Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) price 1519 per MT

Physical Properties
Density
8.25 g/cc

Mechanical Properties
Hardness, Brinell
369 @Temperature 760 °C
Hardness, Knoop
403 @Temperature 760 °C
Hardness, Rockwell B
97 @Temperature 760 °C
Hardness, Rockwell C
40 @Temperature 760 °C
Hardness, Vickers
388 @Temperature 760 °C
Tensile Strength, Ultimate
1014 MPa @Temperature 760 °C
Tensile Strength, Yield
819 MPa @Strain 0.200 %, Temperature 760 °C
Elongation at Break
10 % @Temperature 760 °C
Modulus of Elasticity
150 GPa @Temperature 927 °C
Modulus of Elasticity
160 GPa @Temperature 871 °C
Modulus of Elasticity
163 GPa @Temperature 843 °C
Modulus of Elasticity
166 GPa @Temperature 816 °C
Modulus of Elasticity
171 GPa @Temperature 760 °C
Modulus of Elasticity
178 GPa @Temperature 677 °C
Modulus of Elasticity
179 GPa @Temperature 649 °C
Modulus of Elasticity
182 GPa @Temperature 593 °C
Modulus of Elasticity
188 GPa @Temperature 538 °C
Modulus of Elasticity
190 GPa @Temperature 482 °C
Modulus of Elasticity
198 GPa @Temperature 371 °C
Modulus of Elasticity
204 GPa @Temperature 260 °C
Modulus of Elasticity
213 GPa @Temperature 149 °C
Modulus of Elasticity
218 GPa @Temperature 21.0 °C
Poissons Ratio
0.31 @Temperature 149 °C
Poissons Ratio
0.31 @Temperature 27.0 °C
Poissons Ratio
0.32 @Temperature 482 °C
Poissons Ratio
0.32 @Temperature 371 °C
Poissons Ratio
0.32 @Temperature 260 °C
Poissons Ratio
0.33 @Temperature 649 °C
Poissons Ratio
0.33 @Temperature 760 °C
Poissons Ratio
0.33 @Temperature 677 °C
Poissons Ratio
0.34 @Temperature 843 °C
Poissons Ratio
0.35 @Temperature 927 °C
Shear Modulus
55.0 GPa @Temperature 927 °C
Shear Modulus
61.0 GPa @Temperature 843 °C
Shear Modulus
64.0 GPa @Temperature 760 °C
Shear Modulus
67.0 GPa @Temperature 677 °C
Shear Modulus
69.0 GPa @Temperature 593 °C
Shear Modulus
72.0 GPa @Temperature 482 °C
Shear Modulus
75.0 GPa @Temperature 371 °C
Shear Modulus
77.0 GPa @Temperature 260 °C
Shear Modulus
81.0 GPa @Temperature 149 °C
Shear Modulus
83.0 GPa @Temperature 27.0 °C

Thermal Properties
CTE, linear
13.5 µm/m-°C @Temperature 21.0 - 538 °C
CTE, linear
14.0 µm/m-°C @Temperature 21.0 - 649 °C
CTE, linear
14.8 µm/m-°C @Temperature 21.0 - 760 °C
CTE, linear
15.2 µm/m-°C @Temperature 21.0 - 871 °C
CTE, linear
16.3 µm/m-°C @Temperature 21.0 - 927 °C
CTE, linear
16.8 µm/m-°C @Temperature 21.0 - 982 °C
Specific Heat Capacity
0.452 J/g-°C @Temperature 27.0 °C
Thermal Conductivity
11.5 W/m-K @Temperature 149 °C
Thermal Conductivity
12.5 W/m-K @Temperature 204 °C
Thermal Conductivity
13.6 W/m-K @Temperature 260 °C
Thermal Conductivity
14.7 W/m-K @Temperature 316 °C
Thermal Conductivity
16.8 W/m-K @Temperature 427 °C
Thermal Conductivity
18.8 W/m-K @Temperature 538 °C
Thermal Conductivity
20.0 W/m-K @Temperature 593 °C
Thermal Conductivity
21.0 W/m-K @Temperature 644 °C
Thermal Conductivity
22.0 W/m-K @Temperature 704 °C
Thermal Conductivity
23.1 W/m-K @Temperature 760 °C
Thermal Conductivity
24.1 W/m-K @Temperature 816 °C
Thermal Conductivity
25.1 W/m-K @Temperature 871 °C
Melting Point
1310 - 1345 °C
Solidus
1310 °C
Liquidus
1335 °C

Component Elements Properties
Aluminum, Al
1.4 - 1.6 %
Boron, B
0.0030 - 0.010 %
Carbon, C
0.050 - 0.12 %
Chromium, Cr
18 - 20 %
Cobalt, Co
10 - 12 %
Iron, Fe
<= 5.0 %
Manganese, Mn
<= 0.10 %
Molybdenum, Mo
9.0 - 10.5 %
Nickel, Ni
53 %
Silicon, Si
<= 0.50 %

Electrical Properties
Magnetic Permeability
<= 1.002 @Temperature 21.0 °C

Alternative products

Osprey Metals 80/20 Ni Cr Powder (Grade 95% - 16) accurate 99%

$ 2262/MT

Particle Size: 6.7 µm
Carbon, C: 0.020 %
Carbon, C: <= 0.10 %
Chromium, Cr: 19 - 21 %
Iron, Fe: <= 0.50 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 95% - 16) accurate 99%

$ 1562/MT

Particle Size: 6.7 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals D2 Tool Steel Powder (Grade 90% - 22) accurate 99%

$ 1598/MT

Particle Size: 10 µm
Carbon, C: 1.4 - 1.6 %
Chromium, Cr: 11.5 - 12.5 %
Iron, Fe: 84.2 %
Manganese, Mn: 0.40 %

Osprey Metals 430L Stainless Steel Powder (Grade 80% - 22) accurate 99%

$ 1471/MT

Particle Size: 12 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.030 %
Chromium, Cr: 16 - 18 %
Iron, Fe: 81.79 %

Osprey Metals 410L Stainless Steel Powder (Grade 80% - 22) accurate 99%

$ 2139/MT

Particle Size: 12 µm
Carbon, C: 0.010 %
Carbon, C: <= 0.030 %
Chromium, Cr: 11.5 - 13.5 %
Iron, Fe: 85.89 %

Osprey Metals 420 Stainless Steel Powder (Grade 90% - 22) accurate 99%

$ 2111/MT

Particle Size: 10 µm
Carbon, C: >= 0.15 %
Carbon, C: 0.50 %
Chromium, Cr: 12 - 14 %
Iron, Fe: 85 %

Osprey Metals Co212-e Cobalt Alloy Powder (Grade 95% - 16) accurate 99%

$ 2089/MT

Particle Size: 6.7 µm
Carbon, C: 0.050 %
Carbon, C: <= 0.20 %
Chromium, Cr: 27 - 30 %
Cobalt, Co: 62.85 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 80% - 22) accurate 99%

$ 1507/MT

Particle Size: 12 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 99%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

H.C. Starck Pure Molybdenum OMPP Pellets (99.8%) accurate 99%

$ 2379/MT

Density: >= 7.00 g/cc
Aluminum, Al: 0.0020 %
Aluminum, Al: <= 0.010 %
Calcium, Ca: 0.0010 %
Calcium, Ca: <= 0.010 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale nl. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F)

Seller from Delhi – 2021-08-16:

Seller from Delhi work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2054 per MT

Seller from Ahmadābād – 2021-05-22:

Seller from Ahmadābād work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2555 per MT

Seller from Bengalūru – 2021-06-27:

Seller from Bengalūru work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1660 per MT

Seller from Karachi – 2021-05-20:

Seller from Karachi work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1695 per MT

Seller from Jakarta – 2021-03-12:

Seller from Jakarta work with company: Solvay, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1519 per MT