$ 2316/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 120 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1488/MT
- Melt Flow: >= 35 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 13.0 kJ/m²
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1467/MT
- Density: 1.045 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 3.553 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 2380/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1966/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 100 MPa
- Tensile Strength, Yield: 46.0 MPa
$ 1555/MT
- Melt Flow: >= 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 18.0 kJ/m²
- Vicat Softening Point: 109 °C @Load 5.10 kg
- Gloss: 98 %
$ 1590/MT
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0070 cm/cm
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 100 MPa
- Tensile Strength, Yield: 40.0 MPa
$ 1912/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
$ 2572/MT
- Density: 1.046 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 15.69 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa
$ 1600/MT
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 41.0 MPa
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 89 %
$ 1471/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 46.0 MPa
$ 1568/MT
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 49.0 MPa
- Vicat Softening Point: 100 °C @Load 5.10 kg
- Gloss: 88 %
$ 2068/MT
- Density: 1.04 g/cc
- Water Absorption: 1.0 %
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1567/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 44.0 MPa
$ 1799/MT
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 2.0 g/10 min @Temperature 200 °C
- Tensile Strength, Yield: 48.0 MPa
$ 1736/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 74
- Tensile Strength, Yield: 42.7 MPa
$ 1571/MT
- Density: 1.03 g/cc
- Water Absorption: 1.03 %
- Moisture Absorption at Equilibrium: 0.21 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 0.10 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1457/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: 0.25 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 102 MPa
$ 2353/MT
- Melt Flow: >= 27 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 16.0 kJ/m²
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1969/MT
- Melt Flow: >= 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 13.0 kJ/m²
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1449/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1664/MT
- Density: 1.08 g/cc
- Water Absorption at Saturation: 0.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 17 g/10 min @Load 21.6 kg, Temperature 220 °C
$ 1454/MT
- Melt Flow: >= 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 20.0 kJ/m²
- Vicat Softening Point: 97.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1856/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 104 MPa @Temperature -40.0 °C
- Tensile Strength, Ultimate: 75.0 MPa
$ 1709/MT
- Density: 1.043 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 10.43 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 2225/MT
- Density: 1.045 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 3.553 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1579/MT
- Density: 1.048 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 1.572 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1798/MT
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 46.0 MPa
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 85 %
$ 1586/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1766/MT
- Density: 1.048 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1461/MT
- Melt Flow: 38 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 49.0 MPa
- Vicat Softening Point: 99.0 °C @Load 5.10 kg
- Gloss: 90 %
$ 1899/MT
- Melt Flow: >= 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 35.0 kJ/m²
- Vicat Softening Point: 96.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1570/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.0 MPa
$ 1681/MT
- Melt Flow: >= 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 20.0 kJ/m²
- Vicat Softening Point: 101 °C @Load 5.10 kg
- Gloss: 98 %
$ 1595/MT
- Melt Flow: >= 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 15.0 kJ/m²
- Vicat Softening Point: 99.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1788/MT
- Melt Flow: >= 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 14.0 kJ/m²
- Vicat Softening Point: 103 °C @Load 5.10 kg
- Gloss: 98 %
$ 2404/MT
- Melt Flow: >= 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 20.0 kJ/m²
- Vicat Softening Point: 99.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1827/MT
- Melt Flow: >= 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 17.0 kJ/m²
- Vicat Softening Point: 105 °C @Load 5.10 kg
- Gloss: 98 %
$ 1493/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
$ 1982/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1661/MT
- Density: 1.08 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.16 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1613/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: 0.25 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 114 MPa
$ 2095/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.35 %
- Moisture Absorption at Equilibrium: 0.70 %
- Linear Mold Shrinkage: 0.01397 cm/cm
- Tensile Strength, Yield: 48.0 MPa
$ 1801/MT
- Density: 1.09 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 2.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
$ 2396/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 46.9 MPa
$ 1826/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1683/MT
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 44.0 MPa
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 87 %
$ 1682/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
$ 1488/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 51.0 MPa
$ 2584/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 115 MPa
- Tensile Strength, Yield: 51.0 MPa
$ 1589/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 40.0 MPa
$ 1535/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 44.8 MPa
$ 1562/MT
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 8.0 g/10 min @Temperature 220 °C
- Tensile Strength, Yield: 42.0 MPa
$ 1713/MT
- Density: 1.36 g/cc
- Moisture Absorption at Equilibrium: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Melt Flow: 5.44 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 5.44 g/10 min @Load 21.6 kg, Temperature 200 °C
$ 1466/MT
- Density: 1.022 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 14.308 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 90.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 1722/MT
- Density: 1.028 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 4.112 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 66.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 1673/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.35 %
- Moisture Absorption at Equilibrium: 0.70 %
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm
- Melt Flow: 8.64 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1483/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 90.0 MPa
- Tensile Strength, Yield: 42.0 MPa
$ 1928/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 95.0 MPa
$ 1572/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 96.0 MPa @Temperature -40.0 °C
$ 2499/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 44.8 MPa
$ 1514/MT
- Density: 1.043 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 10.43 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1457/MT
- Density: 1.02 g/cc
- Moisture Absorption at Equilibrium: 0.21 % @Temperature 23.0 °C
- Water Absorption at Saturation: 1.03 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1500/MT
- Density: 1.04 g/cc
- Water Absorption: 0.95 %
- Moisture Absorption at Equilibrium: 0.24 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 3.1 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1666/MT
- Density: 1.05 g/cc
- Melt Flow: 15.75 g/10 min
- Tensile Strength at Break: 44.0 MPa
- Tensile Modulus: 3.30 GPa
- Flexural Strength: 70.0 MPa
$ 1767/MT
- Density: 1.048 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 1.572 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1988/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 31 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 46.0 MPa
$ 1876/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 58.0 MPa
$ 1922/MT
- Melt Flow: 27 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.0 MPa
- Vicat Softening Point: 99.0 °C @Load 5.10 kg
- Gloss: 90 %
$ 1445/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 47.0 MPa
Delivery Molded Styrolution
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.