LyondellBasell Ultrathene® UE637000 Ethylene Vinyl Acetate Copolymer, Film Extrusion Grade price 2156 per MT

Physical Properties
Vinyl Acetate Content
9.0 %
Thickness
50.8 microns
Melt Flow
3.2 g/10 min

Mechanical Properties
Hardness, Shore D
94
Film Tensile Strength at Yield, MD
6.23 MPa
Film Tensile Strength at Yield, TD
5.81 MPa
Film Elongation at Break, MD
350 %
Film Elongation at Break, TD
500 %
Film Elongation at Yield, MD
9.0 %
Film Elongation at Yield, TD
11 %
Dart Drop
7.95 g/micron
Film Tensile Strength at Break, MD
25.9 MPa
Film Tensile Strength at Break, TD
18.9 MPa
1% Secant Modulus, MD
84.8 MPa
1% Secant Modulus, TD
91.0 MPa

Thermal Properties
Vicat Softening Point
80.0 °C
Brittleness Temperature
<= -76.0 °C

Processing Properties
Melt Temperature
<= 221 °C

Alternative products

LyondellBasell Petrothene® NA940085 Low Density Polyethylene (Film Grade) accurate 66%

$ 1839/MT

Density: 0.918 g/cc
Environmental Stress Crack Resistance: >= 168 hour
Thickness: 50.8 microns
Melt Flow: 0.25 g/10 min
Hardness, Shore D: 50

Dielectric Polymers TRANS-SIL® NT-1001 Silicone Transfer Adhesive (discontinued **) accurate 49%

$ 2347/MT

Thickness: 50.8 microns
Thickness: 50.8 microns
Thickness: 50.8 microns
Peel Strength: 0.6027 kN/m
Maximum Service Temperature, Air: 260 °C

LyondellBasell Petrothene® NA940094 Low Density Polyethylene (Film Grade) accurate 66%

$ 1901/MT

Density: 0.918 g/cc
Environmental Stress Crack Resistance: >= 168 hour
Thickness: 50.8 microns
Melt Flow: 0.25 g/10 min
Hardness, Shore D: 50

LyondellBasell Petrothene® NA940000 Low Density Polyethylene (Film Grade) accurate 66%

$ 2003/MT

Density: 0.918 g/cc
Environmental Stress Crack Resistance: >= 168 hour
Thickness: 50.8 microns
Melt Flow: 0.25 g/10 min
Hardness, Shore D: 50

LyondellBasell Petrothene® NA362176 Low Density Polyethylene accurate 49%

$ 1535/MT

Density: 0.926 g/cc
Vinyl Acetate Content: 6.6 %
Thickness: 50.8 microns
Melt Flow: 0.50 g/10 min
Film Elongation at Break, MD: 500 %

3M 7956MP Hi-Performance Acrylic 200MP accurate 49%

$ 1513/MT

Thickness: 50.8 microns
Thickness: 50.8 microns
Thickness: 50.8 microns
Shear Strength: 0.538 MPa
Shear Strength: 0.710 MPa

LyondellBasell Petrothene® NA942094 Low Density Polyethylene accurate 49%

$ 1903/MT

Density: 0.918 g/cc
Environmental Stress Crack Resistance: >= 168 hour
Thickness: 50.8 microns
Melt Flow: 0.18 g/10 min
Hardness, Shore D: 42

LyondellBasell Petrothene® NA362005 Low Density Polyethylene accurate 49%

$ 1480/MT

Density: 0.926 g/cc
Vinyl Acetate Content: 6.6 %
Thickness: 50.8 microns
Melt Flow: 0.50 g/10 min
Film Elongation at Break, MD: 500 %

Carmel Olefins IPETHENE® 113 Low Density Polyethylene accurate 49%

$ 1450/MT

Density: 0.920 g/cc
Thickness: 50.0 microns
Melt Flow: 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C
Film Elongation at Break, MD: 250 %
Film Elongation at Break, TD: 500 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for LyondellBasell Ultrathene® UE637000 Ethylene Vinyl Acetate Copolymer, Film Extrusion Grade

Seller from Sūrat – 2021-05-22:

Seller from Sūrat work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2156 per MT