$ 1961/MT
- Density: 0.868 g/cc
- Mooney Viscosity: 35 @Temperature 121 °C
- Melt Index of Compound: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Hardness, Shore D: 20
$ 2400/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 1478/MT
- Density: 1.234 g/cc
- Viscosity: 50 cP
- Viscosity Measurement: <= 5.0
- Molecular Weight: 290 g/mol
- Vapor Pressure: <= 1.30e-8 bar
$ 2155/MT
- Density: 0.923 g/cc
- Thickness: 76.0 microns
- Melt Flow: 0.22 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1520/MT
- Density: 0.924 g/cc
- ESCR 100% Igepal®: 20 hour @Temperature 50.0 °C
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 7.58 MPa
$ 1553/MT
- Density: 1.08 g/cc
- Solids Content: 57 %
- Particle Size: 1.25 µm
- pH: 7.0
- Brookfield Viscosity: 300 cP
$ 1571/MT
- Density: 0.900 g/cc
- Thickness: 25.4 microns
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 31.5 MPa
- Film Tensile Strength at Yield, TD: 30.4 MPa
$ 2034/MT
- Density: 0.870 g/cc
- Melt Index of Compound: 30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 72
- Hardness, Shore D: 20
- Tensile Strength, Ultimate: 3.30 MPa
$ 2351/MT
- Density: 0.926 g/cc
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 14.0 MPa
- Film Tensile Strength at Yield, TD: 15.0 MPa
- Film Elongation at Break, MD: 615 %
$ 1665/MT
- Density: 0.922 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 3000 ppm
- Slip Level: 1200 ppm
$ 2081/MT
- Density: 0.952 g/cc
- Melt Index of Compound: 66 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 59
- Tensile Strength at Break: 28.3 MPa
- Tensile Strength, Yield: 17.2 MPa
$ 2440/MT
- Density: 0.857 - 0.913 g/cc
- Melt Flow: 0.50 - 30 g/10 min
- Hardness, Shore A: 50 - 95
- Tensile Strength, Ultimate: 4.00 - 35.0 MPa
- Elongation at Break: >= 700 %
$ 1727/MT
- Density: 0.932 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 17.4 MPa
- Tensile Strength, Yield: 8.50 MPa
- Elongation at Break: 520 %
- Vicat Softening Point: 85.0 °C
$ 1650/MT
- Viscosity Measurement: 2.5 @Temperature 160 °C
- Viscosity Measurement: 4.5 @Temperature 160 °C
- Viscosity Measurement: 9.0 @Temperature 160 °C
- Viscosity Measurement: 14.5 @Temperature 160 °C
- Viscosity Measurement: 16 @Temperature 160 °C
$ 1820/MT
- Density: 0.935 g/cc
- Viscosity: 37000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 64000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 79000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 40 g/10 min @Load 2.16 kg
$ 2245/MT
- Density: 0.923 g/cc
- Viscosity: 40000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 93000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 161000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 7.0 g/10 min @Load 2.16 kg
$ 2228/MT
- Density: 0.8965 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.6 g/10 min
- Film Tensile Strength at Yield, MD: 5.79 MPa
- Film Tensile Strength at Yield, TD: 6.34 MPa
$ 2296/MT
- Density: 0.9534 g/cc
- ESCR 100% Igepal®: 50 hour @Temperature 50.0 °C
- High Load Melt Index: 23 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 59
$ 2174/MT
- Density: 0.911 g/cc
- Thickness: >= 6.35 microns
- Melt Index of Compound: 6.0 g/10 min
- Neck In: 11.4 cm
- Coating Weight: >= 6.08 g/m²
$ 2367/MT
- Density: 0.915 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.96 MPa
- Film Tensile Strength at Yield, TD: 8.41 MPa
$ 1763/MT
- Density: 0.919 g/cc
- Viscosity: 82000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 300000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 6.0 g/10 min @Load 2.16 kg
$ 2321/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.9 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1020 MPa
$ 2233/MT
- Water Vapor Transmission: 1.94 g/m²/day
- Oxygen Transmission: 0.571 cc-mm/m²-24hr-atm
- Thickness: 50.8 microns
- Film Elongation at Break, MD: 95 %
- Film Elongation at Break, TD: 80 %
$ 1840/MT
- Density: 0.918 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 15.98 MPa
- Film Tensile Strength at Yield, TD: 15.42 MPa
$ 1682/MT
- Density: 0.917 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 8.80 MPa
- Film Elongation at Break, MD: 460 %
$ 1664/MT
- Density: 0.885 g/cc
- Viscosity: 910000 cP @Shear Rate 100 1/s, Temperature 190 °C
- Viscosity: 2.26e+6 cP @Shear Rate 10.0 1/s, Temperature 190 °C
- Viscosity: 4.06e+6 cP @Shear Rate 1.58 1/s, Temperature 190 °C
- Viscosity: 7.01e+6 cP @Shear Rate 0.100 1/s, Temperature 190 °C
$ 1819/MT
- Viscosity Measurement: 96
- Thickness: 1.80 - 3.60 microns
- Tensile Strength, Ultimate: 78.0 - 96.0 MPa
- Elongation at Break: 5.5 - 10.5 %
- Tensile Modulus: 2.70 - 3.10 GPa
$ 1875/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0055 cm/cm
- Tensile Strength, Ultimate: 15.9 MPa
- Tensile Strength, Yield: 22.1 MPa
- Elongation at Break: 40 %
$ 1451/MT
- Density: 0.916 g/cc
- Viscosity: 34000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 76000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 130000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 8.0 g/10 min @Load 2.16 kg
$ 1608/MT
- Water Vapor Transmission: 7.20 g/m²/day
- Oxygen Transmission: 0.512 cc-mm/m²-24hr-atm
- Thickness: 19.0 microns
- Film Elongation at Break, MD: 80 %
- Film Elongation at Break, TD: 75 %
$ 2248/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.47 g/10 min
- Film Tensile Strength at Yield, MD: 13.30 MPa
- Film Tensile Strength at Yield, TD: 10.73 MPa
$ 1762/MT
- Density: 1.05 g/cc
- Melt Flow: 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Yield: 43.0 MPa
- Tensile Modulus: 2.21 GPa
- Izod Impact, Notched: 1.81 J/cm
$ 1505/MT
- Density: 0.926 g/cc
- ESCR 100% Igepal®: 10 hour @Temperature 50.0 °C
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 51
- Tensile Strength at Break: 7.58 MPa
$ 1531/MT
- Density: 1.10 g/cc
- Brookfield Viscosity: 3500 cP
- Flash Point: >= 110 °C
$ 1473/MT
- Density: 0.963 g/cc
- Thickness: 25.0 microns
- Melt Flow: 5.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 27.5 MPa
- Film Tensile Strength at Yield, TD: 28.3 MPa
$ 1520/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 103
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Yield: 7.0 %
$ 2145/MT
- Specific Gravity: 1.167 - 1.182 g/cc
- Viscosity: 250 - 350 cP
- Maximum Moisture Content: 0.050
- ASTM Color: 0.00 - 100
- Acid Value: 0.00 - 0.10
$ 1506/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 106
- Tensile Strength, Yield: 35.2 MPa
- Elongation at Yield: 7.0 %
$ 1668/MT
- Density: 0.917 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.85 g/10 min
- Film Tensile Strength at Yield, MD: 9.218 MPa
- Film Tensile Strength at Yield, TD: 9.501 MPa
$ 2346/MT
- Density: 1.06 g/cc
- Melt Flow: 5.7 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Yield: 36.0 MPa
- Tensile Modulus: 2.02 GPa
- Izod Impact, Notched: 1.39 J/cm
$ 1861/MT
- Density: 1.13 g/cc
- Melt Index of Compound: 0.45 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 4.0 %
- Flexural Modulus: 2.00 GPa
$ 1912/MT
- Density: 0.902 g/cc
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 94
- Hardness, Shore D: 45
- Tensile Strength, Ultimate: 25.8 MPa
$ 2506/MT
- Specific Gravity: 1.031 g/cc
- Viscosity Measure: 1060 cSt @Temperature 25.0 °C
- Pour Point: -9.44 °C
- Flash Point: >= 163 °C
$ 1967/MT
- Density: 1.28 - 1.34 g/cc
- Solids Content: >= 99 %
- Viscosity: 350000 cP @Shear Rate 1.00 1/s, Temperature 23.0 °C
- Tensile Strength, Ultimate: 13.0 MPa
- Elongation at Break: 11 %
$ 1738/MT
- Density: 0.913 g/cc
- Moisture Vapor Transmission: 0.0300 cc-mm/m²-24hr-atm
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Coefficient of Friction: 0.14
$ 1475/MT
- Mooney Viscosity: 120 @Temperature 100 °C
- Hardness, Shore A: 63
- Tensile Strength, Ultimate: 15.9 MPa
- Elongation at Break: 226 %
- 50% Modulus: 0.00170 GPa
$ 1495/MT
- Bulk Density: 0.880 g/cc
- Viscosity Measurement: 0.74 - 0.78
- Viscosity Measurement: 88
- Crystallinity: >= 50 %
- Melting Point: 247 °C
$ 1777/MT
- Viscosity Measurement: 1100
- Thickness: 7.00 - 14.0 microns
- Tensile Strength, Ultimate: 78.0 - 96.0 MPa
- Elongation at Break: 5.5 - 10.5 %
- Tensile Modulus: 2.70 - 3.10 GPa
$ 1686/MT
- Density: 0.884 g/cc
- High Load Melt Index: 4.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 83
- Hardness, Shore A: 83
$ 2460/MT
- Specific Gravity: 1.28 g/cc
- Viscosity: 200 cP
- Acid Value: 50
- Isocyanate Equivalent Weight: 134.6
- NCO Content wt%: 31.2
$ 2248/MT
- Density: 0.948 g/cc
- Viscosity: 47000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 87000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 132000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 42 g/10 min @Load 2.16 kg
$ 1768/MT
- Density: 1.01 g/cc
- Solids Content: >= 100 %
- Viscosity: 200 cP @Temperature 25.0 °C
- Flash Point: >= 149 °C
$ 2462/MT
- Density: 0.947 g/cc
- Melt Flow: 42 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.3 MPa
- Tensile Strength, Yield: 17.2 MPa
- Elongation at Break: 300 %
$ 1632/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Yield: 11 %
- Flexural Modulus, 1% Secant: 1070 MPa
$ 1453/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1902/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.9 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1020 MPa
$ 1605/MT
- Density: 0.916 g/cc
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 20.0 MPa
- Film Tensile Strength at Yield, MD: 7.60 MPa
- Film Tensile Strength at Yield, TD: 6.90 MPa
$ 1644/MT
- Water Absorption: 0.24 %
- Thickness: 1.045 microns
- Thickness: 0.890 - 1.25 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1733/MT
- Density: 0.924 g/cc
- ESCR 100% Igepal®: 20 hour @Temperature 50.0 °C
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 7.58 MPa
$ 2057/MT
- Density: 0.864 g/cc
- Mooney Viscosity: 5.8 @Temperature 100 °C
- Melt Index of Compound: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 60
- Tensile Strength, Ultimate: 2.00 MPa
$ 1855/MT
- Water Absorption: 0.24 %
- Thickness: 0.360 microns
- Thickness: 0.305 - 0.440 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1877/MT
- Density: 0.0350 g/cc
- Water Absorption: 9.0 %
- Compressive Yield Strength: 0.500 MPa
- CTE, linear: 70.0 µm/m-°C @Temperature 20.0 °C
- Thermal Conductivity: 0.0270 W/m-K
$ 1816/MT
- Density: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1746/MT
- Density: 1.13 g/cc
- Melt Flow: 0.45 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 19.3 MPa
- Elongation at Yield: 4.0 %
- Flexural Modulus: 2.00 GPa
$ 2156/MT
- Density: 1.07 g/cc
- Solids Content: 55 %
- Particle Size: 2.8 µm
- pH: 6.8
- Brookfield Viscosity: 225 cP
- Glass Transition Temp, Tg: 8.80 °C
$ 1526/MT
- Moisture Vapor Transmission: 1.80 cc-mm/m²-24hr-atm
- Oxygen Transmission: 32.0 cc-mm/m²-24hr-atm
- Viscosity Measurement: 17000
- Tensile Strength, Ultimate: 23.0 MPa
- Elongation at Break: 425 %
$ 1450/MT
- Specific Gravity: 1.043 g/cc
- Solids Content: 25.9 - 27.1 %
- Viscosity: 1900 - 2900 cP
- Maximum Moisture Content: 0.070
- Flash Point: >= 180 °C
- Hydroxyl Number mg KOH/g: 24.1 - 28.2
$ 1875/MT
- Melt Flow: 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Ultimate: 29.0 MPa
- Tensile Strength, Yield: 30.3 MPa
- Elongation at Break: 20 %
- Izod Impact, Notched: 1.07 J/cm
$ 1715/MT
- Density: 0.938 g/cc
- Thickness: 60.0 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 24.7 MPa
- Film Tensile Strength at Yield, MD: 8.60 MPa
$ 1795/MT
- Density: 0.0400 g/cc
- Compressive Strength: 0.117 MPa
- Compressive Strength: 0.138 MPa
- Compressive Strength: 0.317 MPa
- Compressive Modulus: 0.00130 GPa
$ 1907/MT
- Density: 0.923 g/cc
- Viscosity: 21000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 32000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 40000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 55 g/10 min @Load 2.16 kg
$ 1560/MT
- Density: 0.930 g/cc
- Viscosity: 23000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 50000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 77000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 150 g/10 min @Load 2.16 kg
$ 1488/MT
- Density: 0.900 g/cc
- Melt Flow: 5.0 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 11 %
- Flexural Modulus: 0.550 GPa
$ 1679/MT
- Moisture Vapor Transmission: 1.80 cc-mm/m²-24hr-atm
- Oxygen Transmission: 32.0 cc-mm/m²-24hr-atm
- Viscosity Measurement: 8000
- Tensile Strength, Ultimate: 23.0 MPa
- Elongation at Break: 425 %
$ 2085/MT
- Density: 0.920 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 10.31 MPa
- Film Tensile Strength at Yield, TD: 11.16 MPa
$ 2518/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 11 %
- Flexural Modulus, 1% Secant: 550 MPa
$ 2469/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.8 MPa
- Film Tensile Strength at Yield, TD: 11.6 MPa
$ 1678/MT
- Viscosity Measurement: 1950
- Thickness: 15.0 - 30.0 microns
- Tensile Strength, Ultimate: 78.0 - 96.0 MPa
- Elongation at Break: 5.5 - 10.5 %
- Tensile Modulus: 2.70 - 3.10 GPa
$ 2038/MT
- Density: 1.24 g/cc
- Solids Content: >= 98.8 %
- Viscosity: 165 cP @Temperature 25.0 °C
- Flash Point: >= 149 °C
$ 1466/MT
- Density: 0.870 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 72
- Tensile Strength at Break: 1.30 MPa
- Elongation at Break: >= 1000 %
$ 1527/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.6 MPa
- Izod Impact, Notched: 0.694 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 115 °C
$ 2168/MT
- Density: 0.8985 g/cc
- Filler Content: 0.50 - 1.0 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 87
- Hardness, Shore A: 90
$ 2420/MT
- Mooney Viscosity: >= 51 @Temperature 121 °C
- Hardness, Shore A: 72
- Tensile Strength, Ultimate: 22.7 MPa
- Elongation at Break: 320 %
- 200% Modulus: 0.0128 GPa
$ 1507/MT
- Specific Gravity: 1.07 g/cc
- pH: 4.5 - 6.5
- Viscosity Measure: 225 - 260 cSt @Temperature 25.0 °C
- Molecular Weight: 700 g/mol
- Maximum Moisture Content: 0.050
$ 1565/MT
- Specific Gravity: 1.02 g/cc
- Viscosity Measure: 62 cSt @Temperature 98.9 °C
- Viscosity Measure: 410 cSt @Temperature 37.8 °C
- Viscosity Measure: 790 cSt @Temperature 25.0 °C
- Maximum Moisture Content: 0.050
$ 1752/MT
- Specific Gravity: 1.019 g/cc
- Viscosity Measure: 61 cSt @Temperature 98.9 °C
- Viscosity Measure: 435 cSt @Temperature 37.8 °C
- Viscosity Measure: 860 cSt @Temperature 25.0 °C
- Viscosity Measure: 4500 cSt @Temperature 0.000 °C
$ 1885/MT
- Density: 0.870 g/cc
- Melt Index of Compound: <= 2.0 g/10 min @Load 2.00 kg, Temperature 190 °C
- Melt Index of Compound: 22.5 g/10 min @Load 10.0 kg, Temperature 190 °C
- Hardness, Shore A: 68
- Tensile Strength, Ultimate: 7.20 MPa
$ 2245/MT
- Density: 1.16 g/cc
- Volatiles: <= 0.50 %
- Mooney Viscosity: 80 @Temperature 121 °C
- Chlorine Content: 36 %
$ 2062/MT
- Density: 1.08 g/cc
- Solids Content: 56.5 %
- Particle Size: 1.45 µm
- pH: 7.5
- Brookfield Viscosity: 480 cP
$ 1731/MT
- Water Absorption: <= 0.20 %
- Viscosity Measure: 14 cSt @Temperature 25.0 °C
- Thickness: 1.00 - 2.40 microns
- Tensile Strength, Ultimate: 80.0 - 94.0 MPa
- Elongation at Break: 5.5 - 10.5 %
$ 1777/MT
- Density: 0.897 g/cc
- Melt Index of Compound: 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 92
- Hardness, Shore D: 41
- Tensile Strength, Ultimate: 24.5 MPa
$ 2469/MT
- Density: 0.902 g/cc
- Thickness: 3180 microns
- Melt Flow: 30 g/10 min
- Slip Level: 600 ppm
- Tensile Strength, Ultimate: 9.142 MPa
$ 2070/MT
- Density: 0.880 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 45 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 0.5 mass%
$ 1474/MT
- Density: 0.863 g/cc
- Mooney Viscosity: 35 @Temperature 121 °C
- Melt Index of Compound: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 66
- Hardness, Shore D: 16
$ 1623/MT
- Density: 0.916 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.3 MPa
- Tensile Strength, Yield: 9.00 MPa
- Elongation at Break: 600 %
$ 1814/MT
- Specific Gravity: 1.026 g/cc
- pH: 7.0 - 9.0
- Viscosity Measure: 434 cSt @Temperature 37.8 °C
- Viscosity Measure: 750 - 870 cSt @Temperature 25.0 °C
- Molecular Weight: 4700 g/mol
$ 1840/MT
- Mold Temperature: 54.4 - 65.6 °C
- Injection Pressure: 6.89 - 10.3 MPa
- Gel Time: 0.167 - 0.200 min
$ 1517/MT
- Density: 0.886 g/cc
- High Load Melt Index: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 82
- Hardness, Shore A: 85
$ 1722/MT
- Density: 0.932 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 3500 ppm
- Slip Level: 1200 ppm
$ 1528/MT
- Density: 0.917 g/cc
- Thickness: 20.3 microns
- Melt Flow: 2.3 g/10 min
- Film Tensile Strength at Yield, MD: 8.791 MPa
- Film Tensile Strength at Yield, TD: 8.163 MPa
$ 2342/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Elmendorf Tear Strength MD: 385 g
- Elmendorf Tear Strength TD: 499 g
$ 1958/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 6.90 MPa
- Film Tensile Strength at Yield, TD: 6.20 MPa
$ 1535/MT
- Water Absorption: 0.24 %
- Thickness: 0.820 microns
- Thickness: 0.720 - 1.02 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1508/MT
- Specific Gravity: 1.072 g/cc
- Viscosity Measure: 200 cSt @Temperature 55.0 °C
- Molecular Weight: 540 g/mol
- Maximum Moisture Content: 0.030
- Melting Point: 15.0 - 20.0 °C
$ 1719/MT
- Density: 0.900 g/cc
- Melt Flow: 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.8 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus: 1.72 GPa
$ 1515/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 13.1 MPa
- Film Tensile Strength at Yield, MD: 7.60 MPa
$ 1653/MT
- Density: 0.935 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 15.23 MPa
- Film Tensile Strength at Yield, TD: 16.72 MPa
$ 1583/MT
- Density: 0.920 g/cc
- High Load Melt Index: 52 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 121 °C
$ 1672/MT
- Density: 1.064 g/cc
- Hardness, Shore A: 74
- Tensile Strength, Ultimate: 26.1 MPa
- Elongation at Break: 266 %
- 100% Modulus: 0.00560 GPa
$ 1476/MT
- Mooney Viscosity: 74 @Temperature 100 °C
- Hardness, Shore A: 69
- Tensile Strength, Ultimate: 9.50 MPa
- Elongation at Break: 383 %
- 50% Modulus: 0.00190 GPa
$ 2354/MT
- Viscosity Measurement: 72
- Ash: 0.030 %
- Collected Volatile Condensable Material: 0.20 %
- Storage Temperature: <= 30.0 °C
- ASTM Color: 5.0
$ 1636/MT
- Density: 0.870 g/cc
- Mooney Viscosity: 23 @Temperature 121 °C
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Hardness, Shore D: 22
$ 1460/MT
- Water Vapor Transmission: 8.70 g/m²/day
- Oxygen Transmission: 0.472 cc-mm/m²-24hr-atm
- Nitrogen Transmission: 0.0709 cc-mm/m²-24hr-atm
- Carbon Dioxide Transmission: 2.13 cc-mm/m²-24hr-atm
- Thickness: 12.7 microns
$ 2168/MT
- Viscosity Measurement: 6.8 @Temperature 160 °C
- Viscosity Measurement: 10.1 @Temperature 160 °C
- Viscosity Measurement: 10.2 @Temperature 160 °C
- Viscosity Measurement: 13.3 @Temperature 160 °C
- Viscosity Measurement: 40 @Temperature 160 °C
$ 1925/MT
- Density: 0.880 g/cc
- Melt Index of Compound: 18 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 81
- Hardness, Shore D: 22
- Tensile Strength, Ultimate: 6.50 MPa
$ 1674/MT
- Density: 0.868 g/cc
- Mooney Viscosity: 37 @Temperature 121 °C
- Melt Flow: 0.50 g/10 min
- Hardness, Shore A: 72
- Tensile Strength, Ultimate: 8.96 MPa
$ 2361/MT
- Density: 0.895 g/cc
- Melt Flow: 1.6 g/10 min @Load 2.16 kg
- Hardness, Shore D: 89
- Tensile Strength, Ultimate: 43.4 MPa
- Tensile Strength, Yield: 5.20 MPa
$ 1450/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 6.90 MPa
- Film Tensile Strength at Yield, TD: 6.20 MPa
$ 2006/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 6.90 MPa
- Film Tensile Strength at Yield, TD: 6.20 MPa
$ 1511/MT
- Density: 0.926 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.9 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.0 MPa
- Film Tensile Strength at Yield, MD: 12.4 MPa
$ 1796/MT
- Density: 1.234 g/cc
- Viscosity: 70 cP
- Molecular Weight: 300 g/mol
- Vapor Pressure: <= 1.33e-8 bar
- Storage Temperature: 24.0 - 38.0 °C
$ 1467/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1617/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1676/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1547/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1661/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 2105/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1736/MT
- Density: 0.900 g/cc
- Melt Flow: 3.4 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus: 1.31 GPa
$ 1456/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 60 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1792/MT
- Density: 0.922 g/cc
- Thickness: 30.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1637/MT
- Density: 0.911 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 9.65 MPa
$ 1716/MT
- Density: 0.0640 g/cc
- Compressive Strength: 0.290 MPa
- Compressive Strength: 0.331 MPa
- Compressive Strength: 0.669 MPa
- Compressive Modulus: 0.01362 GPa
$ 1452/MT
- Density: 0.954 g/cc
- Viscosity: 90000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 220000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 360000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 7.0 g/10 min @Load 2.16 kg
$ 2539/MT
- Density: 0.863 g/cc
- Viscosity: 1.11e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Viscosity: 2.36e+6 cP @Shear Rate 10.0 1/s, Temperature 190 °C
- Viscosity: 3.35e+6 cP @Shear Rate 1.58 1/s, Temperature 190 °C
- Viscosity: 4.14e+6 cP @Shear Rate 0.100 1/s, Temperature 190 °C
$ 2148/MT
- Specific Gravity: 1.065 g/cc
- pH: 6.5 - 8.0
- pH: 7.5
- Viscosity Measure: 300 - 360 cSt @Temperature 25.0 °C
- Molecular Weight: 450 g/mol
$ 2382/MT
- Solids Content: 51.5 - 52.5 %
- Particle Mesh Size: 100 Mesh
- Particle Mesh Size: 325 Mesh
- pH: 7.7 - 8.3
- Brookfield Viscosity: <= 300 cP
$ 1474/MT
- Density: 0.912 g/cc
- Thickness: 38.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Elmendorf Tear Strength MD: 650 g
- Elmendorf Tear Strength TD: 826 g
$ 1880/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 1525/MT
- Density: 0.870 g/cc
- Mooney Viscosity: 23.6 @Temperature 121 °C
- Melt Flow: 1.0 g/10 min
- Hardness, Shore A: 74
- Tensile Strength, Ultimate: 10.60 MPa
$ 1970/MT
- Density: 0.0800 g/cc
- Water Absorption: 2.5 %
- Compressive Strength: 0.586 MPa
- Shrinkage: 1.00 % @Temperature 37.8 °C, Time 605000 sec
- Shrinkage: 2.00 % @Temperature 121 °C, Time 173000 sec
$ 2012/MT
- Density: 0.956 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 11.0 MPa
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Break: 440 %
$ 1751/MT
- Melt Flow: 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Ultimate: 17.9 MPa
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Break: 30 %
- Izod Impact, Notched: 0.534 J/cm
$ 1677/MT
- Density: 0.958 g/cc
- Melt Flow: 13.8 g/10 min @Load 2.16 kg, Temperature 125 °C
- Melt Index of Compound: 300 g/10 min @Load 2.16 kg, Temperature 125 °C
- Hardness, Shore D: 50
- Tensile Strength at Break: 9.65 MPa
$ 1581/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.2 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus, 1% Secant: 1590 MPa
$ 1676/MT
- Density: 0.928 g/cc
- Thickness: 38.0 microns
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 13.0 MPa
- Film Tensile Strength at Yield, TD: 15.0 MPa
$ 1836/MT
- Water Absorption: 0.24 %
- Thickness: 1.50 microns
- Thickness: 1.30 - 1.84 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1865/MT
- Density: 0.980 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 130 @Temperature 125 °C
- Carbon Black Content (N650): 30 phr
- ENB: 4.9 mass%
- Ethylene: 67 mass%
$ 1623/MT
- Water Vapor Transmission: 62.1 g/m²/day
- Thickness: 50.8 microns
- Secant Modulus, MD: 0.138 GPa
- Secant Modulus, TD: 0.145 GPa
- Elmendorf Tear Strength, MD: 5.12 g/micron
$ 1526/MT
- Density: 0.9525 g/cc
- Environmental Stress Crack Resistance: 48 hour
- High Load Melt Index: 21 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 62
$ 1608/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 8.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 69.0 MPa
- Tensile Strength, Yield: 69.0 MPa
$ 1870/MT
- Density: 0.905 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.50 g/10 min
- Film Tensile Strength at Yield, MD: 10.0 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1761/MT
- Thickness: 50.8 microns
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 8.27 MPa
- Film Elongation at Break, MD: 200 %
- Film Elongation at Break, TD: 400 %
$ 1726/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 13.1 MPa
- Film Tensile Strength at Yield, MD: 7.60 MPa
$ 2293/MT
- Water Absorption: 0.24 %
- Thickness: 0.130 microns
- Thickness: 0.110 - 0.170 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1467/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 6.0 %
- Flexural Modulus, 1% Secant: 1030 MPa
$ 2021/MT
- Density: 0.949 g/cc
- High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Break: 800 %
- Flexural Modulus: 1.17 GPa
- Izod Impact, Notched: >= 2.14 J/cm
$ 1714/MT
- Density: 1.339 g/cc
- Mooney Viscosity: 21 @Temperature 100 °C
- Hardness, Shore A: 61
- Tensile Strength, Ultimate: 7.00 MPa
- Elongation at Break: 492 %
$ 1573/MT
- Density: 0.962 g/cc
- Filler Content: >= 1.0 %
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1783/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.4 MPa
- Elongation at Yield: 12 %
- Flexural Modulus, 1% Secant: 1360 MPa
$ 1678/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1860/MT
- Density: 0.870 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 70 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 5 mass%
$ 1813/MT
- Density: 0.955 g/cc
- ESCR 100% Igepal®: 40 hour @Temperature 50.0 °C
- High Load Melt Index: 30 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 63
$ 2276/MT
- Bulk Density: 0.880 g/cc
- Viscosity Measurement: 0.78 - 0.82
- Crystallinity: >= 50 %
- Melting Point: 247 °C
- Glass Transition Temp, Tg: 78.0 °C
$ 2295/MT
- Density: 0.920 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- High Load Melt Index: 44 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 44
$ 1716/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.8 MPa
- Elongation at Yield: 7.0 %
- Flexural Modulus, 1% Secant: 1420 MPa
$ 2454/MT
- Specific Gravity: 1.153 g/cc
- Viscosity Measure: 1150 cSt @Temperature 25.0 °C
- Flash Point: >= 182 °C
$ 1880/MT
- Density: 0.917 g/cc
- Thickness: 25.0 microns
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 9.00 MPa
- Film Tensile Strength at Yield, TD: 10.0 MPa
$ 1712/MT
- Density: 0.900 g/cc
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.7 MPa
- Izod Impact, Notched: 1.82 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 87.0 °C
$ 2048/MT
- Thickness: 50.8 microns
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 550 %
- Secant Modulus, MD: 0.103 GPa
- Secant Modulus, TD: 0.165 GPa
$ 1664/MT
- Density: 1.15 - 1.25 g/cc
- Viscosity: <= 260000 cP
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 2.30 - 2.90 MPa
- Elongation at Break: 450 %
$ 1934/MT
- Density: 1.09 g/cc
- Mooney Viscosity: 27 @Temperature 100 °C
- Hardness, Shore A: 64
- Tensile Strength, Ultimate: 9.50 MPa
- Elongation at Break: 360 %
$ 1494/MT
- Density: 0.880 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 20 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 0.5 mass%
$ 1651/MT
- Thickness: 50.8 microns
- Film Elongation at Break, MD: 280 %
- Film Elongation at Break, TD: 490 %
- Secant Modulus, MD: 0.131 GPa
- Secant Modulus, TD: 0.138 GPa
$ 1744/MT
- Density: 0.916 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg
- Vicat Softening Point: 88.0 °C
$ 1859/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 25.9 MPa
- Elongation at Yield: 7.0 %
- Flexural Modulus: 1.34 GPa
$ 1751/MT
- Density: 0.904 g/cc
- Thickness: 20.3 microns
- Melt Flow: 4.0 g/10 min
- Film Tensile Strength at Yield, MD: 6.998 MPa
- Film Tensile Strength at Yield, TD: 4.92 MPa
$ 1903/MT
- Density: 0.952 g/cc
- Melt Flow: 60 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.0 MPa
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: 225 %
$ 1530/MT
- Density: 0.870 g/cc
- Mooney Viscosity: 8.0 @Temperature 121 °C
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Hardness, Shore D: 21
$ 1766/MT
- Density: 0.929 g/cc
- ESCR 100% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 100 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 8.27 MPa
$ 1879/MT
- Density: 0.885 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Hardness, Shore D: 85
- Tensile Strength, Ultimate: 22.1 MPa
- Tensile Strength, Yield: 3.20 MPa
$ 1705/MT
- Density: 0.923 g/cc
- Viscosity: 27000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 44000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 60000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 35 g/10 min @Load 2.16 kg
$ 1822/MT
- Specific Gravity: 1.04 g/cc
- Tensile Strength, Ultimate: 20.7 MPa
- Elongation at Break: 240 %
- Flexural Modulus: 0.241 GPa
- Tear Strength: 87.7 kN/m
$ 2005/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.7 MPa
- Tensile Modulus: 1.10 GPa
- Flexural Modulus: 1.15 GPa
$ 2033/MT
- Density: 0.921 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 14.5 MPa
- Tensile Strength, Yield: 12.4 MPa
- Elongation at Break: 720 %
$ 1493/MT
- Density: 0.870 g/cc
- Mooney Viscosity: 23 @Temperature 121 °C
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Hardness, Shore D: 22
$ 2198/MT
- Density: 0.961 g/cc
- ESCR 100% Igepal®: 20 hour @Temperature 50.0 °C
- High Load Melt Index: 47 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 58
$ 1486/MT
- Density: 0.922 g/cc
- Thickness: 38.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1477/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 11.4 MPa
$ 1586/MT
- Density: 0.902 g/cc
- Thickness: 51.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Film Elongation at Break, MD: 570 %
- Film Elongation at Break, TD: 560 %
$ 2325/MT
- Density: 0.930 g/cc
- Thickness: 0.0700 - 0.100 microns
- CTE, linear: 49.0 µm/m-°C @Temperature 50.0 - 410 °C
- Decomposition Temperature: >= 500 °C
- Refractive Index: 1.53
$ 1528/MT
- Density: 0.860 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 70 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 5 mass%
$ 1930/MT
- Density: 0.929 g/cc
- ESCR 100% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 100 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 53
- Tensile Strength at Break: 8.27 MPa
$ 2220/MT
- Viscosity Measurement: 2.2 @Temperature 160 °C
- Viscosity Measurement: 3.0 @Temperature 160 °C
- Viscosity Measurement: 6.5 @Temperature 160 °C
- Viscosity Measurement: 11.3 @Temperature 160 °C
- Viscosity Measurement: 17 @Temperature 160 °C
$ 2585/MT
- Viscosity Measurement: 2.2 @Temperature 160 °C
- Viscosity Measurement: 3.0 @Temperature 160 °C
- Viscosity Measurement: 6.5 @Temperature 160 °C
- Viscosity Measurement: 12 @Temperature 160 °C
- Viscosity Measurement: 17.2 @Temperature 160 °C
$ 1695/MT
- Viscosity Measurement: 2.2 @Temperature 160 °C
- Viscosity Measurement: 3.5 @Temperature 160 °C
- Viscosity Measurement: 7.0 @Temperature 160 °C
- Viscosity Measurement: 14 @Temperature 160 °C
- Viscosity Measurement: 16.5 @Temperature 160 °C
$ 2343/MT
- Specific Gravity: 1.04 g/cc
- Tensile Strength, Ultimate: 21.4 MPa
- Elongation at Break: 190 %
- Flexural Modulus: 0.345 GPa
- Tear Strength: 109 kN/m
$ 1603/MT
- Density: 0.913 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Coefficient of Friction: 0.14
- Elmendorf Tear Strength MD: 363 g
$ 1625/MT
- Specific Gravity: 1.204 g/cc
- Density: 1.20 g/cc
- Viscosity: 10 cP
- Vapor Pressure: <= 1.33e-7 bar @Temperature 43.0 °C
- Specific Heat Capacity: 1.80 J/g-°C
$ 1549/MT
- Density: 0.885 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg
- Hardness, Shore D: 85
- Tensile Strength, Yield: 2.50 MPa
- Elongation at Break: >= 1000 %
$ 1869/MT
- Density: 0.908 g/cc
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 96
- Hardness, Shore D: 49
- Tensile Strength, Ultimate: 28.9 MPa
$ 1563/MT
- Density: 0.950 g/cc
- Viscosity: 33000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 40000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 95000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 50 g/10 min @Load 2.16 kg
$ 1605/MT
- Density: 0.920 g/cc
- ESCR 100% Igepal®: >= 1500 hour @Temperature 50.0 °C
- High Load Melt Index: 48 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.65 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 49
$ 2317/MT
- Density: 0.923 g/cc
- Thickness: 76.0 microns
- Melt Flow: 0.22 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1490/MT
- Density: 0.913 g/cc
- Melt Flow: 30 g/10 min @Load 2.16 kg
- Hardness, Shore D: 96
- Tensile Strength, Yield: 8.30 MPa
- Elongation at Break: 700 %
$ 2395/MT
- Density: 0.933 g/cc
- Viscosity: 34000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 54000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 77000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 80 g/10 min @Load 2.16 kg
$ 1785/MT
- Density: 0.923 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg
- Vicat Softening Point: 95.0 °C
$ 1533/MT
- Density: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.7 MPa
- Film Tensile Strength at Yield, TD: 11.4 MPa
$ 2061/MT
- Density: 0.905 g/cc
- Thickness: 38.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg
- Elmendorf Tear Strength MD: 502 g
- Elmendorf Tear Strength TD: 925 g
$ 1470/MT
- Density: 0.918 g/cc
- Thickness: 50.8 microns
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.64 MPa
- Film Tensile Strength at Yield, TD: 11.02 MPa
$ 1464/MT
- Density: 0.926 g/cc
- Thickness: 30.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 24.1 MPa
- Film Tensile Strength at Yield, MD: 11.7 MPa
$ 1865/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus: 1.07 GPa
$ 1902/MT
- Density: 0.912 g/cc
- Water Vapor Transmission: 10.5 g/m²/day
- Oxygen Transmission: 280 cc-mm/m²-24hr-atm
- Carbon Dioxide Transmission: 1235 cc-mm/m²-24hr-atm
- Thickness: 50.8 microns
$ 2169/MT
- Viscosity Measurement: 175
- Mooney Viscosity: 50 @Temperature 100 °C
- Vinyl Acetate Content: 11 %
- Ash: 0.050 %
- Collected Volatile Condensable Material: 0.40 %
$ 1959/MT
- Density: 0.917 g/cc
- Thickness: 58.4 microns
- Melt Flow: 2.3 g/10 min
- Film Tensile Strength at Yield, MD: 9.080 MPa
- Film Tensile Strength at Yield, TD: 8.846 MPa
$ 1512/MT
- Density: 0.924 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 12.3 MPa
- Tensile Strength, Yield: 8.80 MPa
- Elongation at Break: 585 %
- Vicat Softening Point: 88.9 °C
$ 1894/MT
- Density: 0.916 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg
- Vicat Softening Point: 84.0 °C
$ 2575/MT
- Thickness: 19.0 microns
- Film Tensile Strength at Yield, MD: 15.9 MPa
- Film Tensile Strength at Yield, TD: 8.96 MPa
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 500 %
$ 1610/MT
- Density: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.5 MPa
- Izod Impact, Notched: 0.267 J/cm
- Deflection Temperature at 0.46 MPa (66 psi): 99.0 °C
$ 1532/MT
- Moisture Vapor Transmission: 1.80 cc-mm/m²-24hr-atm
- Oxygen Transmission: 32.0 cc-mm/m²-24hr-atm
- Viscosity Measurement: 20000
- Tensile Strength, Ultimate: 23.0 MPa
- Elongation at Break: 425 %
$ 2009/MT
- Specific Gravity: 1.70 g/cc
- Bulk Density: 0.721 - 0.801 g/cc
- Particle Size: 240 - 340 µm
- Moisture Vapor Transmission: 0.157 cc-mm/m²-24hr-atm
- Oxygen Transmission: 0.886 cc-mm/m²-24hr-atm
$ 2173/MT
- Specific Gravity: 1.031 g/cc
- Viscosity Measure: 1060 cSt @Temperature 25.0 °C
- Pour Point: -9.44 °C
- Flash Point: >= 163 °C
$ 1481/MT
- Thickness: 50.8 microns
- Film Elongation at Break, MD: 430 %
- Film Elongation at Break, TD: 490 %
- Secant Modulus, MD: 0.0900 GPa
- Secant Modulus, TD: 0.0960 GPa
$ 2441/MT
- Density: 1.18 g/cc
- Viscosity: 5.0 cP @Temperature 43.0 °C
- Vapor Pressure: <= 1.33e-7 bar @Temperature 43.0 °C
- Heat of Fusion: 136 J/g
- Heat of Vaporization: 360 J/g
$ 1548/MT
- Density: 1.083 g/cc
- Mooney Viscosity: 46 @Temperature 100 °C
- Hardness, Shore A: 63
- Tensile Strength, Ultimate: 10.1 MPa
- Elongation at Break: 340 %
$ 1711/MT
- Density: 0.904 g/cc
- Water Vapor Transmission: 16.7 g/m²/day
- Oxygen Transmission: 445.7 cc-mm/m²-24hr-atm
- Carbon Dioxide Transmission: 2022 cc-mm/m²-24hr-atm
- Thickness: 50.8 microns
$ 1453/MT
- Density: 0.958 g/cc
- Melt Flow: 300 g/10 min @Load 2.16 kg
- Hardness, Shore D: 50
- Tensile Strength, Ultimate: 9.70 MPa
- Elongation at Break: 390 %
$ 1447/MT
- Density: 0.860 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 65 - 75 @Temperature 125 °C
- Ash: <= 0.10 %
- Yellow Index: <= 7.0 %
$ 2103/MT
- Density: 1.156 g/cc
- Mooney Viscosity: 33 @Temperature 100 °C
- Hardness, Shore A: 66
- Tensile Strength, Ultimate: 7.60 MPa
- Elongation at Break: 460 %
$ 1925/MT
- Density: 1.057 g/cc
- Mooney Viscosity: 33 @Temperature 100 °C
- Hardness, Shore A: 58
- Tensile Strength, Ultimate: 13.5 MPa
- Elongation at Break: 685 %
$ 1757/MT
- Density: 1.185 g/cc
- Mooney Viscosity: 37 @Temperature 100 °C
- Hardness, Shore A: 61
- Tensile Strength, Ultimate: 8.30 MPa
- Elongation at Break: 330 %
$ 1657/MT
- Density: 0.860 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 40 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 5 mass%
$ 1569/MT
- Density: 1.157 g/cc
- Mooney Viscosity: 37 @Temperature 100 °C
- Hardness, Shore A: 64
- Tensile Strength, Ultimate: 7.20 MPa
- Elongation at Break: 423 %
$ 2178/MT
- Mooney Viscosity: 55 @Temperature 100 °C
- Hardness, Shore A: 69
- Tensile Strength, Ultimate: 14.4 MPa
- Modulus of Elasticity: 0.00130 GPa
- 50% Modulus: 0.00200 GPa
$ 1776/MT
- Density: 0.860 g/cc
- Mooney Viscosity: 65 @Temperature 125 °C
- ENB: 7.5 mass%
- Ethylene: 50 mass%
- Molecular Weight Distribution: Medium
$ 1755/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 27.6 MPa
- Tensile Strength, Yield: 26.9 MPa
$ 1816/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 29.6 MPa
- Elongation at Yield: 11 %
- Flexural Modulus, 1% Secant: 1100 MPa
$ 2176/MT
- Density: 1.31 - 1.37 g/cc
- Solids Content: >= 99 %
- Viscosity: 650000 cP @Shear Rate 1.00 1/s, Temperature 40.0 °C
- Viscosity: 4.00e+6 cP @Shear Rate 1.00 1/s, Temperature 23.0 °C
- Tensile Strength, Ultimate: 35.0 MPa
$ 1818/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 35.2 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus, 1% Secant: 1590 MPa
$ 1649/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 80 hour @Temperature 50.0 °C
- High Load Melt Index: 33 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
$ 1619/MT
- Density: 0.952 g/cc
- ESCR 100% Igepal®: >= 1500 hour @Temperature 50.0 °C
- High Load Melt Index: 14 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 62
- Tensile Strength at Break: 34.5 MPa
$ 1455/MT
- Density: 0.922 g/cc
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Coefficient of Friction: 0.17
$ 1840/MT
- Density: 0.874 g/cc
- Brookfield Viscosity: 17000 cP @Temperature 177 °C
- Collected Volatile Condensable Material: <= 0.15 %
- Tensile Strength, Ultimate: 1.76 MPa
- Elongation at Break: 185 %
$ 1624/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.2 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 12.4 MPa
- Film Tensile Strength at Yield, MD: 11.7 MPa
$ 1813/MT
- Bulk Density: 0.880 g/cc
- Viscosity Measurement: 0.83 - 0.87
- Viscosity Measurement: 98
- Crystallinity: >= 50 %
- Melting Point: 247 °C
$ 2478/MT
- Water Absorption: 0.24 %
- Thickness: 0.280 microns
- Thickness: 0.2425 - 0.3425 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1476/MT
- Density: 0.9055 g/cc
- High Load Melt Index: 20 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.85 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 91
- Hardness, Shore A: 95
$ 1608/MT
- Density: 0.920 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.50 g/10 min
- Antiblock Level: 5100 ppm
- Slip Level: 900 ppm
$ 1705/MT
- Water Vapor Transmission: 0.970 g/m²/day
- Oxygen Transmission: 0.571 cc-mm/m²-24hr-atm
- Thickness: 102 microns
- Film Elongation at Break, MD: 85 %
- Film Elongation at Break, TD: 80 %
$ 1606/MT
- Density: 0.885 g/cc
- Mooney Viscosity: 22 @Temperature 121 °C
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 86
- Hardness, Shore D: 33
$ 2206/MT
- Density: 0.931 g/cc
- Melt Index of Compound: 127.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 2301/MT
- Density: 0.8985 g/cc
- Melt Index of Compound: 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 91
- Hardness, Shore A: 93
- Tensile Strength at Break: 11.4 MPa
$ 2247/MT
- Density: 0.921 g/cc
- Thickness: 76.0 microns
- Melt Flow: 0.22 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 9.70 MPa
$ 1757/MT
- Density: 0.900 g/cc
- Melt Flow: 1.9 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 1.07 GPa
$ 1878/MT
- Density: 1.91 g/cc
- Filler Content: 76 %
- Tensile Strength, Ultimate: 1000 MPa
- Elongation at Break: 2.2 %
- Modulus of Elasticity: 45.0 GPa
$ 1965/MT
- Density: 0.918 g/cc
- Water Vapor Transmission: 26.4 g/m²/day
- Thickness: >= 7.62 microns
- Melt Index of Compound: 8.0 g/10 min
- Neck In: 5.10 cm
$ 1483/MT
- Viscosity Measurement: 2.8 @Temperature 160 °C
- Viscosity Measurement: 4.4 @Temperature 160 °C
- Viscosity Measurement: 10.9 @Temperature 160 °C
- Viscosity Measurement: 14.3 @Temperature 160 °C
- Viscosity Measurement: 17.9 @Temperature 160 °C
$ 1547/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 76.0 MPa
- Tensile Strength, Yield: 76.0 MPa
$ 1493/MT
- Density: 0.900 g/cc
- Melt Flow: 8.7 g/10 min @Temperature 230 °C
- Hardness, Rockwell R: 102
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 8.0 %
$ 1816/MT
- Density: 0.870 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 7.60 MPa
- Elongation at Break: >= 1000 %
$ 1771/MT
- Density: 0.930 g/cc
- Viscosity: 21000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 29000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 31000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 105 g/10 min @Load 2.16 kg
$ 2006/MT
- Density: 0.930 g/cc
- Viscosity: 21000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 29000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 31000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 105 g/10 min @Load 2.16 kg
$ 1612/MT
- Density: 0.875 g/cc
- Mooney Viscosity: 11 @Temperature 121 °C
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 77
- Hardness, Shore D: 25
$ 1548/MT
- Density: 0.924 g/cc
- Thickness: 30.0 microns
- Melt Flow: 0.90 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.9 MPa
- Film Tensile Strength at Yield, TD: 12.1 MPa
$ 2448/MT
- Density: 0.917 g/cc
- Viscosity: 47000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 86000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 110000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 2.16 kg
$ 1613/MT
- Density: 1.08 g/cc
- Melt Density: 1.00 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 76.0 MPa
$ 1566/MT
- Density: 0.920 g/cc
- Melt Flow: 0.85 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 11.5 MPa
- Film Elongation at Break, MD: 645 %
$ 1515/MT
- Specific Gravity: 1.042 g/cc
- Density: 1.042 g/cc
- Solids Content: 43 %
- Viscosity: 450 cP @Temperature 98.9 °C
- Viscosity: 1090 cP @Temperature 65.6 °C
$ 1476/MT
- Water Absorption: 0.24 %
- Thickness: 0.620 microns
- Thickness: 0.560 - 0.790 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1543/MT
- Density: 0.922 g/cc
- Thickness: 13.0 microns
- Melt Flow: 6.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 12.1 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 1555/MT
- Density: 0.931 g/cc
- Filler Content: 18.5 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 86
- Hardness, Shore D: 30
$ 1902/MT
- Density: 0.9265 g/cc
- Thickness: 19.0 microns
- Melt Flow: 0.50 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 650 ppm
$ 1774/MT
- Density: 0.9255 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.85 g/10 min
- Film Tensile Strength at Yield, MD: 13.89 MPa
- Film Tensile Strength at Yield, TD: 14.58 MPa
$ 2385/MT
- Density: 1.22 g/cc
- Viscosity: 55 cP
- Viscosity Measurement: <= 5.0
- Molecular Weight: 290 g/mol
- Vapor Pressure: <= 1.30e-8 bar
$ 2040/MT
- Density: 0.9035 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 750 ppm
$ 1618/MT
- Density: 0.900 g/cc
- Melt Flow: 0.40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength, Ultimate: 24.0 MPa
- Film Tensile Strength at Yield, MD: 29.0 MPa
$ 2164/MT
- Density: 0.952 g/cc
- Viscosity: 75000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 160000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 250000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 12 g/10 min @Load 2.16 kg
$ 1966/MT
- Density: 0.912 g/cc
- Oxygen Transmission: 282 cc-mm/m²-24hr-atm
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.832 MPa
$ 1626/MT
- Density: 0.941 g/cc
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 125 °C
$ 1919/MT
- Density: 0.938 g/cc
- Thickness: 60.0 microns
- Melt Flow: 1.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 23.4 MPa
- Film Tensile Strength at Yield, MD: 8.60 MPa
$ 2549/MT
- Density: 1.17 g/cc
- Volatiles: <= 0.20 %
- Mooney Viscosity: 88 @Temperature 121 °C
- Chlorine Content: 36 %
$ 1788/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 1538/MT
- Density: 0.928 g/cc
- Filler Content: 10.5 %
- Melt Flow: 1.85 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 40
- Tensile Strength, Ultimate: 19.3 MPa
$ 2216/MT
- Density: 1.046 g/cc
- Mooney Viscosity: 76 @Temperature 100 °C
- Hardness, Shore A: 64
- Tensile Strength, Ultimate: 17.4 MPa
- Elongation at Break: 383 %
$ 2001/MT
- Specific Gravity: 1.401 - 1.42 g/cc
- Maximum Moisture Content: 1.0
- Gardner Color Number: <= 7.0
- Hydroxyl Number mg KOH/g: 187
$ 1486/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 2385/MT
- Density: 0.9178 g/cc
- Thickness: 20.3 microns
- Melt Flow: 2.45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 11.22 MPa
- Film Tensile Strength at Yield, TD: 10.5 MPa
$ 2303/MT
- Specific Gravity: 1.018 g/cc
- Viscosity Measurement: 1100 - 1400
- Maximum Moisture Content: 0.060
- ASTM Color: <= 30
- Flash Point: >= 180 °C
$ 2160/MT
- Permeability: 0.010
- Thickness: 152 microns
- Film Elongation at Break, MD: 145 %
- Film Elongation at Break, TD: 79 %
- Secant Modulus, MD: 0.5330 GPa
$ 1533/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: 290 hour @Temperature 50.0 °C
- High Load Melt Index: 25 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 60
$ 1503/MT
- Density: 0.9218 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 3000 ppm
- Film Tensile Strength at Yield, MD: 10.5 MPa
$ 1895/MT
- Density: 0.916 g/cc
- Thickness: 20.3 microns
- Melt Flow: 4.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.549 MPa
- Film Tensile Strength at Yield, TD: 8.55 MPa
$ 1580/MT
- Density: 1.22 g/cc
- Mooney Viscosity: 64 @Temperature 100 °C
- Hardness, Shore A: 65
- Tensile Strength, Ultimate: 9.30 MPa
- Elongation at Break: 425 %
$ 1646/MT
- Density: 1.03 g/cc
- Solids Content: >= 100 %
- Viscosity: 220 cP @Temperature 25.0 °C
- Flash Point: >= 149 °C
$ 1456/MT
- Density: 0.902 g/cc
- Melt Flow: 7.5 g/10 min @Load 2.16 kg
$ 1470/MT
- Water Vapor Transmission: 6.20 g/m²/day
- Oxygen Transmission: 0.748 cc-mm/m²-24hr-atm
- Thickness: 25.4 microns
- Film Elongation at Break, MD: 90 %
- Film Elongation at Break, TD: 75 %
$ 1725/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.1 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 1.45 GPa
$ 2526/MT
- Density: 1.86 g/cc
- Filler Content: 66 %
- Elongation at Break: 1.5 %
- Flexural Strength: 1050 MPa
- Flexural Modulus: 40.0 GPa
$ 1640/MT
- Density: 0.920 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 10.89 MPa
- Film Tensile Strength at Yield, TD: 12.29 MPa
$ 1857/MT
- Density: 1.09 g/cc
- Melt Density: 0.970 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 27.6 MPa
$ 2074/MT
- Water Absorption: <= 0.20 %
- Viscosity Measure: 259 cSt @Temperature 25.0 °C
- Thickness: 5.70 - 15.6 microns
- Tensile Strength, Ultimate: 80.0 - 94.0 MPa
- Elongation at Break: 5.5 - 10.5 %
$ 1622/MT
- Density: 0.900 g/cc
- Melt Flow: 4.3 g/10 min @Temperature 230 °C
- Hardness, Rockwell R: 102
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 8.0 %
$ 2454/MT
- Density: 0.9188 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.37 MPa
- Film Tensile Strength at Yield, TD: 12.98 MPa
$ 1643/MT
- Density: 0.870 g/cc
- Viscosity: 3.60e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Viscosity: 1.10e+7 cP @Shear Rate 10.0 1/s, Temperature 190 °C
- Viscosity: 1.80e+7 cP @Shear Rate 1.58 1/s, Temperature 190 °C
- Viscosity: 2.83e+7 cP @Shear Rate 0.100 1/s, Temperature 190 °C
$ 1783/MT
- Density: 1.234 g/cc
- Viscosity: 1800 cP
- Molecular Weight: 400 g/mol
- Vapor Pressure: <= 1.33e-8 bar
- Storage Temperature: 24.0 - 41.0 °C
$ 2476/MT
- Density: 1.362 g/cc
- Mooney Viscosity: 70 @Temperature 100 °C
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 11.1 MPa
- Elongation at Break: 393 %
$ 2058/MT
- Thickness: 50.8 microns
- Film Elongation at Break, MD: 320 %
- Film Elongation at Break, TD: 490 %
- Secant Modulus, MD: 0.138 GPa
- Secant Modulus, TD: 0.131 GPa
$ 1764/MT
- Viscosity Measurement: 192
- Thickness: 2.50 - 5.00 microns
- Tensile Strength, Ultimate: 78.0 - 96.0 MPa
- Elongation at Break: 5.5 - 10.5 %
- Tensile Modulus: 2.70 - 3.10 GPa
$ 1601/MT
- Density: 0.912 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.3 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 6.90 MPa
- Film Tensile Strength at Yield, TD: 6.20 MPa
$ 1931/MT
- Viscosity Measurement: 2.5 @Temperature 160 °C
- Viscosity Measurement: 2.5 @Temperature 160 °C
- Viscosity Measurement: 6.5 @Temperature 160 °C
- Viscosity Measurement: 11.5 @Temperature 160 °C
- Viscosity Measurement: 22 @Temperature 160 °C
$ 1472/MT
- Density: 0.926 g/cc
- ESCR 100% Igepal®: 5.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 7.58 MPa
$ 1492/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1456/MT
- Density: 0.922 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 1593/MT
- Density: 0.0320 g/cc
- Compressive Strength: >= 0.0414 MPa
- Shrinkage: 0.00 %
- Shrinkage: 0.400 % @Temperature 37.8 °C, Time 605000 sec
- Shrinkage: 2.40 % @Temperature 121 °C, Time 86400 sec
$ 1629/MT
- Density: 0.9289 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Antiblock Level: 4000 ppm
- Film Tensile Strength at Yield, MD: 16.22 MPa
$ 1959/MT
- Density: 0.920 g/cc
- Thickness: 30.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 2188/MT
- Specific Gravity: 1.70 g/cc
- Bulk Density: 0.801 g/cc
- Particle Size: 280 µm
- Moisture Vapor Transmission: 0.0197 cc-mm/m²-24hr-atm
- Oxygen Transmission: 0.0295 cc-mm/m²-24hr-atm
$ 2256/MT
- Specific Gravity: 1.05 g/cc
- Viscosity: 430 cP @Temperature 25.0 °C
- Flash Point: 160 °C
$ 2431/MT
- Density: 0.902 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.93 MPa
- Film Tensile Strength at Yield, TD: 5.45 MPa
$ 1490/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1070 MPa
$ 1861/MT
- Density: 1.185 g/cc
- Mooney Viscosity: 47 @Temperature 100 °C
- Hardness, Shore A: 70
- Tensile Strength, Ultimate: 10.4 MPa
- Elongation at Break: 446 %
$ 1480/MT
- Density: 0.909 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 8.76 MPa
- Film Tensile Strength at Yield, TD: 8.07 MPa
$ 1496/MT
- Density: 0.911 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.65 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1734/MT
- Density: 0.965 g/cc
- ESCR 100% Igepal®: 2.0 hour @Temperature 50.0 °C
- High Load Melt Index: 180 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 8.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 61
$ 2281/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1560/MT
- Density: 0.950 g/cc
- Melt Flow: 90 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 10.0 MPa
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Break: 150 %
$ 2037/MT
- Density: 0.870 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Tensile Strength at Break: 7.60 MPa
- Elongation at Break: >= 1000 %
$ 1538/MT
- Density: 0.960 g/cc
- Viscosity: 50000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 82000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 153000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 9.0 g/10 min @Load 2.16 kg
$ 1652/MT
- Density: 0.870 g/cc
- Mooney Viscosity: 60 @Temperature 125 °C
- ENB: 5 mass%
- Ethylene: 67.5 mass%
- Molecular Weight Distribution: Medium
$ 1643/MT
- Density: 0.955 g/cc
- Viscosity: 55000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 110000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 2.16 kg
$ 1514/MT
- Mooney Viscosity: 63 @Temperature 100 °C
- Hardness, Shore A: 64
- Tensile Strength, Ultimate: 10.7 MPa
- Elongation at Break: 301 %
- 50% Modulus: 0.00190 GPa
$ 2457/MT
- Density: 1.07 g/cc
- Melt Density: 0.978 g/cc
- Linear Mold Shrinkage: 0.0045 cm/cm
- Melt Flow: 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 69.0 MPa
$ 1744/MT
- Density: 0.931 g/cc
- Melt Index of Compound: 127.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 55
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 11.0 MPa
$ 1585/MT
- Mooney Viscosity: >= 50 @Temperature 121 °C
- Hardness, Shore A: 70
- Tensile Strength, Ultimate: 20.7 MPa
- Elongation at Break: 325 %
- 200% Modulus: 0.0117 GPa
$ 1604/MT
- Density: 0.884 g/cc
- High Load Melt Index: 5.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.090 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 81
- Hardness, Shore A: 82
$ 1738/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 2.1 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1070 MPa
$ 2348/MT
- Density: 0.952 g/cc
- Viscosity: 38000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 80000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 38 g/10 min @Load 2.16 kg
$ 1730/MT
- Density: 0.944 g/cc
- Density: 0.954 g/cc
- High Load Melt Index: 8.3 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- PENT: 200 hour
$ 2127/MT
- Density: 0.970 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 140 @Temperature 125 °C
- Carbon Black Content (N650): 30 phr
- ENB: 4.9 mass%
- Ethylene: 58 mass%
$ 1508/MT
- Specific Gravity: 1.02 g/cc
- Density: 1.02 g/cc
- Viscosity Measure: 600 - 700 cSt @Temperature 37.8 °C
- Maximum Moisture Content: 0.080
- Vapor Pressure: <= 0.000133 bar
$ 1601/MT
- Density: 1.10 g/cc
- Volatiles: <= 0.20 %
- Viscosity: 1.25 cP @Shear Rate 144 1/s, Temperature 190 °C
- Tensile Strength, Ultimate: 10.3 MPa
- Elongation at Break: 800 %
$ 2030/MT
- Density: 0.935 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 10.9 MPa
$ 1459/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 8.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 66.0 MPa
- Tensile Strength, Yield: 66.0 MPa
$ 1476/MT
- Solids Content: 50 - 51 %
- Particle Mesh Size: 100 Mesh
- Particle Mesh Size: 325 Mesh
- pH: 6.7 - 7.3
- Brookfield Viscosity: 100 - 300 cP
$ 1654/MT
- Specific Gravity: 1.017 g/cc
- pH: 8.8
- Viscosity Measure: 86 cSt @Temperature 98.9 °C
- Viscosity Measure: 680 cSt @Temperature 37.8 °C
- Viscosity Measure: 1180 cSt @Temperature 25.0 °C
$ 1942/MT
- Density: 1.055 g/cc
- Mooney Viscosity: 122 @Temperature 100 °C
- Hardness, Shore A: 64
- Tensile Strength, Ultimate: 18.9 MPa
- Elongation at Break: 255 %
$ 1729/MT
- Density: 0.920 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 11.0 MPa
$ 2452/MT
- Solids Content: 52 - 53 %
- Particle Mesh Size: 100 Mesh
- Particle Mesh Size: 325 Mesh
- pH: 7.7 - 8.3
- Brookfield Viscosity: 150 - 300 cP
$ 2365/MT
- Density: 0.912 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 68.3 MPa
- Film Tensile Strength at Yield, TD: 66.9 MPa
- Film Elongation at Break, MD: 605 %
$ 2142/MT
- Density: 0.902 g/cc
- Melt Index of Compound: 30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 94
- Hardness, Shore D: 44
- Tensile Strength, Ultimate: 12.9 MPa
$ 1693/MT
- Density: 0.922 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 2187/MT
- Density: 0.990 g/cc
- Brookfield Viscosity: 500 cP
- Flash Point: >= 110 °C
$ 1464/MT
- Density: 0.900 g/cc
- Melt Flow: 38 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Yield: 7.0 %
- Flexural Modulus: 1.24 GPa
$ 1492/MT
- Specific Gravity: 1.022 g/cc
- pH: 8.0 - 9.5
- Viscosity Measure: 370 cSt @Temperature 50.0 °C
- Viscosity Measure: 600 cSt @Temperature 37.8 °C
- Viscosity Measure: 1060 - 1200 cSt @Temperature 25.0 °C
$ 1589/MT
- Solids Content: 52 %
- Particle Size: 1.4 µm
- pH: 7.85
- Brookfield Viscosity: 176 cP
- Glass Transition Temp, Tg: -2.00 °C
- Minimum film formation temperature: 53.6°F
$ 1696/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1681/MT
- Density: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.9 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1647/MT
- Density: 0.921 g/cc
- Viscosity: 56000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 99000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 265000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
$ 1979/MT
- Moisture Vapor Transmission: 1.50 cc-mm/m²-24hr-atm
- Oxygen Transmission: 12.0 cc-mm/m²-24hr-atm
- Viscosity Measurement: 10000
- Elongation at Break: 700 %
- 100% Modulus: 0.00140 GPa
$ 1757/MT
- Density: 0.941 g/cc
- Thickness: 25.0 microns
- Melt Flow: 4.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 13.1 MPa
- Film Tensile Strength at Yield, MD: 16.5 MPa
$ 2328/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 61
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Yield: 11 %
$ 1493/MT
- Density: 1.22 g/cc
- Viscosity: 1500 cP
- Vapor Pressure: <= 1.33e-8 bar
- Heat of Vaporization: 360 J/g
- CTE, linear: 737 µm/m-°C @Temperature 20.0 °C
$ 1913/MT
- Density: 0.9215 g/cc
- Thickness: 20.3 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 1000 ppm
$ 1805/MT
- Density: 1.194 g/cc
- Mooney Viscosity: 24 @Temperature 100 °C
- Hardness, Shore A: 70
- Tensile Strength, Ultimate: 8.00 MPa
- Elongation at Break: 434 %
$ 1842/MT
- Density: 1.68 g/cc
- Tensile Strength, Ultimate: 179 MPa
- Elongation at Break: 29 %
- Tensile Modulus: 1.03 GPa
$ 1457/MT
- Density: 0.931 g/cc
- Filler Content: 18.5 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 86
- Hardness, Shore D: 31
$ 1646/MT
- Specific Gravity: 1.70 g/cc
- Bulk Density: 0.801 g/cc
- Particle Size: 280 µm
- Moisture Vapor Transmission: 0.0315 cc-mm/m²-24hr-atm
- Oxygen Transmission: 0.0433 cc-mm/m²-24hr-atm
- Melting Point: 158 °C
$ 1848/MT
- Density: 1.057 g/cc
- Mooney Viscosity: 49 @Temperature 100 °C
- Hardness, Shore A: 58
- Tensile Strength, Ultimate: 15.0 MPa
- Elongation at Break: 657 %
$ 2372/MT
- Density: 0.950 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 129 °C
$ 2280/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 12.0 MPa
- Film Tensile Strength at Yield, TD: 11.6 MPa
$ 1587/MT
- Density: 1.00 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 78 @Temperature 125 °C
- Carbon Black Content (N650): 30 phr
- ENB: 2.2 mass%
- Ethylene: 68 mass%
$ 1557/MT
- Density: 0.941 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 16.8 MPa
- Tensile Strength, Yield: 8.50 MPa
- Elongation at Break: 580 %
- Vicat Softening Point: 76.0 °C
$ 1448/MT
- Density: 0.925 g/cc
- Viscosity: 28000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 50000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 76000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 25 g/10 min @Load 2.16 kg
$ 1824/MT
- Density: 0.880 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 20 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 0.5 mass%
$ 1588/MT
- Density: 0.9215 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.85 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 1200 ppm
$ 1475/MT
- Density: 0.930 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 125 °C
$ 1498/MT
- Density: 0.952 g/cc
- ESCR 100% Igepal®: 12 hour @Temperature 50.0 °C
- Melt Index of Compound: 6.75 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 59
- Tensile Strength at Break: 22.8 MPa
$ 2152/MT
- Density: 0.875 g/cc
- Melt Flow: 3.0 g/10 min
- Impact: 190
- Dart Drop Test: 150 g
- Melting Point: 20.0 °C
$ 1600/MT
- Density: 1.168 g/cc
- Mooney Viscosity: 31 @Temperature 100 °C
- Hardness, Shore A: 77
- Tensile Strength, Ultimate: 13.4 MPa
- Elongation at Break: 360 %
$ 1782/MT
- Water Absorption: 0.30 %
- Thickness: 0.0750 - 1.00 microns
- Ball Indentation Hardness: 210 MPa
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2333/MT
- Density: 0.928 g/cc
- Thickness: 50.8 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 14.58 MPa
- Film Tensile Strength at Yield, TD: 14.60 MPa
$ 1663/MT
- Bulk Density: 0.880 g/cc
- Viscosity Measurement: 0.83 - 0.87
- Crystallinity: >= 50 %
- Melting Point: 247 °C
- Glass Transition Temp, Tg: 78.0 °C
$ 1583/MT
- Density: 0.905 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.50 g/10 min
- Film Tensile Strength at Yield, MD: 10.7 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1781/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 35.2 MPa
- Tensile Strength, Yield: 35.2 MPa
$ 1792/MT
- Viscosity Measurement: 7.0 @Temperature 160 °C
- Viscosity Measurement: 9.9 @Temperature 160 °C
- Viscosity Measurement: 10.2 @Temperature 160 °C
- Viscosity Measurement: 13.4 @Temperature 160 °C
- Viscosity Measurement: 39 @Temperature 160 °C
$ 1606/MT
- Density: 0.880 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 25 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 5 mass%
$ 1577/MT
- Water Vapor Transmission: 9.00 g/m²/day
- Oxygen Transmission: 0.512 cc-mm/m²-24hr-atm
- Thickness: 15.2 microns
- Film Elongation at Break, MD: 75 %
- Film Elongation at Break, TD: 55 %
$ 1459/MT
- Density: 1.29 - 1.35 g/cc
- Solids Content: >= 99 %
- Viscosity: 900000 cP @Shear Rate 1.00 1/s, Temperature 40.0 °C
- Viscosity: 2.50e+6 cP @Shear Rate 1.00 1/s, Temperature 23.0 °C
- Tensile Strength, Ultimate: 30.0 MPa
$ 2397/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 64.0 MPa
- Tensile Strength, Yield: 64.0 MPa
$ 1581/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.7 MPa
- Film Tensile Strength at Yield, TD: 10.7 MPa
$ 1678/MT
- Density: 1.38 g/cc
- Brookfield Viscosity: 20000 - 60000 cP
$ 2000/MT
- Mooney Viscosity: >= 38 @Temperature 121 °C
- Hardness, Shore A: 65
- Tensile Strength, Ultimate: 20.7 MPa
- Elongation at Break: 310 %
- 200% Modulus: 0.0117 GPa
$ 2480/MT
- Specific Gravity: 1.07 g/cc
- Viscosity Measure: 3550 cSt @Temperature 37.8 °C
- Viscosity Measure: 15000 - 19000 cSt @Temperature 25.0 °C
- Maximum Moisture Content: 0.10
- Flash Point: 205 °C
$ 1458/MT
- Density: 0.905 g/cc
- High Load Melt Index: 24 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.85 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 91
- Hardness, Shore A: 94
$ 1564/MT
- Density: 0.920 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 2036/MT
- Specific Gravity: 1.153 g/cc
- Viscosity Measure: 1150 cSt @Temperature 25.0 °C
- Flash Point: >= 182 °C
$ 2018/MT
- Specific Gravity: 1.23 g/cc
- Viscosity: 180 cP @Temperature 25.0 °C
- Flash Point: >= 204 °C
$ 1762/MT
- Solids Content: 51 %
- Particle Size: 1.5 µm
- pH: 7.8
- Viscosity: 325 cP
- Glass Transition Temp, Tg: -26.0 °C
$ 1487/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Yield: 10 %
$ 2245/MT
- Solids Content: 50 - 51 %
- Particle Mesh Size: 100 Mesh
- Particle Mesh Size: 325 Mesh
- pH: 7.2 - 7.6
- Brookfield Viscosity: 50 - 350 cP
$ 1687/MT
- Mooney Viscosity: 73 @Temperature 100 °C
- Hardness, Shore A: 73
- Tensile Strength, Ultimate: 10.5 MPa
- Elongation at Break: 344 %
- 50% Modulus: 0.00240 GPa
$ 1853/MT
- Density: 1.00 g/cc
- Solids Content: 99 %
- Viscosity Measurement: 65 - 120
- Collected Volatile Condensable Material: 0.00 %
- Hardness, Shore A: 60
$ 1446/MT
- Density: 0.941 g/cc
- Thickness: 25.4 microns
- Melt Flow: 4.0 g/10 min
- Film Tensile Strength at Yield, MD: 16.22 MPa
- Film Tensile Strength at Yield, TD: 10.76 MPa
$ 1522/MT
- Density: 0.924 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.6 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 22.1 MPa
- Film Tensile Strength at Yield, MD: 11.7 MPa
$ 2027/MT
- Density: 1.03 g/cc
- Solids Content: >= 100 %
- Viscosity: 165 cP @Temperature 25.0 °C
- Flash Point: >= 149 °C
$ 1623/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 24.1 MPa
- Elongation at Yield: 10 %
$ 1707/MT
- Density: 1.24 g/cc
- Melt Density: 1.14 g/cc
- Melt Flow: 22 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 121
- Tensile Strength, Ultimate: 86.0 MPa
$ 1643/MT
- Density: 0.952 g/cc
- ESCR 100% Igepal®: 1100 hour @Temperature 50.0 °C
- High Load Melt Index: 16 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 37.9 MPa
$ 1473/MT
- Density: 0.934 g/cc
- Melt Flow: 7.7 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 16.9 MPa
- Tensile Strength, Yield: 10.7 MPa
- Elongation at Break: 660 %
- Vicat Softening Point: 86.1 °C
$ 1544/MT
- Density: 0.962 g/cc
- Viscosity: 80000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 260000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 10 g/10 min @Load 2.16 kg
$ 1788/MT
- Specific Gravity: 1.028 g/cc
- pH: 7.5 - 9.3
- Viscosity Measure: 65 cSt @Temperature 98.9 °C
- Viscosity Measure: 440 cSt @Temperature 37.8 °C
- Viscosity Measure: 855 cSt @Temperature 25.0 °C
$ 1569/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus: 1.07 GPa
$ 2390/MT
- Density: 0.900 g/cc
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus: 1.07 GPa
$ 2066/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: 180 hour @Temperature 50.0 °C
- High Load Melt Index: 25 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 57
$ 1556/MT
- Water Absorption: 0.24 %
- Thickness: 0.260 microns
- Thickness: 0.230 - 0.320 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2570/MT
- Density: 0.960 g/cc
- Viscosity: 48000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 73000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 105000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 30 g/10 min @Load 2.16 kg
$ 2173/MT
- Water Vapor Transmission: 7.20 g/m²/day
- Oxygen Transmission: 0.472 cc-mm/m²-24hr-atm
- Thickness: 19.0 microns
- Film Elongation at Break, MD: 80 %
- Film Elongation at Break, TD: 50 %
$ 1944/MT
- Density: 0.868 g/cc
- Mooney Viscosity: 35 @Temperature 121 °C
- Melt Index of Compound: 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Hardness, Shore D: 20
$ 1921/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus, 1% Secant: 1030 MPa
$ 1713/MT
- Bulk Density: 0.880 g/cc
- Viscosity Measurement: 0.78 - 0.82
- Viscosity Measurement: 93
- Crystallinity: >= 50 %
- Melting Point: 247 °C
$ 1463/MT
- Density: 0.923 g/cc
- ESCR 100% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 55 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 6.21 MPa
$ 1652/MT
- Density: 1.08 g/cc
- Solids Content: 56.5 %
- Particle Size: 1.53 µm
- pH: 7.5
- Brookfield Viscosity: <= 800 cP
$ 1948/MT
- Density: 0.870 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 70 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 5 mass%
$ 1769/MT
- Density: 0.860 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 40 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 1.8 mass%
$ 1538/MT
- Density: 0.9175 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 2500 ppm
- Slip Level: 1000 ppm
$ 1646/MT
- Density: 0.895 g/cc
- Thickness: 51.0 microns
- Melt Flow: 1.6 g/10 min @Load 2.16 kg
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 710 %
$ 1458/MT
- Density: 1.09 g/cc
- Mooney Viscosity: 64 @Temperature 100 °C
- Hardness, Shore A: 64
- Tensile Strength, Ultimate: 11.1 MPa
- Elongation at Break: 330 %
$ 1829/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 10.7 MPa
$ 1538/MT
- Specific Gravity: 1.325 - 1.335 g/cc
- Maximum Moisture Content: 1.0
- Gardner Color Number: <= 7.0
$ 1753/MT
- Density: 0.980 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 108 @Temperature 125 °C
- Carbon Black Content (N650): 30 phr
- ENB: 4.5 mass%
$ 1616/MT
- Density: 0.908 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 20 @Temperature 125 °C
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ash: <= 0.10 %
$ 1669/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 38 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Yield: 7.0 %
- Flexural Modulus: 1.24 GPa
$ 1651/MT
- Density: 0.862 g/cc
- Viscosity: 2.06e+6 cP @Shear Rate 100 1/s, Temperature 190 °C
- Viscosity: 4.20e+6 cP @Shear Rate 10.0 1/s, Temperature 190 °C
- Viscosity: 5.59e+6 cP @Shear Rate 1.58 1/s, Temperature 190 °C
- Viscosity: 6.58e+6 cP @Shear Rate 0.100 1/s, Temperature 190 °C
$ 2374/MT
- Density: 0.916 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 9.818 MPa
- Film Tensile Strength at Yield, TD: 10.17 MPa
$ 1860/MT
- Density: 0.384 g/cc
- Water Absorption: 0.29 %
- Compressive Strength: 9.10 MPa
- Compressive Modulus: 0.179 GPa
- Shrinkage: 0.400 % @Temperature 70.0 °C
$ 1931/MT
- Density: 1.15 - 1.25 g/cc
- Viscosity: <= 260000 cP
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 2.30 - 2.90 MPa
- Elongation at Break: 450 %
$ 2145/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 758 MPa
$ 2055/MT
- Specific Gravity: 1.049 g/cc
- Solids Content: 39 - 42 %
- Viscosity: 310 cP @Temperature 98.9 °C
- Viscosity: 2360 cP @Temperature 37.8 °C
- Viscosity: 4810 cP @Temperature 25.0 °C
$ 1494/MT
- Density: 0.919 g/cc
- Viscosity: 76000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 176000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 305000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
$ 2172/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1612/MT
- Density: 0.924 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 12.1 MPa
- Film Tensile Strength at Yield, TD: 12.0 MPa
$ 1685/MT
- Density: 0.857 g/cc
- Mooney Viscosity: 27 @Temperature 125 °C
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 50
- Tensile Strength, Ultimate: 2.10 MPa
$ 1579/MT
- Density: 0.935 g/cc
- Thickness: 60.0 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 20.3 MPa
- Film Tensile Strength at Yield, MD: 9.40 MPa
$ 1610/MT
- Density: 0.0800 g/cc
- Water Absorption: 2.5 %
- Compressive Strength: 0.500 MPa
- Shrinkage: 2.00 % @Temperature 102 °C, Time 605000 sec
- Shrinkage: 3.00 % @Temperature 121 °C, Time 173000 sec
$ 1926/MT
- Viscosity Measurement: 6.4 @Temperature 160 °C
- Viscosity Measurement: 10 @Temperature 160 °C
- Viscosity Measurement: 10.8 @Temperature 160 °C
- Viscosity Measurement: 13.1 @Temperature 160 °C
- Viscosity Measurement: 42 @Temperature 160 °C
$ 1954/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.6 MPa
- Elongation at Yield: 5.0 %
- Flexural Modulus, 1% Secant: 1520 MPa
$ 1618/MT
- Density: 0.920 g/cc
- Thickness: 25.4 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 10.28 MPa
- Film Tensile Strength at Yield, TD: 10.03 MPa
$ 2555/MT
- Density: 0.8996 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Antiblock Level: 6000 ppm
- Slip Level: 3500 ppm
$ 1533/MT
- Density: 0.905 g/cc
- Moisture Vapor Transmission: 0.0714 cc-mm/m²-24hr-atm
- Thickness: 51.0 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg
- Coefficient of Friction: 0.53
$ 1946/MT
- Density: 0.927 g/cc
- ESCR 100% Igepal®: 5.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 55 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 7.58 MPa
$ 1506/MT
- Density: 0.902 g/cc
- Thickness: >= 7.62 microns
- Melt Index of Compound: 7.5 g/10 min
- Neck In: 13.5 cm
- Coating Weight: >= 7.20 g/m²
$ 1832/MT
- Density: 0.930 g/cc
- Thickness: 0.220 - 0.310 microns
- CTE, linear: 49.0 µm/m-°C @Temperature 50.0 - 410 °C
- Decomposition Temperature: >= 500 °C
- Refractive Index: 1.53
$ 1973/MT
- Density: 0.952 g/cc
- Melt Index of Compound: 80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 17.9 MPa
- Tensile Strength, Yield: 19.3 MPa
$ 2001/MT
- Density: 1.15 - 1.21 g/cc
- Solids Content: >= 99 %
- Viscosity: 500000 cP @Shear Rate 1.00 1/s, Temperature 40.0 °C
- Tensile Strength, Ultimate: 32.0 MPa
- Elongation at Break: 15 %
$ 1923/MT
- Bulk Density: 0.400 - 0.561 g/cc
- Particle Size: 15 - 25 µm
- Melting Point: 114 - 172 °C
- Oxygen Index: 63 - 77 %
- Optical Density: 0.26 - 2.6
- Optical Density: 0.33 - 2.93
$ 2123/MT
- Density: 0.930 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 26.2 MPa
- Film Tensile Strength at Yield, MD: 14.5 MPa
$ 1938/MT
- Permeability: 0.030
- Thickness: 38.1 microns
- Thickness: 50.8 microns
- Tensile Strength at Break: 0.138 MPa
- Elongation at Break: 120 %
$ 2272/MT
- Density: 0.9178 g/cc
- Thickness: 20.3 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 10.60 MPa
- Film Tensile Strength at Yield, TD: 11.29 MPa
$ 1578/MT
- Viscosity Measurement: 7.6 @Temperature 160 °C
- Viscosity Measurement: 8.8 @Temperature 160 °C
- Viscosity Measurement: 10.5 @Temperature 160 °C
- Viscosity Measurement: 13.9 @Temperature 160 °C
- Viscosity Measurement: 36 @Temperature 160 °C
$ 1863/MT
- Viscosity Measurement: 3.8 @Temperature 160 °C
- Viscosity Measurement: 5.0 @Temperature 160 °C
- Viscosity Measurement: 8.5 @Temperature 160 °C
- Viscosity Measurement: 12.5 @Temperature 160 °C
- Viscosity Measurement: 14.7 @Temperature 160 °C
$ 1619/MT
- Density: 0.9255 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 16.28 MPa
- Film Tensile Strength at Yield, TD: 19.73 MPa
$ 1498/MT
- Mooney Viscosity: >= 37 @Temperature 121 °C
- Hardness, Shore A: 75
- Tensile Strength, Ultimate: 17.9 MPa
- Elongation at Break: 300 %
- 200% Modulus: 0.00970 GPa
$ 1666/MT
- Density: 0.917 g/cc
- Water Vapor Transmission: 27.9 g/m²/day
- Thickness: >= 7.62 microns
- Melt Index of Compound: 10 g/10 min
- Neck In: 3.50 cm
$ 2388/MT
- Density: 0.933 g/cc
- Melt Index of Compound: 155 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 52
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 16.5 MPa
$ 2145/MT
- Specific Gravity: 1.021 g/cc
- pH: 6.0 - 8.0
- Viscosity Measure: 435 cSt @Temperature 37.8 °C
- Viscosity Measure: 790 - 870 cSt @Temperature 25.0 °C
- Molecular Weight: 4700 g/mol
$ 1516/MT
- Specific Gravity: 1.018 g/cc
- Maximum Moisture Content: 0.050
- ASTM Color: <= 35
- Specific Heat Capacity: 2.08 J/g-°C @Temperature 20.0 °C
- Specific Heat Capacity: 2.27 J/g-°C @Temperature 60.0 °C
$ 1515/MT
- Solids Content: 50.5 - 51.5 %
- Particle Mesh Size: 100 Mesh
- Particle Mesh Size: 325 Mesh
- pH: 7.2 - 7.8
- Brookfield Viscosity: 50 - 350 cP
$ 1844/MT
- Density: 0.923 g/cc
- Thickness: 40.0 microns
- Melt Flow: 0.70 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.0 MPa
- Film Tensile Strength at Yield, TD: 11.4 MPa
$ 1939/MT
- Density: 0.935 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.5 g/10 min
- Film Tensile Strength at Yield, MD: 16.9 MPa
- Film Tensile Strength at Yield, TD: 17.59 MPa
$ 1601/MT
- Density: 0.952 g/cc
- Viscosity: 39000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 80000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 180000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 40 g/10 min @Load 2.16 kg
$ 1475/MT
- Density: 0.915 g/cc
- Thickness: 51.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Film Elongation at Break, MD: 640 %
- Film Elongation at Break, TD: 670 %
$ 2159/MT
- Density: 1.116 g/cc
- Mooney Viscosity: 82 @Temperature 100 °C
- Hardness, Shore A: 75
- Tensile Strength, Ultimate: 18.8 MPa
- Elongation at Break: 155 %
$ 2211/MT
- Melt Flow: 6.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Ultimate: 25.5 MPa
- Tensile Strength, Yield: 26.2 MPa
- Elongation at Break: 30 %
- Izod Impact, Notched: 1.01 J/cm
$ 2276/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Film Tensile Strength at Yield, MD: 31.46 MPa
- Film Tensile Strength at Yield, TD: 30.40 MPa
- Film Elongation at Break, MD: 527 %
$ 2423/MT
- Density: 1.10 g/cc
- Solids Content: 57 %
- Particle Size: 1.95 µm
- pH: 8.2
- Brookfield Viscosity: 760 cP
- Glass Transition Temp, Tg: 6.00 °C
$ 1599/MT
- Density: 0.900 g/cc
- Melt Flow: 1.9 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 1.07 GPa
$ 1670/MT
- Specific Gravity: 0.901 g/cc
- Linear Mold Shrinkage: 0.0044 - 0.0048 cm/cm
- Linear Mold Shrinkage: 0.0050 - 0.0055 cm/cm
- Melt Flow: 13.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 16.1 MPa
$ 1579/MT
- Solids Content: 49.5 - 50.5 %
- pH: 7.5 - 8.1
- Brookfield Viscosity: 50 - 200 cP
- Surface Tension: 33 - 43 dynes/cm
- Minimum film formation temperature: <0°C
$ 1493/MT
- Viscosity Measurement: 1.9 @Temperature 160 °C
- Viscosity Measurement: 4.5 @Temperature 160 °C
- Viscosity Measurement: 6.5 @Temperature 160 °C
- Viscosity Measurement: 12 @Temperature 160 °C
- Viscosity Measurement: 16.9 @Temperature 160 °C
$ 1504/MT
- Density: 0.870 g/cc
- Mooney Viscosity: 8.0 @Temperature 121 °C
- Melt Flow: 5.0 g/10 min
- Hardness, Shore A: 70
- Tensile Strength, Ultimate: 6.21 MPa
$ 2294/MT
- Density: 0.910 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.5 g/10 min @Load 2.16 kg
- Film Elongation at Break, MD: 527 %
- Film Elongation at Break, TD: 664 %
$ 1499/MT
- Density: 0.926 g/cc
- Viscosity: 22000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 33000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 39000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 85 g/10 min @Load 2.16 kg
$ 1587/MT
- Density: 0.980 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 100 @Temperature 125 °C
- Crystallization Temperature: 40.0 °C
- Carbon Black Content (N650): 32 phr
$ 1563/MT
- Specific Gravity: 1.14 - 1.158 g/cc
- Viscosity: 550 - 750 cP
- Maximum Moisture Content: 0.050
- ASTM Color: 0.00 - 150
- Acid Value: 0.00 - 0.10
$ 1915/MT
- Water Vapor Transmission: 0.650 g/m²/day
- Oxygen Transmission: 0.571 cc-mm/m²-24hr-atm
- Thickness: 152 microns
- Film Elongation at Break, MD: 80 %
- Film Elongation at Break, TD: 70 %
$ 2101/MT
- Density: 1.339 g/cc
- Mooney Viscosity: 21 @Temperature 100 °C
- Hardness, Shore A: 61
- Tensile Strength, Ultimate: 7.00 MPa
- Elongation at Break: 492 %
$ 2292/MT
- Density: 0.923 g/cc
- Melt Flow: 0.70 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
- Film Elongation at Break, MD: 360 %
$ 1766/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.9 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus, 1% Secant: 1240 MPa
$ 1920/MT
- Density: 0.870 g/cc
- Melt Index of Compound: 30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 72
- Hardness, Shore D: 20
- Tensile Strength, Ultimate: 3.30 MPa
$ 1472/MT
- Density: 0.920 g/cc
- Thickness: 25.0 microns
- Melt Flow: 0.95 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 9.90 MPa
- Film Tensile Strength at Yield, TD: 10.1 MPa
$ 1956/MT
- Density: 0.918 g/cc
- ESCR 100% Igepal®: <= 1.0 hour @Temperature 50.0 °C
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength at Break: 9.65 MPa
$ 1501/MT
- Density: 0.938 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 17.6 MPa
- Tensile Strength, Yield: 7.90 MPa
- Elongation at Break: 600 %
- Vicat Softening Point: 76.1 °C
$ 1896/MT
- Density: 0.930 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 15.2 MPa
- Film Tensile Strength at Yield, TD: 15.2 MPa
$ 1483/MT
- Density: 0.900 g/cc
- Thickness: 50.8 microns
- Melt Index of Compound: 8.7 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 102
- Film Tensile Strength at Yield, MD: 21.6 MPa
$ 1492/MT
- Density: 0.938 g/cc
- Thickness: 60.0 microns
- Melt Flow: 5.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 20.7 MPa
- Film Tensile Strength at Yield, MD: 8.10 MPa
$ 1931/MT
- Density: 0.949 g/cc
- Density: 0.959 g/cc
- High Load Melt Index: 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.080 g/10 min @Load 2.16 kg, Temperature 190 °C
- PENT: >= 6000 hour
$ 1524/MT
- Density: 0.914 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.5 g/10 min
- Film Tensile Strength at Yield, MD: 8.501 MPa
- Film Tensile Strength at Yield, TD: 8.439 MPa
$ 1993/MT
- Density: 1.083 g/cc
- Mooney Viscosity: 62 @Temperature 100 °C
- Hardness, Shore A: 69
- Tensile Strength, Ultimate: 18.8 MPa
- Elongation at Break: 480 %
$ 1884/MT
- Density: 0.860 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 20 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 5 mass%
$ 2101/MT
- Density: 1.083 g/cc
- Mooney Viscosity: 62 @Temperature 100 °C
- Hardness, Shore A: 69
- Tensile Strength, Ultimate: 18.8 MPa
- Elongation at Break: 480 %
$ 2253/MT
- Viscosity Measurement: 3.1
- Viscosity Measurement: 6.9
- Viscosity Measurement: 10.5
- Viscosity Measurement: 16
- Viscosity Measurement: 2.6 @Temperature 160 °C
$ 2117/MT
- Density: 1.083 g/cc
- Mooney Viscosity: 62 @Temperature 100 °C
- Hardness, Shore A: 69
- Tensile Strength, Ultimate: 18.8 MPa
- Elongation at Break: 480 %
$ 1838/MT
- Density: 0.885 g/cc
- Melt Index of Compound: 30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 6.40 MPa
- Tensile Strength, Yield: 3.80 MPa
$ 1699/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.9 MPa
- Elongation at Yield: 10 %
- Flexural Modulus, 1% Secant: 1020 MPa
$ 1864/MT
- Density: 0.930 g/cc
- Filler Content: 15 %
- Melt Flow: 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 87
- Hardness, Shore D: 37
$ 2593/MT
- Density: 0.900 g/cc
- Melt Flow: 7.0 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Yield: 11 %
- Flexural Modulus: 0.550 GPa
$ 2324/MT
- Density: 0.870 g/cc
- Mooney Viscosity: 8.0 @Temperature 121 °C
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 75
- Hardness, Shore D: 21
$ 2310/MT
- Density: 1.055 g/cc
- Solids Content: >= 93.1 %
- Viscosity: 700 cP @Temperature 25.0 °C
- Flash Point: >= 149 °C
$ 1660/MT
- Thickness: 50.8 microns
- Film Elongation at Break, MD: 700 %
- Film Elongation at Break, TD: 750 %
- Secant Modulus, MD: 0.289 GPa
- Secant Modulus, TD: 0.317 GPa
$ 2476/MT
- Density: 0.865 g/cc
- Viscosity: 885000 cP @Shear Rate 100 1/s, Temperature 190 °C
- Viscosity: 1.38e+6 cP @Shear Rate 10.0 1/s, Temperature 190 °C
- Viscosity: 1.51e+6 cP @Shear Rate 1.58 1/s, Temperature 190 °C
- Viscosity: 1.55e+6 cP @Shear Rate 0.100 1/s, Temperature 190 °C
$ 1650/MT
- Hardness, Shore D: 70
- Tensile Strength, Ultimate: >= 28.0 MPa
- Elongation at Break: 3.0 %
- Modulus of Elasticity: 3.10 GPa
- Adhesive Bond Strength: >= 13.0 MPa
- Cure Time: 960 - 1440 min
$ 1920/MT
- Density: 0.885 g/cc
- Melt Flow: 30 g/10 min
- Melting Point: 83.0 °C
$ 1453/MT
- Density: 1.32 g/cc
- Solids Content: >= 99 %
- Viscosity Measurement: 16 - 26
- Collected Volatile Condensable Material: 0.00 %
- Hardness, Shore D: 70
$ 2305/MT
- Density: 0.922 g/cc
- Thickness: 40.0 microns
- Melt Flow: 2.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 11.4 MPa
- Film Tensile Strength at Yield, TD: 10.3 MPa
$ 1845/MT
- Density: 0.902 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.0 g/10 min
- Film Tensile Strength at Yield, MD: 7.24 MPa
- Film Tensile Strength at Yield, TD: 6.89 MPa
$ 2080/MT
- Water Absorption: 0.24 %
- Thickness: 0.380 microns
- Thickness: 0.330 - 0.465 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2494/MT
- Density: 0.910 g/cc
- Melt Index of Compound: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melting Point: 120 °C
- Vicat Softening Point: 90.0 °C
$ 1772/MT
- Density: 0.927 g/cc
- Melt Flow: 11 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 12.3 MPa
- Tensile Strength, Yield: 10.8 MPa
- Elongation at Break: 600 %
- Vicat Softening Point: 92.2 °C
$ 1663/MT
- Density: 0.870 g/cc
- Brookfield Viscosity: 8200 cP @Temperature 177 °C
- Collected Volatile Condensable Material: <= 0.15 %
- Tensile Strength, Ultimate: 1.55 MPa
- Elongation at Break: 106 %
$ 1476/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: >= 1500 hour @Temperature 50.0 °C
- High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 190 °C
- Hardness, Shore D: 57
- Tensile Strength at Break: 36.5 MPa
$ 1465/MT
- Density: 0.935 g/cc
- Thickness: 25.0 microns
- Melt Flow: 2.5 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 15.2 MPa
- Film Tensile Strength at Yield, MD: 17.9 MPa
$ 1645/MT
- Density: 0.910 g/cc
- Melt Index of Compound: 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 96
- Hardness, Shore D: 41
- Tensile Strength, Ultimate: 21.0 MPa
$ 1654/MT
- Density: 0.926 g/cc
- Thickness: 40.0 microns
- Melt Flow: 1.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 24.8 MPa
- Film Tensile Strength at Yield, MD: 12.7 MPa
$ 1538/MT
- Density: 0.920 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- High Load Melt Index: 44 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 44
$ 1651/MT
- Density: 0.920 g/cc
- Thickness: 20.3 microns
- Melt Flow: 0.85 g/10 min
- Antiblock Level: 5000 ppm
- Slip Level: 900 ppm
$ 2112/MT
- Density: 0.870 g/cc
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1495/MT
- Density: 0.953 g/cc
- Viscosity: 32000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 46000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 54000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 65 g/10 min @Load 2.16 kg
$ 1730/MT
- Density: 0.860 g/cc
- Volatiles: <= 0.40 %
- Mooney Viscosity: 27 @Temperature 125 °C
- Ash: <= 0.10 %
- ENB: 0.75 mass%
$ 1967/MT
- Density: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 10 %
- Flexural Modulus: 0.758 GPa
$ 1827/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 22.8 MPa
- Elongation at Yield: 4.5 %
- Flexural Modulus, 1% Secant: 1210 MPa
$ 1492/MT
- Water Vapor Transmission: 4.20 g/m²/day
- Oxygen Transmission: 0.472 cc-mm/m²-24hr-atm
- Nitrogen Transmission: 0.0709 cc-mm/m²-24hr-atm
- Carbon Dioxide Transmission: 2.13 cc-mm/m²-24hr-atm
- Thickness: 25.4 microns
$ 1457/MT
- Water Absorption: <= 0.20 %
- Viscosity Measure: 52 cSt @Temperature 25.0 °C
- Thickness: 2.40 - 5.80 microns
- Tensile Strength, Ultimate: 80.0 - 94.0 MPa
- Elongation at Break: 5.5 - 10.5 %
$ 1521/MT
- Density: 0.951 g/cc
- Melt Index of Compound: 44 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength at Break: 26.9 MPa
- Tensile Strength, Yield: 26.9 MPa
$ 2043/MT
- Density: 0.902 g/cc
- Thickness: 25.0 microns
- Melt Flow: 3.0 g/10 min @Load 2.16 kg
- Film Tensile Strength at Yield, MD: 5.70 MPa
- Film Tensile Strength at Yield, TD: 4.80 MPa
$ 1960/MT
- Density: 0.920 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.85 g/10 min
- Film Tensile Strength at Yield, MD: 11.80 MPa
- Film Tensile Strength at Yield, TD: 12.5 MPa
$ 1692/MT
- Viscosity Measurement: 1.8 @Temperature 160 °C
- Viscosity Measurement: 6.0 @Temperature 160 °C
- Viscosity Measurement: 8.0 @Temperature 160 °C
- Viscosity Measurement: 13 @Temperature 160 °C
- Viscosity Measurement: 20.8 @Temperature 160 °C
$ 2465/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 44 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.9 MPa
- Flexural Modulus, 1% Secant: 1370 MPa
- Izod Impact, Notched: 0.320 J/cm @Temperature -20.0 °C
$ 1535/MT
- Density: 0.930 g/cc
- Thickness: 0.100 - 0.150 microns
- CTE, linear: 49.0 µm/m-°C @Temperature 50.0 - 410 °C
- Decomposition Temperature: >= 500 °C
- Refractive Index: 1.53
$ 1875/MT
- Density: 1.185 g/cc
- Mooney Viscosity: 47 @Temperature 100 °C
- Hardness, Shore A: 70
- Tensile Strength, Ultimate: 10.4 MPa
- Elongation at Break: 446 %
$ 2360/MT
- Thickness: 50.8 microns
- Film Elongation at Break, MD: 450 %
- Film Elongation at Break, TD: 500 %
- Secant Modulus, MD: 0.207 GPa
- Secant Modulus, TD: 0.207 GPa
$ 1602/MT
- Density: 1.16 g/cc
- Volatiles: <= 0.50 %
- Mooney Viscosity: 80 @Temperature 121 °C
- Chlorine Content: 36 %
$ 1608/MT
- Density: 0.9245 g/cc
- Thickness: 50.8 microns
- Melt Flow: 6.4 g/10 min
- Antiblock Level: 2900 ppm
- Slip Level: 2640 ppm
$ 2024/MT
- Density: 0.919 g/cc
- Thickness: 30.0 microns
- Melt Flow: 6.0 g/10 min @Load 2.16 kg
- Tensile Strength, Ultimate: 15.9 MPa
- Film Tensile Strength at Yield, MD: 9.00 MPa
$ 2489/MT
- Density: 0.930 g/cc
- Filler Content: 19.5 %
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 82
- Hardness, Shore D: 27
$ 2400/MT
- Density: 1.02 g/cc
- Solids Content: 52 %
- Particle Size: 1.25 µm
- pH: 7.8
- Brookfield Viscosity: 170 cP
$ 2208/MT
- Density: 1.02 g/cc
- Solids Content: 52 %
- Particle Size: 1.4 µm
- pH: 7.9
- Brookfield Viscosity: 126 cP
- Glass Transition Temp, Tg: 6.00 °C
$ 2046/MT
- Solids Content: 52 %
- Particle Size: 1.4 µm
- pH: 7.85
- Brookfield Viscosity: 180 cP
- Glass Transition Temp, Tg: -20.0 °C
- Minimum film formation temperature: <34°F
$ 1670/MT
- Density: 1.02 g/cc
- Solids Content: 52 %
- Particle Size: 1.4 µm
- pH: 7.8
- Brookfield Viscosity: 210 cP
- Glass Transition Temp, Tg: -11.0 °C
$ 1709/MT
- Solids Content: 51.5 - 52.5 %
- pH: 7.7 - 8.3
- Brookfield Viscosity: 100 - 300 cP
- Surface Tension: 40 - 50 dynes/cm
- Minimum film formation temperature: <0°C
$ 2152/MT
- Specific Gravity: 1.073 g/cc
- Viscosity Measure: 270 cSt @Temperature 55.0 °C
- Molecular Weight: 900 g/mol
- Maximum Moisture Content: 0.030
- Melting Point: 27.0 - 32.0 °C
$ 1671/MT
- Moisture Vapor Transmission: 1.80 cc-mm/m²-24hr-atm
- Oxygen Transmission: 32.0 cc-mm/m²-24hr-atm
- Viscosity Measurement: 24000
- Tensile Strength, Ultimate: 23.0 MPa
- Elongation at Break: 425 %
$ 2186/MT
- Density: 0.930 g/cc
- Filler Content: >= 1.0 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1515/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 102
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 8.0 %
$ 1460/MT
- Density: 1.064 g/cc
- Hardness, Shore A: 74
- Tensile Strength, Ultimate: 26.1 MPa
- Elongation at Break: 266 %
- 100% Modulus: 0.00560 GPa
$ 1684/MT
- Density: 1.283 g/cc
- Mooney Viscosity: 44 @Temperature 100 °C
- Hardness, Shore A: 90
- Hardness, Shore D: 46
- Tensile Strength, Ultimate: 15.13 MPa
$ 1455/MT
- Density: 0.930 g/cc
- Viscosity: 27000 cP @Shear Rate 5000 1/s, Temperature 190 °C
- Viscosity: 44000 cP @Shear Rate 1000 1/s, Temperature 190 °C
- Viscosity: 53000 cP @Shear Rate 300 1/s, Temperature 190 °C
- Melt Flow: 125 g/10 min @Load 2.16 kg
$ 1613/MT
- Density: 1.221 g/cc
- Viscosity: 770 cP
- Viscosity Measurement: 5.0 - 10
- Vapor Pressure: <= 1.30e-8 bar
- Heat of Vaporization: 360 J/g
$ 2275/MT
- Density: 0.8985 g/cc
- Filler Content: 0.25 - 0.50 %
- Melt Flow: 3.3 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 90
- Hardness, Shore A: 91
$ 1921/MT
- Specific Gravity: 1.02 g/cc
- Viscosity Measurement: 1050 - 1250
- Maximum Moisture Content: 0.060
- ASTM Color: <= 30
- Flash Point: >= 200 °C
$ 1633/MT
- Density: 0.919 g/cc
- Thickness: 20.3 microns
- Melt Flow: 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 12.27 MPa
- Film Tensile Strength at Yield, TD: 11.2 MPa
$ 1617/MT
- Density: 0.961 g/cc
- ESCR 100% Igepal®: 20 hour @Temperature 50.0 °C
- High Load Melt Index: 57 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 66
$ 1519/MT
- Viscosity Measurement: 2.5 @Temperature 160 °C
- Viscosity Measurement: 3.0 @Temperature 160 °C
- Viscosity Measurement: 7.5 @Temperature 160 °C
- Viscosity Measurement: 13 @Temperature 160 °C
- Viscosity Measurement: 22 @Temperature 160 °C
$ 1490/MT
- Density: 1.064 g/cc
- Mooney Viscosity: 48 @Temperature 100 °C
- Hardness, Shore A: 78
- Tensile Strength, Ultimate: 22.0 MPa
- Elongation at Break: 502 %
$ 1712/MT
- Density: 0.875 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1676/MT
- Specific Gravity: 0.920 g/cc
- Linear Mold Shrinkage: 0.0034 - 0.0044 cm/cm
- Linear Mold Shrinkage: 0.0041 - 0.0053 cm/cm
- Melt Flow: 14.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 13.62 MPa
$ 2238/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1536/MT
- Specific Gravity: 1.022 g/cc
- Viscosity Measure: 80 cSt @Temperature 98.9 °C
- Viscosity Measure: 600 cSt @Temperature 37.8 °C
- Viscosity Measure: 1250 cSt @Temperature 25.0 °C
- Viscosity Measure: 7200 cSt @Temperature 0.000 °C
$ 1663/MT
- Density: 0.900 g/cc
- Melt Flow: 2.0 g/10 min @Temperature 230 °C
- Tensile Strength, Yield: 35.2 MPa
- Elongation at Yield: 9.0 %
- Flexural Modulus: 1.59 GPa
$ 2078/MT
- Specific Gravity: 1.167 - 1.182 g/cc
- Viscosity: 350 - 450 cP
- Maximum Moisture Content: 0.050
- ASTM Color: 0.00 - 100
- Acid Value: 0.00 - 0.10
$ 1810/MT
- Density: 1.15 - 1.25 g/cc
- Viscosity: <= 260000 cP
- Hardness, Shore A: 40 - 50
- Tensile Strength, Ultimate: 2.30 - 2.90 MPa
- Elongation at Break: 450 %
$ 1540/MT
- Density: 0.905 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 94
- Tensile Strength at Break: 19.3 MPa
$ 2034/MT
- Density: 1.04 g/cc
- Melt Density: 0.963 g/cc
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 8.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 19.3 MPa
$ 1866/MT
- Water Absorption: <= 0.20 %
- Viscosity Measure: 870 cSt @Temperature 25.0 °C
- Thickness: 9.50 - 26.0 microns
- Tensile Strength, Ultimate: 80.0 - 94.0 MPa
- Elongation at Break: 5.5 - 10.5 %
$ 2385/MT
- Density: 1.18 g/cc
- Viscosity: 5.0 cP @Temperature 43.0 °C
- Vapor Pressure: <= 1.33e-7 bar @Temperature 43.0 °C
- Heat of Fusion: 136 J/g
- Heat of Vaporization: 360 J/g
$ 2083/MT
- Density: 0.947 g/cc
- Melt Index of Compound: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
- Tensile Strength at Break: 22.1 MPa
- Tensile Strength, Yield: 23.4 MPa
$ 1741/MT
- Water Absorption: 0.24 %
- Thickness: 0.140 microns
- Thickness: 0.110 - 0.170 microns
- Tensile Strength, Ultimate: 89.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1587/MT
- Density: 1.04 g/cc
- Melt Density: 0.963 g/cc
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 8.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 19.3 MPa
$ 1688/MT
- Density: 0.949 g/cc
- Density: 0.959 g/cc
- High Load Melt Index: 8.5 g/10 min @Load 21.6 kg, Temperature 190 °C
- Melt Index of Compound: 0.080 g/10 min @Load 2.16 kg, Temperature 190 °C
- PENT: >= 4000 hour
$ 2467/MT
- Density: 1.04 g/cc
- Melt Density: 0.963 g/cc
- Linear Mold Shrinkage: 0.0055 cm/cm
- Melt Flow: 8.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 19.3 MPa
Delivery Polymer Dow Chemical
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, general cargo ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.