$ 1697/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 6.6 %
- Thickness: 31.8 microns
- Melt Flow: 1.2 g/10 min
- Film Elongation at Break, MD: 190 %
$ 1458/MT
- Density: 0.965 g/cc
- Melt Flow: 7.7 g/10 min
- Spiral Flow: 26.7 cm
- Hardness, Shore D: 65
- Tensile Strength at Break: 15.33 MPa
$ 2190/MT
- Density: 0.959 g/cc
- Melt Flow: 0.057 g/10 min
- Film Tensile Strength at Yield, MD: 38.6 MPa
- Film Tensile Strength at Yield, TD: 33.1 MPa
- Film Elongation at Break, MD: 300 %
$ 1722/MT
- Density: 0.960 g/cc
- Thickness: 50.8 microns
- Melt Flow: 2.0 g/10 min
- Film Tensile Strength at Yield, MD: 22.8 MPa
- Film Tensile Strength at Yield, TD: 21.4 MPa
$ 1446/MT
- Density: 0.961 g/cc
- Melt Flow: 3.8 g/10 min
- Spiral Flow: 20.8 cm
- Hardness, Shore D: 69
- Tensile Strength at Break: 26.5 MPa
$ 2157/MT
- Density: 0.956 g/cc
- Melt Flow: 18 g/10 min
- Spiral Flow: 33.0 cm
- Hardness, Shore D: 69
- Tensile Strength at Break: 27.6 MPa
$ 1839/MT
- Density: 0.918 g/cc
- Environmental Stress Crack Resistance: >= 168 hour
- Thickness: 50.8 microns
- Melt Flow: 0.25 g/10 min
- Hardness, Shore D: 50
$ 2095/MT
- Density: 0.930 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.6 g/10 min
- Antiblock Level: 1000 ppm
- Slip Level: 300 ppm
$ 1486/MT
- Density: 0.919 g/cc
- Thickness: 31.8 microns
- Melt Flow: 0.70 g/10 min
- Hardness, Shore D: 46
- Tensile Strength at Break: 11.4 MPa
$ 2185/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- ESCR 100% Igepal®: 25 hour
- Melt Flow: 0.35 g/10 min
- Hardness, Shore D: 66
$ 1803/MT
- Density: 0.930 g/cc
- Vinyl Acetate Content: 9.0 %
- Melt Flow: 10 g/10 min
- Vicat Softening Point: 73.0 °C
- Melt Temperature: <= 232 °C
$ 2241/MT
- Density: 0.9205 g/cc
- Melt Flow: 1.8 g/10 min
- Hardness, Shore D: 56
- Tensile Strength at Break: 12.4 MPa
- Elongation at Break: >= 600 %
$ 1764/MT
- Vinyl Acetate Content: 4.0 %
- Thickness: 31.8 microns
- Melt Flow: 1.0 g/10 min
- Slip Level: 0.000 ppm
- Film Elongation at Break, MD: 340 %
$ 2350/MT
- Density: 0.921 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.8 g/10 min
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 300 %
$ 1560/MT
- Density: 0.949 g/cc
- Environmental Stress Crack Resistance: 200 hour
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 21 g/10 min
- Hardness, Shore D: 67
$ 1756/MT
- Density: 0.944 g/cc
- Water Vapor Transmission: 2.90 g/m²/day
- Thickness: 50.8 microns
- Melt Flow: 0.34 g/10 min
- Film Tensile Strength at Yield, MD: 22.1 MPa
$ 2016/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 800 %
$ 2156/MT
- Vinyl Acetate Content: 9.0 %
- Thickness: 50.8 microns
- Melt Flow: 3.2 g/10 min
- Hardness, Shore D: 94
- Film Tensile Strength at Yield, MD: 6.23 MPa
$ 1500/MT
- Vinyl Acetate Content: 4.0 %
- Thickness: 31.8 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 340 %
- Film Elongation at Break, TD: 500 %
$ 1976/MT
- Density: 0.931 g/cc
- Melt Flow: 3.0 g/10 min
- Hardness, Shore D: 59
- Tensile Strength at Break: 15.2 MPa
- Elongation at Break: >= 500 %
$ 1555/MT
- Density: 0.920 g/cc
- Thickness: 31.8 microns
- Melt Flow: 0.90 g/10 min
- Tensile Strength at Break: 14.5 MPa
- Film Elongation at Break, MD: 200 %
$ 1924/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 5.52 MPa
- Elongation at Break: 500 %
- Feed Temperature: 107 - 113 °C
- Zone 2: 116 - 127 °C
$ 2002/MT
- Density: 0.910 g/cc
- Water Vapor Transmission: 5.60 g/m²/day
- Thickness: 50.8 microns
- Melt Flow: 1.7 g/10 min
- Film Tensile Strength at Yield, MD: 8.80 MPa
$ 1802/MT
- Density: 0.9225 g/cc
- Particle Size: 5.0 - 50 µm
- Maximum Moisture Content: 0.10
- Melt Flow: 4.7 g/10 min
- Hardness, Shore D: 53
$ 1605/MT
- Density: 0.9245 g/cc
- Particle Size: 5.0 - 50 µm
- Maximum Moisture Content: 0.10
- Melt Flow: 23 g/10 min
- Hardness, Shore D: 54
$ 1623/MT
- Density: 0.926 g/cc
- Melt Flow: 50 g/10 min
- Spiral Flow: 49.0 cm
- Hardness, Shore D: 52
- Tensile Strength at Break: 10.3 MPa
$ 1567/MT
- Density: 0.946 g/cc
- Melt Flow: 45 g/10 min
- Spiral Flow: 46.7 cm
- Hardness, Shore D: 62
- Tensile Strength at Break: 22.1 MPa
$ 1530/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 760 %
$ 1594/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 30 hour
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.30 g/10 min
- Hardness, Shore D: 67
$ 1721/MT
- Density: 0.930 g/cc
- Melt Flow: 4.0 g/10 min
- Feed Temperature: 141 °C
- Zone 2: 149 °C
- Zone 3: 157 °C
$ 2131/MT
- Density: 1.47 g/cc
- Melt Flow: 0.70 g/10 min
- Feed Temperature: 146 °C
- Zone 2: 154 °C
- Zone 3: 163 °C
$ 1467/MT
- Density: 0.919 g/cc
- Melt Flow: 9.0 g/10 min
- Hardness, Shore D: 48
- Tensile Strength, Yield: 8.96 MPa
- Elongation at Yield: 14 %
$ 1645/MT
- Density: 0.960 g/cc
- Melt Flow: 18 g/10 min
$ 2123/MT
- Density: 0.924 g/cc
- Melt Flow: 20 g/10 min
- Spiral Flow: 32.0 cm
- Hardness, Shore D: 57
- Tensile Strength at Break: 8.27 MPa
$ 1773/MT
- Bulk Density: 0.593 - 0.625 g/cc
- Density: 0.948 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 20.3 cm
- Tensile Strength at Break: 24.1 MPa
$ 2018/MT
- Density: 0.926 g/cc
- Particle Size: 5.0 - 50 µm
- Maximum Moisture Content: 0.10
- Melt Flow: 9.5 g/10 min
- Hardness, Shore D: 38
$ 1694/MT
- Density: 0.946 g/cc
- Melt Flow: 1.2 g/10 min
- Spiral Flow: 18.3 cm
- Hardness, Shore D: 66
- Tensile Strength at Break: 16.0 MPa
$ 1920/MT
- Density: 0.922 g/cc
- Melt Flow: 38 g/10 min
- Hardness, Shore D: 41
- Tensile Strength at Break: 8.96 MPa
- Tensile Strength, Yield: 12.8 MPa
$ 1591/MT
- Density: 0.943 g/cc
- Melt Flow: 13 g/10 min
- Tensile Strength at Break: 15.3 MPa
- Elongation at Break: 650 %
- 1% Secant Modulus: 552 MPa
$ 1846/MT
- Density: 0.954 g/cc
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Yield: 9.0 %
$ 2061/MT
- Density: 0.951 g/cc
- Oxidative Induction Time (OIT): >= 80 min
- Melt Flow: 0.60 g/10 min
- Tensile Strength at Break: 24.7 MPa
- Elongation at Break: 810 %
$ 1755/MT
- Density: 0.930 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.40 g/10 min
- Film Tensile Strength at Yield, MD: 14.5 MPa
- Film Tensile Strength at Yield, TD: 15.2 MPa
$ 2369/MT
- Density: 0.962 g/cc
- Melt Flow: 0.29 g/10 min
- Hardness, Shore D: 68
- Tensile Strength at Break: 30.7 MPa
- Elongation at Break: 960 %
$ 1886/MT
- Density: 0.950 g/cc
- Melt Flow: 0.50 g/10 min
- Hardness, Shore D: 61
- Tensile Strength at Break: 15.2 MPa
- Tensile Strength, Yield: 22.1 MPa
$ 1780/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 30 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.30 g/10 min
- Hardness, Shore D: 67
$ 1457/MT
- Density: 0.924 g/cc
- Thickness: 31.8 microns
- Thickness: 31.8 microns
- Melt Flow: 3.0 g/10 min
- Antiblock Level: 6000 ppm
$ 1909/MT
- Density: 1.39 g/cc
- Tensile Strength at Break: 16.5 MPa
- Elongation at Break: 220 %
- Feed Temperature: 129 - 135 °C
- Zone 2: 129 - 135 °C
$ 1837/MT
- Density: 0.931 g/cc
- Melt Flow: 3.0 g/10 min
- Film Elongation at Break, MD: 450 %
- Film Elongation at Break, TD: 540 %
- Dart Drop Test: 80.0 g
$ 1547/MT
- Density: 0.940 g/cc
- Water Vapor Transmission: 9.00 g/m²/day
- Environmental Stress Crack Resistance: >= 1000 hour
- Thickness: 31.8 microns
- Melt Flow: 0.17 g/10 min
$ 1612/MT
- Density: 0.924 g/cc
- Thickness: 31.8 microns
- Thickness: 31.8 microns
- Melt Flow: 3.0 g/10 min
- Antiblock Level: 0.000 ppm
$ 2078/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 550 %
- Film Elongation at Break, TD: 625 %
$ 1609/MT
- Density: 0.930 g/cc
- Melt Flow: 0.40 g/10 min
- Tensile Strength at Break: 13.8 MPa
- Tensile Strength, Yield: 16.5 MPa
- Elongation at Break: 660 %
$ 1469/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 760 %
$ 1948/MT
- Water Vapor Transmission: 85.3 g/m²/day
- Oxygen Transmission Rate: 8900 cc/m²/day
- Vinyl Acetate Content: 13.5 %
- Thickness: 38.1 microns
- Melt Flow: 0.50 g/10 min
$ 1579/MT
- Density: 0.952 g/cc
- Environmental Stress Crack Resistance: 25 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.35 g/10 min
- Hardness, Shore D: 66
$ 1833/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 760 %
$ 2449/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 30 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.30 g/10 min
- Hardness, Shore D: 67
$ 2550/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 550 %
- Film Elongation at Break, TD: 625 %
$ 1565/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 20.7 MPa
- Elongation at Break: 220 %
- Oxygen Index: 26 %
- Feed Temperature: 107 - 113 °C
$ 2236/MT
- Density: 0.924 g/cc
- Water Vapor Transmission: 6.20 g/m²/day
- Thickness: 50.8 microns
- Melt Flow: 2.2 g/10 min
- Film Tensile Strength at Yield, MD: 12.6 MPa
$ 1503/MT
- Density: 0.930 g/cc
- Thickness: 31.8 microns
- Melt Flow: 6.2 g/10 min
- Film Elongation at Break, MD: 500 %
- Film Elongation at Break, TD: 600 %
$ 1738/MT
- Density: 0.946 g/cc
- Melt Flow: 40 g/10 min
- Spiral Flow: 46.7 cm
- Hardness, Shore D: 62
- Tensile Strength at Break: 22.1 MPa
$ 1984/MT
- Density: 0.919 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.5 g/10 min
- Hardness, Shore D: 51
- Tensile Strength at Break: 10.3 MPa
$ 1636/MT
- Vinyl Acetate Content: 4.0 %
- Thickness: 31.8 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 340 %
- Film Elongation at Break, TD: 500 %
$ 1770/MT
- Density: 0.918 g/cc
- Melt Flow: 16 g/10 min
- Hardness, Shore D: 56
- Tensile Strength at Break: 10.3 MPa
- Elongation at Break: 640 %
$ 1575/MT
- Density: 0.927 g/cc
- ESCR 100% Igepal®: 16 hour
- Melt Flow: 0.30 g/10 min
- Tensile Strength at Break: 15.2 MPa
- Tensile Strength, Yield: 15.2 MPa
$ 1903/MT
- Density: 0.921 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.8 g/10 min
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 300 %
$ 2543/MT
- Density: 0.919 g/cc
- Thickness: 31.8 microns
- Melt Flow: 2.0 g/10 min
- Tensile Strength at Break: 12.4 MPa
- Film Elongation at Break, MD: 200 %
$ 1642/MT
- Vinyl Acetate Content: 4.0 %
- Thickness: 31.8 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 340 %
- Film Elongation at Break, TD: 500 %
$ 2160/MT
- Density: 0.919 g/cc
- Thickness: 50.8 microns
- Melt Flow: 1.5 g/10 min
- Hardness, Shore D: 47
- Tensile Strength at Break: 12.2 MPa
$ 1775/MT
- Density: 0.946 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- ESCR, Bottle: >= 1000 hour
- Melt Flow: 0.20 g/10 min
- Hardness, Shore D: 65
$ 1711/MT
- Density: 0.925 g/cc
- Thickness: 38.1 microns
- Melt Flow: 3.5 g/10 min
- Film Elongation at Break, MD: 690 %
- Film Elongation at Break, TD: 740 %
$ 1901/MT
- Density: 0.918 g/cc
- Environmental Stress Crack Resistance: >= 168 hour
- Thickness: 50.8 microns
- Melt Flow: 0.25 g/10 min
- Hardness, Shore D: 50
$ 1594/MT
- Density: 0.927 g/cc
- Particle Mesh Size: 35 Mesh
- Melt Flow: 11 g/10 min
- Hardness, Shore D: 38
- Tensile Strength at Break: 11.7 MPa
$ 1468/MT
- Density: 0.921 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.8 g/10 min
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 300 %
$ 2384/MT
- Water Vapor Transmission: 85.3 g/m²/day
- Oxygen Transmission Rate: 8900 cc/m²/day
- Vinyl Acetate Content: 13.5 %
- Thickness: 38.1 microns
- Melt Flow: 0.50 g/10 min
$ 1903/MT
- Density: 0.910 g/cc
- Oxidative Induction Time (OIT): 75 min
- Melt Flow: 1.7 g/10 min
- Vicat Softening Point: 74.0 °C
- Melt Temperature: >= 210 °C
$ 2065/MT
- Density: 0.922 g/cc
- Particle Mesh Size: 50 Mesh
- Melt Flow: 4.5 g/10 min
- Hardness, Shore D: 53
- Tensile Strength at Break: 12.4 MPa
$ 1850/MT
- Density: 0.925 g/cc
- Thickness: 12.7 microns
- Melt Flow: 3.5 g/10 min
- Film Elongation at Break, MD: 500 %
- Film Elongation at Break, TD: 630 %
$ 2150/MT
- Density: 0.918 g/cc
- Melt Flow: 13.5 g/10 min
- Hardness, Shore D: 50
- Tensile Strength at Break: 11.0 MPa
- Elongation at Break: 500 %
$ 1957/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 550 %
- Film Elongation at Break, TD: 625 %
$ 1703/MT
- Density: 0.9205 g/cc
- ESCR, Bottle: >= 1000 hour
- Melt Flow: 0.75 g/10 min
- Hardness, Shore D: 51
- Tensile Strength at Break: 15.0 MPa
$ 2049/MT
- Density: 0.931 g/cc
- Water Vapor Transmission: 54.0 g/m²/day
- Thickness: 50.8 microns
- Melt Flow: 3.1 g/10 min
- Film Tensile Strength at Yield, MD: 12.7 MPa
$ 1519/MT
- Density: 0.958 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.85 g/10 min
- Film Tensile Strength at Yield, MD: 25.5 MPa
- Film Tensile Strength at Yield, TD: 26.2 MPa
$ 1457/MT
- Density: 0.9185 g/cc
- Melt Flow: 1.3 g/10 min
- Hardness, Shore D: 48
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: >= 600 %
$ 2041/MT
- Density: 0.927 g/cc
- Water Vapor Transmission: 4.30 g/m²/day
- Thickness: 50.8 microns
- Melt Flow: 4.5 g/10 min
- Film Tensile Strength at Yield, MD: 11.8 MPa
$ 1851/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 30 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.30 g/10 min
- Hardness, Shore D: 67
$ 1468/MT
- Density: 0.921 g/cc
- Water Vapor Transmission: 6.80 g/m²/day
- Thickness: 50.8 microns
- Melt Flow: 2.0 g/10 min
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 2003/MT
- Density: 0.918 g/cc
- Environmental Stress Crack Resistance: >= 168 hour
- Thickness: 50.8 microns
- Melt Flow: 0.25 g/10 min
- Hardness, Shore D: 50
$ 1771/MT
- Density: 0.958 g/cc
- Environmental Stress Crack Resistance: 80 hour
- Melt Flow: 0.35 g/10 min
- High Load Melt Index: 35 g/10 min
- Tensile Strength, Yield: 29.6 MPa
$ 1505/MT
- Density: 0.919 g/cc
- Melt Flow: 4.0 g/10 min
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Yield: 640 %
- 1% Secant Modulus: 198 MPa
- Brittleness Temperature: <= -76.0 °C
$ 2107/MT
- Density: 0.948 g/cc
- Melt Flow: 57 g/10 min
- Spiral Flow: 53.8 cm
- Hardness, Shore D: 66
- Tensile Strength at Break: 25.4 MPa
$ 1810/MT
- Density: >= 0.960 g/cc
- Melt Flow: 0.35 g/10 min
- Hardness, Shore D: 68
- Tensile Strength at Break: 30.3 MPa
- Elongation at Break: >= 600 %
$ 1705/MT
- Density: 0.949 g/cc
- Water Vapor Transmission: 3.30 g/m²/day
- Oxygen Transmission Rate: 2400 cc/m²/day
- Thickness: 50.8 microns
- Melt Flow: 0.33 g/10 min
$ 2117/MT
- Density: 0.912 g/cc
- Particle Mesh Size: 50 Mesh
- Melt Flow: 70 g/10 min
- Hardness, Shore D: 51
- Tensile Strength at Break: 6.89 MPa
$ 1618/MT
- Density: 0.915 g/cc
- Particle Mesh Size: 50 Mesh
- Melt Flow: 22 g/10 min
- Hardness, Shore D: 52
- Tensile Strength at Break: 11.0 MPa
$ 1801/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 2.5 %
- Thickness: 31.8 microns
- Melt Flow: 2.5 g/10 min
- Film Elongation at Break, MD: 350 %
$ 2342/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 800 %
$ 1797/MT
- Density: 0.955 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Absorption Coefficient: 440
- Carbon Black Loading: 2.6 %
- Melt Flow: 0.15 g/10 min
$ 1495/MT
- Density: 0.923 g/cc
- Water Vapor Transmission: 7.80 g/m²/day
- Melt Flow: 5.6 g/10 min
- Hardness, Shore D: 53
- Tensile Strength at Break: 12.4 MPa
$ 2111/MT
- Density: 0.954 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Yield: 9.0 %
$ 2175/MT
- Density: 0.919 g/cc
- Melt Flow: 4.0 g/10 min
- Tensile Strength, Yield: 11.0 MPa
- Elongation at Yield: 640 %
- 1% Secant Modulus: 198 MPa
- Brittleness Temperature: <= -76.0 °C
$ 1667/MT
- Density: 0.933 g/cc
- Melt Flow: 3.0 g/10 min
- Vicat Softening Point: 88.0 °C
- Melt Temperature: >= 210 °C
$ 1535/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 6.6 %
- Thickness: 50.8 microns
- Melt Flow: 0.50 g/10 min
- Film Elongation at Break, MD: 500 %
$ 1678/MT
- Density: 0.918 g/cc
- Melt Flow: 10 g/10 min
- Hardness, Shore D: 54
- Tensile Strength at Break: 10.9 MPa
- Elongation at Break: 580 %
$ 2167/MT
- Density: 0.960 g/cc
- Melt Flow: 7.9 g/10 min
$ 2205/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 25 hour
- ESCR Blow Molding: 25 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.38 g/10 min
$ 1592/MT
- Density: 0.924 g/cc
- Vinyl Acetate Content: 2.5 %
- Thickness: 31.8 microns
- Melt Flow: 2.5 g/10 min
- Antiblock Level: 1900 ppm
$ 1448/MT
- Density: 0.926 g/cc
- Melt Flow: 50 g/10 min
- Spiral Flow: 45.5 cm
- Hardness, Shore D: 60
- Tensile Strength at Break: 8.96 MPa
$ 1936/MT
- Density: 0.923 g/cc
- Melt Flow: 3.7 g/10 min
- Hardness, Shore D: 53
- Tensile Strength at Break: 12.1 MPa
- Elongation at Break: 550 %
$ 2366/MT
- Density: 0.920 g/cc
- ESCR 100% Igepal®: 168 hour
- Thickness: 50.8 microns
- Melt Flow: 0.18 g/10 min
- Antiblock Level: 0.000 ppm
$ 1587/MT
- Density: 0.927 g/cc
- Vinyl Acetate Content: 4.5 %
- Thickness: 31.8 microns
- Melt Flow: 1.2 g/10 min
- Film Elongation at Break, MD: 350 %
$ 1830/MT
- Density: 0.919 g/cc
- Thickness: 31.8 microns
- Melt Flow: 2.2 g/10 min
- Tensile Strength at Break: 13.6 MPa
- Film Elongation at Break, MD: 250 %
$ 2097/MT
- Density: 0.920 g/cc
- Thickness: 31.8 microns
- Melt Flow: 6.5 g/10 min
- Film Elongation at Break, MD: 225 %
- Film Elongation at Break, TD: 450 %
$ 2322/MT
- Bulk Density: 0.593 - 0.625 g/cc
- Density: 0.942 g/cc
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 43.7 cm
- Hardness, Shore D: 61
$ 2310/MT
- Bulk Density: 0.593 - 0.625 g/cc
- Density: 0.946 g/cc
- Melt Flow: 19.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 30.5 cm
- Hardness, Shore D: 70
$ 2382/MT
- Bulk Density: 0.529 - 0.593 g/cc
- Density: 0.952 g/cc
- Melt Flow: 20 g/10 min @Load 0.980 kg, Temperature 190 °C
- Spiral Flow: 29.5 cm
- Hardness, Shore D: 76
$ 1761/MT
- Density: 0.955 g/cc
- Melt Flow: 20 g/10 min
- Spiral Flow: 36.1 cm
- Hardness, Shore D: 65
- Tensile Strength at Break: 22.4 MPa
$ 1661/MT
- Density: 0.960 g/cc
- Thickness: 25.4 microns
- Melt Flow: 12 g/10 min
- Film Tensile Strength at Yield, MD: 25.5 MPa
- Film Tensile Strength at Yield, TD: 31.7 MPa
$ 2054/MT
- Bulk Density: 0.593 - 0.625 g/cc
- Density: 0.960 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 28.2 cm
- Hardness, Shore D: 72
$ 1948/MT
- Density: 0.960 g/cc
- Melt Flow: 18 g/10 min
- Melt Temperature: 199 °C
$ 1967/MT
- Density: 0.949 g/cc
- Thickness: 12.7 microns
- Melt Flow: 0.027 g/10 min
- Film Tensile Strength at Yield, MD: 41.0 MPa
- Film Tensile Strength at Yield, TD: 33.5 MPa
$ 1527/MT
- Density: 0.949 g/cc
- Melt Flow: 0.040 g/10 min
- Melt Flow: 7.0 g/10 min
- PENT: >= 2000 hour @Temperature 80.0 °C
- Tensile Strength at Break: 35.2 MPa
$ 1815/MT
- Density: 0.949 g/cc
- Melt Flow: 0.070 g/10 min
- High Load Melt Index: 16 g/10 min
- Tensile Strength at Break: 35.2 MPa
- Tensile Strength, Yield: 23.4 MPa
$ 1863/MT
- Density: 0.949 g/cc
- Melt Flow: 0.070 g/10 min
- Melt Flow: 16 g/10 min
- PENT: >= 1500 hour @Temperature 80.0 °C
- Tensile Strength at Break: 35.2 MPa
$ 2140/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: >= 1000 hour @Temperature 50.0 °C
- Melt Flow: 0.40 g/10 min
- Hardness, Shore D: 63
- Tensile Strength, Yield: 23.4 MPa
$ 1724/MT
- Density: 0.950 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.45 g/10 min
- Melt Temperature: 199 - 216 °C
$ 1639/MT
- Density: 0.953 g/cc
- Melt Flow: 0.32 g/10 min
- Hardness, Shore D: 66
- Tensile Strength at Break: 36.5 MPa
- Tensile Strength, Yield: 22.4 MPa
$ 2363/MT
- Density: 0.953 g/cc
- ESCR 100% Igepal®: 450 hour
- Melt Flow: 0.32 g/10 min
- Hardness, Shore D: 66
- Tensile Strength at Break: 27.6 MPa
$ 1832/MT
- Density: 0.954 g/cc
- Environmental Stress Crack Resistance: 50 hour
- Melt Flow: 0.35 g/10 min
- Hardness, Shore D: 67
- Tensile Strength, Yield: 28.3 MPa
$ 1444/MT
- Density: 0.954 g/cc
- Thickness: 50.8 microns
- Melt Flow: 0.85 g/10 min
- Film Tensile Strength at Yield, MD: 25.5 MPa
- Film Tensile Strength at Yield, TD: 26.2 MPa
$ 1619/MT
- Density: 0.958 g/cc
- Environmental Stress Crack Resistance: 25 hour
- Melt Flow: 0.35 g/10 min
- Hardness, Shore D: 68
- Tensile Strength, Yield: 30.3 MPa
$ 1806/MT
- Density: 0.958 g/cc
- Thickness: 25.4 microns
- Melt Flow: 0.45 g/10 min
- Film Tensile Strength at Yield, MD: 26.2 MPa
- Film Tensile Strength at Yield, TD: 26.9 MPa
$ 1517/MT
- Density: 0.946 g/cc
- Melt Flow: 2.2 g/10 min
- Spiral Flow: 23.4 cm
- Hardness, Shore D: 65
- Tensile Strength at Break: 14.3 MPa
$ 2069/MT
- Density: 0.946 g/cc
- Melt Flow: 6.1 g/10 min
- Spiral Flow: 24.4 cm
- Hardness, Shore D: 68
- Tensile Strength at Break: 15.2 MPa
$ 1478/MT
- Density: 0.950 g/cc
- Melt Flow: 4.0 g/10 min
- Spiral Flow: 31.5 cm
- Hardness, Shore D: 66
- Tensile Strength at Break: 22.3 MPa
$ 2178/MT
- Bulk Density: 0.593 - 0.625 g/cc
- Density: 0.953 g/cc
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 19.8 cm
- Tensile Strength at Break: 27.6 MPa
$ 1502/MT
- Density: 0.953 g/cc
- Melt Flow: 6.5 g/10 min
- Spiral Flow: 24.1 cm
- Hardness, Shore D: 67
- Tensile Strength at Break: 22.4 MPa
$ 2020/MT
- Density: 0.953 g/cc
- Melt Flow: 7.0 g/10 min
- Spiral Flow: 26.4 cm
- Hardness, Shore D: 67
- Tensile Strength at Break: 22.4 MPa
$ 1480/MT
- Density: 0.953 g/cc
- Melt Flow: 6.8 g/10 min
- Spiral Flow: 24.1 cm
- Hardness, Shore D: 67
- Tensile Strength at Break: 22.4 MPa
$ 1517/MT
- Density: 0.953 g/cc
- Melt Flow: 7.0 g/10 min
- Hardness, Shore D: 67
- Tensile Strength at Break: 24.1 MPa
- Tensile Strength, Yield: 25.5 MPa
$ 1577/MT
- Bulk Density: 0.593 - 0.625 g/cc
- Density: 0.953 g/cc
- Melt Flow: 6.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 22.4 cm
- Hardness, Shore D: 70
$ 1457/MT
- Density: 0.955 g/cc
- Melt Flow: 6.0 g/10 min
- Spiral Flow: 31.5 cm
- Hardness, Shore D: 68
- Tensile Strength at Break: 18.2 MPa
$ 1541/MT
- Density: 0.958 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.1 g/10 min
- Film Tensile Strength at Yield, MD: 27.6 MPa
- Film Tensile Strength at Yield, TD: 33.1 MPa
$ 1658/MT
- Density: 0.958 g/cc
- Melt Flow: 2.8 g/10 min
- Spiral Flow: 15.5 cm
- Hardness, Shore D: 67
- Tensile Strength at Break: 25.0 MPa
$ 2085/MT
- Density: 0.960 g/cc
- Melt Flow: 3.0 g/10 min
- Film Tensile Strength at Yield, MD: 22.1 MPa
- Film Tensile Strength at Yield, TD: 20.7 MPa
- Film Elongation at Break, MD: 860 %
$ 1943/MT
- Density: 0.960 g/cc
- Melt Flow: 6.0 g/10 min
- Film Tensile Strength at Yield, MD: 24.1 MPa
- Film Tensile Strength at Yield, TD: 25.5 MPa
- Film Elongation at Break, MD: 850 %
$ 1794/MT
- Bulk Density: 0.593 - 0.625 g/cc
- Density: 0.960 g/cc
- Melt Flow: 7.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 21.8 cm
- Hardness, Shore D: 70
$ 2075/MT
- Density: 0.958 g/cc
- Melt Flow: 8.0 g/10 min
- Hardness, Shore D: 67
- Tensile Strength at Break: 21.4 MPa
- Tensile Strength, Yield: 26.9 MPa
$ 1841/MT
- Bulk Density: 0.593 - 0.625 g/cc
- Density: 0.951 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Spiral Flow: 35.1 cm
- Hardness, Shore D: 71
$ 1470/MT
- Density: 0.952 g/cc
- Melt Flow: 34 g/10 min
- Spiral Flow: 39.4 cm
- Hardness, Shore D: 67
- Tensile Strength at Break: 26.3 MPa
$ 1830/MT
- Density: 0.949 g/cc
- Thickness: 12.7 microns
- Melt Flow: 0.075 g/10 min
- Film Tensile Strength at Yield, MD: 31.0 MPa
- Film Tensile Strength at Yield, TD: 26.9 MPa
$ 1615/MT
- Density: 0.949 g/cc
- Melt Flow: 0.057 g/10 min
- Film Tensile Strength at Yield, MD: 26.2 MPa
- Film Tensile Strength at Yield, TD: 23.4 MPa
- Film Elongation at Break, MD: 300 %
$ 1489/MT
- Density: 0.940 g/cc
- Water Vapor Transmission: 5.10 g/m²/day
- Oxygen Transmission Rate: 2450 cc/m²/day
- ESCR 100% Igepal®: >= 1000 hour
- Thickness: 50.8 microns
$ 1765/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 25 hour
- ESCR Blow Molding: 25 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.38 g/10 min
$ 1594/MT
- Density: 0.918 g/cc
- Water Vapor Transmission: 0.260 g/m²/day
- Melt Flow: 7.1 g/10 min
- Hardness, Shore D: 50
- Tensile Strength at Break: 11.7 MPa
$ 1919/MT
- Density: 0.922 g/cc
- Melt Flow: 25 g/10 min
- Hardness, Shore D: 44
- Tensile Strength at Break: 8.48 MPa
- Tensile Strength, Yield: 12.2 MPa
$ 1561/MT
- Density: 0.945 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Absorption Coefficient: 450
- Carbon Black Loading: 2.6 %
- Melt Flow: 0.65 g/10 min
$ 1596/MT
- Density: 0.922 g/cc
- Melt Flow: 25 g/10 min
- Hardness, Shore D: 44
- Tensile Strength at Break: 8.48 MPa
- Tensile Strength, Yield: 12.2 MPa
$ 1827/MT
- Density: 0.919 g/cc
- Thickness: 31.8 microns
- Melt Flow: 0.90 g/10 min
- Tensile Strength at Break: 14.5 MPa
- Film Elongation at Break, MD: 200 %
$ 1472/MT
- Density: 0.948 g/cc
- Melt Flow: 0.80 g/10 min
- Tensile Strength at Break: 24.8 MPa
- Tensile Strength, Yield: 20.7 MPa
- Elongation at Break: 800 %
$ 1651/MT
- Density: 0.923 g/cc
- Melt Flow: 1.5 g/10 min
- Tensile Strength at Break: 13.2 MPa
- Elongation at Break: 720 %
- Feed Temperature: 154 °C
$ 1540/MT
- Density: 0.918 g/cc
- Melt Flow: 0.25 g/10 min
- Hardness, Shore D: 50
- Tensile Strength at Break: 14.5 MPa
- Elongation at Break: >= 600 %
$ 1717/MT
- Density: 0.921 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.8 g/10 min
- Film Tensile Strength at Yield, TD: 11.0 MPa
- Film Elongation at Break, MD: 300 %
$ 2319/MT
- Density: 0.924 g/cc
- Water Vapor Transmission: 7.50 g/m²/day
- Thickness: 50.8 microns
- Melt Flow: 6.5 g/10 min
- Film Tensile Strength at Yield, MD: 11.0 MPa
$ 2456/MT
- Density: 0.946 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- ESCR, Bottle: >= 1000 hour
- Melt Flow: 0.20 g/10 min
- Hardness, Shore D: 65
$ 1701/MT
- Density: 0.919 g/cc
- Thickness: 31.8 microns
- Melt Flow: 0.90 g/10 min
- Tensile Strength at Break: 14.5 MPa
- Film Elongation at Break, MD: 200 %
$ 1779/MT
- Density: 0.923 g/cc
- Melt Flow: 10 g/10 min
- Hardness, Shore D: 51
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 226 %
$ 1710/MT
- Density: 0.950 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- ESCR, Bottle: >= 1000 hour
- Melt Flow: 11.5 g/10 min
- Hardness, Shore D: 65
$ 1838/MT
- Density: 0.930 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Absorption Coefficient: 440
- Carbon Black Loading: 2.6 %
- Melt Flow: 0.59 g/10 min
$ 1683/MT
- Density: 0.952 g/cc
- Particle Size: 5.0 - 50 µm
- Maximum Moisture Content: 0.10
- Melt Flow: 10 g/10 min
- Hardness, Shore D: 66
$ 1594/MT
- Density: 0.949 g/cc
- Water Vapor Transmission: 6.60 g/m²/day
- Oxygen Transmission Rate: 2900 cc/m²/day
- Thickness: 31.8 microns
- Melt Flow: 0.33 g/10 min
$ 1901/MT
- Density: >= 0.960 g/cc
- Melt Flow: 0.80 g/10 min
- Hardness, Shore D: 69
- Tensile Strength, Yield: 31.7 MPa
- Elongation at Break: >= 400 %
$ 1819/MT
- Density: 0.9225 g/cc
- Particle Size: 5.0 - 50 µm
- Maximum Moisture Content: 0.10
- Melt Flow: 4.7 g/10 min
- Hardness, Shore D: 53
$ 1723/MT
- Vinyl Acetate Content: 17.9 %
- Melt Flow: 2.2 g/10 min
$ 1648/MT
- Density: 0.952 g/cc
- Particle Size: 5.0 - 50 µm
- Maximum Moisture Content: 0.10
- Melt Flow: 10 g/10 min
- Hardness, Shore D: 66
$ 1532/MT
- Density: >= 0.956 g/cc
- Melt Flow: 0.74 g/10 min
- Hardness, Shore D: 66
- Tensile Strength, Yield: 28.3 MPa
- Elongation at Break: >= 500 %
$ 1587/MT
- Density: 0.924 g/cc
- Melt Flow: 21 g/10 min
- Spiral Flow: 32.8 cm
- Hardness, Shore D: 53
- Tensile Strength at Break: 8.27 MPa
$ 1903/MT
- Density: 0.918 g/cc
- Environmental Stress Crack Resistance: >= 168 hour
- Thickness: 50.8 microns
- Melt Flow: 0.18 g/10 min
- Hardness, Shore D: 42
$ 1681/MT
- Density: 0.946 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- ESCR, Bottle: >= 1000 hour
- Melt Flow: 0.20 g/10 min
- Hardness, Shore D: 65
$ 1528/MT
- Density: 1.40 g/cc
- Hardness, Shore D: 56
- Tensile Strength at Break: 19.4 MPa
- Elongation at Break: 250 %
- Oxygen Index: 25 %
$ 1682/MT
- Density: 0.934 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.70 g/10 min
- Tensile Strength at Break: 20.7 MPa
- Tensile Strength, Yield: 17.9 MPa
$ 1828/MT
- Density: 0.925 g/cc
- Thickness: 25.4 microns
- Melt Flow: 2.0 g/10 min
- Film Tensile Strength at Yield, MD: 10.3 MPa
- Film Tensile Strength at Yield, TD: 11.7 MPa
$ 1754/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 550 %
- Film Elongation at Break, TD: 625 %
$ 1502/MT
- Density: 0.941 g/cc
- Particle Mesh Size: 35 Mesh
- Melt Flow: 22 g/10 min
- Hardness, Shore D: 33
- Tensile Strength at Break: 9.38 MPa
$ 1480/MT
- Density: 0.926 g/cc
- Vinyl Acetate Content: 6.6 %
- Thickness: 50.8 microns
- Melt Flow: 0.50 g/10 min
- Film Elongation at Break, MD: 500 %
$ 2250/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 25 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.38 g/10 min
- Hardness, Shore D: 67
$ 1569/MT
- Density: 0.933 g/cc
- Melt Flow: 140 g/10 min
- Spiral Flow: 67.8 cm
- Hardness, Shore D: 61
- Tensile Strength at Break: 17.3 MPa
$ 1453/MT
- Density: 0.9212 g/cc
- Melt Flow: 8.0 g/10 min
- Vicat Softening Point: 80.0 °C
$ 2125/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: >= 1000 hour
- Melt Flow: 0.40 g/10 min
- Hardness, Shore D: 63
- Tensile Strength, Yield: 23.4 MPa
$ 1969/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 1.0 g/10 min
- Film Elongation at Break, MD: 600 %
- Film Elongation at Break, TD: 760 %
$ 1476/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 30 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.30 g/10 min
- Hardness, Shore D: 67
$ 1895/MT
- Density: 0.927 g/cc
- Vinyl Acetate Content: 5.0 %
- Thickness: 31.8 microns
- Melt Flow: 5.0 g/10 min
- Film Elongation at Break, MD: 320 %
$ 1678/MT
- Density: 0.921 g/cc
- Thickness: 31.8 microns
- Melt Flow: 2.0 g/10 min
- Tensile Strength at Break: 11.9 MPa
- Film Elongation at Break, MD: 300 %
$ 1997/MT
- Density: 0.930 g/cc
- Thickness: 31.8 microns
- Melt Flow: 1.2 g/10 min
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 500 %
$ 1745/MT
- Density: 0.910 g/cc
- Melt Flow: 29 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Temperature: >= 204 °C
$ 1444/MT
- Density: 0.949 g/cc
- ESCR 100% Igepal®: 75 hour
- ESCR 100% Igepal®: >= 500 hour
- Melt Flow: 0.30 g/10 min
- Hardness, Shore D: 65
$ 1636/MT
- Density: 0.943 g/cc
- Oxidative Induction Time (OIT): >= 10 min
- Melt Flow: 6.0 g/10 min
- Tensile Strength at Break: 13.1 MPa
- Elongation at Break: 500 %
$ 1881/MT
- Density: 0.915 g/cc
- Particle Mesh Size: 35 Mesh
- Melt Flow: 22 g/10 min
- Hardness, Shore D: 52
- Tensile Strength at Break: 11.0 MPa
$ 2285/MT
- Density: 0.949 g/cc
- Melt Flow: 0.057 g/10 min
- Film Tensile Strength at Yield, MD: 35.2 MPa
- Film Tensile Strength at Yield, TD: 29.6 MPa
- Film Elongation at Break, MD: 360 %
$ 2136/MT
- Density: 0.9235 g/cc
- Particle Mesh Size: 16 Mesh
- Melt Flow: 22 g/10 min
- Hardness, Shore D: 53
- Tensile Strength at Break: 11.0 MPa
$ 1547/MT
- Density: 0.918 g/cc
- Melt Index of Compound: 7.0 g/10 min
- Hardness, Shore D: 56
- Tensile Strength at Break: 11.7 MPa
- Elongation at Break: 870 %
$ 1502/MT
- Density: 0.953 g/cc
- Environmental Stress Crack Resistance: 25 hour
- ESCR Blow Molding: 25 hour
- ESCR, Bottle: >= 500 hour
- Melt Flow: 0.38 g/10 min
$ 2478/MT
- Density: 0.918 g/cc
- Thickness: 38.1 microns
- Melt Flow: 2.0 g/10 min
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 800 %
$ 2036/MT
- Density: 0.943 g/cc
- Environmental Stress Crack Resistance: >= 168 hour
- Thermal Stress Crack Resistance: >= 336 hour
- Melt Flow: 0.70 g/10 min
- Tensile Strength at Break: 16.2 MPa
$ 1951/MT
- Density: 0.923 g/cc
- Melt Flow: 5.6 g/10 min
- Hardness, Shore D: 53
- Tensile Strength at Break: 12.4 MPa
- Tensile Strength, Yield: 10.3 MPa
$ 1451/MT
- Density: 0.920 g/cc
- Environmental Stress Crack Resistance: >= 1000 hour
- Melt Flow: 0.70 g/10 min
- Hardness, Shore D: 57
- Tensile Strength at Break: 15.2 MPa
$ 2025/MT
- Density: 0.921 g/cc
- Oxidative Induction Time (OIT): 118 min
- Melt Flow: 5.7 g/10 min
- Vicat Softening Point: 99.0 °C
- Melt Temperature: >= 210 °C
Delivery Polymer LyondellBasell (former Equistar)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale romania. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.