break
  • 20 % @Treatment Temp. 760 °C, Time 5.76e+7 sec
  • Elongation at Break
  • 21 % @Treatment Temp. 760 °C, Time 1.44e+7 sec
  • Elongation at Break
  • 23 % @Treatment Temp. 649 °C, Time 5.76e+7 sec
  • Elongation at Break
  • 24 % @Treatment Temp. 649 °C, Time 2.88e+7 sec
  • Elongation at Break
  • 26 % @Treatment Temp. 649 °C, Time 3.60e+6 sec
  • Elongation at Break
  • 26 % @Treatment Temp. 649 °C, Time 1.44e+7 sec
  • Elongation at Break
  • 26 % @Treatment Temp. 760 °C, Time 3.60e+6 sec
  • Elongation at Break
  • 27 % @Treatment Temp. 649 °C, Time 360000 sec
  • Elongation at Break
  • 27 % @Treatment Temp. 760 °C, Time 360000 sec
  • Elongation at Break
  • 30 % @Treatment Temp. 871 °C, Time 3.60e+6 sec
  • Elongation at Break
  • 31 % @Treatment Temp. 871 °C, Time 360000 sec
  • Elongation at Break
  • 32 % @Treatment Temp. 871 °C, Time 1.44e+7 sec
  • Elongation at Break
  • 32 % @Treatment Temp. 871 °C, Time 2.88e+7 sec
  • Elongation at Break
  • 33 % @Treatment Temp. 871 °C, Time 5.76e+7 sec
  • Reduction of Area
  • 33 %
  • Reduction of Area
  • 19 % @Treatment Temp. 760 °C, Time 5.76e+7 sec
  • Reduction of Area
  • 21 % @Treatment Temp. 760 °C, Time 2.88e+7 sec
  • Reduction of Area
  • 22 % @Treatment Temp. 760 °C, Time 1.44e+7 sec
  • Reduction of Area
  • 25 % @Treatment Temp. 649 °C, Time 5.76e+7 sec
  • Reduction of Area
  • 27 % @Treatment Temp. 649 °C, Time 2.88e+7 sec
  • Reduction of Area
  • 29 % @Treatment Temp. 649 °C, Time 3.60e+6 sec
  • Reduction of Area
  • 29 % @Treatment Temp. 649 °C, Time 1.44e+7 sec
  • Reduction of Area
  • 29 % @Treatment Temp. 760 °C, Time 3.60e+6 sec
  • Reduction of Area
  • 30 % @Treatment Temp. 760 °C, Time 360000 sec
  • Reduction of Area
  • 30 % @Treatment Temp. 871 °C, Time 3.60e+6 sec
  • Reduction of Area
  • 31 % @Treatment Temp. 649 °C, Time 360000 sec
  • Reduction of Area
  • 31 % @Treatment Temp. 871 °C, Time 1.44e+7 sec
  • Reduction of Area
  • 31 % @Treatment Temp. 871 °C, Time 2.88e+7 sec
  • Reduction of Area
  • 32 % @Treatment Temp. 871 °C, Time 5.76e+7 sec
  • Reduction of Area
  • 36 % @Treatment Temp. 871 °C, Time 360000 sec
  • Modulus of Elasticity
  • 217 GPa @Temperature 25.0 °C
  • Poissons Ratio
  • 0.319 @Temperature 25.0 °C
  • Shear Modulus
  • 82.0 GPa @Temperature 25.0 °C
  • Electrical Properties
  • Electrical Resistivity
  • 0.0001278 ohm-cm
  • Electrical Resistivity
  • 0.0001299 ohm-cm
  • Electrical Resistivity
  • 0.0001299 ohm-cm
  • Electrical Resistivity
  • 0.0001318 ohm-cm
  • Electrical Resistivity
  • 0.0001326 ohm-cm

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure

Seller from Abidjan – 2021-03-06:

Seller from Abidjan work with company: 3M, RTP Company, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics)

Price: $1454 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit