Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours

Seller in London price: $2449 per MT

Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours in Superalloy, Iron Base

  • Physical Properties
  • Density
  • 8.20 g/cc
  • Mechanical Properties
  • Tensile Strength, Ultimate
  • 675 MPa
  • Tensile Strength, Ultimate
  • 103 MPa @Temperature 1066 °C
  • Tensile Strength, Ultimate
  • 150 MPa @Temperature 982 °C
  • Tensile Strength, Ultimate
  • 230 MPa @Temperature 899 °C
  • Tensile Strength, Ultimate
  • 321 MPa @Temperature 816 °C
  • Tensile Strength, Ultimate
  • 380 MPa @Temperature 732 °C
  • Tensile Strength, Ultimate
  • 446 MPa @Temperature 649 °C
  • Tensile Strength, Ultimate
  • 451 MPa @Temperature 593 °C
  • Tensile Strength, Ultimate
  • 487 MPa @Temperature 538 °C
  • Tensile Strength, Ultimate
  • 530 MPa @Temperature 427 °C
  • Tensile Strength, Ultimate
  • 538 MPa @Temperature 316 °C
  • Tensile Strength, Ultimate
  • 549 MPa @Temperature 204 °C
  • Tensile Strength, Yield
  • 372 MPa @Strain 0.200 %
  • Elongation at Break
  • 23 %
  • Elongation at Break
  • 11 % @Temperature 816 °C
  • Elongation at Break
  • 15 % @Temperature 732 °C
  • Elongation at Break
  • 23 % @Temperature 593 °C
  • Elongation at Break
  • 23 % @Temperature 649 °C
  • Elongation at Break
  • 23 % @Temperature 204 °C
  • Elongation at Break
  • 24 % @Temperature 316 °C
  • Elongation at Break
  • 24 % @Temperature 899 °C
  • Elongation at Break
  • 25 % @Temperature 427 °C
  • Elongation at Break
  • 25 % @Temperature 538 °C
  • Elongation at Break
  • 31 % @Temperature 982 °C
  • Elongation at Break
  • 39 % @Temperature 1066 °C
  • Reduction of Area
  • 25 %
  • Reduction of Area
  • 19 % @Temperature 816 °C
  • Reduction of Area
  • 20 % @Temperature 732 °C
  • Reduction of Area
  • 24 % @Temperature 649 °C
  • Reduction of Area
  • 25 % @Temperature 593 °C
  • Reduction of Area
  • 26 % @Temperature 427 °C
  • Reduction of Area
  • 27 % @Temperature 538 °C
  • Reduction of Area
  • 27 % @Temperature 204 °C
  • Reduction of Area
  • 27 % @Temperature 316 °C
  • Reduction of Area
  • 29 % @Temperature 899 °C
  • Reduction of Area
  • 42 % @Temperature 982 °C
  • Reduction of Area
  • 45 % @Temperature 1066 °C
  • Poissons Ratio
  • 0.298
  • Poissons Ratio
  • 0.315 @Temperature 426 °C
  • Poissons Ratio
  • 0.319 @Temperature -78.0 °C
  • Poissons Ratio
  • 0.325 @Temperature 650 °C
  • Poissons Ratio
  • 0.339 @Temperature 816 °C
  • Thermal Properties
  • CTE, linear
  • 15.3 µm/m-°C @Temperature 23.0 - 300 °C
  • CTE, linear
  • 15.6 µm/m-°C @Temperature 23.0 - 400 °C
  • CTE, linear
  • 16.0 µm/m-°C @Temperature 23.0 - 500 °C
  • CTE, linear
  • 16.7 µm/m-°C @Temperature 23.0 - 600 °C
  • CTE, linear
  • 17.2 µm/m-°C @Temperature 23.0 - 700 °C
  • CTE, linear
  • 17.5 µm/m-°C @Temperature 23.0 - 800 °C
  • CTE, linear
  • 17.8 µm/m-°C @Temperature 23.0 - 900 °C
  • CTE, linear
  • 17.8 µm/m-°C @Temperature 23.0 - 1000 °C
  • CTE, linear
  • 18.4 µm/m-°C @Temperature 23.0 - 1100 °C
  • Specific Heat Capacity
  • 0.435 J/g-°C @Temperature >=100 °C
  • Thermal Conductivity
  • 15.9 W/m-K @Temperature 300 °C
  • Thermal Conductivity
  • 17.3 W/m-K @Temperature 400 °C
  • Thermal Conductivity
  • 18.6 W/m-K @Temperature 500 °C
  • Thermal Conductivity
  • 20.0 W/m-K @Temperature 600 °C
  • Thermal Conductivity
  • 20.0 W/m-K @Temperature 200 °C
  • Melting Point
  • 1288 - 1354 °C
  • Solidus
  • 1288 °C
  • Liquidus
  • 1354 °C
  • Optical Properties
  • Emissivity (0-1)
  • 0.88 @Temperature 1090 °C
  • Component Elements Properties
  • Carbon, C
  • 0.080 - 0.16 %
  • Cb + Ta
  • 0.75 - 1.25 %
  • Chromium, Cr
  • 20 - 22.5 %
  • Cobalt, Co
  • 18.5 - 21 %
  • Iron, Fe
  • 33 %
  • Manganese, Mn
  • 1.0 - 2.0 %
  • Molybdenum, Mo
  • 2.5 - 3.5 %
  • Nickel, Ni
  • 19 - 21 %
  • Nitrogen, N
  • 0.10 - 0.20 %
  • Silicon, Si
  • <= 1.0 %
  • Tungsten, W
  • 2.0 - 3.0 %
  • Electrical Properties
  • Electrical Resistivity
  • 0.0000930 ohm-cm @Temperature 22.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours

Seller from London – 2021-05-19:

Seller from London work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2449 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Container terminal in Singapore open-nearme.com