$ 1668/MT
- Viscosity: >= 500000 cP
- Viscosity: >= 900000 cP
- Hardness, Shore D: >= 80
- Tensile Strength at Break: >= 41.4 MPa
- Shear Strength: >= 10.3 MPa
$ 1941/MT
- Viscosity: 60000 - 70000 cP @Temperature 23.0 °C
- Storage Temperature: 4.44 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
$ 1983/MT
- Viscosity: 5000 cP
- Viscosity: 50000 cP
- Adhesive Bond Strength: 6.89 MPa @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
$ 1687/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
- Color Code: "A" Gray; "B" White
$ 1784/MT
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 4.98 - 9.60 min @Temperature 149 °C
- Cure Time: 19.8 - 30.0 min @Temperature 121 °C
$ 1554/MT
- Viscosity: 600 cP @Temperature 23.0 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 45.0 min @Temperature 149 °C
$ 2210/MT
- Viscosity: 1500 - 2000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 2880 - 3600 min @Temperature 23.0 °C
$ 1665/MT
- Viscosity: 1500 - 3000 cP
- Viscosity: 30000 - 70000 cP
- Hardness, Shore D: 80 - 85
- Tensile Strength at Break: >= 75.8 MPa
- Tensile Modulus: 2.76 GPa
$ 1522/MT
- Water Absorption: <= 1.0 % @Time 86400 sec
- Viscosity: 10 - 110 cP
- Viscosity: 45000 - 75000 cP
- Tensile Strength: >= 34.5 MPa
- Elongation at Break: <= 3.0 %
$ 1717/MT
- Specific Gravity: 1.96 g/cc
- Specific Gravity: 1.97 g/cc
- Viscosity: 4000 - 25000 cP
- Viscosity: 20000 - 40000 cP
- Viscosity: 100000 - 130000 cP
$ 1671/MT
- Solids Content: 100 %
- Hardness, Shore D: >= 75
- Tensile Modulus: 3.10 GPa
- Shear Strength: >= 8.27 MPa
- Peel Strength: >= 1.75 kN/m
$ 1702/MT
- Water Absorption: <= 1.0 %
- Viscosity: 400 - 500 cP
- Hardness, Shore D: 20
- Tensile Strength at Break: >= 6.89 MPa
- Elongation at Break: >= 200 %
$ 1730/MT
- Viscosity: 200000 - 300000 cP
- Hardness, Shore D: >= 85
- Tensile Modulus: >= 3.10 GPa
- Shear Strength: >= 22.1 MPa
- Peel Strength: 2.63 kN/m
$ 1676/MT
- Viscosity: 100000 - 120000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 2880 min @Temperature 23.0 °C
$ 1545/MT
- Viscosity: 35000 - 85000 cP
- Viscosity: 300000 - 800000 cP
- Hardness, Shore D: 30 - 40
- Tensile Strength at Break: >= 20.7 MPa @Temperature 23.9 °C
- Shear Strength: >= 5.52 MPa
$ 2307/MT
- Viscosity: 90000 - 130000 cP
- Hardness, Shore D: 80
- Tensile Strength at Break: >= 13.8 MPa
- Elongation at Break: >= 50 %
- CTE, linear: 75.0 - 85.0 µm/m-°C
$ 1567/MT
- Viscosity: 2000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 480 - 720 min @Temperature 23.0 °C
- Color Code: "A" Clear; "B" Clear
$ 1822/MT
- Viscosity: 250 - 500 cP
- Viscosity: 55000 - 110000 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: 68.9 MPa
- Shear Strength: >= 20.7 MPa
$ 1488/MT
- Viscosity: 40000 - 50000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -62.2 °C
- Cure Time: 120 - 180 min
- Color Code: "A" Clear; "B" Brown
$ 1826/MT
- Viscosity: 2000 - 2300 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 1440 - 2160 min @Temperature 23.0 °C
$ 2052/MT
- Solids Content: 100 %
- Maximum Service Temperature, Air: 87.8 °C
- Minimum Service Temperature, Air: -28.9 °C
$ 2303/MT
- Viscosity: 700 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Transmission, Visible: 90 %
- Cure Time: 480 - 720 min @Temperature 65.6 °C
$ 1700/MT
- Viscosity: 3000 - 5000 cP
- Viscosity: 40000 - 70000 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 51.7 MPa
- Shear Strength: >= 10.3 MPa
$ 2339/MT
- Hardness, Shore D: >= 85
- Tensile Strength at Break: 37.9 MPa
- Tensile Modulus: >= 3.45 GPa
- Shear Strength: 13.1 MPa
- Shear Strength: 13.4 MPa
$ 1563/MT
- Viscosity: 2000 - 3000 cP
- Tensile Strength: >= 51.7 MPa
- Flexural Strength: >= 62.1 MPa
- Compressive Strength: >= 68.9 MPa
- Maximum Service Temperature, Air: 232 °C
$ 1609/MT
- Shear Strength: 6.89 MPa
- Shear Strength: 7.58 MPa
- Peel Strength: 0.877 - 1.75 kN/m
- Thermal Conductivity: 1.30 - 1.44 W/m-K
- Maximum Service Temperature, Air: 177 °C
$ 1466/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 2880 - 3600 min @Temperature 23.0 °C
- Color Code: "A" Black; "B" Tan
$ 1547/MT
- Viscosity: 280 - 500 cP
- Viscosity: 200 - 600 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 65.5 MPa
- Tensile Modulus: >= 2.76 GPa
$ 2053/MT
- Viscosity: 2000 - 3000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 min @Temperature 23.0 °C
$ 1767/MT
- Viscosity: 400 cP
- Viscosity: 1200 - 1400 cP
- Viscosity: 1600 - 1800 cP
- Tensile Strength at Break: >= 65.5 MPa
- Tensile Modulus: 2.76 GPa
$ 2464/MT
- Viscosity: 100 - 200 cP
- Viscosity: 12000 - 20000 cP
- Viscosity: 60000 - 110000 cP
- Hardness, Shore D: >= 75
- Tensile Strength: >= 68.9 MPa
$ 2332/MT
- Solids Content: 30 %
- Cure Time: 720 - 1440 min @Temperature 23.0 °C
$ 1688/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 1440 min @Temperature 23.0 °C
- Color Code: "A" Yellow; "B" Yellow
$ 1743/MT
- Viscosity: 7000 - 11000 cP
- Hardness, Shore D: >= 80
- Tensile Strength at Break: >= 51.7 MPa @Temperature 23.9 °C
- CTE, linear: 50.0 - 55.0 µm/m-°C
- Maximum Service Temperature, Air: 260 °C
$ 1577/MT
- Viscosity: 8000 - 10000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 4.98 - 15.0 min @Temperature 23.0 °C
- Color Code: "A" Clear; "B" Clear Yellow
$ 1816/MT
- Viscosity: >= 200000 cP @Temperature 23.0 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 4.98 - 9.60 min @Temperature 149 °C
$ 1547/MT
- Hardness, Shore D: 75 - 80
- Tensile Strength at Break: >= 20.7 MPa @Temperature 23.9 °C
- Elongation at Break: <= 200 %
- Tensile Modulus: 0.689 - 1.03 GPa @Temperature 23.9 °C
- Shear Strength: >= 5.86 MPa @Temperature 23.9 °C
$ 1562/MT
- Viscosity: 120000 - 150000 cP @Temperature 23.0 °C
- Storage Temperature: 4.44 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -51.1 °C
$ 2473/MT
- Viscosity: 70 - 120 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 34.5 MPa @Temperature 23.9 °C
- Tensile Modulus: >= 1.72 GPa @Temperature 23.9 °C
- CTE, linear: 55.0 - 60.0 µm/m-°C
$ 1607/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
- Color Code: "A" Gray; "B" Gray
$ 1603/MT
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 45.0 min @Temperature 149 °C
- Cure Time: 60.0 min @Temperature 121 °C
$ 1515/MT
- Viscosity: 99000 - 121000 cP
- Viscosity: 108000 - 121200 cP
- Shear Strength: >= 11.0 MPa
- Peel Strength: 4.38 kN/m
- Maximum Service Temperature, Air: 149 °C
$ 2555/MT
- Viscosity: 800 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 240 - 360 min @Temperature 93.3 °C
- Cure Time: 7200 - 10100 min @Temperature 23.0 °C
$ 1845/MT
- Hardness, Shore D: >= 65
- Tensile Strength: >= 13.8 MPa @Temperature 60.0 °C
- Elongation at Break: >= 30 % @Temperature 60.0 °C
- Modulus of Elasticity: 0.827 GPa @Temperature 60.0 °C
- CTE, linear: >= 75.0 µm/m-°C @Temperature 60.0 °C
$ 1465/MT
- Viscosity: 50000 - 60000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 30.0 - 45.0 min @Temperature 93.3 °C
- Cure Time: 720 min @Temperature 23.0 °C
$ 2174/MT
- Viscosity: 35000 - 45000 cP
- Hardness, Shore D: >= 65
- Tensile Strength at Break: >= 55.2 MPa @Temperature 23.9 °C
- Tensile Modulus: >= 2.41 GPa @Temperature 23.9 °C
- CTE, linear: 45.0 - 50.0 µm/m-°C
$ 1912/MT
- Viscosity: 25000 - 30000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 2119/MT
- Viscosity: 100 - 250 cP
- Viscosity: >= 80000 cP
- Tensile Strength at Break: >= 68.9 MPa
- Shear Strength: >= 17.2 MPa
- Shear Strength: >= 17.2 MPa
$ 2161/MT
- Viscosity: 40000 - 50000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 1831/MT
- Viscosity: 30 - 70 cP
- Viscosity: 75000 - 125000 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 68.9 MPa
- Tensile Modulus: >= 2.41 GPa
$ 1891/MT
- Viscosity: 8000 - 9000 cP
- Hardness, Shore D: 65
- Tensile Strength: >= 42.7 MPa
- Elongation at Break: >= 23 %
- Tensile Modulus: 1.93 GPa
$ 1695/MT
- Hardness, Shore D: >= 90
- Tensile Strength at Break: >= 34.5 MPa @Temperature 149 °C
- Tensile Strength at Break: >= 68.9 MPa @Temperature 23.9 °C
- Tensile Modulus: 1.86 GPa @Temperature 149 °C
- Tensile Modulus: 3.72 GPa @Temperature 23.9 °C
$ 1827/MT
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1080 - 1440 min @Temperature 23.0 °C
- Color Code: "A" Off White; "B" Off White
$ 1641/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
- Color Code: "A" Gray; "B" Tan
$ 2049/MT
- Viscosity: 2100 - 2500 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 720 - 1440 min @Temperature 23.0 °C
$ 1549/MT
- Viscosity: 3000 - 4000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 min @Temperature 93.3 °C
- Cure Time: 1440 min @Temperature 23.0 °C
$ 1650/MT
- Viscosity: 10000 - 12000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 240 - 360 min @Temperature 23.0 °C
- Color Code: "A" Clear; "B" Tan
$ 2086/MT
- Viscosity: 20000 - 40000 cP
- Viscosity: 150000 - 300000 cP
- Viscosity: 60000 - 110000 cP @Temperature 40.0 °C
- Hardness, Shore D: >= 75
- Tensile Strength: >= 68.9 MPa
$ 2310/MT
- Viscosity: 80 - 300 cP
- Viscosity: 4000 - 7000 cP
- Viscosity: 5000 - 9000 cP
- Hardness, Shore D: >= 50
- Tensile Strength: >= 20.7 MPa
$ 1934/MT
- Viscosity: 100 - 1000 cP
- Viscosity: 4000 - 8000 cP
- Viscosity: 10000 - 14000 cP
- Hardness, Shore D: >= 80
- Tensile Strength: >= 58.6 MPa
$ 1781/MT
- Viscosity: 1500 - 1800 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 180 min @Temperature 93.3 °C
- Cure Time: 2880 - 4320 min @Temperature 23.0 °C
$ 2357/MT
- Viscosity: 10000 - 14000 cP
- Viscosity: 11000 - 15000 cP
- Hardness, Shore D: >= 70
- Tensile Strength at Break: >= 51.7 MPa @Temperature 23.9 °C
- Tensile Modulus: 2.07 - 2.41 GPa @Temperature 23.9 °C
$ 2437/MT
- Hardness, Shore D: >= 70
- Tensile Strength at Break: >= 51.7 MPa
- Elongation at Break: >= 5.0 %
- Tensile Modulus: >= 2.76 GPa
- Flexural Strength: >= 68.9 MPa
$ 2269/MT
- Viscosity: 70000 - 150000 cP
- Tensile Strength at Break: >= 34.5 MPa
- Tensile Strength at Break: >= 51.7 MPa
- Shear Strength: >= 6.89 MPa
- Shear Strength: >= 12.4 MPa
$ 1491/MT
- Viscosity: 2500 - 5000 cP
- Viscosity: 40000 - 70000 cP
- Hardness, Shore D: >= 75
- Tensile Strength: >= 51.7 MPa
- Adhesive Bond Strength: >= 10.3 MPa
$ 2538/MT
- Viscosity: 1000 - 1500 cP @Temperature 23.0 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 360 min
- Color: Clear with Fluorescent Dye
$ 1759/MT
- Viscosity: 8000 - 10000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 240 - 360 min @Temperature 65.6 °C
$ 1637/MT
- Solids Content: 100 %
- Shear Strength: >= 8.27 MPa
- Peel Strength: >= 0.877 kN/m
- Thermal Conductivity: >= 1.59 W/m-K
- Maximum Service Temperature, Air: 204 °C
$ 1550/MT
- Viscosity: 1800 - 2000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 min @Temperature 23.0 °C
$ 1855/MT
- Viscosity: 75 - 150 cP @Temperature 23.9 °C
- Viscosity: 7000 - 12000 cP @Temperature 23.9 °C
- Hardness, Shore A: <= 5
- Tensile Strength: 2.76 MPa
- Maximum Service Temperature, Air: 93.3 °C
$ 1816/MT
- Viscosity: 30000 - 40000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 135 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 30.0 - 45.0 min @Temperature 93.3 °C
- Cure Time: 1080 - 1440 min @Temperature 23.0 °C
$ 1570/MT
- Viscosity: 4000 - 15000 cP
- Viscosity: 2500 - 18000 cP
- Viscosity: 55000 - 70000 cP
- Hardness, Shore D: >= 75
- Tensile Strength: >= 35.9 MPa
$ 1843/MT
- Viscosity: 3000 - 4000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 2880 min @Temperature 23.0 °C
$ 1570/MT
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
- Melt Temperature: 82.2 °C
- Cure Time: 90.0 - 120 min @Temperature 121 - 149 °C
$ 1762/MT
- Viscosity: 10000 - 20000 cP
- Viscosity: 20000 - 30000 cP
- Hardness, Shore D: 35 - 45
- Tensile Strength at Break: >= 27.6 MPa
- Shear Strength: >= 6.21 MPa
$ 1701/MT
- Viscosity: 8000 - 90000 cP
- Tensile Strength at Break: >= 62.1 MPa
- Compressive Strength: >= 75.8 MPa
- Shear Strength: 17.2 MPa
- Shear Strength: 17.2 MPa
$ 1869/MT
- Viscosity: 8000 - 90000 cP
- Tensile Strength at Break: >= 62.1 MPa
- Compressive Strength: >= 75.8 MPa
- Shear Strength: 17.2 MPa
- Shear Strength: 17.2 MPa
$ 1479/MT
- Viscosity: 8000 - 90000 cP
- Tensile Strength at Break: >= 62.1 MPa
- Compressive Strength: >= 75.8 MPa
- Shear Strength: 17.2 MPa
- Shear Strength: 17.2 MPa
$ 1568/MT
- Hardness, Shore D: >= 85
- Tensile Strength at Break: 27.6 MPa
- Tensile Modulus: >= 3.45 GPa
- Shear Strength: 7.58 MPa
- Shear Strength: 8.62 MPa @Temperature 23.9 °C
$ 2111/MT
- Viscosity: 4000 - 8000 cP
- Viscosity: 50000 - 65000 cP
- Hardness, Shore D: >= 80
- Tensile Strength at Break: >= 34.5 MPa @Temperature 23.9 °C
- Tensile Modulus: >= 3.10 GPa @Temperature 23.9 °C
$ 1494/MT
- Solids Content: 100 %
- Hardness, Shore D: >= 75
- Tensile Modulus: 3.10 GPa
- Shear Strength: >= 8.27 MPa
- Peel Strength: >= 1.75 kN/m
$ 1610/MT
- Viscosity: 350 - 700 cP
- Viscosity: 55000 - 110000 cP
- Hardness, Shore D: 75 - 85
- Tensile Strength: >= 48.3 MPa
- Tensile Modulus: 2.41 - 2.76 GPa
$ 1490/MT
- Water Absorption: <= 1.0 %
- Viscosity: 9000 - 14000 cP
- Viscosity: 225000 - 350000 cP
- Hardness, Shore D: 30
- Tensile Strength: >= 20.7 MPa
$ 1806/MT
- Viscosity: 120000 - 140000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 180 - 240 min @Temperature 93.3 °C
- Cure Time: 2880 - 5760 min @Temperature 23.0 °C
$ 2099/MT
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 90.0 min @Temperature 149 - 177 °C
- Color: Gray
- Viscosity: Paste
$ 1572/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
- Color Code: "A" Gray; "B" White
$ 1724/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -62.2 °C
- Color Code: "A" Tan; "B" Amber
- Mix Ratio By Weight: 100/100
$ 1993/MT
- Viscosity: 5000 - 15000 cP @Temperature 40.0 °C
- Viscosity: 30000 - 45000 cP @Temperature 23.9 °C
- Hardness, Shore D: 80 - 85
- Tensile Strength: >= 55.2 MPa
- Tensile Modulus: >= 1.24 GPa
$ 2255/MT
- Hardness, Shore D: 50 - 55
- Tensile Strength at Break: 51.7 MPa @Temperature 23.9 °C
- Tensile Modulus: 1.72 - 2.07 GPa @Temperature 23.9 °C
- Shear Strength: >= 13.8 MPa
- Peel Strength: 6.14 kN/m
$ 1533/MT
- Viscosity: 50000 - 110000 cP
- Viscosity: 200000 - 600000 cP
- Hardness, Shore D: >= 85
- Tensile Strength at Break: 34.5 MPa @Temperature 23.9 °C
- Tensile Modulus: >= 3.45 GPa @Temperature 23.9 °C
$ 2034/MT
- Viscosity: 30 - 70 cP @Temperature 23.9 °C
- Viscosity: 1000 - 1800 cP @Temperature 52.2 °C
- Viscosity: 55000 - 110000 cP @Temperature 23.9 °C
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 82.7 MPa
$ 2022/MT
- Viscosity: >= 175000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 2880 - 3600 min @Temperature 23.0 °C
$ 1461/MT
- Viscosity: >= 250000 cP @Temperature 23.0 °C
- Storage Temperature: 4.44 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 4.98 - 9.60 min @Temperature 149 °C
$ 1471/MT
- Specific Gravity: 2.90 g/cc
- Solids Content: 100 %
- Hardness, Shore D: 60 - 80
- Tensile Strength at Break: >= 34.5 MPa
- Shear Strength: >= 3.45 MPa @Temperature 93.3 °C
$ 1494/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 min @Temperature 93.3 °C
- Cure Time: 600 min @Temperature 23.0 °C
- Color Code: "A" Gray; "B" Gray
$ 1676/MT
- Viscosity: 100 - 130 cP
- Gardner Impact: >= 31.1 J
- Gardner Impact: >= 36.2 J
- Vicat Softening Point: >= 177 °C
- Flash Point: >= 93.3 °C
$ 2414/MT
- Viscosity: >= 2500 cP
- Hardness, Shore A: 85
- Hardness, Shore D: 45
- Tensile Strength: 10.0 MPa
- Elongation at Break: >= 80 %
$ 1558/MT
- Elongation at Break: >= 60 %
- Adhesive Bond Strength: >= 5.52 MPa
- Adhesive Bond Strength: >= 5.86 MPa
- Peel Strength: >= 3.51 kN/m
- Thermal Conductivity: 1.59 W/m-K
$ 1517/MT
- Viscosity: 6000 - 7000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2160 min @Temperature 23.0 °C
$ 1915/MT
- Viscosity: 350 - 700 cP
- Viscosity: 10000 - 14000 cP
- Hardness, Shore D: 75 - 85
- Tensile Strength at Break: >= 41.4 MPa
- Tensile Modulus: 1.72 - 2.07 GPa
$ 1550/MT
- Shear Strength: 13.1 MPa
- Shear Strength: 14.5 MPa
- Peel Strength: 4.38 kN/m
- Thermal Conductivity: 3.17 - 3.46 W/m-K
- Maximum Service Temperature, Air: 177 °C
$ 1815/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 240 - 480 min @Temperature 23.0 °C
- Color Code: "A" Silver; "B" Silver
- Mix Ratio By Weight: 100/100
$ 1972/MT
- Viscosity: 65000 - 75000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -62.2 °C
- Cure Time: 120 - 180 min
- Color Code: "A" Tan; "B" Brown
$ 2169/MT
- Viscosity: 125000 - 135000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 30.0 - 45.0 min @Temperature 93.3 °C
- Cure Time: 1080 - 1440 min @Temperature 23.0 °C
$ 1612/MT
- Viscosity: 4000 - 6000 cP
- Viscosity: 8000 - 10000 cP
- Viscosity: 10000 - 14000 cP
- Tensile Strength: >= 68.9 MPa
- Tensile Modulus: 2.76 GPa
$ 1458/MT
- Viscosity: 20 - 80 cP @Temperature 23.9 °C
- Viscosity: 50 - 200 cP @Temperature 23.9 °C
- Viscosity: 100 - 500 cP @Temperature 23.9 °C
- Hardness, Shore D: >= 85
- Tensile Strength at Break: >= 75.8 MPa
$ 1725/MT
- Water Absorption: <= 10 %
- Viscosity: 14000 - 18000 cP
- Tensile Strength: >= 68.9 MPa
- Elongation at Break: 1.0 - 2.0 %
- Tensile Modulus: >= 2.76 GPa
$ 1545/MT
- Water Absorption: <= 0.50 %
- Viscosity: 800 - 1000 cP
- Viscosity: 3000 - 5000 cP
- Tensile Strength at Break: 31.1 MPa @Temperature 177 °C
- Tensile Strength at Break: 56.8 MPa @Temperature 121 °C
$ 1633/MT
- Viscosity: 120000 - 135000 cP @Temperature 23.0 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 4.98 - 9.60 min @Temperature 149 °C
$ 1623/MT
- Viscosity: 10000 - 14000 cP
- Viscosity: 11000 - 15000 cP
- Hardness, Shore D: >= 70
- Tensile Strength at Break: >= 51.7 MPa @Temperature 23.9 °C
- Tensile Modulus: 2.07 - 2.41 GPa @Temperature 23.9 °C
$ 1535/MT
- Viscosity: 100000 - 120000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 135 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 2880 - 4320 min @Temperature 23.0 °C
$ 2431/MT
- Viscosity: 1000 - 4000 cP
- Viscosity: 25000 - 40000 cP
- Hardness, Shore D: >= 80
- Tensile Strength: >= 51.7 MPa
- Tensile Modulus: >= 2.76 GPa
$ 1568/MT
- Viscosity: 100000 - 150000 cP
- Hardness, Shore D: 65 - 70
- Tensile Strength: >= 24.1 MPa
- Tensile Modulus: 0.276 - 0.552 GPa
- CTE, linear: 60.0 - 65.0 µm/m-°C
$ 2301/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 180 min @Temperature 93.3 °C
- Cure Time: 2880 - 4320 min @Temperature 23.0 °C
- Color Code: "A" White; "B" Off White
$ 2054/MT
- Viscosity: 70000 - 80000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 4320 min @Temperature 23.0 °C
$ 1678/MT
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 62.1 MPa @Temperature 23.9 °C
- Shear Strength: 17.2 MPa
- CTE, linear: 40.0 - 45.0 µm/m-°C
- Maximum Service Temperature, Air: 204 °C
$ 1974/MT
- Viscosity: 100 - 1000 cP
- Viscosity: 45000 - 55000 cP
- Hardness, Shore D: >= 80
- Tensile Strength: >= 51.7 MPa
- Elongation at Break: >= 2.0 %
$ 1697/MT
- Viscosity: 30000 - 45000 cP
- Viscosity: 40000 - 70000 cP
- Hardness, Shore D: >= 75
- Tensile Strength: >= 20.7 MPa
- Adhesive Bond Strength: >= 8.27 MPa
$ 1507/MT
- Viscosity: 60000 - 70000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 18.0 - 30.0 min @Temperature 23.0 °C
- Color Code: "A" Clear; "B" Dark Purple
$ 1671/MT
- Viscosity: 4000 - 15000 cP
- Viscosity: 2500 - 18000 cP
- Viscosity: 55000 - 70000 cP
- Hardness, Shore D: >= 75
- Tensile Strength: >= 35.9 MPa
$ 1620/MT
- Viscosity: 20000 - 30000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2160 min @Temperature 23.0 °C
$ 1731/MT
- Elongation at Break: >= 60 %
- Adhesive Bond Strength: >= 5.52 MPa
- Adhesive Bond Strength: >= 5.86 MPa @Temperature 23.0 °C
- Peel Strength: >= 3.51 kN/m
- Thermal Conductivity: 1.59 W/m-K
$ 2302/MT
- Viscosity: 15000 - 20000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2160 min @Temperature 23.0 °C
$ 1601/MT
- Viscosity: 200 - 400 cP
- Viscosity: 1000 - 4000 cP
- Viscosity: 11000 - 15000 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 51.7 MPa
$ 1511/MT
- Hardness, Shore D: >= 85
- Tensile Strength: 34.5 MPa
- Tensile Modulus: >= 3.45 GPa
- Compressive Strength: >= 138 MPa
- Compressive Modulus: 4.27 GPa
$ 1507/MT
- Viscosity: 15000 - 20000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 68.3 °C
- Minimum Service Temperature, Air: -48.3 °C
- Cure Time: 60.0 - 90.0 min
- Color Code: "A" Clear; "B" Amber
$ 1636/MT
- Viscosity: >= 150000 cP @Temperature 23.0 °C
- Storage Temperature: 4.44 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -73.3 °C
$ 1489/MT
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 4.98 - 9.60 min @Temperature 149 °C
- Color: Light Yellow
- Viscosity: Thixotropic Paste
$ 1795/MT
- Viscosity: 1500 - 3000 cP
- Viscosity: 5000 - 8000 cP
- Hardness, Shore D: >= 70
- Tensile Strength at Break: >= 48.3 MPa @Temperature 23.9 °C
- Shear Strength: >= 17.2 MPa
$ 2194/MT
- Viscosity: 300 - 400 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min
- Color Code: "A" Clear; "B" Clear
$ 1448/MT
- Viscosity: 50000 - 60000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 1533/MT
- Viscosity: 4000 cP
- Viscosity: 325000 cP
- Hardness, Shore D: >= 80
- Elongation at Break: >= 2.0 %
- Shear Strength: >= 6.89 MPa
$ 1731/MT
- Viscosity: 3000 - 10000 cP
- Viscosity: 50000 - 90000 cP
- Hardness, Shore D: 75 - 80
- Tensile Strength at Break: 34.5 MPa
- Shear Strength: >= 9.65 MPa
$ 1792/MT
- Viscosity: 5000 - 6000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 224 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 30.0 - 45.0 min
- Color Code: "A" Clear; "B" Clear
$ 1714/MT
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 45.0 min @Temperature 149 °C
- Cure Time: 60.0 min @Temperature 121 °C
$ 1616/MT
- Viscosity: 8000 - 9000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 180 - 210 min @Temperature 23.0 °C
- Color Code: "A" Amber; "B" Tan
$ 2140/MT
- Hardness, Shore D: 22 @Temperature 177 °C
- Hardness, Shore D: 27 @Temperature 100 °C
- Hardness, Shore D: 80 @Temperature 23.9 °C
- Tensile Strength: >= 13.8 MPa
- Elongation at Break: >= 50 %
$ 1912/MT
- Viscosity: 4000 - 6000 cP
- Hardness, Shore D: 75 - 90
- Tensile Strength at Break: 58.6 MPa @Temperature 149 °C
- Tensile Strength at Break: 75.8 MPa @Temperature 23.9 °C
- Tensile Modulus: 2.14 GPa @Temperature 149 °C
$ 1800/MT
- Viscosity: 45000 - 100000 cP
- Viscosity: 300000 - 700000 cP
- Hardness, Shore D: 30 - 40
- Tensile Strength at Break: >= 20.7 MPa @Temperature 23.9 °C
- Shear Strength: >= 5.52 MPa
$ 1603/MT
- Viscosity: 10000 - 15000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 135 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 150 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 1660/MT
- Water Absorption: <= 1.0 %
- Shear Strength: >= 10.1 MPa
- Shear Strength: >= 10.5 MPa
- Shear Strength: >= 10.9 MPa
- Peel Strength: 3.86 kN/m
$ 1871/MT
- Viscosity: 14000 - 28000 cP
- Viscosity: 15000 - 30000 cP
- Hardness, Shore A: 70 - 90
- Tensile Strength at Break: 3.45 MPa
- Elongation at Break: >= 100 %
$ 2240/MT
- Density: 1.48 g/cc
- Water Absorption: <= 1.5 %
- Flexural Strength: 59.3 MPa
- Flexural Modulus: 4.00 GPa
- Shear Strength: 9.24 MPa @Temperature 260 °C
$ 2176/MT
- Viscosity: 70000 - 80000 cP
- Hardness, Shore A: 55 - 60
- Hardness, Shore D: 12 - 15
- Tensile Strength: 7.93 MPa
- Elongation at Break: >= 125 %
$ 1646/MT
- Viscosity: 250 - 400 cP
- Viscosity: 60000 - 110000 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 62.1 MPa
- Shear Strength: 18.6 MPa
$ 1716/MT
- Solids Content: 100 %
- Viscosity: 15000 - 25000 cP
- Hardness, Shore D: >= 80
- Tensile Strength at Break: 68.9 MPa
- Tensile Modulus: 2.76 - 3.10 GPa
$ 1793/MT
- Viscosity: 300 - 400 cP
- Viscosity: 10000 - 18000 cP
- Hardness, Shore D: 85 - 90
- Tensile Strength at Break: >= 41.4 MPa
- Compressive Strength: >= 103 MPa
$ 1582/MT
- Elongation at Break: >= 5.0 %
- Adhesive Bond Strength: >= 5.52 MPa
- Adhesive Bond Strength: >= 5.86 MPa
- Thermal Conductivity: 3.75 W/m-K
- Maximum Service Temperature, Air: 121 °C
$ 1625/MT
- Viscosity: 60000 - 80000 cP
- Hardness, Shore D: >= 65
- Tensile Strength: >= 17.2 MPa
- Tensile Modulus: 0.172 - 0.345 GPa
- CTE, linear: 65.0 - 70.0 µm/m-°C
$ 1538/MT
- Adhesive Bond Strength: >= 5.52 MPa
- Adhesive Bond Strength: >= 5.86 MPa @Temperature 23.0 °C
- Peel Strength: >= 1.75 kN/m
- Thermal Conductivity: 1.30 W/m-K
- Maximum Service Temperature, Air: 121 °C
$ 1612/MT
- Hardness, Shore D: >= 85
- Tensile Strength at Break: 37.9 MPa
- Shear Strength: 13.1 MPa
- Shear Strength: 13.4 MPa
- CTE, linear: 22.0 - 24.0 µm/m-°C
$ 1538/MT
- Viscosity: 100000 - 150000 cP
- Hardness, Shore D: 65 - 70
- Tensile Strength: >= 24.1 MPa
- Tensile Modulus: 0.276 - 0.552 GPa
- CTE, linear: 60.0 - 65.0 µm/m-°C
$ 1631/MT
- Water Absorption: <= 0.50 %
- Viscosity: 200 - 300 cP
- Viscosity: 300 - 400 cP
- Tensile Strength at Break: >= 65.5 MPa
- Tensile Modulus: >= 2.76 GPa
$ 2089/MT
- Solids Content: 100 %
- Hardness, Shore D: 70
- Shear Strength: 12.4 MPa
- Peel Strength: >= 3.51 kN/m
- CTE, linear: 40.0 - 45.0 µm/m-°C
$ 1690/MT
- Solids Content: 100 %
- Viscosity: >= 150000 cP
- Shear Strength: 6.76 MPa
- Shear Strength: 12.4 MPa
- Peel Strength: 1.23 kN/m
$ 1939/MT
- Shear Strength: >= 15.9 MPa
- Shear Strength: >= 17.2 MPa
- Peel Strength: >= 2.10 kN/m
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -62.2 °C
$ 1464/MT
- Viscosity: 30 - 70 cP @Temperature 23.9 °C
- Viscosity: 1000 - 1800 cP @Temperature 51.7 °C
- Viscosity: 55000 - 110000 cP @Temperature 23.9 °C
- Hardness, Shore D: >= 75
- Tensile Strength: >= 82.7 MPa
$ 2085/MT
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 min @Temperature 23.0 °C
- Color Code: "A" Dark Gray; "B" Tan
$ 2086/MT
- Solids Content: 100 %
- Viscosity: 80000 - 130000 cP
- Hardness, Shore D: >= 85
- Tensile Strength at Break: >= 552 MPa
- Shear Strength: >= 14.5 MPa
$ 2250/MT
- Water Absorption: <= 1.0 %
- Shear Strength: >= 6.21 MPa
- Shear Strength: >= 6.89 MPa
- Peel Strength: 0.877 - 1.75 kN/m
- CTE, linear: 40.0 - 45.0 µm/m-°C
$ 1497/MT
- Viscosity: 50000 - 60000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 1708/MT
- Elongation at Break: 3.0 %
- Flexural Strength: 71.0 MPa
- Shear Strength: >= 13.8 MPa
- CTE, linear: 29.0 µm/m-°C
- CTE, linear: 72.0 µm/m-°C
$ 2085/MT
- Viscosity: 8000 - 10000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 120 - 180 min @Temperature 23.0 °C
- Color Code: "A" Clear; "B" Clear Yellow
$ 1646/MT
- Viscosity: 300 - 400 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -62.2 °C
- Transmission, Visible: 90 %
- Cure Time: 240 - 360 min @Temperature 93.3 °C
$ 1501/MT
- Viscosity: 50000 - 60000 cP
- Tensile Strength at Break: 85.5 MPa
- Tensile Modulus: 3.31 GPa
- Shear Strength: >= 16.5 MPa
- Shear Strength: >= 17.2 MPa
$ 1688/MT
- Hardness, Shore D: >= 80
- Tensile Strength at Break: >= 75.8 MPa
- Elongation at Break: >= 5.0 %
- Tensile Modulus: 3.45 GPa
- Compressive Strength: >= 131 MPa
$ 1509/MT
- Specific Gravity: 2.90 g/cc
- Solids Content: 100 %
- Hardness, Shore D: 60 - 80
- Tensile Strength at Break: >= 34.5 MPa
- Shear Strength: >= 3.45 MPa @Temperature 93.3 °C
$ 1948/MT
- Tensile Strength at Break: >= 62.1 MPa
- Compressive Strength: >= 96.5 MPa
- Shear Strength: 2.21 MPa
- CTE, linear: 45.0 - 50.0 µm/m-°C
- Maximum Service Temperature, Air: 121 °C
$ 1542/MT
- Adhesive Bond Strength: >= 5.52 MPa
- Adhesive Bond Strength: >= 5.86 MPa
- Peel Strength: >= 0.877 kN/m
- Thermal Conductivity: 1.59 W/m-K
- Maximum Service Temperature, Air: 135 °C
$ 1796/MT
- Viscosity: 6000 - 8000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 1563/MT
- Viscosity: 1500 - 3000 cP
- Viscosity: 55000 - 125000 cP
- Hardness, Shore D: >= 80
- Tensile Strength at Break: >= 34.5 MPa @Temperature 23.9 °C
- Tensile Modulus: >= 3.10 GPa @Temperature 23.9 °C
$ 1458/MT
- Viscosity: 30 - 70 cP
- Viscosity: 10000 - 14000 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 68.9 MPa
- Elongation at Break: 3.4 %
$ 1863/MT
- Viscosity: 70000 - 80000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 1747/MT
- Viscosity: 5000 - 6000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min
- Color Code: "A" Black; "B" Brown
$ 2050/MT
- Viscosity: 27000 - 30000 cP
- Hardness, Shore D: 75 - 90
- Tensile Strength at Break: 73.1 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 3.10 GPa
$ 1690/MT
- Viscosity: 600 - 1200 cP
- Viscosity: 1800 - 2500 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 62.1 MPa @Temperature 23.9 °C
- Tensile Modulus: 2.41 - 2.76 GPa @Temperature 23.9 °C
$ 1942/MT
- Viscosity: 50000 - 60000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 2146/MT
- Density: 1.18 g/cc
- Water Absorption: 0.30 %
- Viscosity: 500 - 1000 cP @Temperature 82.2 °C
- Hardness, Shore D: 20 @Temperature 100 °C
- Hardness, Shore D: 40 @Temperature 25.0 °C
$ 1463/MT
- Adhesive Bond Strength: >= 5.86 MPa
- Adhesive Bond Strength: >= 5.86 MPa
- Peel Strength: >= 1.75 kN/m
- Thermal Conductivity: 1.59 W/m-K
- Maximum Service Temperature, Air: 135 °C
$ 1599/MT
- Viscosity: >= 250000 cP @Temperature 23.0 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 4.98 - 9.60 min @Temperature 149 °C
$ 1685/MT
- Viscosity: 140000 - 200000 cP
- Hardness, Shore D: >= 70
- Tensile Strength at Break: >= 65.5 MPa
- Elongation at Break: >= 5.0 %
- Tensile Modulus: >= 2.76 GPa
$ 1459/MT
- Viscosity: 2000 - 3000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2160 min @Temperature 23.0 °C
$ 2452/MT
- Hardness, Shore D: >= 60
- Tensile Strength at Break: >= 37.9 MPa @Temperature 23.9 °C
- Tensile Modulus: 1.38 - 1.72 GPa @Temperature 23.9 °C
- Shear Strength: >= 18.6 MPa
- Peel Strength: 4.38 kN/m
$ 2579/MT
- Water Absorption: <= 1.0 %
- Shear Strength: 10.6 MPa
- Shear Strength: 11.0 MPa
- Peel Strength: >= 2.63 kN/m
- CTE, linear: 30.0 - 35.0 µm/m-°C
$ 1515/MT
- Viscosity: 60000 - 70000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 177 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 240 - 360 min @Temperature 23.0 °C
- Color Code: "A" Clear; "B" Tan
$ 1641/MT
- Shear Strength: >= 8.27 MPa
- Shear Strength: >= 8.62 MPa
- Peel Strength: >= 1.75 kN/m
- Thermal Conductivity: 1.30 W/m-K
- Maximum Service Temperature, Air: 135 °C
$ 1723/MT
- Viscosity: 200 - 250 cP
- Hardness, Shore D: 93
- Tensile Strength: 35.9 MPa @Temperature 149 °C
- Tensile Strength: 70.3 MPa @Temperature 23.9 °C
- Elongation at Break: 2.4 % @Temperature 75.0 °C
$ 1657/MT
- Viscosity: 35000 - 45000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 min @Temperature 23.0 °C
$ 1648/MT
- Viscosity: >= 250000 cP @Temperature 23.0 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 45.0 min @Temperature 149 °C
$ 1623/MT
- Thickness: 76.2 microns
- Thermal Conductivity: >= 1.44 W/m-K
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 30.0 - 40.2 min @Temperature 149 °C
$ 1733/MT
- Viscosity: 100000 - 120000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -62.2 °C
- Cure Time: 180 - 240 min
- Color Code: "A" Tan; "B" Brown
$ 1886/MT
- Tensile Strength at Break: 88.3 MPa
- Compressive Strength: >= 124 MPa
- Shear Strength: >= 15.9 MPa
- Thermal Conductivity: 1.30 - 1.44 W/m-K
- Maximum Service Temperature, Air: 260 °C
$ 2538/MT
- Viscosity: 3000 - 4000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 1675/MT
- Hardness, Shore D: 50 - 55
- Hardness, Shore D: 75 - 80
- Tensile Strength at Break: >= 34.5 MPa @Temperature 23.9 °C
- Elongation at Break: <= 120 %
- Shear Strength: >= 8.27 MPa @Temperature 23.9 °C
$ 1728/MT
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 45.0 min @Temperature 149 °C
- Cure Time: 60.0 min @Temperature 121 °C
$ 1511/MT
- Solids Content: 100 %
- Viscosity: >= 200000 cP
- Shear Strength: 21.4 MPa
- Maximum Service Temperature, Air: 149 °C
- Minimum Service Temperature, Air: -62.2 °C
$ 2175/MT
- Viscosity: 30 - 70 cP @Temperature 23.9 °C
- Viscosity: 1000 - 1800 cP @Temperature 52.0 °C
- Viscosity: 55000 - 110000 cP @Temperature 23.9 °C
- Hardness, Shore D: >= 75
- Tensile Strength: >= 82.7 MPa
$ 2243/MT
- Viscosity: 30 - 70 cP @Temperature 23.9 °C
- Viscosity: 1000 - 1800 cP @Temperature 52.2 °C
- Viscosity: 55000 - 110000 cP @Temperature 23.9 °C
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 82.7 MPa
$ 1676/MT
- Thickness: 76.2 microns
- Thermal Conductivity: >= 1.44 W/m-K
- Volume Resistivity: >= 1.00e+13 ohm-cm
- Cure Time: 30.0 - 40.2 min @Temperature 149 °C
- Cure Time: 60.0 min @Temperature 121 °C
- Weight Loss, %: max 0.6
$ 1666/MT
- Viscosity: 25000 - 60000 cP
- Hardness, Shore D: >= 85
- Tensile Strength: >= 75.8 MPa @Temperature 23.9 °C
- Compressive Strength: >= 138 MPa
- CTE, linear: 25.0 - 30.0 µm/m-°C
$ 1555/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
- Color Code: "A" Dk Gray/Black; "B" Clear
$ 2381/MT
- Storage Temperature: 4.44 °C
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 30.0 - 39.6 min @Temperature 149 °C
- Cure Time: 60.0 min @Temperature 121 °C
$ 2085/MT
- Viscosity: 30000 - 65000 cP
- Hardness, Shore D: >= 85
- Tensile Strength: >= 75.8 MPa @Temperature 23.9 °C
- Compressive Strength: >= 138 MPa
- CTE, linear: 25.0 - 30.0 µm/m-°C
$ 2482/MT
- Adhesive Bond Strength: >= 17.2 MPa
- Adhesive Bond Strength: >= 17.2 MPa
- Peel Strength: >= 1.75 kN/m
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -73.3 °C
$ 1794/MT
- Viscosity: 6000 - 6500 cP
- Hardness, Shore D: 50 - 55
- Tensile Strength: 8.27 - 10.3 MPa
- Elongation at Break: 110 %
- Tensile Modulus: 0.827 GPa
$ 1572/MT
- Shear Strength: >= 12.4 MPa
- Shear Strength: >= 12.8 MPa
- Peel Strength: >= 3.51 kN/m
- Thermal Conductivity: 1.59 W/m-K
- Maximum Service Temperature, Air: 135 °C
$ 1750/MT
- Viscosity: 50000 - 70000 cP
- Hardness, Shore D: >= 70
- Tensile Strength: >= 34.5 MPa
- Tensile Modulus: >= 2.41 GPa
- CTE, linear: 55.0 - 65.0 µm/m-°C
$ 1876/MT
- Tensile Strength at Break: >= 41.4 MPa @Temperature 23.9 °C
- Compressive Strength: >= 103 MPa
- Shear Strength: >= 8.27 MPa
- CTE, linear: 21.0 - 24.0 µm/m-°C
- Maximum Service Temperature, Air: 121 °C
$ 1981/MT
- Viscosity: 80000 - 90000 cP @Temperature 23.0 °C
- Storage Temperature: 23.9 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 0.330 min @Temperature 204 °C
$ 1493/MT
- Viscosity: 400 - 500 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Transmission, Visible: 90 %
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
$ 1748/MT
- Water Absorption: <= 1.0 %
- Viscosity: >= 100000 cP
- Viscosity: >= 140000 cP
- Tensile Strength at Break: >= 52.4 MPa
- Compressive Strength: <= 68.9 MPa
$ 1487/MT
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -269 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2160 min @Temperature 23.0 °C
- Color Code: "A" Silver; "B" Silver
$ 2434/MT
- Solids Content: 94 %
- Thermal Conductivity: >= 1.61 W/m-K
- Surface Resistivity per Square: 1.0 - 2.0 ohm
$ 1934/MT
- Viscosity: 8000 - 10000 cP
- Viscosity: 55000 - 110000 cP
- Hardness, Shore D: 75 - 85
- Tensile Strength at Break: >= 51.7 MPa
- Tensile Modulus: >= 3.10 GPa
$ 1757/MT
- Viscosity: 280 - 500 cP
- Viscosity: 60000 - 110000 cP
- Hardness, Shore D: 90
- Tensile Strength at Break: >= 41.4 MPa
- Compressive Strength: >= 117 MPa
$ 1477/MT
- Viscosity: 4000 - 6000 cP
- Viscosity: 60000 - 110000 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 62.1 MPa @Temperature 23.9 °C
- Shear Strength: 17.2 MPa
$ 1762/MT
- Water Absorption: <= 0.10 % @Temperature 23.9 °C, Time 86400 sec
- Viscosity: 100 - 150 cP
- Viscosity: 10000 - 14000 cP
- Hardness, Shore D: >= 75
- Tensile Strength at Break: >= 75.8 MPa @Temperature 23.9 °C
$ 2106/MT
- Viscosity: 1600 - 1800 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 120 - 180 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
$ 2330/MT
- Maximum Service Temperature, Air: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
- Cure Time: 60.0 min @Temperature 93.3 °C
- Cure Time: 1440 - 2160 min @Temperature 23.0 °C
- Color Code: "A" Gray; "B" White
$ 1808/MT
- Viscosity: 1500 - 3000 cP
- Viscosity: 14000 - 18000 cP
- Viscosity: 100000 - 150000 cP
- Hardness, Shore D: 85 - 90
- Tensile Strength at Break: >= 58.6 MPa
$ 1954/MT
- Viscosity: 200 - 1000 cP
- Viscosity: 50000 - 120000 cP
- Hardness, Shore D: >= 80
- Tensile Strength at Break: >= 51.7 MPa
- Elongation at Break: >= 2.0 %
$ 1995/MT
- Hardness, Shore D: >= 80
- Tensile Strength at Break: >= 48.3 MPa
- Tensile Modulus: 3.45 - 3.79 GPa
- Compressive Strength: 110 - 124 MPa
- Shear Strength: >= 18.6 MPa
$ 1697/MT
- Viscosity: 2000 - 3000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 121 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 180 - 240 min @Temperature 93.3 °C
- Cure Time: 2880 - 4320 min @Temperature 23.0 °C
$ 1444/MT
- Viscosity: >= 200000 cP
- Viscosity: >= 1.00e+6 cP
- Hardness, Shore D: >= 75
- Tensile Strength: >= 82.7 MPa
- Elongation at Break: <= 3.0 %
$ 1785/MT
- Viscosity: 400000 - 600000 cP
- Hardness, Shore D: 85 - 90
- Tensile Strength at Break: >= 55.2 MPa
- Tensile Modulus: 3.45 GPa
- Shear Strength: >= 13.8 MPa
$ 1917/MT
- Viscosity: 70000 - 80000 cP @Temperature 23.0 °C
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -51.1 °C
- Cure Time: 60.0 - 120 min @Temperature 93.3 °C
- Cure Time: 1440 - 2880 min @Temperature 23.0 °C
Delivery Epoxy Master Bond Inc.
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, chemical carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.