$ 1726/MT
- Density: 1.04 g/cc
- Water Absorption at Saturation: 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 80
$ 2316/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 120 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1465/MT
- Linear Mold Shrinkage, Flow: 0.01143 cm/cm
- Melt Flow: 1.5 g/10 min
- Hardness, Rockwell M: 78
- Tensile Strength at Break: 52.0 MPa
- Flexural Modulus: 3.31 GPa
$ 1604/MT
- Density: 1.18 g/cc
- Water Absorption: 1.42 %
- Moisture Absorption at Equilibrium: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Melt Flow: 5.9 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1514/MT
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): 6.00 kJ/m²
- Vicat Softening Point: 106 °C @Load 5.10 kg
- Gloss: 98 %
$ 1696/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Melt Flow: 44.8 g/10 min @Load 10.0 kg, Temperature 240 °C
- Ball Indentation Hardness: 62.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 1634/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 1715/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 1678/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0090 cm/cm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 25 %
- Elongation at Yield: 3.1 %
$ 1629/MT
- Density: 1.01 g/cc
- Water Absorption: 0.070 %
- Moisture Absorption at Equilibrium: 0.070 %
- Moisture Vapor Transmission: 1.70 cc-mm/m²-24hr-atm
- Oxygen Transmission Rate: 500 cc/m²/day
$ 2108/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Melt Flow: 5.35 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1677/MT
- Density: 1.02 g/cc
- Water Absorption: 0.070 %
- Moisture Absorption at Equilibrium: 0.070 %
- Melt Flow: 13 g/10 min @Load 5.00 kg, Temperature 200 °C
- Film Tensile Strength at Yield, MD: 29.0 MPa
$ 1774/MT
- Density: 1.029 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 3.602 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Yield: 22.0 MPa
$ 1488/MT
- Melt Flow: >= 35 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 13.0 kJ/m²
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1467/MT
- Density: 1.045 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 3.553 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1605/MT
- Density: 1.01 g/cc
- Water Absorption: 0.070 %
- Moisture Absorption at Equilibrium: 0.070 %
- Moisture Vapor Transmission: 2.90 cc-mm/m²-24hr-atm
- Oxygen Transmission Rate: 520 cc/m²/day
$ 2380/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1475/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Melt Flow: 42.8 g/10 min @Load 10.0 kg, Temperature 240 °C
- Hardness, Rockwell R: 103
$ 1966/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 100 MPa
- Tensile Strength, Yield: 46.0 MPa
$ 1455/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
- Melt Flow: 21.6 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 24.84 g/10 min @Load 21.6 kg, Temperature 200 °C
$ 1555/MT
- Melt Flow: >= 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 18.0 kJ/m²
- Vicat Softening Point: 109 °C @Load 5.10 kg
- Gloss: 98 %
$ 1590/MT
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0070 cm/cm
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 100 MPa
- Tensile Strength, Yield: 40.0 MPa
$ 1912/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
$ 1821/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.4 %
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 33.0 MPa
- Tensile Strength, Yield: 36.0 MPa
$ 1492/MT
- Density: 1.15 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.25 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.18 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1639/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1493/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 3.1 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 50
- Tensile Strength, Yield: 24.1 MPa
$ 2308/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 32.0 MPa
$ 2572/MT
- Density: 1.046 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 15.69 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa
$ 1600/MT
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 41.0 MPa
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 89 %
$ 1773/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 31.0 MPa
- Tensile Strength, Ultimate: 48.0 MPa
$ 1802/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
- Melt Flow: 7.56 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 9.72 g/10 min @Load 21.6 kg, Temperature 200 °C
$ 2524/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 1.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 78
- Tensile Strength, Yield: 52.4 MPa
$ 1532/MT
- Water Absorption at Saturation: 0.070 % @Temperature 23.0 °C
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore D: 83
- Tensile Strength, Yield: 2.00 MPa
- Elongation at Break: 2.5 %
$ 1511/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength, Yield: 50.0 MPa
$ 1592/MT
- Density: 1.15 g/cc
- Moisture Absorption at Equilibrium: 1.3 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 280 °C
- Tensile Strength, Yield: 50.0 MPa
$ 1657/MT
- Melt Flow: >= 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 35.0 kJ/m²
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1471/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 46.0 MPa
$ 1960/MT
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 46.0 MPa
- Vicat Softening Point: 102 °C @Load 5.10 kg
- Gloss: 90 %
$ 1669/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 1550/MT
- Melt Flow: 10 g/10 min
- Hardness, Shore D: 69
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 100 %
- Tensile Modulus: 1.73 GPa
$ 1471/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 1879/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.9 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 50
- Tensile Strength, Yield: 23.4 MPa
$ 1462/MT
- Density: 1.16 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Ultimate: 70.0 MPa
$ 2115/MT
- Density: 1.07 g/cc
- Tensile Strength, Yield: 36.0 MPa
- Elongation at Break: 50 %
- Elongation at Yield: 5.0 %
- Tensile Modulus: 1.40 GPa
$ 1644/MT
- Water Absorption at Saturation: 0.070 % @Temperature 23.0 °C
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore D: 67
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: 250 %
$ 1907/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 50
- Tensile Strength, Yield: 20.3 MPa
$ 1568/MT
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 49.0 MPa
- Vicat Softening Point: 100 °C @Load 5.10 kg
- Gloss: 88 %
$ 1933/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 44.1 MPa
$ 1934/MT
- Density: 1.046 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 6.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2247/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 55
- Tensile Strength, Yield: 22.3 MPa
$ 1639/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: 1.5 %
$ 1996/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 28 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2068/MT
- Density: 1.04 g/cc
- Water Absorption: 1.0 %
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1469/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1477/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1567/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 44.0 MPa
$ 1514/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1525/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1775/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1799/MT
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 2.0 g/10 min @Temperature 200 °C
- Tensile Strength, Yield: 48.0 MPa
$ 1469/MT
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 68.0 MPa
- Vicat Softening Point: 104 °C @Load 5.10 kg
$ 1736/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 74
- Tensile Strength, Yield: 42.7 MPa
$ 1534/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 55
- Tensile Strength, Yield: 28.3 MPa
$ 1869/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell M: 83
$ 1947/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Melt Flow: 12.84 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1476/MT
- Melt Flow: 16 g/10 min
- Hardness, Shore D: 74
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 43 %
- Tensile Modulus: 1.68 GPa
$ 1626/MT
- Melt Flow: 2.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 38.0 MPa
- Vicat Softening Point: 95.0 °C @Load 5.10 kg
- Gloss: 90 %
$ 1571/MT
- Density: 1.03 g/cc
- Water Absorption: 1.03 %
- Moisture Absorption at Equilibrium: 0.21 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 0.10 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1518/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
- Melt Flow: 10.8 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 12.96 g/10 min @Load 21.6 kg, Temperature 200 °C
$ 1457/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: 0.25 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 102 MPa
$ 2256/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Melt Flow: 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Yield: 22.0 MPa
$ 1621/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.4 %
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 39.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 2079/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 44.0 MPa
$ 1892/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 1551/MT
- Density: 1.05 g/cc
- Melt Flow: 15.75 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 38.0 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 2.30 GPa
$ 2024/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Melt Flow: 7.35 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 102 MPa @Load 36.5 kg, Time 30.0 sec
- Tensile Strength, Yield: 51.0 MPa
$ 1548/MT
- Density: 1.02 g/cc
- Melt Flow: 3.06 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 39.0 MPa
- Tensile Modulus: 1.78 GPa
- Flexural Modulus: 1.78 GPa
$ 2241/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Melt Flow: 26.75 g/10 min @Load 10.0 kg, Temperature 240 °C
- Hardness, Rockwell R: 94
$ 1506/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 1.9 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 6.2 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2353/MT
- Melt Flow: >= 27 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 16.0 kJ/m²
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1666/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2423/MT
- Melt Flow: >= 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 35.0 kJ/m²
- Vicat Softening Point: 96.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1969/MT
- Melt Flow: >= 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 13.0 kJ/m²
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 2131/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 1.1 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 240 °C
- Ball Indentation Hardness: 95.0 MPa
$ 1449/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 2166/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 42
- Tensile Strength, Yield: 20.3 MPa
$ 1707/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 46.9 MPa
$ 1664/MT
- Density: 1.08 g/cc
- Water Absorption at Saturation: 0.70 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 17 g/10 min @Load 21.6 kg, Temperature 220 °C
$ 2041/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1457/MT
- Density: 1.11 g/cc
- Moisture Absorption at Equilibrium: 0.35 % @Temperature 23.0 °C
- Water Absorption at Saturation: 0.90 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0050 - 0.0090 cm/cm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 2264/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1632/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.4 %
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 32.0 MPa
$ 1454/MT
- Melt Flow: >= 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 20.0 kJ/m²
- Vicat Softening Point: 97.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1715/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.01143 cm/cm
- Melt Flow: 1.5 g/10 min
- Hardness, Rockwell M: 78
- Tensile Strength at Break: 52.0 MPa
$ 1856/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 104 MPa @Temperature -40.0 °C
- Tensile Strength, Ultimate: 75.0 MPa
$ 1740/MT
- Density: 1.07 g/cc
- Water Absorption: 0.10 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 65
$ 1709/MT
- Density: 1.043 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 10.43 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 2225/MT
- Density: 1.045 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 3.553 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1579/MT
- Density: 1.048 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 1.572 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1477/MT
- Density: 1.029 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 4.116 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Yield: 23.0 MPa
$ 1798/MT
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 46.0 MPa
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 85 %
$ 1633/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 9.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1599/MT
- Density: 1.04 g/cc
- Water Absorption at Saturation: 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 70
$ 1672/MT
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): 6.00 kJ/m²
- Vicat Softening Point: 105 °C @Load 5.10 kg
- Gloss: 98 %
$ 1657/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 23 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 74
- Tensile Strength, Yield: 34.5 MPa
$ 2096/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 1586/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 2042/MT
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 52.0 MPa
- Tensile Strength, Ultimate: 60.0 MPa
$ 1529/MT
- Density: 1.002 g/cc
- Water Absorption: <= 0.070 %
- Moisture Absorption at Equilibrium: <= 0.070 %
- Melt Flow: 3.006 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 13.026 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1766/MT
- Density: 1.048 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2077/MT
- Density: 1.27 g/cc
- Water Absorption: 3.4 %
- Moisture Absorption at Equilibrium: 1.0 %
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength, Ultimate: 85.0 MPa
$ 1461/MT
- Melt Flow: 38 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 49.0 MPa
- Vicat Softening Point: 99.0 °C @Load 5.10 kg
- Gloss: 90 %
$ 1461/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Melt Flow: 64.2 g/10 min @Load 10.0 kg, Temperature 240 °C
- Hardness, Rockwell R: 103
$ 2595/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1801/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.4 %
- Melt Flow: 19 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 36.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1899/MT
- Melt Flow: >= 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 35.0 kJ/m²
- Vicat Softening Point: 96.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1570/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.0 MPa
$ 1766/MT
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 73.0 MPa
- Tensile Strength at Break: 115 MPa @Temperature -40.0 °C
$ 1895/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.4 %
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 35.0 MPa
- Tensile Strength, Yield: 40.0 MPa
$ 1681/MT
- Melt Flow: >= 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 20.0 kJ/m²
- Vicat Softening Point: 101 °C @Load 5.10 kg
- Gloss: 98 %
$ 1772/MT
- Density: 1.01 g/cc
- Water Absorption: <= 0.070 %
- Moisture Absorption at Equilibrium: <= 0.070 %
- Melt Flow: 12.63 g/10 min
- Hardness, Shore D: 64
$ 1809/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1595/MT
- Melt Flow: >= 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 15.0 kJ/m²
- Vicat Softening Point: 99.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1788/MT
- Melt Flow: >= 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 14.0 kJ/m²
- Vicat Softening Point: 103 °C @Load 5.10 kg
- Gloss: 98 %
$ 1517/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2404/MT
- Melt Flow: >= 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 20.0 kJ/m²
- Vicat Softening Point: 99.0 °C @Load 5.10 kg
- Gloss: 98 %
$ 1587/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.1 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1827/MT
- Melt Flow: >= 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): >= 17.0 kJ/m²
- Vicat Softening Point: 105 °C @Load 5.10 kg
- Gloss: 98 %
$ 1688/MT
- Density: 1.048 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 3.144 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1809/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1624/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 50
- Tensile Strength, Yield: 17.2 MPa
$ 1493/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
$ 1982/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1661/MT
- Density: 1.08 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.16 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1613/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: 0.25 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 114 MPa
$ 1523/MT
- Density: 1.15 g/cc
- Water Absorption: 0.90 %
- Water Absorption: 0.30 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1857/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.01143 cm/cm
- Melt Flow: 6.0 g/10 min
- Tensile Strength at Break: 44.0 MPa
- Tensile Modulus: 2.48 GPa
$ 2042/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.30 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell M: 84
$ 2095/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.35 %
- Moisture Absorption at Equilibrium: 0.70 %
- Linear Mold Shrinkage: 0.01397 cm/cm
- Tensile Strength, Yield: 48.0 MPa
$ 1900/MT
- Density: 1.08 g/cc
- Melt Flow: >= 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 700 MPa
- Vicat Softening Point: 105 °C @Load 5.10 kg
$ 1801/MT
- Density: 1.09 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 2.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
$ 2153/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 2396/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 46.9 MPa
$ 1686/MT
- Density: 1.028 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 9.766 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 74.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 1826/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1533/MT
- Density: 1.03 g/cc
- Moisture Absorption at Equilibrium: 0.21 % @Temperature 23.0 °C
- Water Absorption at Saturation: 0.95 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 2307/MT
- Density: 1.048 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 3.144 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1683/MT
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 44.0 MPa
- Vicat Softening Point: 98.0 °C @Load 5.10 kg
- Gloss: 87 %
$ 1682/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
$ 1488/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 51.0 MPa
$ 2584/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 115 MPa
- Tensile Strength, Yield: 51.0 MPa
$ 1589/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 40.0 MPa
$ 1535/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 44.8 MPa
$ 1458/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 36.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1562/MT
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 8.0 g/10 min @Temperature 220 °C
- Tensile Strength, Yield: 42.0 MPa
$ 1713/MT
- Density: 1.36 g/cc
- Moisture Absorption at Equilibrium: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
- Melt Flow: 5.44 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 5.44 g/10 min @Load 21.6 kg, Temperature 200 °C
$ 2005/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
- Melt Flow: 20.52 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 29.16 g/10 min @Load 21.6 kg, Temperature 200 °C
$ 1950/MT
- Density: 1.02 g/cc
- Water Absorption: 0.070 %
- Moisture Absorption at Equilibrium: 0.070 %
- Linear Mold Shrinkage: 0.0065 cm/cm
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2413/MT
- Density: 1.08 g/cc
- Melt Flow: >= 45 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 700 MPa
- Vicat Softening Point: 104 °C @Load 5.10 kg
$ 2350/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1466/MT
- Density: 1.022 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 14.308 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 90.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 2194/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1895/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1930/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 2240/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1459/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1508/MT
- Density: 1.16 g/cc
- Water Absorption: 0.60 %
- Water Absorption: 0.20 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.16 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1746/MT
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 220 °C
- Izod Impact, Notched (ISO): 7.00 kJ/m²
- Vicat Softening Point: 103 °C @Load 5.10 kg
- Gloss: 98 %
$ 1610/MT
- Density: 1.01 g/cc
- Water Absorption: <= 0.070 %
- Moisture Absorption at Equilibrium: <= 0.070 %
- Melt Flow: 11.11 g/10 min
- Hardness, Shore D: 68
$ 1722/MT
- Density: 1.028 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 4.112 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 66.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 1869/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 9.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1673/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.35 %
- Moisture Absorption at Equilibrium: 0.70 %
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm
- Melt Flow: 8.64 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1692/MT
- Density: 1.08 g/cc
- Melt Flow: >= 11 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 800 MPa
- Vicat Softening Point: 107 °C @Load 5.10 kg
$ 2583/MT
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Vicat Softening Point: 106 °C @Load 5.10 kg
$ 2169/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 85.0 MPa
- Tensile Strength, Yield: 40.0 MPa
$ 1801/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.3 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 114 MPa @Load 36.5 kg, Time 30.0 sec
- Tensile Strength, Yield: 58.0 MPa
$ 1532/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Melt Flow: 5.35 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1549/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1483/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 1769/MT
- Water Absorption at Saturation: 0.070 % @Temperature 23.0 °C
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 97
- Hardness, Shore D: 58
- Tensile Strength, Yield: 15.0 MPa
$ 1810/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 3.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
- Tensile Strength, Yield: 41.0 MPa
$ 1979/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 2.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1483/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 90.0 MPa
- Tensile Strength, Yield: 42.0 MPa
$ 1979/MT
- Density: 1.048 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2034/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
- Ball Indentation Hardness: 100 MPa
$ 1459/MT
- Melt Flow: 13 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: >= 50 %
- Tensile Modulus: 1.60 GPa
- Charpy Impact, Notched: 8.00 J/cm²
$ 1649/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
- Melt Flow: 20.52 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 29.16 g/10 min @Load 21.6 kg, Temperature 200 °C
$ 1812/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
$ 2598/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Melt Flow: 44.8 g/10 min @Load 10.0 kg, Temperature 240 °C
- Hardness, Rockwell L: 78
$ 1928/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 95.0 MPa
$ 1572/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength at Break: 96.0 MPa @Temperature -40.0 °C
$ 1610/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 44
- Tensile Strength, Yield: 20.0 MPa
$ 1610/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Melt Flow: 42.8 g/10 min @Load 10.0 kg, Temperature 240 °C
- Hardness, Rockwell R: 103
$ 1628/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 240 °C
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Ultimate: 55.0 MPa
$ 2037/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 2.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 8.6 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2035/MT
- Density: 1.19 g/cc
- Water Absorption: 0.40 %
- Water Absorption: 0.40 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
$ 1605/MT
- Density: 1.05 g/cc
- Water Absorption at Saturation: 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 62
$ 2200/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Flow: 3.3 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2499/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 44.8 MPa
$ 2075/MT
- Density: 1.03 g/cc
- Water Absorption: 1.03 %
- Moisture Absorption at Equilibrium: 0.21 %
- Melt Flow: 5.665 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 74.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 1514/MT
- Density: 1.043 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 10.43 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1478/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 95.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1612/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0060 cm/cm
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114.5
- Tensile Strength, Yield: 48.0 MPa
$ 1466/MT
- Density: 1.07 g/cc
- Water Absorption: 1.65 %
- Water Absorption: 0.45 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.35 %
- Melt Flow: 12.84 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1685/MT
- Density: 1.02 g/cc
- Water Absorption: <= 0.070 %
- Moisture Absorption at Equilibrium: <= 0.070 %
- Melt Flow: 16.32 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore D: 72
$ 1457/MT
- Density: 1.02 g/cc
- Moisture Absorption at Equilibrium: 0.21 % @Temperature 23.0 °C
- Water Absorption at Saturation: 1.03 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1533/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 2.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell L: 45
- Tensile Strength, Yield: 17.7 MPa
$ 1500/MT
- Density: 1.04 g/cc
- Water Absorption: 0.95 %
- Moisture Absorption at Equilibrium: 0.24 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 3.1 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1666/MT
- Density: 1.05 g/cc
- Melt Flow: 15.75 g/10 min
- Tensile Strength at Break: 44.0 MPa
- Tensile Modulus: 3.30 GPa
- Flexural Strength: 70.0 MPa
$ 2130/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 75
- Tensile Strength, Yield: 41.4 MPa
$ 1905/MT
- Density: 1.08 g/cc
- Melt Flow: >= 45 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 690 MPa
- Vicat Softening Point: 103 °C @Load 5.10 kg
$ 1767/MT
- Density: 1.048 g/cc
- Water Absorption: <= 0.10 %
- Moisture Absorption at Equilibrium: <= 0.10 %
- Melt Flow: 1.572 g/10 min @Load 5.00 kg, Temperature 200 °C
- Ball Indentation Hardness: 150 MPa @Load 36.5 kg, Time 30.0 sec
$ 1988/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 31 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 46.0 MPa
$ 1460/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 13 g/10 min @Load 5.00 kg, Temperature 260 °C
- Ball Indentation Hardness: 85.0 MPa
$ 1990/MT
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: <= 0.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: <= 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Melt Flow: 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1876/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 58.0 MPa
$ 1922/MT
- Melt Flow: 27 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.0 MPa
- Vicat Softening Point: 99.0 °C @Load 5.10 kg
- Gloss: 90 %
$ 2270/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.3 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 114 MPa @Load 36.5 kg, Time 30.0 sec
- Tensile Strength, Yield: 58.0 MPa
$ 1874/MT
- Density: 1.02 g/cc
- Water Absorption: 0.070 %
- Linear Mold Shrinkage, Flow: 0.01651 cm/cm
- Melt Flow: 11 g/10 min
- Hardness, Shore D: 75
$ 1465/MT
- Density: 1.04 g/cc
- Water Absorption at Saturation: 0.10 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 84
$ 1987/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 1.6 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell M: 78
- Tensile Strength, Yield: 52.4 MPa
$ 1445/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Ball Indentation Hardness: 105 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 1705/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 0.35 % @Temperature 23.0 °C
- Water Absorption at Saturation: 1.65 % @Temperature 23.0 °C
- Linear Mold Shrinkage: 0.0050 - 0.0090 cm/cm
- Melt Flow: 17 g/10 min @Load 10.0 kg, Temperature 220 °C
Delivery Polymer Styrolution
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale france. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.