Haynes 282® Nickel Alloy Sheet, Plate and Bar, Solution Annealed

Seller in Mumbai price: $1492 per MT
Seller in Hāora price: $1963 per MT

Haynes 282® Nickel Alloy Sheet, Plate and Bar, Solution Annealed in Nickel Alloy

  • Physical Properties
  • Density
  • 8.27 g/cc
  • Mechanical Properties
  • Hardness, Rockwell B
  • 93
  • Hardness, Rockwell C
  • 15
  • Tensile Strength, Ultimate
  • 816 MPa
  • Tensile Strength, Ultimate
  • 830 MPa
  • Tensile Strength, Ultimate
  • 834 MPa @Thickness 3.20 mm
  • Tensile Strength, Yield
  • 348 MPa @Strain 0.200 %
  • Tensile Strength, Yield
  • 384 MPa @Strain 0.200 %
  • Tensile Strength, Yield
  • 383 MPa @Strain 0.200 %, Thickness 3.20 mm
  • Elongation at Break
  • 60 %
  • Elongation at Break
  • 62 %
  • Elongation at Break
  • 58 % @Thickness 3.20 mm
  • Reduction of Area
  • 61 %
  • Reduction of Area
  • 69 %
  • Creep Strength
  • 12.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
  • Creep Strength
  • 29.0 MPa @Temperature 982 °C, Time 360000 sec
  • Creep Strength
  • 33.0 MPa @Temperature 927 °C, Time 3.60e+6 sec
  • Creep Strength
  • 65.0 MPa @Temperature 927 °C, Time 360000 sec
  • Creep Strength
  • 76.0 MPa @Temperature 871 °C, Time 3.60e+6 sec
  • Creep Strength
  • 124 MPa @Temperature 871 °C, Time 360000 sec
  • Creep Strength
  • 138 MPa @Temperature 816 °C, Time 3.60e+6 sec
  • Creep Strength
  • 221 MPa @Temperature 816 °C, Time 360000 sec
  • Creep Strength
  • 241 MPa @Temperature 760 °C, Time 3.60e+6 sec
  • Creep Strength
  • 338 MPa @Temperature 760 °C, Time 360000 sec
  • Creep Strength
  • 365 MPa @Temperature 704 °C, Time 3.60e+6 sec
  • Creep Strength
  • 503 MPa @Temperature 704 °C, Time 360000 sec
  • Creep Strength
  • 558 MPa @Temperature 649 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 25.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 43.0 MPa @Temperature 982 °C, Time 360000 sec
  • Rupture Strength
  • 48.0 MPa @Temperature 927 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 90.0 MPa @Temperature 927 °C, Time 360000 sec
  • Rupture Strength
  • 97.0 MPa @Temperature 871 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 159 MPa @Temperature 871 °C, Time 360000 sec
  • Rupture Strength
  • 172 MPa @Temperature 816 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 186 MPa @Temperature 760 °C, Time 3.60e+7 sec
  • Rupture Strength
  • 262 MPa @Temperature 816 °C, Time 360000 sec
  • Rupture Strength
  • 283 MPa @Temperature 760 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 310 MPa @Temperature 704 °C, Time 3.60e+7 sec
  • Rupture Strength
  • 393 MPa @Temperature 760 °C, Time 360000 sec
  • Rupture Strength
  • 421 MPa @Temperature 704 °C, Time 3.60e+6 sec
  • Rupture Strength
  • 441 MPa @Temperature 649 °C, Time 3.60e+7 sec
  • Rupture Strength
  • 552 MPa @Temperature 704 °C, Time 360000 sec
  • Rupture Strength
  • 586 MPa @Temperature 649 °C, Time 3.60e+6 sec
  • Modulus of Elasticity
  • 140 GPa @Temperature 1000 °C
  • Modulus of Elasticity
  • 154 GPa @Temperature 900 °C
  • Modulus of Elasticity
  • 166 GPa @Temperature 800 °C
  • Modulus of Elasticity
  • 175 GPa @Temperature 700 °C
  • Modulus of Elasticity
  • 183 GPa @Temperature 600 °C
  • Modulus of Elasticity
  • 190 GPa @Temperature 500 °C
  • Modulus of Elasticity
  • 196 GPa @Temperature 400 °C
  • Modulus of Elasticity
  • 202 GPa @Temperature 300 °C
  • Modulus of Elasticity
  • 209 GPa @Temperature 200 °C
  • Modulus of Elasticity
  • 213 GPa @Temperature 100 °C
  • Modulus of Elasticity
  • 217 GPa @Temperature 25.0 °C
  • Poissons Ratio
  • 0.319 @Temperature 25.0 °C
  • Poissons Ratio
  • 0.326 @Temperature 100 °C
  • Poissons Ratio
  • 0.335 @Temperature 200 °C
  • Poissons Ratio
  • 0.335 @Temperature 300 °C
  • Poissons Ratio
  • 0.337 @Temperature 400 °C
  • Poissons Ratio
  • 0.341 @Temperature 500 °C
  • Poissons Ratio
  • 0.346 @Temperature 600 °C
  • Poissons Ratio
  • 0.352 @Temperature 700 °C
  • Poissons Ratio
  • 0.355 @Temperature 800 °C
  • Poissons Ratio
  • 0.357 @Temperature 900 °C
  • Poissons Ratio
  • 0.363 @Temperature 1000 °C
  • Shear Modulus
  • 51.0 GPa @Temperature 1000 °C
  • Shear Modulus
  • 57.0 GPa @Temperature 900 °C
  • Shear Modulus
  • 61.0 GPa @Temperature 800 °C
  • Shear Modulus
  • 65.0 GPa @Temperature 700 °C
  • Shear Modulus
  • 68.0 GPa @Temperature 600 °C
  • Shear Modulus
  • 71.0 GPa @Temperature 500 °C
  • Shear Modulus
  • 73.0 GPa @Temperature 400 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, oil tanker ship sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes 282® Nickel Alloy Sheet, Plate and Bar, Solution Annealed

Seller from Mumbai – 2021-05-05:

Seller from Mumbai work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $1492 per MT

Seller from Hāora – 2021-07-27:

Seller from Hāora work with company: Solvay, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $1963 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit