Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet price 1620 per MT

Physical Properties
Density
9.13 g/cc

Mechanical Properties
Tensile Strength, Ultimate
1005 MPa
Tensile Strength, Ultimate
160 MPa @Temperature 1095 °C
Tensile Strength, Ultimate
235 MPa @Temperature 980 °C
Tensile Strength, Ultimate
415 MPa @Temperature 870 °C
Tensile Strength, Ultimate
640 MPa @Temperature 760 °C
Tensile Strength, Ultimate
745 MPa @Temperature 650 °C
Tensile Strength, Ultimate
770 MPa @Temperature 540 °C
Tensile Strength, Yield
475 MPa @Strain 0.200 %
Tensile Strength, Yield
76.0 MPa @Strain 0.200 %, Temperature 1095 °C
Tensile Strength, Yield
125 MPa @Strain 0.200 %, Temperature 980 °C
Tensile Strength, Yield
250 MPa @Strain 0.200 %, Temperature 870 °C
Tensile Strength, Yield
285 MPa @Strain 0.200 %, Temperature 760 °C
Tensile Strength, Yield
330 MPa @Strain 0.200 %, Temperature 540 °C
Tensile Strength, Yield
330 MPa @Strain 0.200 %, Temperature 650 °C
Elongation at Break
51 %
Elongation at Break
36 % @Temperature 980 °C
Elongation at Break
42 % @Temperature 760 °C
Elongation at Break
45 % @Temperature 870 °C
Elongation at Break
48 % @Temperature 1095 °C
Elongation at Break
60 % @Temperature 540 °C
Elongation at Break
60 % @Temperature 650 °C
Modulus of Elasticity
225 GPa
Modulus of Elasticity
146 GPa @Temperature 1000 °C
Modulus of Elasticity
154 GPa @Temperature 900 °C
Modulus of Elasticity
163 GPa @Temperature 800 °C
Modulus of Elasticity
174 GPa @Temperature 700 °C
Modulus of Elasticity
181 GPa @Temperature 600 °C
Modulus of Elasticity
188 GPa @Temperature 500 °C
Modulus of Elasticity
197 GPa @Temperature 400 °C
Modulus of Elasticity
204 GPa @Temperature 300 °C
Modulus of Elasticity
214 GPa @Temperature 200 °C
Modulus of Elasticity
222 GPa @Temperature 100 °C
Charpy Impact
262 J
Charpy Impact
144 J @Temperature 980 °C
Charpy Impact
148 J @Temperature -196 °C
Charpy Impact
163 J @Temperature 870 °C
Charpy Impact
182 J @Temperature -138 °C
Charpy Impact
194 J @Temperature 760 °C
Charpy Impact
212 J @Temperature -78.0 °C
Charpy Impact
230 J @Temperature 650 °C
Charpy Impact
243 J @Temperature -29.0 °C
Charpy Impact
273 J @Temperature 540 °C
Charpy Impact
297 J @Temperature 260 °C

Thermal Properties
CTE, linear
12.3 µm/m-°C @Temperature 25.0 - 100 °C
CTE, linear
12.9 µm/m-°C @Temperature 25.0 - 200 °C
CTE, linear
13.6 µm/m-°C @Temperature 25.0 - 300 °C
CTE, linear
14.3 µm/m-°C @Temperature 25.0 - 500 °C
CTE, linear
14.3 µm/m-°C @Temperature 25.0 - 400 °C
CTE, linear
14.6 µm/m-°C @Temperature 25.0 - 600 °C
CTE, linear
15.1 µm/m-°C @Temperature 25.0 - 700 °C
CTE, linear
15.8 µm/m-°C @Temperature 25.0 - 800 °C
CTE, linear
16.5 µm/m-°C @Temperature 25.0 - 900 °C
CTE, linear
17.0 µm/m-°C @Temperature 25.0 - 1000 °C
Thermal Conductivity
9.40 W/m-K
Thermal Conductivity
10.9 W/m-K @Temperature 100 °C
Thermal Conductivity
12.9 W/m-K @Temperature 200 °C
Thermal Conductivity
14.8 W/m-K @Temperature 300 °C
Thermal Conductivity
16.8 W/m-K @Temperature 400 °C
Thermal Conductivity
18.7 W/m-K @Temperature 500 °C
Thermal Conductivity
20.7 W/m-K @Temperature 600 °C
Thermal Conductivity
22.6 W/m-K @Temperature 700 °C
Thermal Conductivity
24.7 W/m-K @Temperature 800 °C

Electrical Properties
Electrical Resistivity
0.0000886 ohm-cm
Electrical Resistivity
0.0000950 ohm-cm @Temperature 1000 °C
Electrical Resistivity
0.0001011 ohm-cm @Temperature 900 °C
Electrical Resistivity
0.0001066 ohm-cm @Temperature 700 °C
Electrical Resistivity
0.0001078 ohm-cm @Temperature 800 °C

Alternative products

Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes accurate 79%

$ 1509/MT

Density: 9.13 g/cc
Hardness, Brinell: 266
Hardness, Knoop: 283
Hardness, Rockwell C: 26
Hardness, Vickers: 275

Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure accurate 79%

$ 1984/MT

Density: 9.13 g/cc
Tensile Strength, Ultimate: 785 MPa
Tensile Strength, Yield: 495 MPa @Strain 0.200 %
Elongation at Break: 9.1 %
Modulus of Elasticity: 225 GPa

Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes accurate 79%

$ 1729/MT

Density: 9.13 g/cc
Hardness, Brinell: 304
Hardness, Knoop: 326
Hardness, Rockwell C: 32
Hardness, Vickers: 316

Haynes 25 alloy, vacuum investment castings, solution treated accurate 79%

$ 1607/MT

Density: 9.13 g/cc
Tensile Strength, Ultimate: 675 MPa
Tensile Strength, Ultimate: 195 MPa @Temperature 980 °C
Tensile Strength, Ultimate: 295 MPa @Temperature 870 °C
Tensile Strength, Ultimate: 315 MPa @Temperature 760 °C

Haynes 25 alloy, cold worked sheet, 20 % cold reduction accurate 79%

$ 1577/MT

Density: 9.13 g/cc
Tensile Strength, Ultimate: 1260 MPa
Tensile Strength, Ultimate: 285 MPa @Temperature 980 °C
Tensile Strength, Ultimate: 740 MPa @Temperature 760 °C
Tensile Strength, Ultimate: 945 MPa @Temperature 650 °C

Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour accurate 79%

$ 2367/MT

Density: 9.13 g/cc
Tensile Strength, Ultimate: 1160 MPa
Tensile Strength, Ultimate: 885 MPa @Temperature 650 °C
Tensile Strength, Yield: 940 MPa @Strain 0.200 %
Tensile Strength, Yield: 715 MPa @Strain 0.200 %, Temperature 650 °C

Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure accurate 79%

$ 2522/MT

Density: 9.13 g/cc
Tensile Strength, Ultimate: 900 MPa
Tensile Strength, Yield: 655 MPa @Strain 0.200 %
Elongation at Break: 12 %
Modulus of Elasticity: 225 GPa

Haynes 25 alloy, cold worked sheet, 10% cold reduction accurate 79%

$ 1766/MT

Density: 9.13 g/cc
Tensile Strength, Ultimate: 1070 MPa
Tensile Strength, Ultimate: 270 MPa @Temperature 980 °C
Tensile Strength, Ultimate: 425 MPa @Temperature 870 °C
Tensile Strength, Ultimate: 600 MPa @Temperature 760 °C

Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes accurate 79%

$ 1831/MT

Density: 9.13 g/cc
Hardness, Brinell: 304
Hardness, Knoop: 326
Hardness, Rockwell C: 32
Hardness, Vickers: 316

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships sales. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

5 prices for Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet

Seller from Kolkata – 2021-07-14:

Seller from Kolkata work with company: RTP Company, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $2302 per MT

Seller from Hanoi – 2021-07-08:

Seller from Hanoi work with company: Solvay, Techmer ES, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2373 per MT

Seller from Miami – 2021-08-03:

Seller from Miami work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1796 per MT

Seller from Montréal – 2021-03-07:

Seller from Montréal work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2319 per MT

Seller from Tianjin – 2021-07-11:

Seller from Tianjin work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1620 per MT