$ 1955/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 50.0 MPa
- Elongation at Break: 5.0 %
$ 1515/MT
- Density: 2.25 g/cc
- Filler Content: 75 %
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 20.0 MPa
- Elongation at Yield: 5.0 %
$ 2079/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2214/MT
- Density: 0.980 g/cc
- Filler Content: 12 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1854/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 20.0 MPa
- Elongation at Yield: 7.0 %
$ 1481/MT
- Density: 1.08 g/cc
- Filler Content: 25 %
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 55.0 MPa
- Flexural Strength: <= 95.0 MPa
$ 1770/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1447/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1887/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2036/MT
- Density: 0.960 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1928/MT
- Density: 1.10 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1552/MT
- Density: 1.08 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1811/MT
- Density: 1.10 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1913/MT
- Density: 1.01 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.012 - 0.015 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.015 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1483/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2182/MT
- Density: 1.10 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1795/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1566/MT
- Density: 2.17 g/cc
- Filler Content: 75 %
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 57.0 MPa
- Elongation at Break: 5.0 %
$ 1582/MT
- Density: 1.40 g/cc
- Filler Content: 52 %
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 23.0 MPa
- Elongation at Yield: 4.0 %
$ 1934/MT
- Density: 1.11 g/cc
- Melt Index of Compound: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 25.0 MPa
- Elongation at Yield: 5.5 %
- Flexural Strength: <= 45.0 MPa
$ 1564/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2483/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1765/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1525/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1702/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1824/MT
- Density: 1.09 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.013 - 0.015 cm/cm
- Linear Mold Shrinkage: 0.013 - 0.015 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1515/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1751/MT
- Density: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1490/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1895/MT
- Density: 1.10 g/cc
- Filler Content: 10 %
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 29.0 MPa
- Elongation at Break: 4.0 %
$ 1612/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 25.0 MPa
$ 2390/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1596/MT
- Density: 1.22 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1474/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2403/MT
- Density: 0.960 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1975/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1533/MT
- Density: 1.07 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.0010 - 0.0030 cm/cm
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1607/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0080 cm/cm
- Linear Mold Shrinkage: 0.012 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1690/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1757/MT
- Density: 1.20 g/cc
- Filler Content: 40 %
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 15.0 MPa
- Elongation at Yield: 6.0 %
$ 1471/MT
- Density: 1.22 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1714/MT
- Density: 1.10 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1609/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1557/MT
- Density: 1.18 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1648/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 30.0 MPa
- Elongation at Yield: 6.0 %
$ 1476/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2182/MT
- Density: 1.22 g/cc
- Filler Content: 38 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1690/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 70.0 MPa
- Elongation at Break: 4.0 %
$ 2117/MT
- Density: 0.980 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1476/MT
- Density: 1.84 g/cc
- Filler Content: 65 %
- Linear Mold Shrinkage: 0.0045 cm/cm
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1453/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1864/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1625/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1470/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1496/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1553/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1912/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1466/MT
- Density: 1.18 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1451/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 65 @Time 15.0 sec
$ 2216/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2178/MT
- Density: 2.25 g/cc
- Filler Content: 75 %
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 17.0 MPa
- Elongation at Yield: 5.0 %
$ 1960/MT
- Density: 1.86 g/cc
- Filler Content: 65 %
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1576/MT
- Density: 1.06 g/cc
- Filler Content: 23 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1636/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1677/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1762/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1586/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1481/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1557/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1682/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1874/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1761/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 24.0 MPa
- Elongation at Yield: 10 %
- Flexural Strength: <= 28.0 MPa
$ 2236/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1767/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.011 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1531/MT
- Density: 1.21 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.012 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1680/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1477/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1883/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1674/MT
- Density: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1601/MT
- Density: 1.21 g/cc
- Filler Content: 38 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1475/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2148/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1513/MT
- Density: 1.14 g/cc
- Filler Content: 30 %
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 25.0 MPa
- Elongation at Yield: 7.0 %
$ 1740/MT
- Density: 1.51 g/cc
- Filler Content: 60 %
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 26.0 MPa
- Elongation at Yield: 3.0 %
$ 1545/MT
- Density: 1.22 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Index of Compound: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1448/MT
- Density: 0.990 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Melt Index of Compound: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1843/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1653/MT
- Density: 2.25 g/cc
- Filler Content: 75 %
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 17.0 MPa
- Elongation at Yield: 5.0 %
$ 2024/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1956/MT
- Density: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2179/MT
- Density: 1.05 g/cc
- Filler Content: 22 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2072/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1488/MT
- Density: 1.86 g/cc
- Filler Content: 65 %
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1652/MT
- Density: 1.86 g/cc
- Filler Content: 65 %
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1947/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1911/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1454/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1567/MT
- Density: 1.07 g/cc
- Filler Content: 25 %
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 47 @Time 15.0 sec
- Flexural Strength: <= 32.0 MPa
$ 1494/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2560/MT
- Density: 1.06 g/cc
- Melt Index of Compound: 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 23.0 MPa
- Elongation at Break: 558 %
- Elongation at Yield: 9.0 %
$ 2546/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1597/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Elongation at Yield: 6.0 %
- Flexural Modulus: 3.00 GPa @Temperature 23.0 °C
$ 2106/MT
- Density: 1.90 g/cc
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 73 @Time 15.0 sec
- Tensile Strength at Break: <= 28.0 MPa
- Elongation at Yield: 6.0 %
$ 1652/MT
- Density: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1505/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.011 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1852/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 27.0 MPa
- Elongation at Break: 24 %
$ 1526/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1659/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1551/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 60.0 MPa
- Elongation at Yield: 7.0 %
$ 1936/MT
- Density: 0.900 g/cc
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore A: 88 @Time 15.0 sec
$ 1848/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1554/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2217/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1979/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1923/MT
- Density: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1450/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1480/MT
- Density: 1.28 g/cc
- Filler Content: 45 %
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 114 MPa
- Elongation at Break: 4.0 %
$ 1806/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1497/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1788/MT
- Density: 1.40 g/cc
- Filler Content: 51 %
- Linear Mold Shrinkage: 0.0080 cm/cm
- Linear Mold Shrinkage: 0.011 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1468/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 70.0 MPa
- Elongation at Break: 4.0 %
$ 1637/MT
- Density: 1.43 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage: 0.013 cm/cm
- Tensile Strength at Break: <= 115 MPa
$ 2211/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1693/MT
- Density: 1.21 g/cc
- Filler Content: 38 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1605/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1611/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 32.0 MPa
- Elongation at Yield: 17 %
- Flexural Strength: <= 28.0 MPa
$ 1554/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1482/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1582/MT
- Density: 1.18 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2088/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 21.0 MPa
- Elongation at Break: 9.0 %
$ 1842/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1894/MT
- Density: 0.960 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm
- Linear Mold Shrinkage: 0.015 - 0.020 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2341/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1560/MT
- Density: 1.10 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1602/MT
- Density: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1556/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage: 0.015 cm/cm
- Linear Mold Shrinkage: 0.015 cm/cm
- Melt Index of Compound: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 35.0 MPa
$ 2269/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2253/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2356/MT
- Density: 1.17 g/cc
- Filler Content: 35 %
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 30.0 MPa
- Elongation at Yield: 8.0 %
$ 1656/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1646/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1832/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.013 - 0.015 cm/cm
- Linear Mold Shrinkage: 0.013 - 0.015 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2259/MT
- Density: 1.11 g/cc
- Filler Content: 30 %
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 65.0 MPa
- Elongation at Yield: 7.0 %
$ 2046/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 24.0 MPa
$ 1605/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 28.0 MPa
$ 1576/MT
- Density: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1614/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1651/MT
- Density: 1.03 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1628/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1596/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.014 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1665/MT
- Density: 1.09 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1684/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1814/MT
- Density: 1.12 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1852/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1488/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 20.0 MPa
- Elongation at Yield: 6.0 %
$ 2067/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1763/MT
- Density: 1.22 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1738/MT
- Density: 1.10 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1575/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.013 - 0.015 cm/cm
- Linear Mold Shrinkage: 0.013 - 0.015 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1445/MT
- Density: 1.00 g/cc
- Filler Content: 15 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1773/MT
- Density: 1.51 g/cc
- Filler Content: 60 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1858/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2375/MT
- Density: 1.33 g/cc
- Filler Content: 50 %
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 104 MPa
- Elongation at Break: 3.0 %
$ 1572/MT
- Density: 0.980 g/cc
- Filler Content: 12 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1530/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1854/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1605/MT
- Density: 0.910 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 21.0 MPa
$ 1444/MT
- Density: 0.960 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1579/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1528/MT
- Density: 0.960 g/cc
- Filler Content: 10 %
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 50.0 MPa
- Elongation at Break: 6.0 %
$ 1585/MT
- Density: 0.940 g/cc
- Filler Content: 7 %
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 30.0 MPa
- Elongation at Break: 13 %
$ 1468/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1471/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1942/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1570/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1742/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1507/MT
- Density: 0.900 g/cc
- Melt Index of Compound: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 29.0 MPa
- Elongation at Yield: 9.0 %
- Flexural Strength: <= 39.0 MPa
$ 1659/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1507/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1976/MT
- Density: 1.35 g/cc
- Filler Content: 50 %
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 25.0 MPa
- Flexural Strength: <= 56.0 MPa
$ 1614/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0080 cm/cm
- Melt Index of Compound: 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1691/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1904/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2394/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1449/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1830/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1900/MT
- Density: 0.960 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1675/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2490/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1627/MT
- Density: 1.17 g/cc
- Filler Content: 35 %
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm
- Linear Mold Shrinkage: 0.0025 - 0.0035 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1955/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1523/MT
- Density: 1.06 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1783/MT
- Density: 1.10 g/cc
- Filler Content: 25 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1715/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.010 - 0.013 cm/cm
- Melt Index of Compound: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2048/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Linear Mold Shrinkage: 0.0090 - 0.011 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1811/MT
- Density: 1.05 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1688/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1672/MT
- Density: 1.08 g/cc
- Filler Content: 25 %
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: <= 20.0 MPa
- Elongation at Yield: 7.0 %
$ 2191/MT
- Density: 1.13 g/cc
- Filler Content: 30 %
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Linear Mold Shrinkage: 0.012 - 0.014 cm/cm
- Melt Index of Compound: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1576/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1716/MT
- Density: 1.23 g/cc
- Filler Content: 40 %
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Linear Mold Shrinkage: 0.0080 - 0.010 cm/cm
- Melt Index of Compound: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2272/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Linear Mold Shrinkage: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
Delivery Polypropylene (PP) Polykemi AB
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
bulk vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.