Haynes Ultimet® alloy, 12.7-50.8 mm bar price 1471 per MT

Physical Properties
Density
8.47 g/cc

Mechanical Properties
Tensile Strength, Ultimate
1014 MPa
Tensile Strength, Ultimate
793 MPa @Temperature 538 °C
Tensile Strength, Ultimate
903 MPa @Temperature 427 °C
Tensile Strength, Ultimate
910 MPa @Temperature 316 °C
Tensile Strength, Ultimate
965 MPa @Temperature 93.0 °C
Tensile Strength, Ultimate
965 MPa @Temperature 204 °C
Tensile Strength, Yield
524 MPa @Strain 0.200 %
Tensile Strength, Yield
276 MPa @Strain 0.200 %, Temperature 538 °C
Tensile Strength, Yield
296 MPa @Strain 0.200 %, Temperature 427 °C
Tensile Strength, Yield
303 MPa @Strain 0.200 %, Temperature 316 °C
Tensile Strength, Yield
359 MPa @Strain 0.200 %, Temperature 204 °C
Tensile Strength, Yield
483 MPa @Strain 0.200 %, Temperature 93.0 °C
Elongation at Break
38 %
Elongation at Break
49 % @Temperature 93.0 °C
Elongation at Break
66 % @Temperature 204 °C
Elongation at Break
77 % @Temperature 316 °C
Elongation at Break
79 % @Temperature 538 °C
Elongation at Break
84 % @Temperature 427 °C
Modulus of Elasticity
180 GPa @Temperature 649 °C
Modulus of Elasticity
189 GPa @Temperature 538 °C
Modulus of Elasticity
197 GPa @Temperature 427 °C
Modulus of Elasticity
206 GPa @Temperature 316 °C
Modulus of Elasticity
215 GPa @Temperature 204 °C
Charpy Impact
176 J @Temperature 23.0 °C

Thermal Properties
CTE, linear
14.0 µm/m-°C @Temperature 26.0 - 316 °C
CTE, linear
14.5 µm/m-°C @Temperature 26.0 - 427 °C
CTE, linear
14.8 µm/m-°C @Temperature 26.0 - 538 °C
CTE, linear
15.1 µm/m-°C @Temperature 26.0 - 649 °C
CTE, linear
15.9 µm/m-°C @Temperature 26.0 - 760 °C
CTE, linear
16.4 µm/m-°C @Temperature 26.0 - 871 °C
CTE, linear
16.9 µm/m-°C @Temperature 26.0 - 982 °C
Specific Heat Capacity
0.456 J/g-°C @Temperature 23.0 °C
Specific Heat Capacity
0.470 J/g-°C @Temperature 100 °C
Specific Heat Capacity
0.482 J/g-°C @Temperature 200 °C
Specific Heat Capacity
0.504 J/g-°C @Temperature 300 °C
Specific Heat Capacity
0.525 J/g-°C @Temperature 400 °C
Specific Heat Capacity
0.545 J/g-°C @Temperature 500 °C
Specific Heat Capacity
0.573 J/g-°C @Temperature 600 °C
Thermal Conductivity
12.3 W/m-K @Temperature 23.0 °C
Thermal Conductivity
13.8 W/m-K @Temperature 100 °C
Thermal Conductivity
15.6 W/m-K @Temperature 200 °C
Thermal Conductivity
17.5 W/m-K @Temperature 300 °C
Thermal Conductivity
19.4 W/m-K @Temperature 400 °C
Thermal Conductivity
21.5 W/m-K @Temperature 500 °C
Thermal Conductivity
23.9 W/m-K @Temperature 600 °C
Melting Point
1332 - 1354 °C
Solidus
1332 °C
Liquidus
1354 °C

Component Elements Properties
Carbon, C
0.060 %
Chromium, Cr
26 %
Cobalt, Co
54 %
Iron, Fe
3.0 %
Manganese, Mn
0.80 %
Molybdenum, Mo
5.0 %
Nickel, Ni
9.0 %
Nitrogen, N
0.080 %
Silicon, Si
0.30 %
Tungsten, W
2.0 %

Electrical Properties
Electrical Resistivity
0.0000870 ohm-cm @Temperature 23.0 °C
Electrical Resistivity
0.0000890 ohm-cm @Temperature 100 °C
Electrical Resistivity
0.0000930 ohm-cm @Temperature 200 °C
Electrical Resistivity
0.0000960 ohm-cm @Temperature 300 °C
Electrical Resistivity
0.000100 ohm-cm @Temperature 400 °C
Electrical Resistivity
0.000103 ohm-cm @Temperature 500 °C
Electrical Resistivity
0.000105 ohm-cm @Temperature 600 °C

Alternative products

Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) accurate 68%

$ 1654/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 958 MPa
Tensile Strength, Yield: 490 MPa @Strain 0.200 %
Elongation at Break: 28 %
Modulus of Elasticity: 180 GPa @Temperature 649 °C

Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld accurate 68%

$ 1896/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 876 MPa
Tensile Strength, Yield: 614 MPa @Strain 0.200 %
Elongation at Break: 11 %
Modulus of Elasticity: 180 GPa @Temperature 649 °C

Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) accurate 68%

$ 1540/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 1020 MPa
Tensile Strength, Yield: 545 MPa @Strain 0.200 %
Elongation at Break: 34 %
Modulus of Elasticity: 180 GPa @Temperature 649 °C

Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld accurate 68%

$ 2022/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 931 MPa
Tensile Strength, Yield: 669 MPa @Strain 0.200 %
Elongation at Break: 9.0 %
Modulus of Elasticity: 180 GPa @Temperature 649 °C

Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) accurate 68%

$ 1892/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 1069 MPa
Tensile Strength, Yield: 558 MPa @Strain 0.200 %
Elongation at Break: 47 %
Modulus of Elasticity: 180 GPa @Temperature 649 °C

Haynes Ultimet® alloy, 1.6 mm sheet accurate 68%

$ 2205/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 952 MPa
Tensile Strength, Ultimate: 827 MPa @Temperature 427 °C
Tensile Strength, Ultimate: 896 MPa @Temperature 316 °C
Tensile Strength, Ultimate: 924 MPa @Temperature 204 °C

Haynes Ultimet® alloy, plate, GMAW weld (short) accurate 68%

$ 1885/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 676 MPa @Thickness 19.0 mm, Temperature 538 °C
Tensile Strength, Ultimate: 786 MPa @Thickness 12.7 mm, Temperature 538 °C
Tensile Strength, Ultimate: 800 MPa @Thickness 19.0 mm, Temperature 260 °C
Tensile Strength, Ultimate: 834 MPa @Thickness 12.7 mm, Temperature 20.0 °C

Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld accurate 68%

$ 1599/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 896 MPa
Tensile Strength, Ultimate: 752 MPa @Temperature 538 °C
Tensile Strength, Yield: 600 MPa @Strain 0.200 %
Tensile Strength, Yield: 331 MPa @Strain 0.200 %, Temperature 538 °C

Haynes Ultimet® alloy, all-weld metal, SMAW weld accurate 68%

$ 1770/MT

Density: 8.47 g/cc
Tensile Strength, Ultimate: 924 MPa
Tensile Strength, Ultimate: 690 MPa @Temperature 538 °C
Tensile Strength, Yield: 641 MPa @Strain 0.200 %
Tensile Strength, Yield: 421 MPa @Strain 0.200 %, Temperature 538 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship for sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

6 prices for Haynes Ultimet® alloy, 12.7-50.8 mm bar

Seller from Guadalajara – 2021-05-28:

Seller from Guadalajara work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2572 per MT

Seller from Ōsaka – 2021-04-09:

Seller from Ōsaka work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), BASF

Price: $1471 per MT

Seller from Phoenix – 2021-04-01:

Seller from Phoenix work with company: 3M, RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics)

Price: $1659 per MT

Seller from Washington – 2021-08-12:

Seller from Washington work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2146 per MT

Seller from Guangzhou – 2021-03-31:

Seller from Guangzhou work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2049 per MT

Seller from Seoul – 2021-06-14:

Seller from Seoul work with company: Techmer ES, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2018 per MT