Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched

Seller in Lahore price: $2514 per MT
Seller in Beijing price: $2267 per MT

Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched in Nickel Alloy, Superalloy

  • Physical Properties
  • Density
  • 8.64 g/cc
  • Mechanical Properties
  • Hardness, Brinell
  • 155 @Thickness 1.70 mm
  • Hardness, Brinell
  • 159 @Thickness 3.20 mm
  • Hardness, Knoop
  • 172 @Thickness 1.70 mm
  • Hardness, Knoop
  • 176 @Thickness 3.20 mm
  • Hardness, Rockwell B
  • 90 @Thickness 1.70 mm
  • Hardness, Rockwell B
  • 92 @Thickness 3.20 mm
  • Hardness, Rockwell B
  • 91 @Thickness 4.00 mm, Temperature 204 °C
  • Hardness, Vickers
  • 191 @Thickness 1.70 mm
  • Hardness, Vickers
  • 201 @Thickness 3.20 mm
  • Tensile Strength, Ultimate
  • 476 MPa @Thickness 3.20 mm, Temperature 760 °C
  • Tensile Strength, Ultimate
  • 571 MPa @Thickness 3.20 mm, Temperature 649 °C
  • Tensile Strength, Ultimate
  • 644 MPa @Thickness 3.20 mm, Temperature 427 °C
  • Tensile Strength, Ultimate
  • 645 MPa @Thickness 3.20 mm, Temperature 538 °C
  • Tensile Strength, Ultimate
  • 656 MPa @Thickness 1.70 mm, Temperature 427 °C
  • Tensile Strength, Ultimate
  • 656 MPa @Thickness 4.00 mm, Temperature 427 °C
  • Tensile Strength, Ultimate
  • 657 MPa @Thickness 4.00 mm, Temperature 316 °C
  • Tensile Strength, Ultimate
  • 672 MPa @Thickness 3.20 mm, Temperature 316 °C
  • Tensile Strength, Ultimate
  • 675 MPa @Thickness 1.70 mm, Temperature 316 °C
  • Tensile Strength, Ultimate
  • 678 MPa @Thickness 3.20 mm, Temperature 204 °C
  • Tensile Strength, Ultimate
  • 689 MPa @Thickness 4.00 mm, Temperature 204 °C
  • Tensile Strength, Ultimate
  • 706 MPa @Thickness 1.70 mm, Temperature 204 °C
  • Tensile Strength, Ultimate
  • 768 MPa @Thickness 1.70 mm, Temperature 20.0 °C
  • Tensile Strength, Ultimate
  • 783 MPa @Thickness 4.00 mm, Temperature 20.0 °C
  • Tensile Strength, Ultimate
  • 801 MPa @Thickness 3.20 mm, Temperature 20.0 °C
  • Tensile Strength, Yield
  • 249 MPa @Thickness 4.00 mm, Temperature 316 °C
  • Tensile Strength, Yield
  • 250 MPa @Thickness 4.00 mm, Temperature 427 °C
  • Tensile Strength, Yield
  • 260 MPa @Thickness 3.20 mm, Temperature 760 °C
  • Tensile Strength, Yield
  • 275 MPa @Thickness 4.00 mm, Temperature 204 °C
  • Tensile Strength, Yield
  • 291 MPa @Thickness 3.20 mm, Temperature 649 °C
  • Tensile Strength, Yield
  • 299 MPa @Thickness 3.20 mm, Temperature 538 °C
  • Tensile Strength, Yield
  • 303 MPa @Thickness 3.20 mm, Temperature 316 °C
  • Tensile Strength, Yield
  • 303 MPa @Thickness 3.20 mm, Temperature 427 °C
  • Tensile Strength, Yield
  • 320 MPa @Thickness 1.70 mm, Temperature 427 °C
  • Tensile Strength, Yield
  • 320 MPa @Thickness 3.20 mm, Temperature 204 °C
  • Tensile Strength, Yield
  • 365 MPa @Thickness 4.00 mm, Temperature 20.0 °C
  • Tensile Strength, Yield
  • 371 MPa @Thickness 1.70 mm, Temperature 316 °C
  • Tensile Strength, Yield
  • 403 MPa @Thickness 1.70 mm, Temperature 204 °C
  • Tensile Strength, Yield
  • 416 MPa @Thickness 1.70 mm, Temperature 20.0 °C
  • Tensile Strength, Yield
  • 421 MPa @Thickness 3.20 mm, Temperature 20.0 °C
  • Elongation at Break
  • 44 % @Thickness 3.20 mm, Temperature 760 °C
  • Elongation at Break
  • 49 % @Thickness 1.70 mm, Temperature 204 °C
  • Elongation at Break
  • 50 % @Thickness 3.20 mm, Temperature 649 °C
  • Elongation at Break
  • 52 % @Thickness 1.70 mm, Temperature 20.0 °C
  • Elongation at Break
  • 52 % @Thickness 1.70 mm, Temperature 316 °C
  • Elongation at Break
  • 54 % @Thickness 3.20 mm, Temperature 20.0 °C
  • Elongation at Break
  • 54 % @Thickness 3.20 mm, Temperature 204 °C
  • Elongation at Break
  • 55 % @Thickness 4.00 mm, Temperature 20.0 °C
  • Elongation at Break
  • 55 % @Thickness 3.20 mm, Temperature 538 °C
  • Elongation at Break
  • 55 % @Thickness 4.00 mm, Temperature 204 °C
  • Elongation at Break
  • 59 % @Thickness 3.20 mm, Temperature 316 °C
  • Elongation at Break
  • 61 % @Thickness 4.00 mm, Temperature 316 °C
  • Elongation at Break
  • 62 % @Thickness 3.20 mm, Temperature 427 °C
  • Elongation at Break
  • 64 % @Thickness 1.70 mm, Temperature 427 °C
  • Elongation at Break
  • 68 % @Thickness 4.00 mm, Temperature 427 °C
  • Modulus of Elasticity
  • 211 GPa
  • Modulus of Elasticity
  • 141 GPa @Temperature 982 °C
  • Modulus of Elasticity
  • 152 GPa @Temperature 871 °C
  • Modulus of Elasticity
  • 162 GPa @Temperature 760 °C
  • Modulus of Elasticity
  • 171 GPa @Temperature 649 °C
  • Modulus of Elasticity
  • 179 GPa @Temperature 538 °C
  • Modulus of Elasticity
  • 187 GPa @Temperature 427 °C
  • Modulus of Elasticity
  • 194 GPa @Temperature 316 °C
  • Modulus of Elasticity
  • 201 GPa @Temperature 204 °C
  • Modulus of Elasticity
  • 207 GPa @Temperature 93.0 °C
  • Electrical Properties
  • Electrical Resistivity
  • 0.000125 ohm-cm @Temperature 23.0 °C
  • Electrical Resistivity
  • 0.000125 ohm-cm @Temperature 100 °C
  • Electrical Resistivity
  • 0.000126 ohm-cm @Temperature 200 °C
  • Electrical Resistivity
  • 0.000127 ohm-cm @Temperature 300 °C
  • Electrical Resistivity
  • 0.000128 ohm-cm @Temperature 400 °C
  • Electrical Resistivity
  • 0.000129 ohm-cm @Temperature 500 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, chemical tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched

Seller from Lahore – 2021-04-23:

Seller from Lahore work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2514 per MT

Seller from Beijing – 2021-05-23:

Seller from Beijing work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2267 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Port operating company in Singapore open-nearme.com