Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled

Seller in Chengdu price: $1997 per MT

Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled in Superalloy, Iron Base

  • Physical Properties
  • Density
  • 8.20 g/cc
  • Mechanical Properties
  • Hardness, Brinell
  • 159
  • Hardness, Knoop
  • 176
  • Hardness, Rockwell B
  • 92
  • Hardness, Vickers
  • 201
  • Tensile Strength, Ultimate
  • 814 MPa
  • Tensile Strength, Ultimate
  • 18.0 MPa @Temperature 1288 °C
  • Tensile Strength, Ultimate
  • 23.0 MPa @Temperature 1260 °C
  • Tensile Strength, Ultimate
  • 33.0 MPa @Temperature 1204 °C
  • Tensile Strength, Ultimate
  • 48.0 MPa @Temperature 1149 °C
  • Tensile Strength, Ultimate
  • 90.0 MPa @Temperature 1093 °C
  • Tensile Strength, Ultimate
  • 170 MPa @Temperature 982 °C
  • Tensile Strength, Ultimate
  • 268 MPa @Temperature 871 °C
  • Tensile Strength, Ultimate
  • 403 MPa @Temperature 760 °C
  • Tensile Strength, Ultimate
  • 507 MPa @Temperature 649 °C
  • Tensile Strength, Ultimate
  • 647 MPa @Temperature 538 °C
  • Tensile Strength, Ultimate
  • 676 MPa @Temperature 427 °C
  • Tensile Strength, Yield
  • 400 MPa @Strain 0.200 %
  • Tensile Strength, Yield
  • 21.0 MPa @Strain 0.200 %, Temperature 1204 °C
  • Tensile Strength, Yield
  • 30.0 MPa @Strain 0.200 %, Temperature 1149 °C
  • Tensile Strength, Yield
  • 58.0 MPa @Strain 0.200 %, Temperature 1093 °C
  • Tensile Strength, Yield
  • 117 MPa @Strain 0.200 %, Temperature 982 °C
  • Tensile Strength, Yield
  • 207 MPa @Strain 0.200 %, Temperature 871 °C
  • Tensile Strength, Yield
  • 247 MPa @Strain 0.200 %, Temperature 760 °C
  • Tensile Strength, Yield
  • 259 MPa @Strain 0.200 %, Temperature 649 °C
  • Tensile Strength, Yield
  • 274 MPa @Strain 0.200 %, Temperature 538 °C
  • Tensile Strength, Yield
  • 292 MPa @Strain 0.200 %, Temperature 427 °C
  • Elongation at Break
  • 49 %
  • Elongation at Break
  • 7.0 % @Temperature 1288 °C
  • Elongation at Break
  • 12 % @Temperature 760 °C
  • Elongation at Break
  • 15 % @Temperature 871 °C
  • Elongation at Break
  • 19 % @Temperature 1260 °C
  • Elongation at Break
  • 28 % @Temperature 649 °C
  • Elongation at Break
  • 29 % @Temperature 1204 °C
  • Elongation at Break
  • 36 % @Temperature 1149 °C
  • Elongation at Break
  • 38 % @Temperature 1093 °C
  • Elongation at Break
  • 51 % @Temperature 982 °C
  • Elongation at Break
  • 54 % @Temperature 427 °C
  • Elongation at Break
  • 54 % @Temperature 538 °C
  • Modulus of Elasticity
  • 200 GPa
  • Modulus of Elasticity
  • 124 GPa @Temperature 871 °C
  • Modulus of Elasticity
  • 152 GPa @Temperature 649 °C
  • Modulus of Elasticity
  • 152 GPa @Temperature 760 °C
  • Modulus of Elasticity
  • 165 GPa @Temperature 427 °C
  • Modulus of Elasticity
  • 172 GPa @Temperature 538 °C
  • Poissons Ratio
  • 0.298
  • Poissons Ratio
  • 0.315 @Temperature 426 °C
  • Poissons Ratio
  • 0.319 @Temperature -78.0 °C
  • Poissons Ratio
  • 0.325 @Temperature 650 °C
  • Poissons Ratio
  • 0.339 @Temperature 816 °C
  • Shear Modulus
  • 77.0 GPa
  • Thermal Properties
  • CTE, linear
  • 15.3 µm/m-°C @Temperature 23.0 - 300 °C
  • CTE, linear
  • 15.6 µm/m-°C @Temperature 23.0 - 400 °C
  • CTE, linear
  • 16.0 µm/m-°C @Temperature 23.0 - 500 °C
  • CTE, linear
  • 16.7 µm/m-°C @Temperature 23.0 - 600 °C
  • CTE, linear
  • 17.2 µm/m-°C @Temperature 23.0 - 700 °C
  • CTE, linear
  • 17.5 µm/m-°C @Temperature 23.0 - 800 °C
  • CTE, linear
  • 17.8 µm/m-°C @Temperature 23.0 - 1000 °C
  • CTE, linear
  • 17.8 µm/m-°C @Temperature 23.0 - 900 °C
  • CTE, linear
  • 18.4 µm/m-°C @Temperature 23.0 - 1100 °C
  • Specific Heat Capacity
  • 0.435 J/g-°C @Temperature >=100 °C
  • Thermal Conductivity
  • 15.9 W/m-K @Temperature 300 °C
  • Thermal Conductivity
  • 17.3 W/m-K @Temperature 400 °C
  • Thermal Conductivity
  • 18.6 W/m-K @Temperature 500 °C
  • Thermal Conductivity
  • 20.0 W/m-K @Temperature 600 °C
  • Thermal Conductivity
  • 20.0 W/m-K @Temperature 200 °C
  • Melting Point
  • 1288 - 1354 °C
  • Solidus
  • 1288 °C
  • Liquidus
  • 1354 °C
  • Optical Properties
  • Emissivity (0-1)
  • 0.88 @Temperature 1090 °C
  • Component Elements Properties
  • Carbon, C
  • 0.080 - 0.16 %
  • Cb + Ta
  • 0.75 - 1.25 %
  • Chromium, Cr
  • 20 - 22.5 %
  • Electrical Properties
  • Electrical Resistivity
  • 0.0000930 ohm-cm @Temperature 22.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled

Seller from Chengdu – 2021-08-11:

Seller from Chengdu work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1997 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit