Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours

Seller in Bogotá price: $2089 per MT
Seller in Phoenix price: $1993 per MT

Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours in Nickel Alloy, Superalloy

  • Physical Properties
  • Density
  • 8.75 g/cc
  • Mechanical Properties
  • Hardness, Rockwell A
  • 63 @Thickness 12.7 mm
  • Hardness, Rockwell A
  • 66 @Thickness 1.45 mm
  • Tensile Strength, Ultimate
  • 1207 MPa @Thickness 12.7 mm
  • Tensile Strength, Ultimate
  • 1253 MPa @Thickness 1.45 mm
  • Tensile Strength, Yield
  • 707 MPa @Strain 0.200 %, Thickness 12.7 mm
  • Tensile Strength, Yield
  • 741 MPa @Strain 0.200 %, Thickness 1.45 mm
  • Elongation at Break
  • 41 % @Thickness 1.45 mm
  • Elongation at Break
  • 44 % @Thickness 12.7 mm
  • Modulus of Elasticity
  • 132 GPa @Temperature 1093 °C
  • Modulus of Elasticity
  • 151 GPa @Temperature 927 °C
  • Modulus of Elasticity
  • 161 GPa @Temperature 813 °C
  • Modulus of Elasticity
  • 166 GPa @Temperature 760 °C
  • Modulus of Elasticity
  • 174 GPa @Temperature 649 °C
  • Modulus of Elasticity
  • 182 GPa @Temperature 538 °C
  • Modulus of Elasticity
  • 194 GPa @Temperature 357 °C
  • Modulus of Elasticity
  • 212 GPa @Temperature 24.0 °C
  • Charpy Impact
  • 104 J @Temperature 427 °C
  • Thermal Properties
  • CTE, linear
  • 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C
  • CTE, linear
  • 12.2 µm/m-°C @Temperature 20.0 - 204 °C
  • CTE, linear
  • 12.8 µm/m-°C @Temperature 20.0 - 316 °C
  • CTE, linear
  • 13.1 µm/m-°C @Temperature 20.0 - 427 °C
  • CTE, linear
  • 13.3 µm/m-°C @Temperature 20.0 - 538 °C
  • CTE, linear
  • 14.4 µm/m-°C @Temperature 20.0 - 760 °C
  • CTE, linear
  • 14.9 µm/m-°C @Temperature 20.0 - 871 °C
  • CTE, linear
  • 15.5 µm/m-°C @Temperature 20.0 - 982 °C
  • CTE, linear
  • 16.0 µm/m-°C @Temperature 20.0 - 1093 °C
  • Specific Heat Capacity
  • 0.398 J/g-°C @Temperature 0.000 °C
  • Specific Heat Capacity
  • 0.414 J/g-°C @Temperature 50.0 °C
  • Specific Heat Capacity
  • 0.440 J/g-°C @Temperature 150 °C
  • Specific Heat Capacity
  • 0.456 J/g-°C @Temperature 250 °C
  • Specific Heat Capacity
  • 0.473 J/g-°C @Temperature 350 °C
  • Specific Heat Capacity
  • 0.481 J/g-°C @Temperature 450 °C
  • Specific Heat Capacity
  • 0.494 J/g-°C @Temperature 550 °C
  • Specific Heat Capacity
  • 0.502 J/g-°C @Temperature 650 °C
  • Specific Heat Capacity
  • 0.590 J/g-°C @Temperature 800 °C
  • Specific Heat Capacity
  • 0.594 J/g-°C @Temperature 850 °C
  • Specific Heat Capacity
  • 0.594 J/g-°C @Temperature 900 °C
  • Specific Heat Capacity
  • 0.594 J/g-°C @Temperature 700 °C
  • Specific Heat Capacity
  • 0.594 J/g-°C @Temperature 750 °C
  • Specific Heat Capacity
  • 0.598 J/g-°C @Temperature 950 °C
  • Specific Heat Capacity
  • 0.598 J/g-°C @Temperature 1000 °C
  • Specific Heat Capacity
  • 0.598 J/g-°C @Temperature 1050 °C
  • Specific Heat Capacity
  • 0.603 J/g-°C @Temperature 1100 °C
  • Thermal Conductivity
  • 14.0 W/m-K @Temperature 200 °C
  • Thermal Conductivity
  • 16.1 W/m-K @Temperature 300 °C
  • Thermal Conductivity
  • 17.9 W/m-K @Temperature 400 °C
  • Thermal Conductivity
  • 19.5 W/m-K @Temperature 500 °C
  • Thermal Conductivity
  • 21.0 W/m-K @Temperature 600 °C
  • Thermal Conductivity
  • 26.1 W/m-K @Temperature 700 °C
  • Thermal Conductivity
  • 26.1 W/m-K @Temperature 800 °C
  • Thermal Conductivity
  • 26.1 W/m-K @Temperature 900 °C
  • Thermal Conductivity
  • 27.1 W/m-K @Temperature 950 °C
  • Thermal Conductivity
  • 28.0 W/m-K @Temperature 1000 °C
  • Melting Point
  • 1335 - 1380 °C
  • Solidus
  • 1335 °C
  • Liquidus
  • 1380 °C
  • Maximum Service Temperature, Air
  • 1093 °C
  • Component Elements Properties
  • Aluminum, Al
  • 0.10 - 0.50 %
  • Boron, B
  • <= 0.015 %
  • Carbon, C
  • <= 0.020 %
  • Chromium, Cr
  • 14.5 - 17 %
  • Cobalt, Co
  • <= 2.0 %
  • Copper, Cu
  • <= 0.35 %
  • Iron, Fe
  • <= 3.0 %
  • Lanthanum, La
  • 0.010 - 0.10 %
  • Manganese, Mn
  • 0.30 - 1.0 %
  • Molybdenum, Mo
  • 14 - 16.5 %
  • Nickel, Ni
  • 67 %
  • Electrical Properties
  • Electrical Resistivity
  • 0.000128 ohm-cm @Temperature 25.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo boats for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours

Seller from Bogotá – 2021-04-10:

Seller from Bogotá work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2089 per MT

Seller from Phoenix – 2021-03-30:

Seller from Phoenix work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1993 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Tennis court construction company in Singapore open-nearme.com