$ 1603/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: 5.52 MPa
- Elongation at Break: 225 %
- Tear Strength: 15.8 kN/m
$ 2215/MT
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 140 microns
- Thickness: 267 microns
- Hardness, Shore A: 45
$ 2001/MT
- Density: 1.60 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 88
$ 1777/MT
- Specific Gravity: 1.24 g/cc
- Thickness: 19.0 microns
- Thickness: 19.0 microns
- Thickness: 203 microns
- Thickness: 267 microns
$ 1555/MT
- Density: 1.18 g/cc
- Thickness: 127 microns
- Thickness: 1570 microns
- Hardness, Shore A: 50
- Tensile Strength: 7.58 MPa
$ 2522/MT
- Density: 1.43 g/cc
- Hardness, Shore A: 75 - 85
- Tensile Strength: >= 6.21 MPa
- Elongation at Break: >= 150 %
- Maximum Service Temperature, Air: 232 °C
$ 2104/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.40 %
- Thickness: 508 microns
- Hardness, Shore A: 50
- Tensile Strength, Ultimate: 6.89 MPa
$ 2064/MT
- Density: 1.27 g/cc
- Thickness: 50.8 microns
- Thickness: 1270 microns
- Hardness, Shore A: 52
- Tensile Strength: 7.557 MPa
$ 1787/MT
- Density: 1.22 g/cc
- Thickness: 88.9 microns
- Thickness: 88.9 microns
- Thickness: 203 microns
- Thickness: 381 microns
$ 1907/MT
- Density: 1.15 g/cc
- Water Absorption: 2.0 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1708/MT
- Thickness: 76.2 microns
- Thickness: 140 - 216 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
- Hardness, Shore A: >= 40
$ 1715/MT
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
- Tensile Strength: >= 5.52 MPa
$ 1989/MT
- Thickness: 12.7 microns
- Thickness: 50.8 microns
- Thickness: 127 microns
- Thickness: >= 203 microns
- Thickness: 457 microns
$ 1509/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
$ 1519/MT
- Thickness: 127 microns
- Thickness: 381 microns
- Hardness, Shore A: 45
- Tensile Strength: 6.21 MPa
- Elongation at Break: 600 %
$ 1868/MT
- Thickness: 76.2 microns
- Thickness: 127 - 152 microns
- Thickness: 127 - 152 microns
- Thickness: 203 microns
- Thickness: 457 - 559 microns
$ 1512/MT
- Thickness: 76.2 microns
- Thickness: 127 - 178 microns
- Thickness: 127 - 178 microns
- Thickness: 356 microns
- Thickness: 584 - 686 microns
$ 2242/MT
- Thickness: 127 microns
- Thickness: 381 microns
- Hardness, Shore A: 45
- Tensile Strength: 6.21 MPa
- Elongation at Break: 600 %
$ 1552/MT
- Density: 1.26 g/cc
- Hardness, Shore A: 40 - 50
- Tensile Strength: >= 5.52 MPa
- Elongation at Break: >= 500 %
- Maximum Service Temperature, Air: 232 °C
$ 1861/MT
- Thickness: 38.1 microns
- Thickness: 127 microns
- Thickness: 457 - 559 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 40 - 50
$ 1600/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 229 microns
- Thickness: 508 microns
$ 1969/MT
- Density: 1.80 g/cc
- Water Absorption: 0.090 %
- Thickness: 99.1 microns
- Thickness: 147 microns
- Thickness: 170 microns
$ 1914/MT
- Density: 1.26 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
$ 1903/MT
- Thickness: 76.2 microns
- Thickness: 178 - 330 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 1803/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 2870 - 3480 microns
- Thickness: 2870 - 3480 microns
- Hardness, Shore A: 50 - 60
$ 1787/MT
- Thickness: 76.2 microns
- Thickness: 940 - 1090 microns
- Thickness: 17460 - 20640 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 1501/MT
- Density: 1.62 g/cc
- Thickness: 76.2 microns
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
$ 1797/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: >= 5.50 MPa
- Elongation at Yield: >= 500 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1547/MT
- Density: 1.17 g/cc
- Water Absorption: 2.8 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1939/MT
- Density: 1.26 g/cc
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 356 microns
$ 1796/MT
- Density: 2.30 g/cc
- Water Absorption: 0.040 %
- Tensile Strength: >= 138 MPa
- Modulus of Elasticity: >= 4.83 GPa
- Flexural Modulus: >= 3.72 GPa
$ 2081/MT
- Density: 3.70 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 70
$ 1795/MT
- Density: 1.20 g/cc
- Density: 1.70 g/cc
- Thickness: 50.8 microns
- Thickness: 203 microns
- Thickness: 254 microns
$ 1881/MT
- Density: 1.20 g/cc
- Water Absorption: 2.5 %
- Thickness: 76.2 microns
- Thickness: 254 microns
- Hardness, Shore A: 55
$ 1548/MT
- Density: 3.70 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 84
$ 1493/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1618/MT
- Density: 1.35 g/cc
- Thickness: 88.9 microns
- Thickness: 178 microns
- Thickness: 483 microns
- Thickness: 749 microns
$ 2069/MT
- Shear Modulus: 0.000350 - 0.000450 GPa
- Adhesive Bond Strength: >= 1.40 MPa
- Thermal Conductivity: >= 1.20 W/m-K
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -56.6 °C
$ 1736/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 102 microns
- Thickness: 165 microns
- Thickness: 483 microns
- Thickness: 749 microns
$ 1733/MT
- Thickness: >= 25.4 microns
- Thickness: 38.1 microns
- Thickness: >= 50.8 microns
- Thickness: 63.5 microns
- Thickness: 127 - 165 microns
$ 1706/MT
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 381 microns
- Thickness: 635 microns
- Hardness, Shore A: 50
$ 1520/MT
- Thickness: 38.1 microns
- Thickness: >= 127 microns
- Thickness: 127 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
$ 1592/MT
- Thickness: 76.2 microns
- Thickness: 356 microns
- Thickness: >= 508 microns
- Thickness: >= 660 microns
- Thickness: 1370 - 1680 microns
$ 1641/MT
- Thickness: 76.2 microns
- Thickness: 940 - 1090 microns
- Thickness: 17460 - 20640 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 1818/MT
- Density: 1.275 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 203 microns
- Thickness: 279 microns
$ 2221/MT
- Density: 1.20 g/cc
- Density: 1.35 g/cc
- Thickness: 50.8 microns
- Thickness: 178 microns
- Thickness: 406 microns
$ 1494/MT
- Density: 2.50 g/cc
- Water Absorption: 0.060 %
- Thickness: 3.05 microns
- Peel Strength: 2.10 kN/m
- CTE, linear: 10.0 µm/m-°C
$ 1534/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 711 - 813 microns
- Thickness: 23810 - 26990 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 2100/MT
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 381 microns
- Shear Strength: >= 1.38 MPa
- Thermal Conductivity: >= 0.450 W/m-K
$ 1968/MT
- Density: 1.26 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
$ 2466/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 686 - 838 microns
- Thickness: 686 - 838 microns
- Hardness, Shore A: 40 - 50
$ 1474/MT
- Thickness: 38.1 microns
- Thickness: >= 50.8 microns
- Thickness: >= 50.8 microns
- Thickness: 127 microns
- Thickness: 254 - 305 microns
$ 1775/MT
- Density: 1.16 g/cc
- Thickness: 762 microns
- Hardness, Shore A: 55
- Tensile Strength: 9.467 MPa
- Elongation at Break: 481 %
$ 2155/MT
- Thickness: 127 microns
- Thickness: 1520 microns
- Hardness, Shore A: 55
- Tensile Strength: 6.21 - 7.58 MPa
- Elongation at Break: 450 - 550 %
$ 2068/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 457 - 559 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 2339/MT
- Density: 1.18 g/cc
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 508 microns
- Thickness: 508 microns
$ 1814/MT
- Thickness: 102 microns
- Thickness: 178 microns
- Thickness: 356 microns
- Thickness: 635 microns
- Hardness, Shore A: 60
$ 1540/MT
- Density: 1.17 g/cc
- Thickness: 19.0 microns
- Thickness: 19.0 microns
- Thickness: 38.1 microns
- Thickness: 152 microns
$ 2055/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 343 - 419 microns
- Thickness: 343 - 419 microns
- Hardness, Shore A: 55 - 65
$ 2297/MT
- Thickness: 76.2 microns
- Thickness: 191 microns
- Thickness: 254 - 292 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 35 - 45
$ 1756/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 229 microns
- Thickness: 508 microns
$ 2201/MT
- Thickness: 38.1 microns
- Thickness: 102 - 152 microns
- Thickness: 102 - 152 microns
- Thickness: 203 microns
- Thickness: 406 - 508 microns
$ 1996/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: 5.52 MPa
- Elongation at Break: 225 %
- Tear Strength: 15.8 kN/m
$ 1553/MT
- Specific Gravity: 1.10 g/cc
- Specific Gravity: 1.70 g/cc
- Thickness: 50.8 microns
- Thickness: 203 microns
- Thickness: 254 microns
$ 2337/MT
- Density: 1.60 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 83
$ 1913/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 36
- Tensile Strength: 6.38 MPa
- Elongation at Break: 550 %
- Tear Strength: 14.5 kN/m
$ 1490/MT
- Density: 1.20 g/cc
- Water Absorption: 1.1 %
- Thickness: 63.5 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1633/MT
- Density: 1.85 g/cc
- Water Absorption: 0.10 %
- Modulus of Elasticity: 19.3 GPa
- Poissons Ratio: 0.20
- Peel Strength: 1.40 kN/m
$ 1866/MT
- Thickness: >= 50.8 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: >= 254 microns
- Thickness: 343 - 419 microns
$ 2124/MT
- Density: 1.30 g/cc
- Thickness: 50.8 microns
- Thickness: 88.9 microns
- Thickness: 140 microns
- Hardness, Shore A: 60
$ 1676/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1020 microns
- Thickness: 1020 microns
$ 1449/MT
- Density: 1.81 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1520 microns
- Thickness: 1520 microns
$ 1711/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 254 microns
- Thickness: 292 microns
- Thickness: 292 microns
$ 1571/MT
- Density: 1.80 g/cc
- Thickness: 38.1 microns
- Thickness: 203 microns
- Thickness: 318 microns
- Thickness: 521 microns
$ 2023/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 368 microns
- Thickness: 508 microns
$ 2314/MT
- Thickness: 76.2 microns
- Thickness: >= 102 microns
- Thickness: 203 microns
- Thickness: >= 635 microns
- Thickness: 965 - 1070 microns
$ 1847/MT
- Density: 1.593 g/cc
- Hardness, Shore A: 55 - 65
- Tensile Strength: >= 3.10 MPa
- Elongation at Break: >= 275 %
- Maximum Service Temperature, Air: 232 °C
$ 1669/MT
- Density: 1.22 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
$ 1521/MT
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 203 microns
- Thickness: >= 203 microns
- Thickness: 457 - 559 microns
$ 1518/MT
- Thickness: 76.2 microns
- Thickness: 330 - 432 microns
- Thickness: 330 - 432 microns
- Hardness, Shore A: 40 - 50
- Tensile Strength: >= 5.52 MPa
$ 1465/MT
- Density: 1.20 g/cc
- Water Absorption: 2.7 %
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 55
$ 1492/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 1520/MT
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 203 - 229 microns
- Thickness: 457 - 559 microns
$ 2049/MT
- Thickness: 76.2 microns
- Thickness: 356 microns
- Thickness: >= 584 microns
- Thickness: 660 microns
- Thickness: 1470 - 1730 microns
$ 2030/MT
- Density: 1.20 g/cc
- Water Absorption: 3.0 %
- Thickness: 76.2 microns
- Thickness: 305 microns
- Hardness, Shore A: 55
$ 1909/MT
- Hardness, Shore A: 50 - 60
- Tensile Strength, Ultimate: 7.47 - 9.13 MPa
- Elongation at Break: 540 - 660 %
- 100% Modulus: 0.00172 GPa
- Tear Strength: >= 43.8 kN/m
$ 2035/MT
- Density: 1.40 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 63.5 microns
- Thickness: 63.5 microns
$ 1575/MT
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 305 microns
- Thickness: 305 microns
- Thickness: 711 - 864 microns
$ 1595/MT
- Density: 1.36 g/cc
- Thickness: 76.2 microns
- Thickness: 1570 microns
- Hardness, Shore A: 45
- Tensile Strength: 5.52 MPa
$ 1819/MT
- Density: 2.10 g/cc
- Water Absorption: 0.060 %
- Peel Strength: 2.98 kN/m
- CTE, linear: 9.00 µm/m-°C
- CTE, linear: 9.00 µm/m-°C
$ 1481/MT
- Density: 1.15 g/cc
- Thickness: 76.2 microns
- Thickness: 1270 microns
- Hardness, Shore A: 55
- Tensile Strength: 7.93 MPa
$ 1477/MT
- Density: 1.35 g/cc
- Thickness: 203 microns
- Thickness: 241 microns
- Thickness: 241 microns
- Thickness: 686 microns
$ 1563/MT
- Thickness: >= 25.4 microns
- Thickness: 38.1 microns
- Thickness: >= 50.8 microns
- Thickness: 63.5 microns
- Thickness: 127 - 165 microns
$ 1931/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 76.2 microns
- Thickness: 457 - 559 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
$ 1567/MT
- Thickness: >= 25.4 microns
- Thickness: 38.1 microns
- Thickness: >= 50.8 microns
- Thickness: 63.5 microns
- Thickness: 127 - 165 microns
$ 1674/MT
- Thickness: 25.4 microns
- Thickness: 38.1 microns
- Thickness: >= 102 microns
- Thickness: 178 microns
- Hardness, Shore A: 40 - 50
$ 1951/MT
- Density: 1.20 g/cc
- Water Absorption: 1.0 %
- Thickness: 508 microns
- Hardness, Shore A: 55
- Tensile Strength: 7.674 MPa
$ 1656/MT
- Density: 1.27 g/cc
- Thickness: 406 microns
- Thickness: 584 microns
- Thickness: 584 microns
- Thickness: 1570 microns
$ 1769/MT
- Density: 1.32 g/cc
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 483 microns
$ 1993/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 1626/MT
- Density: 1.60 g/cc
- Thickness: 127 microns
- Thickness: 1980 microns
- Hardness, Shore A: 72
- Tensile Strength: 4.83 MPa
$ 1964/MT
- Density: 1.35 g/cc
- Thickness: 203 microns
- Thickness: 229 microns
- Thickness: 508 microns
- Thickness: 940 microns
$ 1818/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 178 microns
- Thickness: 203 microns
- Thickness: 381 microns
$ 1520/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 343 - 419 microns
$ 1485/MT
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 203 microns
- Thickness: 381 microns
- Thickness: 610 - 660 microns
$ 1868/MT
- Density: 2.10 g/cc
- Water Absorption: 0.10 %
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.020 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.020 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1481/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: >= 152 microns
- Thickness: 457 microns
- Thickness: 699 - 775 microns
$ 2166/MT
- Thickness: 76.2 microns
- Thickness: 686 - 838 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 1960/MT
- Specific Gravity: 1.44 g/cc
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
- Thickness: 711 microns
$ 1757/MT
- Thickness: 267 microns
- Thickness: 381 microns
- Thickness: 635 microns
- Hardness, Shore A: 50
- Tensile Strength: >= 5.52 MPa
$ 1490/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 343 - 419 microns
$ 2411/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 343 - 419 microns
$ 1539/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 343 - 419 microns
$ 1694/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 343 - 419 microns
$ 1873/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 343 - 419 microns
$ 1766/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 343 - 419 microns
$ 1831/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 343 - 419 microns
$ 1540/MT
- Thickness: >= 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: >= 229 microns
- Thickness: 457 - 559 microns
$ 1907/MT
- Density: 1.32 g/cc
- Thickness: 63.5 microns
- Thickness: 165 microns
- Thickness: 191 microns
- Thickness: 406 microns
$ 2065/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
$ 1583/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1420 - 1730 microns
- Thickness: 1420 - 1730 microns
- Hardness, Shore A: 67
$ 1636/MT
- Density: 1.70 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Outgassing - Total Mass Loss: 0.30 %
$ 2185/MT
- Density: 1.47 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Hardness, Shore A: 66
$ 1546/MT
- Density: 1.17 g/cc
- Water Absorption: 1.6 %
- Thickness: 76.2 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
$ 1979/MT
- Thickness: 38.1 microns
- Thickness: 127 microns
- Thickness: 229 - 279 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
$ 1645/MT
- Density: 2.31 g/cc
- Water Absorption: 0.030 %
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1709/MT
- Thickness: 76.2 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 35 - 45
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
$ 2527/MT
- Density: 1.24 g/cc
- Thickness: 19.0 microns
- Thickness: 19.0 microns
- Thickness: 38.1 microns
- Thickness: 203 microns
$ 1862/MT
- Density: 1.20 g/cc
- Thickness: 74.9 microns
- Thickness: 330 microns
- Thickness: 330 microns
- Thickness: 478 microns
$ 1984/MT
- Thickness: 127 microns
- Thickness: 508 microns
- Hardness, Shore A: 45
- Tensile Strength: >= 5.52 MPa
- Elongation at Break: >= 500 %
$ 1548/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 203 microns
- Thickness: 406 microns
$ 1798/MT
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 50
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 250 %
$ 2464/MT
- Density: 1.20 g/cc
- Thickness: 203 microns
- Thickness: 508 microns
- Hardness, Shore A: 52
- Tensile Strength: 8.839 MPa
$ 1499/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 55 - 65
- Tensile Strength: >= 6.21 MPa
- Elongation at Break: >= 200 %
- Maximum Service Temperature, Air: 232 °C
$ 1995/MT
- Density: 1.30 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
$ 2094/MT
- Density: 2.40 g/cc
- Water Absorption: 0.070 %
- Peel Strength: 2.45 kN/m
- CTE, linear: 12.0 µm/m-°C
- CTE, linear: 15.0 µm/m-°C
$ 1595/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 76.2 microns
- Thickness: 457 - 559 microns
- Thickness: 17460 - 20640 microns
- Tensile Strength: >= 4.83 MPa
$ 1845/MT
- Density: 1.34 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 203 microns
- Thickness: 381 microns
$ 1873/MT
- Density: 1.375 g/cc
- Thickness: 63.5 microns
- Thickness: 152 microns
- Thickness: 356 microns
- Thickness: 508 microns
$ 1626/MT
- Specific Gravity: 1.33 g/cc
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
- Thickness: 711 microns
$ 1943/MT
- Density: 1.35 g/cc
- Thickness: 102 microns
- Thickness: 165 microns
- Thickness: 483 microns
- Thickness: 749 microns
$ 1485/MT
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 305 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 53 - 63
$ 1959/MT
- Hardness, Shore A: >= 60
- Tensile Strength, Ultimate: 4.68 - 5.72 MPa
- Elongation at Break: 250 - 300 %
- Shear Modulus: <= 0.000700 GPa
- Adhesive Bond Strength: >= 2.80 MPa
$ 2168/MT
- Thickness: 76.2 microns
- Thickness: 229 - 279 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 50 - 60
- Tensile Strength: 7.45 - 9.10 MPa
$ 1504/MT
- Density: 1.20 g/cc
- Water Absorption: 0.20 %
- Thickness: 508 microns
- Hardness, Shore A: 49
- Tensile Strength: 8.129 MPa
$ 1461/MT
- Density: 1.85 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 87
$ 1962/MT
- Density: 1.15 g/cc
- Water Absorption: 2.9 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1825/MT
- Thickness: 50.8 microns
- Thickness: 203 microns
- Thickness: 254 microns
- Thickness: 508 microns
- Hardness, Shore A: 58
$ 1805/MT
- Density: 2.10 g/cc
- Water Absorption: 0.020 %
- Peel Strength: 2.28 kN/m
- CTE, linear: 12.0 µm/m-°C
- CTE, linear: 12.0 µm/m-°C
$ 2134/MT
- Density: 1.50 g/cc
- Water Absorption: 0.80 %
- Modulus of Elasticity: 27.6 GPa
- Poissons Ratio: 0.20
- Peel Strength: 1.05 kN/m
$ 1793/MT
- Density: 1.35 g/cc
- Thickness: 50.8 microns
- Thickness: 127 microns
- Thickness: 203 microns
- Thickness: 381 microns
$ 1991/MT
- Density: 1.17 g/cc
- Water Absorption: 2.0 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1786/MT
- Thickness: >= 50.8 microns
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1573/MT
- Density: 3.70 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 102 microns
- Hardness, Shore A: 70
$ 1480/MT
- Specific Gravity: 1.38 g/cc
- Thickness: 102 microns
- Thickness: 165 microns
- Thickness: 483 microns
- Thickness: 749 microns
$ 1831/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 254 microns
- Thickness: 483 microns
- Thickness: 838 microns
- Thickness: 1570 microns
$ 1650/MT
- Thickness: 203 microns
- Thickness: 305 microns
- Thickness: 508 microns
- Hardness, Shore A: 58
- Tensile Strength: 6.21 MPa
$ 1516/MT
- Density: 1.17 g/cc
- Water Absorption: 2.8 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 2150/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 203 microns
- Thickness: >= 330 microns
- Thickness: 622 - 749 microns
$ 1762/MT
- Thickness: >= 76.2 microns
- Thickness: >= 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1530/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 305 microns
- Thickness: 457 microns
- Thickness: 762 microns
$ 1925/MT
- Density: 1.20 g/cc
- Water Absorption: 1.1 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1470/MT
- Thickness: >= 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: >= 610 microns
- Thickness: 838 - 940 microns
$ 2089/MT
- Density: 1.18 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 406 microns
- Thickness: 508 microns
$ 2597/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 203 microns
- Thickness: 419 microns
$ 1910/MT
- Density: 1.20 g/cc
- Thickness: 203 microns
- Thickness: 508 microns
- Hardness, Shore A: 52
- Tensile Strength: 8.839 MPa
$ 1464/MT
- Thickness: >= 25.4 microns
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 457 microns
- Thickness: 813 - 914 microns
$ 2024/MT
- Density: 1.75 g/cc
- Water Absorption: 0.10 %
- Modulus of Elasticity: 17.9 GPa
- Poissons Ratio: 0.17
- Peel Strength: 1.58 kN/m
$ 1859/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 38.1 microns
- Thickness: 63.5 microns
- Thickness: 76.2 microns
$ 2213/MT
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 63.5 microns
- Thickness: 152 microns
- Thickness: 279 microns
$ 1476/MT
- Density: 1.17 g/cc
- Density: 1.23 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 203 microns
$ 2586/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 457 - 559 microns
- Thickness: 23810 - 26990 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 1921/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 203 microns
$ 1882/MT
- Density: 1.24 g/cc
- Thickness: 102 microns
- Thickness: 203 microns
- Thickness: 406 microns
- Thickness: 711 microns
$ 1803/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 40 - 50
- Tensile Strength: >= 5.52 MPa
- Elongation at Break: >= 500 %
- Maximum Service Temperature, Air: 232 °C
$ 2099/MT
- Density: 1.25 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1880 microns
- Thickness: 2010 microns
$ 1630/MT
- Density: 1.85 g/cc
- Water Absorption: 0.10 %
- Modulus of Elasticity: 19.3 GPa
- Poissons Ratio: 0.15
- Peel Strength: 1.40 kN/m
$ 1545/MT
- Density: 1.17 g/cc
- Water Absorption: 1.3 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1660/MT
- Hardness, Shore A: >= 50
- Tensile Strength, Ultimate: 4.68 - 5.72 MPa
- Elongation at Break: 250 - 300 %
- Shear Modulus: <= 0.000700 GPa
- Adhesive Bond Strength: >= 2.80 MPa
$ 1976/MT
- Thickness: 12.7 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: >= 203 microns
- Thickness: 457 microns
$ 1495/MT
- Density: 1.28 g/cc
- Hardness, Shore A: 53
- Tensile Strength: 5.52 MPa
- Elongation at Break: 230 %
- Tear Strength: 8.41 kN/m
$ 1632/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 203 microns
- Thickness: 419 microns
$ 1735/MT
- Thickness: >= 76.2 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: >= 165 microns
- Thickness: 343 - 419 microns
$ 2371/MT
- Thickness: 457 microns
- Thickness: 457 microns
- Thickness: 813 microns
- Thickness: 1600 - 1850 microns
- Hardness, Shore A: 45 - 55
$ 1448/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: >= 127 microns
- Thickness: 127 microns
- Thickness: 343 - 419 microns
$ 2060/MT
- Thickness: >= 76.2 microns
- Thickness: >= 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 318 - 394 microns
$ 1746/MT
- Thickness: 76.2 microns
- Thickness: 63.5 - 114 microns
- Thickness: 63.5 - 114 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1665/MT
- Density: 1.35 g/cc
- Thickness: 127 microns
- Thickness: 483 microns
- Thickness: 610 microns
- Hardness, Shore A: 60
$ 1943/MT
- Thickness: 38.1 microns
- Thickness: 127 microns
- Thickness: 127 - 203 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 55 - 65
$ 1513/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 178 microns
- Thickness: 381 microns
- Thickness: 381 microns
$ 1510/MT
- Hardness, Shore A: 45 - 55
- Tensile Strength, Ultimate: 7.61 - 8.99 MPa
- Elongation at Break: 300 - 500 %
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -97.8 °C
- Dielectric Strength: >= 15.75 kV/mm
$ 1858/MT
- Thickness: 76.2 microns
- Thickness: 432 - 584 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 2426/MT
- Thickness: 76.2 microns
- Thickness: 432 - 584 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 1834/MT
- Density: 2.23 g/cc
- Water Absorption: 0.040 %
- Outgassing - Total Mass Loss: 0.00 %
- Outgassing - Total Mass Loss: 0.020 %
- Peel Strength: 1.75 kN/m
$ 1638/MT
- Thickness: 76.2 microns
- Thickness: 432 - 584 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 1464/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 584 - 686 microns
- Thickness: 584 - 686 microns
- Hardness, Shore A: 55 - 65
$ 1619/MT
- Density: 1.10 g/cc
- Thickness: 38.1 microns
- Thickness: 127 microns
- Thickness: 762 microns
- Hardness, Shore A: 20
$ 1709/MT
- Density: 1.35 g/cc
- Thickness: 88.9 microns
- Thickness: 88.9 microns
- Thickness: 203 microns
- Thickness: 381 microns
$ 1595/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: >= 5.50 MPa
- Elongation at Break: >= 500 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1914/MT
- Thickness: >= 50.8 microns
- Thickness: 76.2 microns
- Thickness: >= 114 microns
- Thickness: >= 114 microns
- Thickness: 127 microns
$ 1607/MT
- Density: 1.30 g/cc
- Thickness: 76.2 microns
- Thickness: 254 microns
- Hardness, Shore A: 52
- Tensile Strength: 6.37 MPa
$ 2306/MT
- Thickness: >= 76.2 microns
- Thickness: 127 - 152 microns
- Thickness: 127 - 152 microns
- Thickness: >= 203 microns
- Thickness: 457 - 559 microns
$ 1464/MT
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 102 microns
- Thickness: 165 microns
- Thickness: 483 microns
$ 1882/MT
- Thickness: 203 microns
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -56.7 °C
- Shelf Life: 60.0 Month @Temperature 23.9 °C
- Color: Red
$ 1912/MT
- Density: 2.40 g/cc
- Water Absorption: 0.070 %
- Peel Strength: 2.45 kN/m
- CTE, linear: 12.0 µm/m-°C
- CTE, linear: 15.0 µm/m-°C
$ 1908/MT
- Density: 1.16 g/cc
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 53
- Tensile Strength: 9.31 MPa
$ 1457/MT
- Thickness: 50.8 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: >= 203 microns
- Thickness: 457 microns
$ 1536/MT
- Density: 1.24 g/cc
- Thickness: 254 microns
- Thickness: 457 microns
- Thickness: 711 microns
- Hardness, Shore A: 44
$ 1960/MT
- Density: 1.20 g/cc
- Water Absorption: 0.10 %
- Thickness: 305 microns
- Hardness, Shore A: 46
- Tensile Strength: 8.839 MPa
$ 1615/MT
- Thickness: 50.8 microns
- Thickness: 140 microns
- Thickness: 191 microns
- Hardness, Shore A: 60
- Tensile Strength: 4.48 MPa
$ 2034/MT
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 88.9 microns
- Thickness: 191 - 292 microns
$ 1832/MT
- Thickness: 76.2 microns
- Thickness: 63.5 - 140 microns
- Thickness: 140 - 216 microns
- Thickness: 356 microns
- Thickness: 597 - 673 microns
$ 1677/MT
- Density: 1.47 g/cc
- Thickness: 38.1 microns
- Thickness: 63.5 microns
- Thickness: 140 microns
- Thickness: 203 microns
$ 2131/MT
- Density: 1.60 g/cc
- Water Absorption: 0.21 %
- Modulus of Elasticity: 22.1 GPa
- Poissons Ratio: 0.15
- Peel Strength: 1.26 kN/m
$ 1766/MT
- Thickness: 76.2 microns
- Thickness: 356 microns
- Thickness: >= 584 microns
- Thickness: 660 microns
- Thickness: 1470 - 1730 microns
$ 1795/MT
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 2030 microns
- Thickness: 2130 microns
- Peel Strength: >= 0.175 kN/m
$ 1671/MT
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 457 - 559 microns
- Thickness: 457 - 559 microns
- Maximum Service Temperature, Air: 232 °C
$ 1478/MT
- Density: 1.75 g/cc
- Water Absorption: 0.10 %
- Modulus of Elasticity: 17.9 GPa
- Flexural Strength: 579 MPa
- Poissons Ratio: 0.17
$ 1775/MT
- Density: 2.10 g/cc
- Water Absorption: 0.0050 %
- Thickness: 0.0381 microns
- Thickness: 0.0762 microns
- Thermal Conductivity: 0.170 W/m-K
$ 1774/MT
- Density: 1.32 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 203 microns
$ 1670/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 152 microns
- Thickness: 368 - 445 microns
$ 2153/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 50
- Tensile Strength: 6.21 MPa
- Elongation at Break: 500 %
- Tear Strength: 14.0 kN/m
$ 1463/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 88.9 microns
- Thickness: 178 microns
$ 1734/MT
- Density: 1.24 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 216 microns
- Thickness: 406 microns
$ 1612/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: >= 5.50 MPa
- Elongation at Yield: >= 500 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1476/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 203 microns
- Thickness: 254 microns
$ 1871/MT
- Thickness: 76.2 microns
- Thickness: >= 88.9 microns
- Thickness: >= 88.9 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1681/MT
- Density: 1.81 g/cc
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 102 microns
- Thickness: 102 microns
$ 2307/MT
- Density: 2.80 g/cc
- Hardness, Shore A: 77
- Tensile Strength: 4.72 MPa
- Tensile Strength, Yield: 24.5 MPa @Strain <=1.00 %
- Elongation at Break: 125 %
$ 2097/MT
- Thickness: 76.2 microns
- Thickness: >= 88.9 microns
- Thickness: >= 88.9 microns
- Thickness: 203 microns
- Thickness: 330 - 432 microns
$ 2092/MT
- Thickness: 76.2 microns
- Thickness: 76.2 - 102 microns
- Thickness: 76.2 - 102 microns
- Thickness: 102 microns
- Thickness: 279 - 330 microns
$ 2423/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 88.9 microns
$ 1775/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 88.9 microns
- Thickness: 88.9 microns
- Thickness: 254 microns
$ 1596/MT
- Thickness: >= 38.1 microns
- Thickness: >= 38.1 microns
- Thickness: >= 203 microns
- Thickness: 254 - 305 microns
- Hardness, Shore A: 60 - 70
$ 1573/MT
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: >= 152 microns
- Thickness: 457 microns
- Thickness: 686 - 787 microns
$ 1823/MT
- Density: 1.24 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 178 microns
- Thickness: 381 microns
$ 1847/MT
- Thickness: 25.4 microns
- Thickness: >= 25.4 microns
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 63.5 microns
$ 1465/MT
- Thickness: 127 microns
- Thickness: 3180 microns
- Hardness, Shore A: 40
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
$ 2233/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 203 microns
- Thickness: 406 microns
$ 2426/MT
- Density: 1.34 g/cc
- Thickness: 127 microns
- Thickness: 381 microns
- Thickness: 508 microns
- Hardness, Shore A: 37
$ 1503/MT
- Density: 1.38 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 152 microns
- Thickness: 457 microns
$ 2076/MT
- Thickness: 432 - 584 microns
- Thickness: 23810 - 26990 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
- Maximum Service Temperature, Air: 204 °C
$ 1472/MT
- Thickness: 38.1 microns
- Thickness: >= 50.8 microns
- Thickness: 203 microns
- Thickness: >= 254 microns
- Thickness: 457 - 559 microns
$ 1516/MT
- Density: 1.06 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 254 microns
- Thickness: 254 microns
$ 2104/MT
- Density: 1.17 g/cc
- Thickness: 254 microns
- Hardness, Shore A: 56
- Tensile Strength: 8.260 MPa
- Tensile Strength: 8.69 MPa
$ 1616/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 508 - 610 microns
- Thickness: 508 - 610 microns
- Hardness, Shore A: 40 - 50
$ 2064/MT
- Density: 1.15 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 203 microns
- Thickness: 203 microns
$ 1912/MT
- Density: 1.24 g/cc
- Thickness: 305 microns
- Thickness: 406 microns
- Thickness: 711 microns
- Hardness, Shore A: 44
$ 2010/MT
- Density: 2.80 g/cc
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
$ 1767/MT
- Hardness, Shore A: 50 - 60
- Tensile Strength, Ultimate: 7.47 - 9.13 MPa
- Elongation at Break: 540 - 660 %
- 100% Modulus: 0.00172 GPa
- Tear Strength: >= 43.8 kN/m
$ 1804/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1834/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 381 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 55 - 65
$ 1496/MT
- Density: 1.20 g/cc
- Density: 1.70 g/cc
- Thickness: 50.8 microns
- Thickness: 203 microns
- Thickness: 254 microns
$ 1781/MT
- Thickness: 76.2 microns
- Thickness: >= 165 microns
- Thickness: >= 165 microns
- Thickness: 457 microns
- Thickness: 686 - 838 microns
$ 1498/MT
- Thickness: 76.2 microns
- Thickness: 432 - 584 microns
- Thickness: 36510 - 39690 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 1766/MT
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 254 microns
- Hardness, Shore A: 58
$ 1470/MT
- Thickness: 76.2 microns
- Thickness: 432 - 584 microns
- Thickness: 17460 - 20640 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 1728/MT
- Density: 1.40 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
$ 1598/MT
- Density: 1.21 g/cc
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 88.9 microns
- Thickness: 191 microns
$ 1445/MT
- Density: 1.25 g/cc
- Thickness: 25.4 microns
- Thickness: 38.1 microns
- Thickness: 63.5 microns
- Thickness: 203 microns
$ 2256/MT
- Thickness: 76.2 microns
- Thickness: 254 microns
- Thickness: 457 microns
- Thickness: 711 microns
- Hardness, Shore A: 40 - 50
$ 1552/MT
- Density: 2.84 g/cc
- Water Absorption: 0.080 %
- Outgassing - Total Mass Loss: 0.00 %
- Outgassing - Total Mass Loss: 0.020 %
- Peel Strength: 0.877 kN/m
$ 1825/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 76.2 microns
- Thickness: 457 - 559 microns
- Thickness: 11110 - 14290 microns
- Tensile Strength: >= 4.83 MPa
$ 1501/MT
- Density: 2.40 g/cc
- Thickness: 203 microns
- Hardness, Shore A: 50
- Tensile Strength: 2.76 MPa
- Tensile Strength, Yield: 3.45 MPa @Strain <=1.00 %
$ 2035/MT
- Density: 1.20 g/cc
- Density: 1.35 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 305 microns
$ 2232/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 457 microns
- Thickness: 533 microns
$ 1448/MT
- Density: 1.45 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 88.9 microns
$ 1595/MT
- Specific Gravity: 2.80 g/cc
- Thickness: 76.2 microns
- Thickness: 229 microns
- Thickness: 457 microns
- Thickness: 762 microns
$ 1996/MT
- Density: 1.37 g/cc
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 1560/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 165 microns
- Thickness: 191 microns
- Thickness: 406 microns
$ 1983/MT
- Density: 1.22 g/cc
- Thickness: 76.2 microns
- Thickness: 88.9 microns
- Thickness: 88.9 microns
- Thickness: 203 microns
$ 1540/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 483 microns
- Thickness: 610 microns
$ 1480/MT
- Density: 1.35 g/cc
- Thickness: 203 microns
- Thickness: 254 microns
- Thickness: 356 microns
- Thickness: 813 microns
$ 1701/MT
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: >= 127 microns
- Thickness: 457 microns
- Thickness: 635 - 787 microns
$ 1628/MT
- Density: 1.17 g/cc
- Water Absorption: 1.1 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1486/MT
- Thickness: >= 50.8 microns
- Thickness: >= 50.8 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 229 - 305 microns
$ 1746/MT
- Thickness: 203 microns
- Thickness: 305 microns
- Thickness: 508 microns
- Hardness, Shore A: 45
- Tensile Strength: 6.21 MPa
$ 2151/MT
- Density: 3.20 g/cc
- Water Absorption: 0.030 %
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1720/MT
- Thickness: >= 25.4 microns
- Thickness: >= 50.8 microns
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: 203 microns
$ 1753/MT
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1624/MT
- Density: 1.20 g/cc
- Water Absorption: 1.0 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1695/MT
- Density: 1.19 g/cc
- Thickness: 1270 microns
- Hardness, Shore A: 70
- Tensile Strength: 4.83 MPa
- Elongation at Break: 290 %
$ 1649/MT
- Density: 1.20 g/cc
- Thickness: 63.5 microns
- Thickness: 2030 microns
- Hardness, Shore A: 61
- Tensile Strength: 8.101 MPa
$ 1466/MT
- Thickness: 432 - 584 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
- Maximum Service Temperature, Air: 204 °C
$ 1624/MT
- Thickness: 76.2 microns
- Thickness: 178 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
- Hardness, Shore A: 53 - 63
$ 1775/MT
- Density: 2.06 g/cc
- Water Absorption: 0.030 %
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.040 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1782/MT
- Density: 1.60 g/cc
- Thickness: 127 microns
- Thickness: 381 microns
- Thickness: 381 microns
- Hardness, Shore A: 72
$ 1757/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: >= 178 microns
- Thickness: 381 microns
- Thickness: 610 - 711 microns
$ 1853/MT
- Density: 2.45 g/cc
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.020 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Peel Strength: 2.10 kN/m
$ 1762/MT
- Density: 1.20 g/cc
- Water Absorption: 1.3 %
- Thickness: 63.5 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
$ 1883/MT
- Density: 1.20 g/cc
- Water Absorption: 1.0 %
- Thickness: 1020 microns
- Hardness, Shore A: 60
- Tensile Strength: 10.0 MPa
$ 1502/MT
- Thickness: 76.2 microns
- Thickness: 686 - 838 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 1735/MT
- Density: 1.60 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 88
$ 1452/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.40 %
- Thickness: 508 microns
- Hardness, Shore A: 50
- Tensile Strength, Ultimate: 6.55 MPa
$ 1850/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 457 microns
- Thickness: 533 microns
- Thickness: 533 microns
- Thickness: 1520 microns
$ 2372/MT
- Density: 1.40 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 63.5 microns
- Thickness: 63.5 microns
$ 1748/MT
- Density: 1.40 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 63.5 microns
- Thickness: 63.5 microns
$ 1887/MT
- Density: 1.26 g/cc
- Thickness: 25.4 microns
- Thickness: 229 microns
- Thickness: 406 microns
- Thickness: 635 microns
$ 2369/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: >= 152 microns
- Thickness: 457 microns
- Thickness: 699 - 775 microns
$ 1670/MT
- Density: 1.60 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1980 microns
- Thickness: 1980 microns
$ 2455/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 406 microns
- Thickness: 610 microns
- Thickness: 1020 microns
$ 1496/MT
- Thickness: 38.1 microns
- Thickness: >= 50.8 microns
- Thickness: >= 50.8 microns
- Thickness: 127 microns
- Thickness: 254 - 305 microns
$ 1768/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 102 microns
- Thickness: 178 microns
- Thickness: 381 microns
$ 1655/MT
- Density: 1.15 g/cc
- Water Absorption: 2.0 %
- Thickness: 76.2 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
$ 1503/MT
- Hardness, Shore A: 55 - 65
- Tensile Strength, Ultimate: >= 6.90 MPa
- Elongation at Break: >= 200 %
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -56.6 °C
$ 2296/MT
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 432 - 584 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 2012/MT
- Density: 1.34 g/cc
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 203 microns
- Thickness: 457 microns
$ 1541/MT
- Specific Gravity: 1.38 g/cc
- Thickness: 102 microns
- Thickness: 102 microns
- Thickness: 178 microns
- Thickness: 381 microns
$ 2390/MT
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 406 microns
- Thickness: 610 - 711 microns
$ 1611/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 457 - 559 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 2232/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1714/MT
- Specific Gravity: 1.10 g/cc
- Thickness: 254 microns
- Hardness, Shore A: 18
- Tensile Strength, Ultimate: 6.89 MPa
- Elongation at Break: 950 %
$ 1581/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1781/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1633/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1655/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1455/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1496/MT
- Density: 1.15 g/cc
- Water Absorption: 0.50 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 2169/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 178 microns
- Thickness: 178 microns
- Thickness: 406 microns
$ 1945/MT
- Density: 1.16 g/cc
- Thickness: 1020 microns
- Hardness, Shore A: 55
- Tensile Strength: 9.467 MPa
- Elongation at Break: 481 %
$ 2257/MT
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 241 - 292 microns
$ 1485/MT
- Density: 1.20 g/cc
- Water Absorption: 3.0 %
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 55
$ 1612/MT
- Density: 2.80 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 77
$ 1567/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 165 microns
- Thickness: 267 microns
$ 1739/MT
- Density: 1.20 g/cc
- Thickness: 25.4 microns
- Thickness: 203 microns
- Thickness: 508 microns
- Thickness: 25400 microns
$ 2034/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: 406 microns
$ 1901/MT
- Thickness: 127 microns
- Thickness: 508 microns
- Hardness, Shore A: 45
- Tensile Strength: 6.21 MPa
- Elongation at Break: 600 %
$ 1673/MT
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 152 microns
$ 1668/MT
- Density: 1.34 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 305 microns
- Thickness: 457 microns
$ 1706/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 191 microns
- Thickness: 483 microns
- Thickness: 749 microns
$ 1951/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 5.58 - 6.82 MPa
- Elongation at Break: 540 - 660 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1565/MT
- Thickness: 76.2 microns
- Thickness: 940 - 1090 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 2063/MT
- Thickness: 76.2 microns
- Thickness: 457 microns
- Thickness: 432 - 559 microns
- Thickness: 432 - 559 microns
- Thickness: 1450 - 1700 microns
$ 1963/MT
- Density: 1.10 g/cc
- Density: 1.70 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 381 microns
$ 1579/MT
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 203 microns
- Thickness: 508 microns
- Hardness, Shore A: 50
$ 1680/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 1455/MT
- Thickness: >= 25.4 microns
- Thickness: >= 25.4 microns
- Thickness: 38.1 microns
- Thickness: 140 microns
- Thickness: 203 - 241 microns
$ 1675/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
$ 1452/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 165 microns
- Thickness: 191 microns
- Thickness: 406 microns
$ 1764/MT
- Density: 2.80 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 77
$ 2203/MT
- Thickness: 76.2 microns
- Thickness: >= 88.9 microns
- Thickness: >= 88.9 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1900/MT
- Density: 1.21 g/cc
- Thickness: 76.2 microns
- Thickness: 305 microns
- Thickness: 457 microns
- Thickness: 762 microns
$ 2237/MT
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 152 microns
- Thickness: 457 microns
- Thickness: 737 - 813 microns
$ 2503/MT
- Thickness: >= 76.2 microns
- Thickness: 63.5 - 140 microns
- Thickness: 140 - 216 microns
- Thickness: >= 356 microns
- Thickness: 597 - 673 microns
$ 1993/MT
- Thickness: 457 microns
- Thickness: 559 microns
- Thickness: 559 microns
- Thickness: 1570 microns
- Hardness, Shore A: 50
$ 1636/MT
- Thickness: 76.2 microns
- Thickness: 165 microns
- Thickness: 165 microns
- Thickness: 457 microns
- Thickness: 762 microns
$ 1999/MT
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 203 microns
- Shear Modulus: 0.552 - 0.621 GPa
- Shear Strength: >= 1.38 MPa
$ 1467/MT
- Thickness: 76.2 microns
- Surface Tension: <= 30 dynes/cm
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -40.0 °C
- Shelf Life: 60.0 Month @Temperature 23.9 °C
$ 1982/MT
- Hardness, Shore A: 50 - 60
- Tensile Strength, Ultimate: 4.32 - 5.28 MPa
- Elongation at Break: 320 - 380 %
- Maximum Service Temperature, Air: 204 °C
$ 1752/MT
- Thickness: 76.2 microns
- Thickness: 1370 - 1680 microns
- Thickness: 1370 - 1680 microns
- Hardness, Shore A: 50 - 60
- Tensile Strength: 7.45 - 9.10 MPa
$ 2268/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 114 microns
- Thickness: 140 microns
- Thickness: 254 microns
$ 1617/MT
- Density: 1.24 g/cc
- Thickness: 76.2 microns
- Thickness: 254 microns
- Hardness, Shore A: 44
- Tensile Strength: 7.58 MPa
$ 1501/MT
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 102 - 152 microns
- Thickness: 102 - 152 microns
- Hardness, Shore A: 35 - 45
$ 1625/MT
- Density: 1.22 g/cc
- Density: 1.33 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 229 microns
$ 1866/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 165 microns
- Thickness: 457 microns
$ 2061/MT
- Thickness: >= 50.8 microns
- Thickness: >= 50.8 microns
- Thickness: 76.2 microns
- Thickness: 88.9 microns
- Thickness: 165 - 216 microns
$ 1714/MT
- Thickness: 3180 microns
- Hardness, Shore A: 50 - 60
- Tensile Strength: 7.45 - 9.10 MPa
- Elongation at Break: 540 - 660 %
- 100% Modulus: >= 0.00172 GPa
$ 1711/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 457 - 559 microns
- Thickness: 23810 - 26990 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 2085/MT
- Thickness: 76.2 microns
- Thickness: 457 microns
- Thickness: >= 533 microns
- Thickness: >= 533 microns
- Thickness: 1400 - 1650 microns
$ 1587/MT
- Density: 1.20 g/cc
- Thickness: 508 microns
- Hardness, Shore A: 55
- Tensile Strength: 7.93 MPa
- Elongation at Break: 430 %
$ 2333/MT
- Density: 1.60 g/cc
- Thickness: 127 microns
- Thickness: 381 microns
- Hardness, Shore A: 72
- Tensile Strength: 4.83 MPa
$ 1858/MT
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: >= 140 microns
- Thickness: 305 - 356 microns
$ 1544/MT
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 102 microns
$ 1677/MT
- Thickness: 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 356 - 406 microns
$ 1989/MT
- Thickness: 1190 - 1350 microns
- Thickness: 36510 - 39690 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
- Maximum Service Temperature, Air: 204 °C
$ 1855/MT
- Density: 1.20 g/cc
- Water Absorption: 0.90 %
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 55
$ 1864/MT
- Density: 1.20 g/cc
- Thickness: 25.4 microns
- Thickness: 203 microns
- Thickness: 762 microns
- Thickness: 25400 microns
$ 1579/MT
- Water Absorption: 0.27 %
- Modulus of Elasticity: 22.1 GPa
- Poissons Ratio: 0.15
- Peel Strength: 1.24 kN/m
- Peel Strength: 1.24 kN/m
$ 1706/MT
- Thickness: 127 microns
- Thickness: 3050 microns
- Thickness: 3180 microns
- Hardness, Shore A: 40
- Tensile Strength: 6.21 - 7.58 MPa
$ 2125/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 102 microns
- Thickness: 165 microns
- Thickness: 483 microns
- Thickness: 749 microns
$ 2278/MT
- Thickness: 76.2 microns
- Thickness: >= 381 microns
- Thickness: 457 microns
- Thickness: 762 - 914 microns
- Hardness, Shore A: 40 - 50
$ 2058/MT
- Thickness: 25.4 microns
- Thickness: 50.8 microns
- Thickness: 25.4 - 76.2 microns
- Thickness: 76.2 - 127 microns
- Hardness, Shore A: 40 - 50
$ 1452/MT
- Specific Gravity: 1.38 g/cc
- Thickness: 102 microns
- Thickness: 203 microns
- Thickness: 406 microns
- Thickness: 711 microns
$ 1818/MT
- Hardness, Shore A: >= 60
- Tensile Strength, Ultimate: 4.68 - 5.72 MPa
- Elongation at Break: 250 - 300 %
- Shear Modulus: <= 0.000700 GPa
- Adhesive Bond Strength: >= 2.80 MPa
$ 1735/MT
- Thickness: >= 43.2 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 457 microns
- Thickness: 991 - 1190 microns
$ 1736/MT
- Thickness: 76.2 microns
- Thickness: >= 88.9 microns
- Thickness: >= 88.9 microns
- Thickness: 203 microns
- Thickness: 356 - 406 microns
$ 1492/MT
- Density: 1.15 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 102 microns
- Thickness: 203 microns
$ 2206/MT
- Thickness: 38.1 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
$ 1503/MT
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 241 - 292 microns
$ 1782/MT
- Specific Gravity: 1.44 g/cc
- Thickness: 88.9 microns
- Thickness: 140 microns
- Thickness: 203 microns
- Thickness: 432 microns
$ 1692/MT
- Density: 1.34 g/cc
- Thickness: 76.2 microns
- Thickness: 254 microns
- Thickness: 457 microns
- Thickness: 711 microns
$ 1573/MT
- Specific Gravity: 1.35 g/cc
- Specific Gravity: 1.35 g/cc
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 457 microns
$ 1444/MT
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
$ 1563/MT
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: >= 229 microns
- Thickness: 394 - 470 microns
$ 1705/MT
- Density: 1.34 g/cc
- Thickness: 63.5 microns
- Thickness: 127 microns
- Thickness: 508 microns
- Thickness: 508 microns
$ 1877/MT
- Density: 2.80 g/cc
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
$ 1458/MT
- Density: 1.24 g/cc
- Thickness: 305 microns
- Thickness: 457 microns
- Thickness: 762 microns
- Hardness, Shore A: 44
$ 2137/MT
- Density: 1.22 g/cc
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
$ 1981/MT
- Density: 1.44 g/cc
- Thickness: 50.8 microns
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 63.5 microns
$ 1890/MT
- Water Absorption: <= 1.0 %
- Tensile Strength: 221 MPa
- Modulus of Elasticity: 14.5 GPa
- Flexural Strength: 414 MPa
- Poissons Ratio: 0.18
$ 1644/MT
- Density: 1.16 g/cc
- Hardness, Shore A: 46
- Tensile Strength: 8.584 MPa
- Elongation at Break: 565 %
- Tear Strength: 17.5 kN/m
$ 1643/MT
- Density: 1.34 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1520 microns
- Thickness: 1520 microns
$ 1554/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 76.2 microns
- Thickness: 254 - 356 microns
- Thickness: 23810 - 26990 microns
- Tensile Strength: >= 4.83 MPa
$ 1522/MT
- Density: 1.17 g/cc
- Water Absorption: 2.0 %
- Thickness: 76.2 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
$ 2154/MT
- Thickness: >= 25.4 microns
- Thickness: >= 102 microns
- Thickness: 203 microns
- Thickness: 279 - 330 microns
- Hardness, Shore A: 40 - 50
$ 1811/MT
- Density: 2.05 g/cc
- Water Absorption: 0.13 %
- Flexural Strength: 214 - 338 MPa
- Peel Strength: 0.789 kN/m
- Peel Strength: 0.877 kN/m
$ 1888/MT
- Hardness, Shore A: >= 50
- Tensile Strength, Ultimate: 4.68 - 5.72 MPa
- Elongation at Break: 250 - 300 %
- Shear Modulus: <= 0.000700 GPa
- Adhesive Bond Strength: >= 2.80 MPa
$ 1876/MT
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 127 microns
- Thickness: 203 microns
- Thickness: 356 - 406 microns
$ 1564/MT
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: >= 76.2 microns
- Thickness: 88.9 microns
- Thickness: 216 - 267 microns
$ 1484/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 152 microns
- Thickness: 152 microns
$ 2575/MT
- Density: 3.20 g/cc
- Water Absorption: 0.030 %
- Outgassing - Total Mass Loss: 0.00 %
- Outgassing - Total Mass Loss: 0.020 %
- Peel Strength: 1.40 kN/m
$ 1549/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: >= 5.50 MPa
- Elongation at Break: >= 500 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 2061/MT
- Thickness: 12.7 microns
- Thickness: 12.7 microns
- Thickness: 191 microns
- Thickness: 216 microns
- Hardness, Shore A: 30
$ 1529/MT
- Thickness: >= 25.4 microns
- Thickness: >= 50.8 microns
- Thickness: 76.2 microns
- Thickness: >= 203 microns
- Thickness: 457 microns
$ 1552/MT
- Density: 1.20 g/cc
- Water Absorption: 0.10 %
- Thickness: 25.4 microns
- Thickness: 1020 microns
- Hardness, Shore A: 49
$ 1451/MT
- Thickness: 76.2 microns
- Thickness: >= 229 microns
- Thickness: 432 microns
- Thickness: 610 - 711 microns
- Hardness, Shore A: 40 - 50
$ 1956/MT
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: >= 127 microns
- Thickness: 457 microns
- Thickness: 711 - 787 microns
$ 2066/MT
- Thickness: 38.1 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
$ 1635/MT
- Density: 1.25 g/cc
- Thickness: 127 microns
- Thickness: 1880 microns
- Thickness: 2010 microns
- Hardness, Shore A: 65
$ 2119/MT
- Density: 1.27 g/cc
- Density: 2.70 g/cc
- Thickness: 102 microns
- Thickness: 305 microns
- Thickness: 406 microns
$ 1549/MT
- Density: 1.20 g/cc
- Thickness: 63.5 microns
- Thickness: 127 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
$ 2086/MT
- Thickness: 25.4 microns
- Thickness: 50.8 microns
- Thickness: 63.5 microns
- Thickness: 140 microns
- Hardness, Shore A: 45
$ 1877/MT
- Specific Gravity: 1.70 g/cc
- Thickness: 203 microns
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 2.07 MPa
- Elongation at Break: 28 %
$ 1625/MT
- Thickness: 50.8 - 76.2 microns
- Thickness: 76.2 microns
- Thickness: 102 - 127 microns
- Thickness: 203 microns
- Thickness: 368 - 445 microns
$ 1543/MT
- Specific Gravity: 3.70 g/cc
- Thickness: 203 microns
- Hardness, Shore A: 84
- Tensile Strength, Ultimate: 3.34 MPa
- Elongation at Break: 60 %
$ 1452/MT
- Thickness: 38.1 microns
- Thickness: >= 254 microns
- Thickness: 381 microns
- Thickness: 584 - 686 microns
- Hardness, Shore A: 55 - 65
$ 2432/MT
- Density: 1.32 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 203 microns
$ 2430/MT
- Thickness: 25.4 microns
- Thickness: 38.1 microns
- Thickness: 584 - 686 microns
- Thickness: 584 - 686 microns
- Hardness, Shore A: 65 - 75
$ 2058/MT
- Density: 2.10 g/cc
- Water Absorption: 0.060 %
- Peel Strength: 2.98 kN/m
- CTE, linear: 9.00 µm/m-°C
- CTE, linear: 9.00 µm/m-°C
$ 1822/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1520 microns
- Thickness: 1520 microns
$ 1678/MT
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 406 microns
- Thickness: 610 - 711 microns
$ 1663/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 5.58 - 6.82 MPa
- Elongation at Break: 540 - 660 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1491/MT
- Water Absorption: <= 1.0 %
- Tensile Strength: 221 MPa
- Flexural Strength: 414 MPa
- Poissons Ratio: 0.17
- Peel Strength: 0.736 kN/m
$ 2294/MT
- Specific Gravity: 1.38 g/cc
- Thickness: 127 microns
- Thickness: 152 microns
- Thickness: 432 microns
- Thickness: 711 microns
$ 1551/MT
- Density: 1.20 g/cc
- Water Absorption: 0.38 %
- Thickness: 25.4 microns
- Thickness: 305 microns
- Hardness, Shore A: 50
$ 1719/MT
- Thickness: 50.8 microns
- Thickness: 889 - 1040 microns
- Thickness: 940 - 1090 microns
- Hardness, Shore A: 55 - 65
- Tensile Strength: 6.21 - 7.58 MPa
$ 1568/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: >= 152 microns
- Thickness: 457 microns
- Thickness: 699 - 775 microns
$ 1469/MT
- Thickness: 50.8 microns
- Thickness: 1400 - 1550 microns
- Thickness: 1450 - 1600 microns
- Hardness, Shore A: 55 - 65
- Tensile Strength: 6.21 - 7.58 MPa
$ 1596/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 165 microns
- Thickness: 191 microns
- Thickness: 406 microns
$ 1579/MT
- Thickness: 127 microns
- Thickness: 635 microns
- Hardness, Shore A: 45
- Tensile Strength: 6.21 MPa
- Elongation at Break: 600 %
$ 1581/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 229 - 279 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 55 - 65
$ 1469/MT
- Density: 1.26 g/cc
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: 457 microns
- Thickness: 686 microns
$ 1778/MT
- Density: 1.35 g/cc
- Thickness: 127 microns
- Thickness: 165 microns
- Thickness: 457 microns
- Thickness: 749 microns
$ 1941/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 203 microns
- Thickness: 508 microns
$ 2547/MT
- Density: 1.17 g/cc
- Water Absorption: 0.80 %
- Thickness: 76.2 microns
- Thickness: 1270 microns
- Hardness, Shore A: 55
$ 1758/MT
- Density: 1.24 g/cc
- Thickness: 254 microns
- Thickness: 457 microns
- Thickness: 711 microns
- Hardness, Shore A: 44
$ 2373/MT
- Density: 1.24 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 152 microns
- Thickness: 203 microns
$ 1609/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 5.58 - 6.82 MPa
- Elongation at Yield: 540 - 660 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1569/MT
- Density: 1.36 g/cc
- Density: 1.38 g/cc
- Thickness: 63.5 microns
- Thickness: 102 microns
- Thickness: 178 microns
$ 1778/MT
- Density: 1.29 g/cc
- Thickness: 19.0 microns
- Thickness: 19.0 microns
- Thickness: 38.1 microns
- Thickness: 152 microns
$ 2184/MT
- Density: 1.35 g/cc
- Thickness: 254 microns
- Thickness: 483 microns
- Thickness: 838 microns
- Thickness: 1570 microns
$ 1530/MT
- Density: 1.62 g/cc
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 203 microns
$ 1728/MT
- Specific Gravity: 2.70 g/cc
- Thickness: 102 microns
- Thickness: 305 microns
- Thickness: 457 microns
- Thickness: 864 microns
$ 1486/MT
- Density: 1.18 g/cc
- Thickness: 203 microns
- Thickness: 318 microns
- Thickness: 521 microns
- Hardness, Shore A: 47
$ 1581/MT
- Density: 1.20 g/cc
- Water Absorption: 2.2 %
- Thickness: 25.4 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1773/MT
- Density: 1.32 g/cc
- Density: 3.80 g/cc
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 203 microns
$ 1564/MT
- Density: 2.30 g/cc
- Water Absorption: 0.050 %
- Outgassing - Total Mass Loss: 0.010 %
- Outgassing - Total Mass Loss: 0.020 %
- Peel Strength: 1.23 kN/m
$ 2177/MT
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 152 - 203 microns
- Thickness: 279 - 330 microns
- Hardness, Shore A: 40 - 50
$ 1454/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 203 microns
$ 1474/MT
- Density: 1.26 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 432 microns
- Thickness: 635 microns
$ 1449/MT
- Density: 1.24 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 216 microns
- Thickness: 406 microns
$ 2148/MT
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: >= 102 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1771/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 457 microns
- Thickness: >= 533 microns
- Thickness: 1090 - 1220 microns
$ 1461/MT
- Thickness: 127 microns
- Thickness: 762 microns
- Hardness, Shore A: 45
- Tensile Strength: 6.21 MPa
- Elongation at Break: 600 %
$ 2081/MT
- Density: 1.09 g/cc
- Thickness: 211 microns
- Thickness: 290 microns
- Thickness: 290 microns
- Thickness: 790 microns
$ 1690/MT
- Density: 1.09 g/cc
- Thickness: 211 microns
- Thickness: 290 microns
- Thickness: 290 microns
- Thickness: 790 microns
$ 1585/MT
- Density: 1.09 g/cc
- Thickness: 211 microns
- Thickness: 290 microns
- Thickness: 290 microns
- Thickness: 790 microns
$ 1948/MT
- Density: 1.09 g/cc
- Thickness: 74.9 microns
- Thickness: 480 microns
- Thickness: 551 microns
- Thickness: 551 microns
$ 1729/MT
- Thickness: 3180 microns
- Hardness, Shore A: 35 - 45
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
- 100% Modulus: 0.00103 GPa
$ 1566/MT
- Density: 1.25 g/cc
- Hardness, Shore A: 55 - 65
- Tensile Strength: >= 6.21 MPa
- Elongation at Break: >= 300 %
- Maximum Service Temperature, Air: 232 °C
$ 1534/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1570 microns
- Thickness: 1570 microns
$ 1520/MT
- Density: 1.60 g/cc
- Thickness: 127 microns
- Thickness: 1270 microns
- Hardness, Shore A: 72
- Tensile Strength: 4.83 MPa
$ 1524/MT
- Density: 1.35 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 203 microns
$ 1957/MT
- Density: 1.20 g/cc
- Water Absorption: 3.0 %
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 55
$ 1532/MT
- Thickness: 178 microns
- Thickness: 203 microns
- Thickness: 381 microns
- Hardness, Shore A: 60
- Tensile Strength: >= 6.21 MPa
$ 1674/MT
- Thickness: 127 microns
- Thickness: 2160 microns
- Hardness, Shore A: 40
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
$ 1461/MT
- Density: 1.32 g/cc
- Density: 1.32 g/cc
- Density: 1.56 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
$ 1539/MT
- Density: 1.37 g/cc
- Water Absorption: 0.60 %
- Tensile Strength: 44.8 MPa
- Modulus of Elasticity: 15.9 GPa
- Flexural Strength: 234 MPa
$ 1545/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 356 - 406 microns
- Thickness: 356 - 406 microns
- Hardness, Shore A: 40 - 50
$ 2009/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 165 microns
- Thickness: 216 microns
$ 1924/MT
- Density: 1.26 g/cc
- Hardness, Shore A: 40 - 50
- Tensile Strength: >= 5.52 MPa
- Elongation at Break: >= 500 %
- Maximum Service Temperature, Air: 232 °C
$ 1829/MT
- Density: 1.20 g/cc
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 229 microns
$ 1747/MT
- Density: 1.17 g/cc
- Water Absorption: 1.6 %
- Thickness: 76.2 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
$ 1699/MT
- Thickness: 76.2 microns
- Thickness: >= 330 microns
- Thickness: 381 microns
- Thickness: 660 - 762 microns
- Hardness, Shore A: 40 - 50
$ 1929/MT
- Density: 2.20 g/cc
- Water Absorption: 0.12 %
- Tensile Strength: 60.0 MPa
- Flexural Strength: 180 MPa
- Peel Strength: 0.841 kN/m
$ 2214/MT
- Hardness, Shore A: 55 - 65
- Tensile Strength, Ultimate: >= 6.90 MPa
- Elongation at Break: >= 200 %
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -56.6 °C
$ 1878/MT
- Density: 1.06 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Hardness, Shore A: 35
- Tensile Strength: 6.89 MPa
$ 1479/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 5.58 - 6.82 MPa
- Elongation at Break: 540 - 660 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1870/MT
- Thickness: 25.4 microns
- Thickness: 25.4 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Hardness, Shore A: 40
$ 1503/MT
- Density: 1.34 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 2005/MT
- Thickness: 432 - 584 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
- Maximum Service Temperature, Air: 204 °C
$ 2344/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 381 microns
- Thickness: 381 microns
- Hardness, Shore A: 45
$ 1659/MT
- Density: 2.80 g/cc
- Thickness: 76.2 microns
- Thickness: 432 microns
- Thickness: 508 microns
- Hardness, Shore A: 77
$ 1900/MT
- Density: 1.21 g/cc
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 88.9 microns
- Thickness: 191 microns
$ 2067/MT
- Thickness: 127 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
- Tensile Strength: 6.89 MPa
- Elongation at Break: 450 %
$ 1455/MT
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 203 - 229 microns
- Thickness: 457 - 559 microns
$ 2088/MT
- Density: 1.81 g/cc
- Thickness: 127 microns
- Thickness: 1520 microns
- Hardness, Shore A: 65
- Tensile Strength: 3.85 MPa
$ 1903/MT
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 2030 microns
- Thickness: 2130 microns
- Peel Strength: >= 0.175 kN/m
$ 1635/MT
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: >= 60
- Tensile Strength: 5.17 MPa
- Elongation at Break: 275 %
$ 1469/MT
- Density: 1.45 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 152 microns
$ 1626/MT
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 432 microns
- Thickness: 559 - 711 microns
- Hardness, Shore A: 40 - 50
$ 1465/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 102 microns
$ 1712/MT
- Density: 1.20 g/cc
- Water Absorption: 1.0 %
- Thickness: 63.5 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1683/MT
- Density: 1.35 g/cc
- Thickness: 88.9 microns
- Thickness: 140 microns
- Thickness: 203 microns
- Thickness: 432 microns
$ 1622/MT
- Density: 1.24 g/cc
- Thickness: 19.0 microns
- Thickness: 19.0 microns
- Thickness: 38.1 microns
- Thickness: 152 microns
$ 1685/MT
- Density: 1.34 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 254 microns
- Thickness: 254 microns
$ 2037/MT
- Thickness: 76.2 microns
- Thickness: 889 - 1090 microns
- Hardness, Shore A: 60 - 70
- Tensile Strength: >= 2.07 MPa
- Elongation at Break: >= 60 %
$ 1642/MT
- Density: 1.24 g/cc
- Thickness: 254 microns
- Thickness: 457 microns
- Thickness: 711 microns
- Hardness, Shore A: 44
$ 2079/MT
- Thickness: 76.2 microns
- Thickness: 178 - 330 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 1467/MT
- Density: 1.20 g/cc
- Water Absorption: 3.0 %
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 55
$ 1572/MT
- Density: 1.37 g/cc
- Thickness: 63.5 microns
- Thickness: 229 microns
- Thickness: 406 microns
- Thickness: 635 microns
$ 2054/MT
- Density: 1.40 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 60
$ 1485/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
- Tensile Strength: 4.21 MPa
$ 1883/MT
- Density: 1.30 g/cc
- Thickness: 50.8 microns
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
$ 1624/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 36
- Tensile Strength: 6.38 MPa
- Elongation at Break: 550 %
- Tear Strength: 14.5 kN/m
$ 2244/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: >= 5.50 MPa
- Elongation at Break: >= 500 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1572/MT
- Specific Gravity: 1.44 g/cc
- Thickness: 102 microns
- Thickness: 102 microns
- Thickness: 381 microns
- Thickness: 584 microns
$ 2154/MT
- Density: 1.30 g/cc
- Thickness: 50.8 microns
- Thickness: 102 microns
- Thickness: 152 microns
- Hardness, Shore A: 60
$ 1861/MT
- Density: 1.30 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 140 microns
$ 1900/MT
- Thickness: 38.1 microns
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 127 microns
- Thickness: 229 - 279 microns
$ 2191/MT
- Density: 1.17 g/cc
- Water Absorption: 2.8 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1875/MT
- Density: 1.20 g/cc
- Water Absorption: 1.0 %
- Thickness: 76.2 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
$ 1461/MT
- Thickness: 76.2 microns
- Thickness: 178 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
- Hardness, Shore A: 40 - 50
$ 1580/MT
- Thickness: 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 356 - 406 microns
$ 1487/MT
- Density: 1.30 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 140 microns
$ 1456/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 305 microns
- Thickness: 406 microns
- Thickness: 711 microns
$ 1968/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 305 microns
- Thickness: 457 microns
- Thickness: 762 microns
$ 1479/MT
- Density: 1.16 g/cc
- Thickness: 76.2 microns
- Thickness: 813 microns
- Hardness, Shore A: 53
- Tensile Strength: 9.31 MPa
$ 2047/MT
- Thickness: 76.2 microns
- Thickness: 838 - 940 microns
- Thickness: 914 - 1120 microns
- Hardness, Shore A: 50 - 60
- Tensile Strength: 7.45 - 9.10 MPa
$ 2051/MT
- Density: 1.24 g/cc
- Thickness: 140 microns
- Thickness: 203 microns
- Thickness: 406 microns
- Thickness: 749 microns
$ 1690/MT
- Density: 1.35 g/cc
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
- Thickness: 711 microns
$ 1463/MT
- Thickness: 76.2 microns
- Thickness: 229 - 305 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 1591/MT
- Density: 1.62 g/cc
- Thickness: 88.9 microns
- Thickness: 88.9 microns
- Thickness: 203 microns
- Thickness: 381 microns
$ 2232/MT
- Density: 2.80 g/cc
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 77
$ 2444/MT
- Density: 1.35 g/cc
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
$ 1491/MT
- Thickness: 12.7 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: >= 203 microns
- Thickness: 457 microns
$ 1492/MT
- Specific Gravity: 1.44 g/cc
- Thickness: 178 microns
- Thickness: 381 microns
- Hardness, Shore A: 62
- Tensile Strength, Ultimate: 8.89 MPa
$ 1794/MT
- Density: 1.45 g/cc
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 203 microns
- Thickness: 508 microns
$ 1603/MT
- Thickness: 76.2 microns
- Thickness: >= 203 microns
- Thickness: 432 microns
- Thickness: 584 - 686 microns
- Hardness, Shore A: 55 - 60
$ 1554/MT
- Density: 1.26 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 152 microns
- Thickness: 330 microns
$ 1582/MT
- Density: 1.21 g/cc
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 88.9 microns
- Thickness: 191 microns
$ 1804/MT
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 203 microns
- Thickness: 457 microns
- Hardness, Shore A: 45
$ 1488/MT
- Density: 1.60 g/cc
- Water Absorption: 0.16 %
- Tensile Strength: 241 MPa
- Modulus of Elasticity: 27.6 GPa
- Flexural Strength: 400 MPa
$ 1503/MT
- Density: 1.34 g/cc
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 76.2 microns
- Thickness: 88.9 microns
$ 1744/MT
- Thickness: 102 microns
- Thickness: 127 microns
- Thickness: >= 152 microns
- Thickness: 457 microns
- Thickness: 737 - 787 microns
$ 1689/MT
- Specific Gravity: 1.44 g/cc
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
- Thickness: 711 microns
$ 1578/MT
- Density: 1.60 g/cc
- Water Absorption: 0.26 %
- Tensile Strength: 250 MPa
- Tensile Strength: 476 MPa
- Modulus of Elasticity: 26.2 GPa
$ 1835/MT
- Density: 1.50 g/cc
- Thickness: 63.5 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 1715/MT
- Density: 1.24 g/cc
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 381 microns
$ 1516/MT
- Specific Gravity: 1.24 g/cc
- Thickness: 19.0 microns
- Thickness: 19.0 microns
- Thickness: 203 microns
- Thickness: 394 microns
$ 1599/MT
- Thickness: >= 254 microns
- Thickness: >= 381 microns
- Thickness: 635 - 686 microns
- Hardness, Shore A: 60 - 70
- Tensile Strength: 6.21 - 7.58 MPa
$ 1590/MT
- Specific Gravity: 1.20 g/cc
- Thickness: 508 microns
- Hardness, Shore A: 55
- Tensile Strength, Ultimate: 4.21 MPa
- Elongation at Break: 500 %
$ 1502/MT
- Density: 1.22 g/cc
- Thickness: 140 microns
- Thickness: 140 microns
- Thickness: 279 microns
- Hardness, Shore A: 45
$ 1596/MT
- Density: 1.20 g/cc
- Water Absorption: 3.0 %
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 55
$ 1636/MT
- Density: 2.80 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 152 microns
$ 2071/MT
- Density: 1.32 g/cc
- Density: 1.56 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 229 microns
$ 1459/MT
- Density: 1.35 g/cc
- Thickness: 102 microns
- Thickness: 457 microns
- Thickness: 1020 microns
- Thickness: 1570 microns
$ 1734/MT
- Density: 1.18 g/cc
- Thickness: 203 microns
- Thickness: 216 microns
- Thickness: 419 microns
- Hardness, Shore A: 47
$ 1856/MT
- Thickness: 25.4 microns
- Thickness: 50.8 microns
- Thickness: 140 microns
- Thickness: 191 microns
- Hardness, Shore A: 60
$ 1539/MT
- Density: 1.62 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 229 microns
- Thickness: 508 microns
$ 2374/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: >= 5.50 MPa
- Elongation at Yield: >= 500 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 2177/MT
- Density: 1.24 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 178 microns
- Thickness: 406 microns
$ 1598/MT
- Thickness: 76.2 microns
- Thickness: 191 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 55 - 65
- Tensile Strength: >= 6.21 MPa
$ 1725/MT
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 203 microns
- Thickness: 381 microns
- Hardness, Shore A: 58
$ 1638/MT
- Thickness: 3180 microns
- Hardness, Shore A: 35 - 45
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
- 100% Modulus: 0.00103 GPa
$ 1768/MT
- Specific Gravity: 1.35 g/cc
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: 5.52 MPa
- Elongation at Break: 225 %
- Tear Strength: 15.8 kN/m
$ 1483/MT
- Thickness: 76.2 microns
- Thickness: 114 microns
- Thickness: >= 114 microns
- Thickness: 406 microns
- Thickness: 660 - 686 microns
$ 1545/MT
- Density: 1.22 g/cc
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 69
- Tensile Strength: 10.0 MPa
$ 1544/MT
- Thickness: 38.1 microns
- Thickness: 127 microns
- Thickness: 457 - 559 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 35 - 45
$ 1664/MT
- Density: 1.33 g/cc
- Thickness: 76.2 microns
- Thickness: 178 microns
- Thickness: 635 microns
- Thickness: 635 microns
$ 1895/MT
- Density: 1.17 g/cc
- Water Absorption: 1.1 %
- Thickness: 76.2 microns
- Thickness: 254 microns
- Hardness, Shore A: 55
$ 1475/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 508 microns
- Thickness: 508 microns
$ 2086/MT
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 178 microns
$ 1804/MT
- Specific Gravity: 1.32 g/cc
- Thickness: 127 microns
- Thickness: 165 microns
- Thickness: 457 microns
- Thickness: 749 microns
$ 1724/MT
- Density: 1.33 g/cc
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 229 microns
$ 1897/MT
- Density: 1.17 g/cc
- Thickness: 63.5 microns
- Thickness: 127 microns
- Thickness: 203 microns
- Thickness: 330 microns
$ 1633/MT
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: >= 152 microns
- Thickness: 457 microns
- Thickness: 737 - 813 microns
$ 2015/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 88.9 microns
- Thickness: 178 microns
- Thickness: 483 microns
- Thickness: 749 microns
$ 1789/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1520 microns
- Thickness: 1520 microns
$ 1444/MT
- Thickness: 76.2 microns
- Thickness: 114 microns
- Thickness: 140 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
$ 2292/MT
- Density: 2.80 g/cc
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 356 microns
- Hardness, Shore A: 77
$ 1798/MT
- Thickness: >= 25.4 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 203 - 241 microns
$ 1837/MT
- Thickness: 76.2 microns
- Thickness: 330 microns
- Thickness: 737 - 889 microns
- Thickness: 1070 - 1220 microns
- Hardness, Shore A: 50 - 60
$ 1786/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 584 - 686 microns
- Thickness: 584 - 686 microns
- Hardness, Shore A: 40 - 50
$ 1497/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 5.58 - 6.82 MPa
- Elongation at Break: 540 - 660 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 2080/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 229 microns
- Thickness: 508 microns
$ 1671/MT
- Density: 1.35 g/cc
- Water Absorption: 0.040 %
- Tensile Strength: 51.0 MPa
- Tensile Strength: 53.8 MPa
- Modulus of Elasticity: 4.62 GPa
$ 1699/MT
- Density: 1.11 g/cc
- Thickness: 457 microns
- Thickness: 457 microns
- Thickness: 457 microns
- Hardness, Shore A: 40
$ 1572/MT
- Density: 1.16 g/cc
- Thickness: 76.2 microns
- Thickness: 152 microns
- Thickness: 381 microns
- Thickness: 508 microns
$ 1486/MT
- Hardness, Shore A: 50 - 60
- Tensile Strength, Ultimate: 4.32 - 5.28 MPa
- Elongation at Break: 315 - 385 %
- Maximum Service Temperature, Air: 204 °C
$ 2058/MT
- Thickness: 127 microns
- Thickness: 381 microns
- Hardness, Shore A: 45
- Tensile Strength: >= 5.52 MPa
- Elongation at Break: >= 500 %
$ 1595/MT
- Density: 1.15 g/cc
- Water Absorption: 2.9 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1926/MT
- Density: 1.35 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 88.9 microns
- Thickness: 88.9 microns
$ 1445/MT
- Density: 2.26 g/cc
- Water Absorption: 0.020 %
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.020 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1687/MT
- Specific Gravity: 1.15 g/cc
- Thickness: 25.4 microns
- Thickness: 50.8 microns
- Thickness: 140 microns
- Thickness: 203 microns
$ 1503/MT
- Thickness: 38.1 - 76.2 microns
- Thickness: 38.1 - 76.2 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 165 - 203 microns
$ 1707/MT
- Density: 1.35 g/cc
- Water Absorption: 0.15 %
- Tensile Strength: 44.8 MPa
- Modulus of Elasticity: 17.9 GPa
- Flexural Strength: 579 MPa
$ 1466/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 1470 - 1570 microns
- Thickness: 36510 - 39690 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 2189/MT
- Thickness: 38.1 microns
- Thickness: >= 102 microns
- Thickness: 127 microns
- Thickness: 203 - 254 microns
- Hardness, Shore A: 40 - 50
$ 1614/MT
- Density: 1.15 g/cc
- Water Absorption: 2.0 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1588/MT
- Density: 1.18 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 203 microns
- Thickness: 254 microns
$ 1457/MT
- Density: 1.20 g/cc
- Water Absorption: 2.2 %
- Thickness: 25.4 microns
- Thickness: 1270 microns
- Hardness, Shore A: 55
$ 2003/MT
- Density: 1.34 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 889 microns
- Thickness: 889 microns
$ 1462/MT
- Density: 1.20 g/cc
- Water Absorption: 2.2 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1546/MT
- Density: 1.19 g/cc
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 25
- Tensile Strength: 4.83 MPa
$ 1552/MT
- Specific Gravity: 1.38 g/cc
- Outgassing - Total Mass Loss: 0.34 %
- Outgassing - Total Mass Loss: 1.07 %
- Hardness, Shore A: 48
- Tensile Strength, Ultimate: 5.86 MPa
$ 2341/MT
- Density: 1.20 g/cc
- Thickness: 25.4 microns
- Thickness: 203 microns
- Thickness: 381 microns
- Thickness: 25400 microns
$ 1713/MT
- Density: 1.20 g/cc
- Thickness: 38.1 microns
- Thickness: 508 microns
- Maximum Service Temperature, Inert: 204 °C
- Minimum Service Temperature, Air: -73.3 °C
$ 1453/MT
- Density: 2.60 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 57
$ 1537/MT
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 241 - 292 microns
$ 1829/MT
- Density: 1.28 g/cc
- Thickness: 76.2 microns
- Thickness: 432 microns
- Thickness: 508 microns
- Hardness, Shore A: 60
$ 1675/MT
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1896/MT
- Thickness: 76.2 microns
- Thickness: 127 - 152 microns
- Thickness: 127 - 152 microns
- Thickness: 203 microns
- Thickness: 457 - 559 microns
$ 1831/MT
- Density: 1.20 g/cc
- Water Absorption: 0.90 %
- Thickness: 76.2 microns
- Thickness: 254 microns
- Hardness, Shore A: 55
$ 1537/MT
- Density: 1.33 g/cc
- Thickness: 63.5 microns
- Thickness: 102 microns
- Thickness: 203 microns
- Thickness: 406 microns
$ 2230/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 152 microns
- Thickness: >= 254 microns
- Thickness: 457 - 533 microns
$ 2002/MT
- Density: 1.17 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 203 microns
$ 1452/MT
- Thickness: 76.2 microns
- Thickness: 88.9 microns
- Thickness: 178 microns
- Thickness: 457 microns
- Thickness: 724 microns
$ 1967/MT
- Thickness: 25.4 - 38.1 microns
- Thickness: 25.4 - 38.1 microns
- Thickness: 38.1 microns
- Thickness: 140 microns
- Thickness: 203 - 241 microns
$ 1885/MT
- Density: 1.15 g/cc
- Water Absorption: 2.9 %
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1496/MT
- Density: 1.30 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
$ 1663/MT
- Density: 1.19 g/cc
- Thickness: 76.2 microns
- Thickness: 2160 microns
- Hardness, Shore A: 70
- Tensile Strength: 4.83 MPa
$ 1878/MT
- Thickness: 76.2 microns
- Thickness: >= 102 microns
- Thickness: 127 microns
- Thickness: 406 microns
- Thickness: 584 - 660 microns
$ 1568/MT
- Density: 1.47 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 88.9 microns
- Thickness: 140 microns
$ 1680/MT
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: >= 60
- Tensile Strength: 5.17 MPa
- Elongation at Break: 275 %
$ 1708/MT
- Density: 1.32 g/cc
- Density: 1.56 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 457 microns
$ 2184/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 229 microns
- Thickness: 508 microns
$ 2077/MT
- Thickness: 50.8 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: >= 203 microns
- Thickness: 457 microns
$ 1958/MT
- Density: 1.34 g/cc
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
$ 2004/MT
- Thickness: 3180 microns
- Hardness, Shore A: 35 - 45
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
- 100% Modulus: 0.00103 GPa
$ 1584/MT
- Hardness, Shore A: 50 - 60
- Tensile Strength, Ultimate: >= 6.90 MPa
- Elongation at Break: >= 500 %
- 100% Modulus: 0.00172 GPa
- Tear Strength: >= 35.1 kN/m
$ 2585/MT
- Density: 0.930 g/cc
- Thickness: 0.0381 microns
- Thermal Conductivity: 0.170 W/m-K
- Maximum Service Temperature, Air: <= 75.0 °C
- Brittleness Temperature: -60.0 °C
$ 1924/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 508 microns
- Thickness: 762 microns
- Hardness, Shore A: 45
$ 1463/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: >= 127 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
$ 1669/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 1773/MT
- Density: 1.30 g/cc
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 203 microns
$ 1565/MT
- Density: 1.20 g/cc
- Density: 1.35 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 178 microns
$ 1549/MT
- Density: 2.30 g/cc
- Water Absorption: 0.050 %
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.020 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1501/MT
- Density: 1.34 g/cc
- Thickness: 127 microns
- Thickness: 762 microns
- Hardness, Shore A: 37
- Tensile Strength: 6.55 MPa
$ 1488/MT
- Thickness: 76.2 microns
- Thickness: 457 microns
- Thickness: >= 686 microns
- Thickness: 1040 - 1240 microns
- Hardness, Shore A: 20 - 30
$ 2051/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 76.2 microns
- Thickness: 457 - 559 microns
- Thickness: 49210 - 52390 microns
- Tensile Strength: >= 4.83 MPa
$ 1882/MT
- Thickness: 127 microns
- Thickness: 406 microns
- Thickness: 508 microns
- Tensile Strength: >= 5.52 MPa
- Elongation at Break: >= 400 %
$ 1500/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 88.9 microns
$ 1708/MT
- Thickness: 76.2 microns
- Thickness: 1450 - 1700 microns
- Thickness: 1450 - 1700 microns
- Hardness, Shore A: 63 - 73
- Tensile Strength: >= 6.55 MPa
$ 1991/MT
- Thickness: 76.2 microns
- Thickness: 584 - 686 microns
- Thickness: 584 - 686 microns
- Hardness, Shore A: 40 - 50
- Tensile Strength: >= 5.52 MPa
$ 1875/MT
- Thickness: 127 microns
- Thickness: 381 microns
- Hardness, Shore A: 45
- Tensile Strength: >= 5.52 MPa
- Elongation at Break: >= 500 %
$ 1508/MT
- Thickness: 88.9 microns
- Thickness: 88.9 microns
- Thickness: 203 microns
- Thickness: 381 microns
- Hardness, Shore A: 45
$ 1827/MT
- Density: 2.31 g/cc
- Water Absorption: 0.030 %
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.020 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1537/MT
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 203 microns
$ 1514/MT
- Thickness: 127 microns
- Thickness: 2160 microns
- Hardness, Shore A: 55
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 500 %
$ 1575/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
$ 1792/MT
- Thickness: 127 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
- Tensile Strength: 6.21 - 7.58 MPa
- Elongation at Break: 450 - 550 %
$ 2016/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
$ 1829/MT
- Density: 2.27 g/cc
- Water Absorption: 0.050 %
- Outgassing - Total Mass Loss: 0.00 %
- Outgassing - Total Mass Loss: 0.030 %
- Peel Strength: 1.75 kN/m
$ 2329/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 635 microns
- Thickness: 635 microns
- Hardness, Shore A: 45
$ 2027/MT
- Thickness: 127 microns
- Thickness: 635 microns
- Hardness, Shore A: 60
- Tensile Strength: 6.21 MPa
- Elongation at Break: 300 %
$ 1699/MT
- Density: 1.62 g/cc
- Hardness, Shore A: 74
- Tensile Strength: 5.79 MPa
- Elongation at Break: 130 %
- Tear Strength: 15.8 kN/m
$ 1941/MT
- Specific Gravity: 1.24 g/cc
- Thickness: 25.4 microns
- Thickness: 25.4 microns
- Thickness: 31.8 microns
- Thickness: 31.8 microns
$ 1769/MT
- Thickness: 76.2 microns
- Thickness: 127 - 152 microns
- Thickness: 127 - 152 microns
- Thickness: 203 microns
- Thickness: 457 - 559 microns
$ 2056/MT
- Density: 1.20 g/cc
- Thickness: 74.9 microns
- Thickness: 478 microns
- Thickness: 551 microns
- Thickness: 551 microns
$ 1596/MT
- Shear Modulus: 0.000370 GPa
- Adhesive Bond Strength: >= 2.40 MPa
- Thermal Conductivity: >= 1.20 W/m-K
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -56.6 °C
- Processing Temperature: 140 °C
$ 1595/MT
- Density: 1.57 g/cc
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 381 microns
$ 1938/MT
- Density: 1.60 g/cc
- Thickness: 127 microns
- Thickness: 1020 microns
- Hardness, Shore A: 72
- Tensile Strength: 4.83 MPa
$ 1555/MT
- Density: 1.24 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 889 microns
- Thickness: 889 microns
$ 1474/MT
- Density: 1.65 g/cc
- Water Absorption: 0.15 %
- Modulus of Elasticity: 20.7 GPa
- Poissons Ratio: 0.15
- Peel Strength: 1.24 kN/m
$ 1476/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 457 microns
$ 1504/MT
- Density: 2.30 g/cc
- Water Absorption: 0.040 %
- Tensile Strength: >= 138 MPa
- Compressive Modulus: >= 2.41 GPa
- Peel Strength: 2.10 kN/m
$ 2022/MT
- Density: 1.15 g/cc
- Thickness: 76.2 microns
- Thickness: 88.9 microns
- Thickness: 88.9 microns
- Thickness: 203 microns
$ 1844/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 2259/MT
- Thickness: 127 microns
- Thickness: 3180 microns
- Hardness, Shore A: 40
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
$ 1525/MT
- Thickness: 2160 microns
- Hardness, Shore A: 35 - 45
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
- Tear Strength: >= 35.1 kN/m
$ 1744/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 2105/MT
- Density: 1.25 g/cc
- Water Absorption: 1.0 %
- Thickness: 63.5 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1643/MT
- Density: 1.24 g/cc
- Thickness: 127 microns
- Thickness: 508 microns
- Hardness, Shore A: 44
- Tensile Strength: 7.58 MPa
$ 2382/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 152 microns
$ 1838/MT
- Density: 1.47 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
$ 1976/MT
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: >= 50.8 microns
- Thickness: 88.9 microns
- Thickness: 165 - 216 microns
$ 1449/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1520 microns
- Hardness, Shore A: 55
$ 1510/MT
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 305 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 53 - 63
$ 2218/MT
- Water Absorption: <= 3.0 % @Time 166000 sec
- Thickness: 1220 - 1320 microns
- Thickness: 36510 - 39690 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 1539/MT
- Density: 1.62 g/cc
- Hardness, Shore A: 74
- Tensile Strength: 5.79 MPa
- Elongation at Break: 130 %
- Tear Strength: 15.8 kN/m
$ 1869/MT
- Density: 1.33 g/cc
- Hardness, Shore A: 40 - 50
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 450 %
- Maximum Service Temperature, Air: 232 °C
$ 1536/MT
- Density: 1.62 g/cc
- Thickness: 165 microns
- Thickness: 178 microns
- Thickness: 406 microns
- Thickness: 749 microns
$ 2017/MT
- Thickness: >= 76.2 microns
- Thickness: >= 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 318 - 394 microns
$ 1856/MT
- Density: 1.25 g/cc
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 406 microns
- Thickness: 584 microns
$ 2064/MT
- Thickness: 76.2 microns
- Thickness: 508 microns
- Thickness: 508 microns
- Hardness, Shore A: 45
- Tensile Strength: 6.21 MPa
$ 1762/MT
- Hardness, Shore A: 50 - 60
- Tensile Strength, Ultimate: >= 7.90 MPa
- Elongation at Break: >= 500 %
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -56.6 °C
$ 1777/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 5.58 - 6.82 MPa
- Elongation at Break: 540 - 660 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1646/MT
- Density: 1.47 g/cc
- Thickness: 50.8 microns
- Thickness: 50.8 microns
- Thickness: 63.5 microns
- Thickness: 76.2 microns
$ 2414/MT
- Thickness: 76.2 microns
- Thickness: 965 - 1070 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 2449/MT
- Density: 2.30 g/cc
- Water Absorption: 0.040 %
- Peel Strength: 2.10 kN/m
- CTE, linear: 16.0 µm/m-°C
- CTE, linear: 16.0 µm/m-°C
$ 1573/MT
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 76.2 microns
- Thickness: 88.9 microns
- Thickness: 114 microns
$ 2097/MT
- Thickness: 635 microns
- Thickness: 813 microns
- Hardness, Shore A: 60
- Tensile Strength: 5.52 MPa
- Elongation at Break: 225 %
$ 2490/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 102 microns
- Thickness: 457 microns
- Thickness: 965 microns
$ 1757/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 203 microns
- Thickness: 406 microns
- Thickness: 610 microns
$ 2296/MT
- Density: 1.30 g/cc
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
$ 1587/MT
- Thickness: 127 microns
- Thickness: 762 microns
- Hardness, Shore A: 55
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 500 %
$ 2011/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 76.2 microns
$ 2235/MT
- Density: 1.45 g/cc
- Hardness, Shore A: 55
- Tensile Strength: 5.55 MPa
- Tensile Strength, Yield: 6.03 MPa @Strain <=1.00 %
- Elongation at Break: 400 %
$ 1715/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 88.9 microns
- Thickness: 88.9 microns
- Thickness: 203 microns
- Thickness: 381 microns
$ 1703/MT
- Density: 3.70 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 84
$ 2486/MT
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 279 microns
- Thickness: 305 microns
- Thickness: 711 - 864 microns
$ 1987/MT
- Thickness: 38.1 microns
- Thickness: 63.5 microns
- Thickness: >= 76.2 microns
- Thickness: >= 76.2 microns
- Thickness: 203 - 254 microns
$ 1708/MT
- Specific Gravity: 1.44 g/cc
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
- Thickness: 711 microns
$ 1965/MT
- Density: 1.20 g/cc
- Water Absorption: 1.1 %
- Thickness: 63.5 microns
- Thickness: 508 microns
- Hardness, Shore A: 55
$ 1988/MT
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 203 microns
$ 1532/MT
- Thickness: >= 76.2 microns
- Thickness: >= 178 microns
- Thickness: >= 203 microns
- Thickness: 343 - 419 microns
- Hardness, Shore A: 40 - 50
$ 1732/MT
- Density: 1.70 g/cc
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 88
- Tensile Strength: 4.41 MPa
$ 1473/MT
- Density: 1.20 g/cc
- Water Absorption: 0.10 %
- Thickness: 508 microns
- Hardness, Shore A: 46
- Tensile Strength: 9.846 MPa
$ 1608/MT
- Density: 1.62 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 229 microns
$ 1527/MT
- Density: 1.21 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 88.9 microns
- Thickness: 88.9 microns
$ 2019/MT
- Density: 1.45 g/cc
- Hardness, Shore A: 50 - 60
- Tensile Strength: >= 4.48 MPa
- Elongation at Break: >= 300 %
- Maximum Service Temperature, Air: 204 °C
$ 1677/MT
- Thickness: 12.7 microns
- Thickness: 50.8 microns
- Thickness: 76.2 microns
- Thickness: >= 203 microns
- Thickness: 457 microns
$ 1533/MT
- Density: 1.24 g/cc
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
$ 2360/MT
- Density: 1.33 g/cc
- Thickness: 63.5 microns
- Thickness: 152 microns
- Thickness: 203 microns
- Thickness: 406 microns
$ 1447/MT
- Density: 1.474 g/cc
- Hardness, Shore A: 60 - 70
- Tensile Strength: >= 5.52 MPa
- Elongation at Break: >= 150 %
- Maximum Service Temperature, Air: 232 °C
$ 1464/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 165 microns
- Thickness: 483 microns
$ 2400/MT
- Density: 2.90 g/cc
- Water Absorption: 0.020 %
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.020 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1814/MT
- Density: 1.35 g/cc
- Thickness: 127 microns
- Thickness: 1520 microns
- Hardness, Shore A: 60
- Tensile Strength: 5.52 MPa
$ 1590/MT
- Density: 2.23 g/cc
- Water Absorption: 0.020 %
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
- Outgassing - Total Mass Loss: 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C
$ 1846/MT
- Density: 1.20 g/cc
- Water Absorption: 2.1 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 1601/MT
- Thickness: 12.7 microns
- Thickness: 12.7 microns
- Thickness: 191 microns
- Thickness: 216 microns
- Hardness, Shore A: 30
$ 2212/MT
- Density: 1.15 g/cc
- Thickness: 25.4 microns
- Thickness: 152 microns
- Hardness, Shore A: 18
- Tensile Strength: 6.89 MPa
$ 1663/MT
- Specific Gravity: 1.36 g/cc
- Specific Gravity: 1.38 g/cc
- Thickness: 102 microns
- Thickness: 178 microns
- Thickness: 356 microns
$ 1671/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 343 - 419 microns
- Thickness: 343 - 419 microns
- Hardness, Shore A: 40 - 50
$ 2020/MT
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1551/MT
- Thickness: 63.5 microns
- Thickness: 127 microns
- Thickness: 267 microns
- Thickness: 406 microns
- Thickness: 800 microns
$ 1555/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 83.8 microns
- Thickness: 152 microns
$ 1558/MT
- Density: 1.26 g/cc
- Thickness: 102 microns
- Thickness: 178 microns
- Thickness: 457 microns
- Thickness: 737 microns
$ 1604/MT
- Density: 1.34 g/cc
- Density: 1.56 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 203 microns
$ 1752/MT
- Thickness: 76.2 microns
- Thickness: 152 microns
- Thickness: >= 178 microns
- Thickness: 356 microns
- Thickness: 660 - 762 microns
$ 1457/MT
- Thickness: 76.2 microns
- Thickness: 940 - 1090 microns
- Thickness: 17460 - 20640 microns
- Tensile Strength: >= 4.83 MPa
- Tensile Strength: >= 4.83 MPa
$ 1944/MT
- Density: 1.18 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1570 microns
- Hardness, Shore A: 50
$ 1473/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 5.58 - 6.82 MPa
- Elongation at Break: 540 - 660 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1494/MT
- Density: 1.12 g/cc
- Thickness: 74.9 microns
- Thickness: 480 microns
- Thickness: 551 microns
- Thickness: 551 microns
$ 1530/MT
- Density: 1.11 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 254 microns
- Thickness: 254 microns
$ 1980/MT
- Density: 1.18 g/cc
- Thickness: 25.4 microns
- Thickness: 25.4 microns
- Thickness: 152 microns
- Thickness: 203 microns
$ 2077/MT
- Density: 1.35 g/cc
- Thickness: <= 12.7 microns
- Thickness: 63.5 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
$ 1605/MT
- Density: 2.80 g/cc
- Thickness: 50.8 microns
- Thickness: 457 microns
- Thickness: 508 microns
- Hardness, Shore A: 77
$ 1930/MT
- Thickness: 76.2 microns
- Thickness: >= 152 microns
- Thickness: >= 152 microns
- Thickness: 203 microns
- Thickness: 457 - 559 microns
$ 2174/MT
- Density: 1.20 g/cc
- Water Absorption: 2.2 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 2367/MT
- Hardness, Shore A: 55 - 65
- Tensile Strength, Ultimate: >= 6.20 MPa
- Elongation at Break: >= 200 %
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -56.6 °C
$ 2058/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1520 microns
- Hardness, Shore A: 55
$ 1644/MT
- Density: 1.62 g/cc
- Thickness: 76.2 microns
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
$ 1834/MT
- Hardness, Shore A: 55 - 65
- Tensile Strength, Ultimate: >= 6.20 MPa
- Elongation at Break: >= 200 %
- Maximum Service Temperature, Air: 260 °C
- Minimum Service Temperature, Air: -56.6 °C
$ 2009/MT
- Density: 1.20 g/cc
- Thickness: 203 microns
- Thickness: 508 microns
- Hardness, Shore A: 50
- Tensile Strength: 9.65 MPa
$ 1609/MT
- Hardness, Shore A: 50 - 60
- Tensile Strength, Ultimate: 6.21 - 7.59 MPa
- Elongation at Break: 450 - 550 %
- Tear Strength: >= 35.1 kN/m
- Compression Set: 28 %
$ 1673/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 102 microns
- Thickness: 178 microns
- Thickness: 356 microns
$ 1770/MT
- Density: 1.30 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 381 microns
- Hardness, Shore A: 83
$ 1610/MT
- Density: 1.47 g/cc
- Hardness, Shore A: 55
- Tensile Strength: 4.83 MPa
- Elongation at Break: 550 %
- Poissons Ratio: 0.50
$ 1537/MT
- Thickness: 38.1 microns
- Thickness: >= 63.5 microns
- Thickness: >= 63.5 microns
- Thickness: 203 microns
- Thickness: 330 - 381 microns
$ 1444/MT
- Density: 1.33 g/cc
- Hardness, Shore A: 40 - 50
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 450 %
- Maximum Service Temperature, Air: 232 °C
$ 1673/MT
- Thickness: 38.1 microns
- Thickness: 127 microns
- Thickness: 229 - 279 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
$ 1927/MT
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: 305 microns
- Thickness: 457 - 559 microns
$ 2565/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 1810/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
$ 1671/MT
- Specific Gravity: 3.70 g/cc
- Thickness: 381 microns
- Hardness, Shore A: 84
- Tensile Strength, Ultimate: 3.34 MPa
- Elongation at Break: 60 %
$ 1519/MT
- Density: 1.25 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1880 microns
- Thickness: 2010 microns
$ 1471/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 102 microns
- Thickness: 165 microns
- Thickness: 483 microns
- Thickness: 749 microns
$ 1870/MT
- Hardness, Shore A: 50 - 60
- Tensile Strength, Ultimate: >= 6.90 MPa
- Elongation at Break: >= 450 %
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -56.6 °C
$ 2214/MT
- Density: 1.18 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1570 microns
- Thickness: 1570 microns
$ 1846/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 2.8 %
- Thickness: 508 microns
- Hardness, Shore A: 55
- Tensile Strength, Ultimate: 7.93 MPa
$ 1543/MT
- Density: 1.10 g/cc
- Density: 1.70 g/cc
- Thickness: 50.8 microns
- Thickness: 457 microns
- Thickness: 508 microns
$ 1741/MT
- Thickness: 38.1 microns
- Thickness: >= 102 microns
- Thickness: 127 microns
- Thickness: 229 - 279 microns
- Hardness, Shore A: 40 - 50
$ 1472/MT
- Density: 1.35 g/cc
- Thickness: 63.5 microns
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 406 microns
$ 1753/MT
- Thickness: 127 microns
- Thickness: 762 microns
- Hardness, Shore A: 45
- Tensile Strength: 6.21 MPa
- Elongation at Break: 600 %
$ 1688/MT
- Hardness, Shore A: 55 - 65
- Tensile Strength, Ultimate: >= 6.90 MPa
- Elongation at Break: 250 %
- Maximum Service Temperature, Air: 232 °C
- Minimum Service Temperature, Air: -56.6 °C
$ 2404/MT
- Specific Gravity: 1.25 g/cc
- Thickness: 140 microns
- Thickness: 419 microns
- Thickness: 457 microns
- Thickness: 1020 microns
$ 1522/MT
- Density: 1.26 g/cc
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 406 microns
- Thickness: 508 microns
$ 1656/MT
- Density: 1.15 g/cc
- Thickness: 25.4 microns
- Thickness: 38.1 microns
- Thickness: 203 microns
- Thickness: 267 microns
$ 1658/MT
- Density: 1.38 g/cc
- Thickness: 38.1 microns
- Thickness: 38.1 microns
- Thickness: 102 microns
- Thickness: 102 microns
$ 1536/MT
- Density: 1.24 g/cc
- Thickness: 19.0 microns
- Thickness: 19.0 microns
- Thickness: 38.1 microns
- Thickness: 203 microns
$ 1719/MT
- Density: 1.20 g/cc
- Water Absorption: 2.2 %
- Thickness: 76.2 microns
- Thickness: 1020 microns
- Hardness, Shore A: 55
$ 2564/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 47
- Tensile Strength: 5.17 MPa
- Elongation at Break: 450 %
- Maximum Service Temperature, Inert: 232 °C
$ 1952/MT
- Thickness: 152 microns
- Thickness: 152 microns
- Thickness: 203 microns
- Thickness: 508 microns
- Hardness, Shore A: 45
$ 1641/MT
- Density: 1.20 g/cc
- Thickness: 203 microns
- Thickness: 305 microns
- Thickness: 508 microns
- Hardness, Shore A: 62
$ 1612/MT
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: >= 152 microns
- Thickness: 457 microns
- Thickness: 737 - 813 microns
$ 1670/MT
- Specific Gravity: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 229 microns
- Thickness: 508 microns
$ 1982/MT
- Density: 2.07 g/cc
- Water Absorption: 0.060 %
- Tensile Strength: 40.7 MPa
- Tensile Strength: 52.4 MPa
- Modulus of Elasticity: 3.86 GPa
$ 1923/MT
- Thickness: 76.2 microns
- Thickness: 229 - 381 microns
- Thickness: 23810 - 26990 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
$ 2093/MT
- Density: 1.22 g/cc
- Thickness: 127 microns
- Thickness: 508 microns
- Thickness: 635 microns
- Hardness, Shore A: 45
$ 1659/MT
- Thickness: 2290 microns
- Hardness, Shore A: 35 - 45
- Tensile Strength: >= 6.89 MPa
- Elongation at Break: >= 700 %
- Tear Strength: >= 35.1 kN/m
$ 2004/MT
- Density: 1.20 g/cc
- Thickness: 25.4 microns
- Thickness: 203 microns
- Thickness: 381 microns
- Thickness: 25400 microns
$ 2023/MT
- Density: 1.35 g/cc
- Thickness: 76.2 microns
- Thickness: 1570 microns
- Thickness: 1570 microns
- Hardness, Shore A: 60
$ 2106/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 343 - 419 microns
- Thickness: 343 - 419 microns
- Hardness, Shore A: 40 - 50
$ 1722/MT
- Density: 1.22 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
$ 1501/MT
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: 432 microns
- Thickness: >= 584 microns
- Thickness: 1120 - 1190 microns
$ 1465/MT
- Density: 1.27 g/cc
- Density: 2.70 g/cc
- Thickness: 102 microns
- Thickness: 305 microns
- Thickness: 660 microns
$ 2208/MT
- Thickness: 50.8 microns
- Thickness: 127 microns
- Thickness: 203 microns
- Thickness: 381 microns
- Hardness, Shore A: 58
$ 1502/MT
- Density: 1.34 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 254 microns
$ 1483/MT
- Density: 1.32 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 229 microns
- Thickness: 381 microns
$ 1626/MT
- Density: 2.80 g/cc
- Thickness: 63.5 microns
- Thickness: 203 microns
- Thickness: 305 microns
- Thickness: 508 microns
$ 1687/MT
- Thickness: 76.2 microns
- Thickness: 63.5 - 140 microns
- Thickness: 140 - 216 microns
- Thickness: 356 microns
- Thickness: 597 - 673 microns
$ 1894/MT
- Density: 1.19 g/cc
- Thickness: 63.5 microns
- Thickness: 1270 microns
- Hardness, Shore A: 70
- Tensile Strength: 4.83 MPa
$ 2022/MT
- Density: 1.22 g/cc
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 1020 microns
- Thickness: 1020 microns
$ 1646/MT
- Density: 1.24 g/cc
- Thickness: 38.1 microns
- Thickness: 76.2 microns
- Thickness: 292 microns
- Thickness: 483 microns
$ 1452/MT
- Density: 1.60 g/cc
- Thickness: 127 microns
- Thickness: 1520 microns
- Hardness, Shore A: 72
- Tensile Strength: 4.83 MPa
$ 1775/MT
- Thickness: 76.2 microns
- Thickness: 457 microns
- Thickness: 546 microns
- Thickness: 546 microns
- Thickness: 1520 microns
$ 1592/MT
- Density: 2.60 g/cc
- Thickness: 203 microns
- Hardness, Shore A: 57
- Tensile Strength: 2.28 MPa
- Elongation at Break: 170 %
$ 1608/MT
- Density: 1.09 g/cc
- Thickness: 74.9 microns
- Thickness: 210 microns
- Thickness: 290 microns
- Thickness: 290 microns
$ 1707/MT
- Thickness: 38.1 - 114 microns
- Thickness: 76.2 microns
- Thickness: 102 microns
- Thickness: 88.9 - 165 microns
- Thickness: 267 - 343 microns
$ 1504/MT
- Thickness: 1450 - 1600 microns
- Thickness: 36510 - 39690 microns
- Tensile Strength: >= 4.83 MPa
- Elongation at Break: >= 300 %
- Maximum Service Temperature, Air: 204 °C
$ 1668/MT
- Density: 1.19 g/cc
- Thickness: 76.2 microns
- Thickness: 508 microns
- Hardness, Shore A: 70
- Tensile Strength: 4.83 MPa
$ 1840/MT
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 5.58 - 6.82 MPa
- Elongation at Break: 540 - 660 %
- Maximum Service Temperature, Air: 200 °C
- Maximum Service Temperature, Air: 232 °C
$ 1853/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 381 microns
- Thickness: 457 - 559 microns
- Hardness, Shore A: 55 - 65
$ 2160/MT
- Density: 1.11 g/cc
- Thickness: 76.2 microns
- Thickness: 457 microns
- Hardness, Shore A: 40
- Tensile Strength: 8.62 MPa
$ 2456/MT
- Density: 1.20 g/cc
- Water Absorption: 1.0 %
- Thickness: 1020 microns
- Hardness, Shore A: 60
- Tensile Strength: 10.0 MPa
$ 1829/MT
- Density: 1.25 g/cc
- Thickness: 76.2 microns
- Thickness: 305 microns
- Thickness: 457 microns
- Thickness: 762 microns
$ 2066/MT
- Thickness: 76.2 microns
- Thickness: 305 microns
- Thickness: 457 microns
- Thickness: 686 - 838 microns
- Hardness, Shore A: 40 - 50
$ 2378/MT
- Density: 2.40 g/cc
- Water Absorption: 0.060 %
- Peel Strength: 2.98 kN/m
- CTE, linear: 12.0 µm/m-°C
- CTE, linear: 15.0 µm/m-°C
$ 1590/MT
- Thickness: 76.2 microns
- Thickness: 127 microns
- Thickness: 127 microns
- Thickness: 203 microns
- Thickness: 457 microns
$ 1893/MT
- Density: 1.20 g/cc
- Thickness: 508 microns
- Hardness, Shore A: 55
- Tensile Strength: 11.40 MPa
- Elongation at Break: 519 %
$ 1683/MT
- Thickness: 76.2 microns
- Thickness: 1370 - 1680 microns
- Thickness: 1370 - 1680 microns
- Hardness, Shore A: 35 - 45
- Tensile Strength: >= 6.89 MPa
$ 1656/MT
- Thickness: 76.2 microns
- Thickness: >= 127 microns
- Thickness: >= 178 microns
- Thickness: 457 microns
- Thickness: 762 - 838 microns
$ 1680/MT
- Thickness: 76.2 microns
- Thickness: >= 88.9 microns
- Thickness: >= 88.9 microns
- Thickness: 203 microns
- Thickness: 343 - 419 microns
$ 1444/MT
- Density: 1.34 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Thickness: 241 microns
$ 1720/MT
- Density: 2.40 g/cc
- Thickness: 25.4 microns
- Thickness: 76.2 microns
- Thickness: 203 microns
- Hardness, Shore A: 50
$ 2596/MT
- Density: 1.35 g/cc
- Thickness: 152 microns
- Thickness: 203 microns
- Thickness: 914 microns
- Thickness: 1270 microns
$ 1540/MT
- Density: 1.20 g/cc
- Thickness: 76.2 microns
- Thickness: 76.2 microns
- Thickness: 140 microns
- Thickness: 305 microns
Delivery Polymer Arlon
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.