$ 1654/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 958 MPa
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
- Elongation at Break: 28 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1444/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1000 MPa
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
- Elongation at Break: 41 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1594/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1069 MPa
- Tensile Strength, Yield: 552 MPa @Strain 0.200 %
- Elongation at Break: 47 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1813/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 246
- Hardness, Knoop: 267
- Hardness, Rockwell C: 21.9
- Hardness, Vickers: 252
$ 2256/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 164
- Hardness, Knoop: 182
- Hardness, Rockwell B: 95.6
- Hardness, Vickers: 223
$ 2075/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1027 MPa
- Tensile Strength, Yield: 531 MPa @Strain 0.200 %
- Elongation at Break: 44 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1771/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1007 MPa
- Tensile Strength, Yield: 586 MPa @Strain 0.200 %
- Elongation at Break: 29 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1548/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 169
- Hardness, Knoop: 187
- Hardness, Rockwell B: 98.5
- Hardness, Vickers: 245
$ 1931/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 306
- Hardness, Knoop: 373
- Hardness, Rockwell C: 37.1
- Hardness, Vickers: 359
$ 1509/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 266
- Hardness, Knoop: 283
- Hardness, Rockwell C: 26
- Hardness, Vickers: 275
$ 2435/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 848 MPa
- Tensile Strength, Yield: 586 MPa @Strain 0.200 %
- Elongation at Break: 18 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1471/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1014 MPa
- Tensile Strength, Ultimate: 793 MPa @Temperature 538 °C
- Tensile Strength, Ultimate: 903 MPa @Temperature 427 °C
- Tensile Strength, Ultimate: 910 MPa @Temperature 316 °C
$ 1522/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 945 MPa
- Tensile Strength, Ultimate: 130 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 245 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 415 MPa @Temperature 870 °C
$ 1984/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 785 MPa
- Tensile Strength, Yield: 495 MPa @Strain 0.200 %
- Elongation at Break: 9.1 %
- Modulus of Elasticity: 225 GPa
$ 1451/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 282
- Hardness, Knoop: 323
- Hardness, Rockwell C: 31.1
- Hardness, Vickers: 309
$ 1877/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Yield: 485 MPa @Strain 0.200 %
- Elongation at Break: 50.4 %
- Modulus of Elasticity: 232 GPa
$ 1579/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1075 MPa
- Tensile Strength, Yield: 475 MPa @Strain 0.200 %
- Elongation at Break: 26.6 %
- Modulus of Elasticity: 232 GPa
$ 1729/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 2386/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 411
- Hardness, Knoop: 451
- Hardness, Rockwell C: 44
- Hardness, Vickers: 434
$ 2063/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 389
- Hardness, Knoop: 426
- Hardness, Rockwell C: 42
- Hardness, Vickers: 410
$ 1543/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 256
- Hardness, Knoop: 271
- Hardness, Rockwell C: 24
- Hardness, Vickers: 263
$ 1607/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 675 MPa
- Tensile Strength, Ultimate: 195 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 295 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 315 MPa @Temperature 760 °C
$ 1870/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1085 MPa
- Tensile Strength, Yield: 490 MPa @Strain 0.200 %
- Elongation at Break: 28.7 %
- Modulus of Elasticity: 232 GPa
$ 1577/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1260 MPa
- Tensile Strength, Ultimate: 285 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 740 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 945 MPa @Temperature 650 °C
$ 1467/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 167
- Hardness, Knoop: 185
- Hardness, Rockwell B: 97.2
- Hardness, Vickers: 235
$ 1739/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 910 MPa
- Tensile Strength, Yield: 614 MPa @Strain 0.200 %
- Elongation at Break: 17 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1643/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 985 MPa
- Tensile Strength, Ultimate: 83.0 MPa @Temperature 1205 °C
- Tensile Strength, Ultimate: 96.0 MPa @Temperature 1150 °C
- Tensile Strength, Ultimate: 145 MPa @Temperature 1095 °C
$ 2367/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1160 MPa
- Tensile Strength, Ultimate: 885 MPa @Temperature 650 °C
- Tensile Strength, Yield: 940 MPa @Strain 0.200 %
- Tensile Strength, Yield: 715 MPa @Strain 0.200 %, Temperature 650 °C
$ 1658/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Yield: 440 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- Modulus of Elasticity: 232 GPa
$ 2522/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 900 MPa
- Tensile Strength, Yield: 655 MPa @Strain 0.200 %
- Elongation at Break: 12 %
- Modulus of Elasticity: 225 GPa
$ 1766/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1070 MPa
- Tensile Strength, Ultimate: 270 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 425 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 600 MPa @Temperature 760 °C
$ 1896/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 876 MPa
- Tensile Strength, Yield: 614 MPa @Strain 0.200 %
- Elongation at Break: 11 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1772/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 276
- Hardness, Knoop: 312
- Hardness, Rockwell C: 29.6
- Hardness, Vickers: 298
$ 1831/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1500/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 334
- Hardness, Knoop: 362
- Hardness, Rockwell C: 36
- Hardness, Vickers: 349
$ 1540/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1020 MPa
- Tensile Strength, Yield: 545 MPa @Strain 0.200 %
- Elongation at Break: 34 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 2022/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 931 MPa
- Tensile Strength, Yield: 669 MPa @Strain 0.200 %
- Elongation at Break: 9.0 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 2028/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1250 MPa
- Tensile Strength, Ultimate: 295 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 510 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 745 MPa @Temperature 760 °C
$ 1465/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 917 MPa
- Tensile Strength, Yield: 655 MPa @Strain 0.200 %
- Elongation at Break: 10 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 2554/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1145 MPa
- Tensile Strength, Ultimate: 275 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 485 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 715 MPa @Temperature 760 °C
$ 1619/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1045 MPa
- Tensile Strength, Yield: 550 MPa @Strain 0.200 %
- Elongation at Break: 29.1 %
- Modulus of Elasticity: 232 GPa
$ 2336/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 266
- Hardness, Knoop: 283
- Hardness, Rockwell C: 26
- Hardness, Vickers: 275
$ 1835/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 241
- Hardness, Knoop: 255
- Hardness, Rockwell C: 21
- Hardness, Vickers: 247
$ 2074/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 168
- Hardness, Knoop: 186
- Hardness, Rockwell B: 98.1
- Hardness, Vickers: 241
$ 1737/MT
- Rupture Strength: 45.0 MPa @Temperature 982 °C, Time 3.60e+6 sec
- Rupture Strength: 67.0 MPa @Temperature 982 °C, Time 360000 sec
- Maximum Service Temperature, Air: 1200 °C
- Chromium, Cr: 28 %
- Cobalt, Co: 39.75 %
$ 1720/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1015 MPa
- Tensile Strength, Ultimate: 195 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 370 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 620 MPa @Temperature 760 °C
$ 1657/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 331
- Hardness, Knoop: 443
- Hardness, Rockwell C: 43.5
- Hardness, Vickers: 428
$ 1877/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 276
- Hardness, Knoop: 311
- Hardness, Rockwell C: 29.5
- Hardness, Vickers: 297
$ 1562/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 290
- Hardness, Knoop: 311
- Hardness, Rockwell C: 30
- Hardness, Vickers: 301
$ 1892/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1069 MPa
- Tensile Strength, Yield: 558 MPa @Strain 0.200 %
- Elongation at Break: 47 %
- Modulus of Elasticity: 180 GPa @Temperature 649 °C
$ 1571/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 930 MPa
- Tensile Strength, Yield: 460 MPa @Strain 0.200 %
- Elongation at Break: 48.7 %
- Modulus of Elasticity: 225 GPa
$ 1620/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1005 MPa
- Tensile Strength, Ultimate: 160 MPa @Temperature 1095 °C
- Tensile Strength, Ultimate: 235 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 415 MPa @Temperature 870 °C
$ 1736/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 1315 MPa
- Tensile Strength, Ultimate: 290 MPa @Temperature 980 °C
- Tensile Strength, Ultimate: 490 MPa @Temperature 870 °C
- Tensile Strength, Ultimate: 800 MPa @Temperature 760 °C
$ 1469/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 369
- Hardness, Knoop: 403
- Hardness, Rockwell C: 40
- Hardness, Vickers: 388
$ 2463/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 870 MPa
- Tensile Strength, Yield: 535 MPa @Strain 0.200 %
- Elongation at Break: 3.5 %
- Modulus of Elasticity: 225 GPa
$ 1760/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 268
- Hardness, Knoop: 299
- Hardness, Rockwell C: 27.6
- Hardness, Vickers: 285
$ 1562/MT
- Density: 9.13 g/cc
- Tensile Strength, Ultimate: 965 MPa
- Tensile Strength, Yield: 635 MPa @Strain 0.200 %
- Elongation at Break: 24.8 %
- Modulus of Elasticity: 225 GPa
$ 1767/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 1020 MPa
- Tensile Strength, Ultimate: 214 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 352 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 524 MPa @Temperature 760 °C
$ 2205/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 952 MPa
- Tensile Strength, Ultimate: 827 MPa @Temperature 427 °C
- Tensile Strength, Ultimate: 896 MPa @Temperature 316 °C
- Tensile Strength, Ultimate: 924 MPa @Temperature 204 °C
$ 1885/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 676 MPa @Thickness 19.0 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 786 MPa @Thickness 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 800 MPa @Thickness 19.0 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 834 MPa @Thickness 12.7 mm, Temperature 20.0 °C
$ 1599/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 896 MPa
- Tensile Strength, Ultimate: 752 MPa @Temperature 538 °C
- Tensile Strength, Yield: 600 MPa @Strain 0.200 %
- Tensile Strength, Yield: 331 MPa @Strain 0.200 %, Temperature 538 °C
$ 1716/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 304
- Hardness, Knoop: 326
- Hardness, Rockwell C: 32
- Hardness, Vickers: 316
$ 1902/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 167
- Hardness, Knoop: 185
- Hardness, Rockwell B: 97.1
- Hardness, Vickers: 234
$ 1517/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 256
- Hardness, Knoop: 281
- Hardness, Rockwell C: 24.5
- Hardness, Vickers: 266
$ 1770/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 924 MPa
- Tensile Strength, Ultimate: 690 MPa @Temperature 538 °C
- Tensile Strength, Yield: 641 MPa @Strain 0.200 %
- Tensile Strength, Yield: 421 MPa @Strain 0.200 %, Temperature 538 °C
$ 1637/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 322
- Hardness, Knoop: 416
- Hardness, Rockwell C: 41.2
- Hardness, Vickers: 401
$ 2378/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1015 MPa
- Tensile Strength, Yield: 445 MPa @Strain 0.200 %
- Elongation at Break: 22.2 %
- Modulus of Elasticity: 232 GPa
$ 1786/MT
- Density: 8.47 g/cc
- Tensile Strength, Ultimate: 779 MPa @Thickness 12.7 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 779 MPa @Thickness 19.0 mm, Temperature 538 °C
- Tensile Strength, Ultimate: 834 MPa @Thickness 12.7 mm, Temperature 260 °C
- Tensile Strength, Ultimate: 834 MPa @Thickness 19.0 mm, Temperature 260 °C
$ 1539/MT
- Density: 8.98 g/cc
- Tensile Strength, Ultimate: 1020 MPa
- Tensile Strength, Yield: 510 MPa @Strain 0.200 %
- Elongation at Break: 10.8 %
- Modulus of Elasticity: 232 GPa
$ 1515/MT
- Density: 9.13 g/cc
- Hardness, Brinell: 261
- Hardness, Knoop: 277
- Hardness, Rockwell C: 25
- Hardness, Vickers: 269
$ 1717/MT
- Density: 8.47 g/cc
- Hardness, Brinell: 290
- Hardness, Knoop: 311
- Hardness, Rockwell C: 30
- Hardness, Vickers: 301
$ 1712/MT
- Density: 8.98 g/cc
- Hardness, Brinell: 269
- Hardness, Knoop: 300
- Hardness, Rockwell C: 27.8
- Hardness, Vickers: 286
Delivery Cobalt Alloy Haynes International, Inc.
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
cargo ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.