$ 1599/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 56
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1795/MT
- Density: 0.580 g/cc
- Apparent Bulk Density: 0.580 g/cc
- Linear Mold Shrinkage: 0.0024 cm/cm
- Hardness, Shore D: 43
- Tensile Strength, Ultimate: 17.0 MPa
$ 1597/MT
- Density: 1.25 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 50
- Elongation at Break: >= 50 %
- Compression Set: 25 %
$ 1726/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 25.0 MPa
- Tensile Strength, Yield: 2.50 MPa @Strain 100 %
$ 1563/MT
- Density: 1.05 g/cc
- Water Absorption: 2.0 %
- Water Absorption at Saturation: 2.0 %
- Tensile Strength, Ultimate: 50.0 MPa
- Elongation at Break: 12 %
$ 1907/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 33
- Tensile Strength at Break: 45.0 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1721/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Tensile Strength, Ultimate: 28.0 MPa
- Elongation at Break: 50 %
- Flexural Modulus: 1.47 GPa
$ 1515/MT
- Density: 1.25 g/cc
- Hardness, Shore D: 55
- Elongation at Break: >= 50 %
- Compression Set: 30 %
- Compression Set: 50 % @Temperature 70.0 °C
- CTE, linear, Parallel to Flow: 170 µm/m-°C @Temperature 20.0 °C
$ 1563/MT
- Density: 1.60 g/cc
- Tensile Strength, Ultimate: 303 MPa
- Elongation at Break: 2.5 %
- Flexural Yield Strength: 430 MPa
- Flexural Modulus: 12.57 GPa
$ 1768/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 60
- Tensile Strength at Break: 64.0 MPa
- Tensile Strength, Yield: 64.0 MPa
$ 1645/MT
- Density: 0.580 g/cc
- Apparent Bulk Density: 0.580 g/cc
- Linear Mold Shrinkage: 0.0056 cm/cm
- Hardness, Shore D: 68
- Tensile Strength, Ultimate: 19.0 MPa
$ 2123/MT
- Density: 1.08 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 43
- Tensile Strength at Break: 39.0 MPa
- Tensile Strength, Yield: 39.0 MPa
$ 2260/MT
- Density: 1.69 g/cc
- Water Absorption: 0.090 %
- Water Absorption at Saturation: 0.090 %
- Tensile Strength, Ultimate: 75.0 MPa
- Elongation at Break: 1.1 %
$ 1594/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Tensile Strength, Ultimate: 24.0 MPa
- Elongation at Break: 135 %
- Flexural Modulus: 0.600 GPa
$ 2138/MT
- Density: 1.24 g/cc
- Water Absorption: 1.22 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 1.22 %
- Hardness, Shore D: 73
$ 1791/MT
- Density: 0.945 g/cc
- Density: 1.11 g/cc
- Hardness, Shore A: 82
- Hardness, Shore D: 31
- Abrasion: 20
$ 1644/MT
- Density: 0.640 g/cc
- Apparent Bulk Density: 0.640 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Shore D: 67
- Tensile Strength, Ultimate: 22.0 MPa
$ 2224/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage: 0.0059 cm/cm
- Tensile Strength, Ultimate: 28.0 MPa
- Elongation at Break: 140 %
- Flexural Modulus: 1.44 GPa
$ 2405/MT
- Density: 1.12 g/cc
- Tensile Strength, Yield: 5.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- Vicat Softening Point: 80.0 °C
- Glass Transition Temp, Tg: -46.0 °C
$ 1695/MT
- Density: 0.320 g/cc
- Apparent Bulk Density: 0.320 g/cc
- Hardness, Shore D: 37
- Tensile Strength, Ultimate: 6.10 MPa
- Elongation at Break: 7.0 %
$ 2571/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 32
- Abrasion: 30
- Compression Set: 30 % @Temperature 23.0 °C
$ 2108/MT
- Density: 0.640 g/cc
- Apparent Bulk Density: 0.640 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Hardness, Shore D: 70
- Tensile Strength, Ultimate: 19.0 MPa
$ 1650/MT
- Density: 1.26 g/cc
- Tensile Strength, Yield: 6.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- Vicat Softening Point: 88.0 °C
- Glass Transition Temp, Tg: -30.0 °C
$ 1826/MT
- Density: 1.03 g/cc
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 33
- Tensile Strength at Break: 50.0 MPa
$ 1602/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 59
- Abrasion: 18
- Compression Set: 24 % @Temperature 23.0 °C
$ 1874/MT
- Density: 1.01 g/cc
- Density: 1.19 g/cc
- Hardness, Shore A: 86
- Hardness, Shore D: 38
- Abrasion: 32
$ 1496/MT
- Density: 1.38 g/cc
- Hardness, Shore A: 99
- Hardness, Shore D: 70
- Tensile Strength at Break: 64.0 MPa
- Tensile Strength, Yield: 64.0 MPa
$ 1456/MT
- Density: 1.14 g/cc
- Tensile Strength, Yield: 33.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 160 µm/m-°C @Temperature 20.0 °C
- Vicat Softening Point: 116 °C
$ 1649/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 91
- Hardness, Shore D: 40
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1984/MT
- Density: 0.0480 g/cc
- Tensile Strength, Ultimate: 0.115 MPa
- Elongation at Break: 139 %
- Tear Strength: 0.210 kN/m
$ 2011/MT
- Density: 0.0480 g/cc
- Tensile Strength, Ultimate: 0.130 MPa
- Elongation at Break: 176 %
- Tear Strength: 0.540 kN/m
$ 1541/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0085 cm/cm
- Tensile Strength, Ultimate: 17.0 MPa
- Elongation at Break: 250 %
- Flexural Modulus: 0.110 GPa
$ 2562/MT
- Density: 1.02 g/cc
- Density: 1.22 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 48
- Abrasion: 23
$ 1611/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 42
- Elongation at Break: >= 50 %
- Compression Set: 25 %
$ 1887/MT
- Density: 0.480 g/cc
- Apparent Bulk Density: 0.480 g/cc
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
- Hardness, Shore D: 55
- Tensile Strength, Ultimate: 13.0 MPa
$ 1481/MT
- Density: 1.80 g/cc
- Water Absorption: 0.050 %
- Water Absorption at Saturation: 0.050 %
- Tensile Strength, Ultimate: 88.0 MPa
- Elongation at Break: 1.3 %
$ 1699/MT
- Density: 0.0960 g/cc
- Apparent Bulk Density: 0.0720 g/cc
- Tensile Strength, Ultimate: 0.270 MPa
- Elongation at Break: 52 %
- Compressive Yield Strength: 0.0440 MPa
$ 1663/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
- Hardness, Shore D: 76
- Tensile Strength, Ultimate: 39.0 MPa
- Elongation at Break: 10 %
$ 1532/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Elongation at Break: >= 50 %
- Compression Set: 30 %
- Compression Set: 65 % @Temperature 70.0 °C
$ 1893/MT
- Density: 1.02 g/cc
- Density: 1.20 g/cc
- Hardness, Shore A: 80
- Hardness, Shore D: 30
- Tensile Strength at Break: 30.0 MPa
$ 1446/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 33
- Abrasion: 40
- Compression Set: 25 % @Temperature 23.0 °C
$ 1697/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 41
- Abrasion: 26
- Compression Set: 20 % @Temperature 23.0 °C
$ 2080/MT
- Density: 0.510 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Tensile Strength, Ultimate: 21.0 MPa
- Elongation at Break: 1.7 %
- Flexural Yield Strength: 39.0 MPa
$ 1444/MT
- Density: 1.14 g/cc
- Water Absorption at Saturation: 2.6 %
- Linear Mold Shrinkage: 0.0070 cm/cm
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 19.0 MPa
$ 1840/MT
- Density: 0.400 g/cc
- Water Absorption: 0.30 %
- Water Absorption at Saturation: 0.30 %
- Tensile Strength, Ultimate: 11.0 MPa
- Elongation at Break: 6.0 %
$ 2028/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 43
- Abrasion: 25
- Compression Set: 22 % @Temperature 23.0 °C
$ 2124/MT
- Density: 0.640 g/cc
- Apparent Bulk Density: 0.640 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Hardness, Shore D: 66
- Tensile Strength, Ultimate: 21.0 MPa
$ 1592/MT
- Density: 0.915 g/cc
- Density: 1.08 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 51
- Tensile Strength at Break: 48.0 MPa
$ 1743/MT
- Density: 0.281 g/cc
- Apparent Bulk Density: 0.248 g/cc
- Water Absorption: 0.70 %
- Water Absorption: 2.4 %
- Linear Mold Shrinkage: 0.00080 cm/cm
$ 1692/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 65
- Tensile Strength at Break: 64.0 MPa
- Tensile Strength, Yield: 64.0 MPa
$ 1643/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Elongation at Break: >= 50 %
- Compression Set: 25 %
- Compression Set: 65 % @Temperature 70.0 °C
$ 1644/MT
- Density: 1.04 g/cc
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage: 0.017 cm/cm
- Hardness, Shore D: 69
- Tensile Strength, Ultimate: 28.0 MPa
$ 1847/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 33
- Tensile Strength at Break: 43.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1491/MT
- Density: 0.500 g/cc
- Linear Mold Shrinkage: 0.10 cm/cm
- Tensile Strength, Ultimate: 22.0 MPa
- Flexural Yield Strength: 26.0 MPa
- Flexural Modulus: 1.65 GPa
$ 1839/MT
- Density: 1.76 g/cc
- Water Absorption: 0.060 %
- Water Absorption at Saturation: 0.060 %
- Tensile Strength, Ultimate: 84.0 MPa
- Elongation at Break: 1.4 %
$ 1766/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0085 cm/cm
- Tensile Strength, Ultimate: 29.0 MPa
- Elongation at Break: 80 %
- Flexural Modulus: 0.980 GPa
$ 2024/MT
- Density: 0.970 g/cc
- Density: 1.18 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 65
- Abrasion: 19
$ 1602/MT
- Density: 0.0560 g/cc
- Apparent Bulk Density: 0.0350 g/cc
- Water Absorption: 18 %
- Water Absorption: 25.7 %
- Tensile Strength, Ultimate: 0.310 MPa
$ 2299/MT
- Density: 1.20 g/cc
- Water Absorption: 4.0 %
- Water Absorption at Saturation: 4.0 %
- Tensile Strength, Ultimate: 42.0 MPa
- Elongation at Break: 4.0 %
$ 1515/MT
- Density: 0.0480 g/cc
- Apparent Bulk Density: 0.0340 g/cc
- Water Absorption: 25.6 %
- Water Absorption: 38 %
- Tensile Strength, Ultimate: 0.220 MPa
$ 2024/MT
- Density: 0.115 g/cc
- Apparent Bulk Density: 0.0800 g/cc
- Tensile Strength, Ultimate: 0.560 MPa
- Elongation at Break: 14 %
- Compressive Yield Strength: 1.00 MPa
- Tear Strength: 2.10 kN/m
$ 2372/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 75
- Tensile Strength at Break: 34.0 MPa
- Tensile Strength, Yield: 34.0 MPa
$ 1523/MT
- Density: 0.985 g/cc
- Density: 1.18 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 62
- Abrasion: 20
$ 2014/MT
- Density: 1.10 g/cc
- Water Absorption: 3.3 %
- Water Absorption at Saturation: 5.0 %
- Linear Mold Shrinkage: 0.0125 cm/cm
- Tensile Strength, Ultimate: 13.0 MPa
$ 1992/MT
- Density: 1.17 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 58
- Tensile Strength at Break: 63.0 MPa
- Tensile Strength, Yield: 63.0 MPa
$ 2020/MT
- Density: 1.08 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 33.0 MPa
- Tensile Strength, Yield: 33.0 MPa
- Tensile Strength, Yield: 7.00 MPa @Strain 100 %
$ 2304/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 63
- Abrasion: 30
- Availability: Asia Pacific
$ 1852/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 30.0 MPa
- Tensile Strength, Yield: 2.50 MPa @Strain 100 %
$ 1843/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 40
- Elongation at Break: >= 50 %
- Compression Set: 25 %
$ 1602/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Hardness, Shore A: 75
- Tensile Strength, Ultimate: 11.0 MPa
- Elongation at Break: 450 %
$ 1819/MT
- Density: 1.03 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 40
- Abrasion: 30
$ 1938/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Tensile Strength, Ultimate: 22.0 MPa
- Elongation at Break: 75 %
- Flexural Modulus: 1.03 GPa
$ 1521/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 33
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1585/MT
- Density: 0.960 g/cc
- Density: 1.13 g/cc
- Hardness, Shore A: 85
- Abrasion: 28
- Compression Set: 18 % @Temperature 23.0 °C
$ 1911/MT
- Density: 0.980 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 53
- Abrasion: 25
- Compression Set: 23 % @Temperature 23.0 °C
$ 1760/MT
- Density: 1.12 g/cc
- Tensile Strength, Yield: 12.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- Vicat Softening Point: 80.0 °C
- Glass Transition Temp, Tg: -46.0 °C
$ 2226/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0085 cm/cm
- Tensile Strength, Ultimate: 28.0 MPa
- Elongation at Break: 140 %
- Flexural Modulus: 0.700 GPa
$ 1768/MT
- Density: 0.0640 g/cc
- Compressive Yield Strength: 0.680 MPa
$ 2522/MT
- Density: 1.02 g/cc
- Density: 1.14 g/cc
- Hardness, Shore A: 80
- Hardness, Shore D: 29
- Abrasion: 70
$ 1628/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 33
- Abrasion: 60
- Compression Set: 25 % @Temperature 23.0 °C
$ 2172/MT
- Density: 1.03 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 50
- Abrasion: 70
$ 2368/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 73
- Tensile Strength at Break: 55.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 1511/MT
- Density: 0.112 g/cc
- Apparent Bulk Density: 0.0800 g/cc
- Tensile Strength, Ultimate: 0.570 MPa
- Elongation at Break: 14 %
- Compressive Yield Strength: 0.960 MPa
- Tear Strength: 2.10 kN/m
$ 1786/MT
- Density: 1.22 g/cc
- Tensile Strength, Yield: 9.60 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 130 µm/m-°C @Temperature 20.0 °C
- Vicat Softening Point: 115 °C
$ 1979/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 65
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1447/MT
- Density: 0.970 g/cc
- Density: 1.15 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 43
- Tensile Strength at Break: 50.0 MPa
$ 1621/MT
- Density: 1.21 g/cc
- Water Absorption: 1.1 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 1.1 %
- Hardness, Shore A: 86
$ 2201/MT
- Density: 1.23 g/cc
- Hardness, Shore D: 59
- Elongation at Break: >= 50 %
- Compression Set: 30 %
- Compression Set: 60 % @Temperature 70.0 °C
- CTE, linear, Parallel to Flow: 181 µm/m-°C @Temperature 20.0 °C
$ 1536/MT
- Density: 0.0640 g/cc
- Tensile Strength, Ultimate: 0.127 MPa
- Elongation at Break: 171 %
- Tear Strength: 0.540 kN/m
$ 1596/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 32
- Abrasion: 30
- Compression Set: 25 % @Temperature 23.0 °C
$ 1664/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Hardness, Shore D: 51
- Tensile Strength, Ultimate: 23.0 MPa
- Elongation at Break: 360 %
$ 2002/MT
- Density: 0.0960 g/cc
- Apparent Bulk Density: 0.0400 g/cc
- Tensile Strength, Ultimate: 0.290 MPa
- Elongation at Break: 50 %
- Compressive Yield Strength: 0.0620 MPa
$ 1774/MT
- Density: 1.71 g/cc
- Linear Mold Shrinkage: 0.00050 cm/cm
- Tensile Strength, Ultimate: 221 MPa
- Elongation at Break: 1.8 %
- Flexural Yield Strength: 432 MPa
$ 1618/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Elongation at Break: >= 50 %
- Compression Set: 30 %
- Compression Set: 55 % @Temperature 70.0 °C
$ 1613/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Tensile Strength, Ultimate: 103 MPa
- Flexural Yield Strength: 178 MPa
- Flexural Modulus: 8.30 GPa
$ 1740/MT
- Density: 0.0720 g/cc
- Apparent Bulk Density: 0.0480 g/cc
- Water Absorption: 8.9 %
- Water Absorption: 15.9 %
- Tensile Strength, Ultimate: 0.350 MPa
$ 1582/MT
- Density: 0.240 g/cc
- Apparent Bulk Density: 0.240 g/cc
- Hardness, Shore D: 28
- Tensile Strength, Ultimate: 3.90 MPa
- Elongation at Break: 7.0 %
$ 1450/MT
- Density: 1.17 g/cc
- Water Absorption: 3.3 %
- Water Absorption at Saturation: 3.3 %
- Tensile Strength, Ultimate: 45.0 MPa
- Elongation at Break: 23 %
$ 1983/MT
- Density: 0.880 g/cc
- Apparent Bulk Density: 0.880 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Hardness, Shore D: 81
- Tensile Strength, Ultimate: 33.0 MPa
$ 2451/MT
- Density: 1.21 g/cc
- Tensile Strength, Yield: 12.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 131 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 98.0 °C
$ 2340/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Tensile Strength, Ultimate: 26.0 MPa
- Elongation at Break: 75 %
- Flexural Modulus: 1.19 GPa
$ 1468/MT
- Density: 1.22 g/cc
- Hardness, Shore D: 55
- Tensile Strength at Break: 58.0 MPa
- Tensile Strength, Yield: 58.0 MPa
- Tensile Strength, Yield: 14.0 MPa @Strain 100 %
$ 2015/MT
- Density: 1.18 g/cc
- CTE, linear, Parallel to Flow: 90.0 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 68.0 °C
- Deflection Temperature at 1.8 MPa (264 psi): 45.0 °C
- Vicat Softening Point: 140 °C
$ 2476/MT
- Density: 1.25 g/cc
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage: 0.0055 cm/cm
- Tensile Strength, Ultimate: 35.0 MPa
- Elongation at Break: 22 %
$ 1620/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 26.0 MPa
- Tensile Strength, Yield: 26.0 MPa
- Tensile Strength, Yield: 6.30 MPa @Strain 100 %
$ 2598/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 72
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1735/MT
- Density: 0.980 g/cc
- Density: 1.15 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 42
- Abrasion: 20
$ 1616/MT
- Density: 0.560 g/cc
- Apparent Bulk Density: 0.560 g/cc
- Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
- Hardness, Shore D: 65
- Tensile Strength, Ultimate: 14.0 MPa
$ 1457/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 68
- Tensile Strength at Break: 67.0 MPa
- Tensile Strength, Yield: 67.0 MPa
$ 1446/MT
- Density: 0.0370 g/cc
- Apparent Bulk Density: 0.0220 g/cc
- Water Absorption: 4.3 %
- Water Absorption: 9.4 %
- Linear Mold Shrinkage: 0.010 cm/cm
- Compressive Yield Strength: 0.180 MPa
$ 1991/MT
- Density: 1.25 g/cc
- Water Absorption at Saturation: 0.10 %
- Linear Mold Shrinkage: 0.0075 cm/cm
- Tensile Strength, Ultimate: 38.0 MPa
- Elongation at Break: 15 %
$ 1704/MT
- Density: 1.09 g/cc
- Hardness, Shore A: 74
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 25.0 MPa
- Tensile Strength, Yield: 3.30 MPa @Strain 100 %
$ 1719/MT
- Density: 1.15 g/cc
- Tensile Strength, Yield: 8.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 224 µm/m-°C @Temperature 20.0 °C
- Vicat Softening Point: 128 °C
$ 1863/MT
- Density: 1.22 g/cc
- Tensile Strength, Yield: 19.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 181 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 60.0 °C
$ 1581/MT
- Density: 1.20 g/cc
- Tensile Strength, Yield: 5.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 150 µm/m-°C @Temperature 20.0 °C
- Vicat Softening Point: 91.0 °C
$ 1951/MT
- Density: 1.13 g/cc
- Tensile Strength, Yield: 5.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- Vicat Softening Point: 106 °C
- Glass Transition Temp, Tg: -44.0 °C
$ 1491/MT
- Density: 1.24 g/cc
- Tensile Strength, Yield: 28.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 140 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 46.0 °C
$ 1719/MT
- Density: 1.11 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 34
- Abrasion: 84
- Compression Set: 28 % @Temperature 23.0 °C
$ 2259/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0085 cm/cm
- Tensile Strength, Ultimate: 24.0 MPa
- Elongation at Break: 200 %
- Flexural Modulus: 0.350 GPa
$ 1481/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 91
- Hardness, Shore D: 36
- Abrasion: 27
- Compression Set: 20 % @Temperature 23.0 °C
$ 1536/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0085 cm/cm
- Tensile Strength, Ultimate: 26.0 MPa
- Elongation at Break: 150 %
- Flexural Modulus: 0.580 GPa
$ 1549/MT
- Density: 1.02 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 40
- Abrasion: 25
$ 1595/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 23.0 MPa
- Elongation at Break: 140 %
$ 1876/MT
- Density: 0.900 g/cc
- Density: 1.06 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 1950/MT
- Density: 0.0550 g/cc
- Apparent Bulk Density: 0.0400 g/cc
- Water Absorption: 2.0 %
- Water Absorption: 6.7 %
- Compressive Yield Strength: 0.450 MPa
$ 1643/MT
- Density: 1.22 g/cc
- Hardness, Shore D: 65
- Tensile Strength at Break: 55.0 MPa
- Tensile Strength, Yield: 55.0 MPa
- Tensile Strength, Yield: 20.0 MPa @Strain 100 %
$ 1483/MT
- Density: 0.0640 g/cc
- Apparent Bulk Density: 0.0350 g/cc
- Tensile Strength, Ultimate: 0.520 MPa
- Elongation at Break: 18.2 %
- Compressive Yield Strength: 0.550 MPa
- Tear Strength: 1.70 kN/m
$ 2409/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 53
- Tensile Strength at Break: 65.0 MPa
- Tensile Strength, Yield: 65.0 MPa
$ 1468/MT
- Density: 1.04 g/cc
- Density: 1.22 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 53
- Abrasion: 25
$ 1481/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 33
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 2004/MT
- Density: 0.144 g/cc
- Apparent Bulk Density: 0.0720 g/cc
- Tensile Strength, Ultimate: 0.290 MPa
- Elongation at Break: 35 %
- Compressive Yield Strength: 0.0950 MPa
$ 1468/MT
- Density: 0.0960 g/cc
- Apparent Bulk Density: 0.0560 g/cc
- Tensile Strength, Ultimate: 0.230 MPa
- Elongation at Break: 54 %
- Compressive Yield Strength: 0.0410 MPa
$ 1853/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 44
- Tensile Strength at Break: 38.0 MPa
- Tensile Strength, Yield: 38.0 MPa
$ 1447/MT
- Density: 1.02 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 92
- Abrasion: 60
- Compression Set: 24 % @Temperature 23.0 °C
$ 1498/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 52
- Abrasion: 29
- Compression Set: 25 % @Temperature 23.0 °C
$ 2173/MT
- Density: 0.0480 g/cc
- Tensile Strength, Ultimate: 0.100 - 0.230 MPa
- Elongation at Break: 130 %
- Compression Set: 6.0 - 12 %
$ 1485/MT
- Density: 0.0270 g/cc
- Tensile Strength, Ultimate: 0.120 - 0.200 MPa
- Elongation at Break: 125 %
- Compression Set: 12 - 22 %
$ 1479/MT
- Density: 1.01 g/cc
- Density: 1.15 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 46
- Abrasion: 30
$ 2439/MT
- Density: 1.16 g/cc
- Water Absorption: 3.0 %
- Water Absorption at Saturation: 3.0 %
- Tensile Strength, Ultimate: 27.0 MPa
- Elongation at Break: 18 %
$ 1454/MT
- Density: 1.04 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 80
- Abrasion: 35
- Compression Set: 22 % @Temperature 23.0 °C
$ 2059/MT
- Density: 1.20 g/cc
- Water Absorption: 2.8 %
- Water Absorption at Saturation: 2.8 %
- Linear Mold Shrinkage: 0.013 cm/cm
- Hardness, Shore D: 58
$ 1462/MT
- Density: 1.10 g/cc
- Water Absorption: 3.3 %
- Water Absorption at Saturation: 5.0 %
- Linear Mold Shrinkage: 0.0142 cm/cm
- Tensile Strength, Ultimate: 15.0 MPa
$ 1461/MT
- Density: 1.22 g/cc
- Water Absorption: 0.96 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.96 %
- Hardness, Shore A: 97
$ 2259/MT
- Density: 0.0960 g/cc
- Apparent Bulk Density: 0.0400 g/cc
- Tensile Strength, Ultimate: 0.250 MPa
- Elongation at Break: 49 %
- Compressive Yield Strength: 0.0340 MPa
$ 1449/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 61
- Tensile Strength at Break: 22.0 MPa
- Tensile Strength, Yield: 22.0 MPa
- Tensile Strength, Yield: 2.50 MPa @Strain 100 %
$ 2181/MT
- Density: 1.25 g/cc
- Water Absorption at Saturation: 0.10 %
- Linear Mold Shrinkage: 0.0043 cm/cm
- Tensile Strength, Ultimate: 38.0 MPa
- Elongation at Break: 40 %
$ 2078/MT
- Density: 1.02 g/cc
- Density: 1.22 g/cc
- Hardness, Shore A: 86
- Hardness, Shore D: 33
- Tensile Strength at Break: 46.0 MPa
$ 2158/MT
- Density: 1.02 g/cc
- Density: 1.20 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 40
- Abrasion: 25
$ 1510/MT
- Density: 1.17 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 66
- Abrasion: 30
- Compression Set: 73 % @Temperature 23.0 °C
$ 1818/MT
- Density: 0.925 g/cc
- Density: 1.08 g/cc
- Hardness, Shore A: 66
- Abrasion: 150
- Compression Set: 16 % @Temperature 23.0 °C
$ 1616/MT
- Density: 1.02 g/cc
- Density: 1.23 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 62
- Abrasion: 23
$ 1605/MT
- Density: 0.400 g/cc
- Apparent Bulk Density: 0.400 g/cc
- Hardness, Shore D: 46
- Tensile Strength, Ultimate: 8.30 MPa
- Elongation at Break: 7.0 %
$ 2392/MT
- Density: 0.980 g/cc
- Density: 1.12 g/cc
- Hardness, Shore A: 86
- Hardness, Shore D: 35
- Abrasion: 25
Delivery Polyurethane Covestro
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.