$ 1930/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 1803/MT
- Density: 1.35 g/cc
- Water Absorption: 0.29 %
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.29 %
- Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2278/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1674/MT
- Density: 1.20 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1972/MT
- Density: 1.20 g/cc
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 6.0 %
$ 1510/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 2.00 mm
$ 2113/MT
- Density: 1.19 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1622/MT
- Density: 1.27 g/cc
- Water Absorption: 0.29 %
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.29 %
- Linear Mold Shrinkage: 0.0030 - 0.0050 cm/cm
$ 1551/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Oxygen Transmission: 67.0 cc-mm/m²-24hr-atm @Thickness 0.100 mm
$ 1704/MT
- Density: 1.23 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
$ 1599/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 56
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1557/MT
- Density: 1.19 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1666/MT
- Density: 1.18 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 38 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 60.0 MPa
$ 1619/MT
- Density: 1.15 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1614/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 125000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 2301/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1597/MT
- Density: 1.25 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 50
- Elongation at Break: >= 50 %
- Compression Set: 25 %
$ 1726/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 25.0 MPa
- Tensile Strength, Yield: 2.50 MPa @Strain 100 %
$ 2158/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1907/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 33
- Tensile Strength at Break: 45.0 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1515/MT
- Density: 1.25 g/cc
- Hardness, Shore D: 55
- Elongation at Break: >= 50 %
- Compression Set: 30 %
- Compression Set: 50 % @Temperature 70.0 °C
- CTE, linear, Parallel to Flow: 170 µm/m-°C @Temperature 20.0 °C
$ 1587/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 2077/MT
- Density: 1.18 g/cc
- Density: 1.02 g/cc @Temperature 240 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 240 °C
$ 1532/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 46 g/10 min @Load 2.16 kg, Temperature 330 °C
- Tensile Strength, Yield: 68.0 MPa
$ 1768/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 60
- Tensile Strength at Break: 64.0 MPa
- Tensile Strength, Yield: 64.0 MPa
$ 1500/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
$ 2326/MT
- Density: 1.28 g/cc
- Water Absorption: 0.28 %
- Moisture Absorption at Equilibrium: 0.090 %
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 265 °C
- Tensile Strength, Yield: 58.0 MPa
$ 1466/MT
- Density: 1.15 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1787/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2123/MT
- Density: 1.08 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 43
- Tensile Strength at Break: 39.0 MPa
- Tensile Strength, Yield: 39.0 MPa
$ 1844/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1666/MT
- Density: 1.34 g/cc
- Density: 1.14 g/cc @Temperature 300 °C
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
$ 1547/MT
- Density: 1.20 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 2138/MT
- Density: 1.24 g/cc
- Water Absorption: 1.22 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 1.22 %
- Hardness, Shore D: 73
$ 1730/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1557/MT
- Density: 1.17 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 2450/MT
- Density: 1.30 g/cc
- Density: 1.11 g/cc @Temperature 270 °C
- Water Absorption: 0.90 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1445/MT
- Density: 1.14 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1791/MT
- Density: 0.945 g/cc
- Density: 1.11 g/cc
- Hardness, Shore A: 82
- Hardness, Shore D: 31
- Abrasion: 20
$ 1530/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 2116/MT
- Density: 1.13 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 19 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1926/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 150000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0065 cm/cm @Thickness 3.00 mm
$ 2186/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 160000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1563/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1852/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1931/MT
- Density: 1.20 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 65.0 MPa
$ 1655/MT
- Density: 1.10 g/cc
- Density: 0.935 g/cc @Temperature 260 °C
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1635/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1695/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1711/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1750/MT
- Density: 1.18 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 60.0 MPa
$ 1832/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1449/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 2405/MT
- Density: 1.12 g/cc
- Tensile Strength, Yield: 5.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- Vicat Softening Point: 80.0 °C
- Glass Transition Temp, Tg: -46.0 °C
$ 1489/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1628/MT
- Density: 1.19 g/cc
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 127 °C
- Deflection Temperature at 1.8 MPa (264 psi): 115 °C
$ 2571/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 32
- Abrasion: 30
- Compression Set: 30 % @Temperature 23.0 °C
$ 2015/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 2028/MT
- Density: 1.20 g/cc
- Density: 1.03 g/cc @Temperature 270 °C
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: >= 50 %
$ 2076/MT
- Density: 1.24 g/cc
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 22 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 66.0 MPa
$ 1707/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1549/MT
- Density: 1.19 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 1629/MT
- Density: 1.25 g/cc
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 13 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 60.0 MPa
$ 1731/MT
- Density: 1.14 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Viscosity: 210000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm @Thickness 3.00 mm
$ 1650/MT
- Density: 1.26 g/cc
- Tensile Strength, Yield: 6.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- Vicat Softening Point: 88.0 °C
- Glass Transition Temp, Tg: -30.0 °C
$ 1496/MT
- Density: 1.18 g/cc
- Density: 1.01 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1931/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1867/MT
- Density: 1.15 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1815/MT
- Density: 1.30 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1826/MT
- Density: 1.03 g/cc
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 33
- Tensile Strength at Break: 50.0 MPa
$ 1471/MT
- Density: 1.19 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2179/MT
- Density: 1.02 g/cc
- Density: 1.20 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Viscosity Test: 64 cm³/g
$ 1582/MT
- Density: 1.19 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 1602/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 59
- Abrasion: 18
- Compression Set: 24 % @Temperature 23.0 °C
$ 1533/MT
- Density: 1.11 g/cc
- Density: 0.935 g/cc @Temperature 260 °C
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 2563/MT
- Density: 1.20 g/cc
- Water Absorption: 0.20 %
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1874/MT
- Density: 1.01 g/cc
- Density: 1.19 g/cc
- Hardness, Shore A: 86
- Hardness, Shore D: 38
- Abrasion: 32
$ 1496/MT
- Density: 1.38 g/cc
- Hardness, Shore A: 99
- Hardness, Shore D: 70
- Tensile Strength at Break: 64.0 MPa
- Tensile Strength, Yield: 64.0 MPa
$ 2314/MT
- Density: 1.17 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
$ 2284/MT
- Density: 1.19 g/cc
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 138 °C
- Deflection Temperature at 1.8 MPa (264 psi): 125 °C
$ 1832/MT
- Density: 1.18 g/cc
- Density: 1.01 g/cc @Temperature 240 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 40 g/10 min @Load 5.00 kg, Temperature 240 °C
$ 1759/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
$ 2150/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1691/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1793/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1464/MT
- Density: 1.20 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
$ 1590/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 21 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1456/MT
- Density: 1.14 g/cc
- Tensile Strength, Yield: 33.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 160 µm/m-°C @Temperature 20.0 °C
- Vicat Softening Point: 116 °C
$ 1635/MT
- Density: 1.20 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 55.0 MPa
$ 1801/MT
- Density: 1.20 g/cc
- Water Absorption: 0.20 %
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 2146/MT
- Density: 1.13 g/cc
- Density: 0.945 g/cc @Temperature 260 °C
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1896/MT
- Density: 1.19 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 65.0 MPa
$ 1959/MT
- Density: 1.10 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1869/MT
- Density: 1.40 g/cc
- Ball Indentation Hardness: 90.0 MPa
- Tensile Strength at Break: 100 MPa
- Tensile Strength, Yield: 100 MPa
- Elongation at Break: 3.0 %
$ 1512/MT
- Density: 1.15 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 2041/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 2.00 mm
$ 1672/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2283/MT
- Density: 1.25 g/cc
- Density: 1.07 g/cc @Temperature 260 °C
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 77.0 MPa
$ 1649/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 91
- Hardness, Shore D: 40
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1545/MT
- Density: 1.15 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 330 °C
- Tensile Strength, Yield: 74.0 MPa
$ 1557/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1856/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1759/MT
- Density: 1.13 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 1973/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1517/MT
- Density: 1.22 g/cc
- Water Absorption: 0.20 %
- Availability: Europe
- Availability: Near East/Africa
- Availability: South and Central America
$ 1875/MT
- Density: 1.27 g/cc
- Moisture Absorption at Equilibrium: 0.10 %
- Water Absorption at Saturation: 0.26 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0045 cm/cm @Thickness 2.00 mm
$ 2126/MT
- Density: 1.19 g/cc
- Density: 1.01 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 2202/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1651/MT
- Density: 1.18 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 60.0 MPa
$ 1557/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 2562/MT
- Density: 1.02 g/cc
- Density: 1.22 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 48
- Abrasion: 23
$ 1611/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 42
- Elongation at Break: >= 50 %
- Compression Set: 25 %
$ 1670/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 1484/MT
- Density: 1.23 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1482/MT
- Density: 1.19 g/cc
- Melt Flow: 10.5 g/10 min @Load 1.20 kg, Temperature 300 °C
- Deflection Temperature at 0.46 MPa (66 psi): 133 °C
- Deflection Temperature at 1.8 MPa (264 psi): 120 °C
- Vicat Softening Point: 140 °C @Load 5.10 kg
$ 1806/MT
- Viscosity: 410000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 5.0 %
$ 2308/MT
- Density: 1.11 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 2563/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2593/MT
- Density: 1.23 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1531/MT
- Density: 1.22 g/cc
- Water Absorption: 0.25 %
- Moisture Absorption at Equilibrium: 0.11 %
- Melt Flow: 28 g/10 min @Load 5.00 kg, Temperature 265 °C
- Tensile Strength, Yield: 56.0 MPa
$ 1841/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1480/MT
- Density: 1.34 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1775/MT
- Density: 1.20 g/cc
- Water Absorption: 0.20 %
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1532/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Elongation at Break: >= 50 %
- Compression Set: 30 %
- Compression Set: 65 % @Temperature 70.0 °C
$ 1608/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1923/MT
- Density: 1.34 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Tensile Strength, Ultimate: 79.0 MPa
$ 1595/MT
- Density: 1.19 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 60.0 MPa
$ 1858/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 2065/MT
- Density: 1.15 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1893/MT
- Density: 1.02 g/cc
- Density: 1.20 g/cc
- Hardness, Shore A: 80
- Hardness, Shore D: 30
- Tensile Strength at Break: 30.0 MPa
$ 1676/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 4.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1446/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 33
- Abrasion: 40
- Compression Set: 25 % @Temperature 23.0 °C
$ 1697/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 41
- Abrasion: 26
- Compression Set: 20 % @Temperature 23.0 °C
$ 1878/MT
- Density: 1.37 g/cc
- Water Absorption: 0.23 %
- Moisture Absorption at Equilibrium: 0.080 %
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 265 °C
- Tensile Strength, Yield: 90.0 MPa
$ 2271/MT
- Melt Flow: 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 75.0 MPa
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 100 %
- Elongation at Yield: 5.0 %
$ 2202/MT
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 26 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 56.0 MPa
- Elongation at Yield: 5.0 %
$ 2572/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 210000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1589/MT
- Density: 1.15 g/cc
- Density: 0.980 g/cc @Temperature 260 °C
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1659/MT
- Tensile Modulus: 3.10 GPa
- CTE, linear, Parallel to Flow: 60.0 µm/m-°C
- CTE, linear, Transverse to Flow: 60.0 µm/m-°C
- Deflection Temperature at 0.46 MPa (66 psi): 128 °C
- Deflection Temperature at 1.8 MPa (264 psi): 110 °C
$ 2090/MT
- Density: 1.29 g/cc
- Density: 1.10 g/cc @Temperature 300 °C
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 8.5 %
$ 2455/MT
- Density: 1.17 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 2028/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 43
- Abrasion: 25
- Compression Set: 22 % @Temperature 23.0 °C
$ 1592/MT
- Density: 0.915 g/cc
- Density: 1.08 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 51
- Tensile Strength at Break: 48.0 MPa
$ 2170/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 2193/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 310 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1745/MT
- Density: 1.50 g/cc
- Water Absorption: 0.27 %
- Moisture Absorption at Equilibrium: 0.11 %
- Water Absorption at Saturation: 0.27 %
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1692/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 65
- Tensile Strength at Break: 64.0 MPa
- Tensile Strength, Yield: 64.0 MPa
$ 1903/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Viscosity: 200000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1643/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Elongation at Break: >= 50 %
- Compression Set: 25 %
- Compression Set: 65 % @Temperature 70.0 °C
$ 1460/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 19 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2342/MT
- Density: 1.18 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1536/MT
- Density: 1.12 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1825/MT
- Density: 1.11 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Viscosity: 300000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm @Thickness 3.00 mm
$ 1588/MT
- Density: 1.34 g/cc
- Water Absorption: 0.24 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
$ 1847/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 33
- Tensile Strength at Break: 43.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1540/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
$ 1946/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1566/MT
- Density: 1.20 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 1953/MT
- Density: 1.20 g/cc
- Density: 1.03 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 7.2 g/10 min @Load 2.16 kg, Temperature 250 °C
$ 1738/MT
- Density: 1.29 g/cc
- Density: 1.10 g/cc @Temperature 300 °C
- Water Absorption: 0.24 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 2049/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 16 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1517/MT
- Density: 1.17 g/cc
- Density: 0.995 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1595/MT
- Density: 1.23 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
$ 1781/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1630/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 2366/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1499/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1612/MT
- Density: 1.23 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1573/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2110/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1528/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1515/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2096/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1526/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1643/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1598/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1445/MT
- Density: 1.13 g/cc
- Density: 0.960 g/cc @Temperature 260 °C
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1576/MT
- Density: 1.15 g/cc
- Density: 0.980 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 2197/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1892/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 155000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 2024/MT
- Density: 0.970 g/cc
- Density: 1.18 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 65
- Abrasion: 19
$ 1610/MT
- Density: 1.18 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 50 g/10 min @Load 5.00 kg, Temperature 240 °C
$ 1690/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
$ 1492/MT
- Density: 1.15 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1918/MT
- Density: 1.31 g/cc
- Water Absorption: 0.24 %
- Moisture Absorption at Equilibrium: 0.10 %
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 265 °C
- Tensile Strength, Yield: 76.0 MPa
$ 1699/MT
- Density: 1.35 g/cc
- Density: 1.16 g/cc @Temperature 270 °C
- Melt Flow: 4.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Modulus: 4.20 GPa
- CTE, linear, Parallel to Flow: 50.0 µm/m-°C
$ 2282/MT
- Density: 1.28 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 65.0 MPa
$ 1618/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1666/MT
- Density: 1.27 g/cc
- Density: 1.08 g/cc @Temperature 300 °C
- Water Absorption: 0.26 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 1901/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 2372/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 75
- Tensile Strength at Break: 34.0 MPa
- Tensile Strength, Yield: 34.0 MPa
$ 2280/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1726/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1681/MT
- Density: 1.41 g/cc
- Water Absorption: 0.20 %
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1714/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 1587/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 200000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 2018/MT
- Density: 1.18 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 240 °C
$ 1523/MT
- Density: 0.985 g/cc
- Density: 1.18 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 62
- Abrasion: 20
$ 1726/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1603/MT
- Density: 1.29 g/cc
- Density: 1.07 g/cc @Temperature 260 °C
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 120 MPa
$ 2271/MT
- Density: 1.18 g/cc
- Density: 1.01 g/cc @Temperature 240 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 240 °C
$ 1856/MT
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 75.0 MPa
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 100 %
- Elongation at Yield: 5.0 %
$ 1789/MT
- Density: 1.12 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1992/MT
- Density: 1.17 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 58
- Tensile Strength at Break: 63.0 MPa
- Tensile Strength, Yield: 63.0 MPa
$ 1552/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 2020/MT
- Density: 1.08 g/cc
- Hardness, Shore A: 86
- Tensile Strength at Break: 33.0 MPa
- Tensile Strength, Yield: 33.0 MPa
- Tensile Strength, Yield: 7.00 MPa @Strain 100 %
$ 2304/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 97
- Hardness, Shore D: 63
- Abrasion: 30
- Availability: Asia Pacific
$ 2515/MT
- Density: 1.17 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1842/MT
- Density: 1.11 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Viscosity: 190000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm @Thickness 3.00 mm
$ 2158/MT
- Density: 1.13 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 19 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1741/MT
- Density: 1.11 g/cc
- Density: 0.950 g/cc @Temperature 260 °C
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 4.8 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1744/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1852/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 65
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 30.0 MPa
- Tensile Strength, Yield: 2.50 MPa @Strain 100 %
$ 1620/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2168/MT
- Density: 1.51 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1616/MT
- Density: 1.22 g/cc
- Water Absorption: 0.25 %
- Moisture Absorption at Equilibrium: 0.11 %
- Melt Flow: 28 g/10 min @Load 5.00 kg, Temperature 265 °C
- Tensile Strength, Yield: 56.0 MPa
$ 1563/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 35 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1843/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 40
- Elongation at Break: >= 50 %
- Compression Set: 25 %
$ 1999/MT
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 360000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0050 cm/cm @Thickness 3.00 mm
$ 1819/MT
- Density: 1.03 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 40
- Abrasion: 30
$ 1475/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 160000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1610/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
$ 1917/MT
- Density: 1.18 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 240 °C
- Tensile Strength, Yield: 60.0 MPa
$ 2195/MT
- Density: 1.19 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 480000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 2357/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1521/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 33
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1459/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
$ 2018/MT
- Density: 1.20 g/cc
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.60 %
- Linear Mold Shrinkage: 0.0030 - 0.0040 cm/cm
$ 1585/MT
- Density: 0.960 g/cc
- Density: 1.13 g/cc
- Hardness, Shore A: 85
- Abrasion: 28
- Compression Set: 18 % @Temperature 23.0 °C
$ 2090/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1568/MT
- Density: 1.17 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1911/MT
- Density: 0.980 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 53
- Abrasion: 25
- Compression Set: 23 % @Temperature 23.0 °C
$ 1791/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1553/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
$ 1472/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1760/MT
- Density: 1.12 g/cc
- Tensile Strength, Yield: 12.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- Vicat Softening Point: 80.0 °C
- Glass Transition Temp, Tg: -46.0 °C
$ 2036/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
$ 1692/MT
- Density: 1.18 g/cc
- Viscosity: 120000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0065 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0065 cm/cm @Thickness 3.00 mm
- Tensile Strength at Break: 49.0 MPa
$ 1580/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2070/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 1471/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1563/MT
- Density: 1.15 g/cc
- Density: 0.980 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1742/MT
- Density: 1.20 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
$ 2522/MT
- Density: 1.02 g/cc
- Density: 1.14 g/cc
- Hardness, Shore A: 80
- Hardness, Shore D: 29
- Abrasion: 70
$ 1628/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 33
- Abrasion: 60
- Compression Set: 25 % @Temperature 23.0 °C
$ 1614/MT
- Density: 1.14 g/cc
- Density: 0.980 g/cc @Temperature 260 °C
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 19 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 2172/MT
- Density: 1.03 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 50
- Abrasion: 70
$ 2212/MT
- Density: 1.15 g/cc
- Density: 0.980 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1867/MT
- Density: 1.30 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1853/MT
- Density: 1.19 g/cc
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 128 °C
- Deflection Temperature at 1.8 MPa (264 psi): 116 °C
$ 2368/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 73
- Tensile Strength at Break: 55.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 1581/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 1445/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Spiral Flow: 58.0 cm @Thickness 2.50 mm
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Break: 130 %
$ 1517/MT
- Density: 1.14 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1954/MT
- Density: 1.19 g/cc
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 137 °C
- Deflection Temperature at 1.8 MPa (264 psi): 124 °C
$ 2187/MT
- Bulk Density: 0.660 g/cc
- Density: 1.19 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 2.00 mm
$ 1445/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 135000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1786/MT
- Density: 1.22 g/cc
- Tensile Strength, Yield: 9.60 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 130 µm/m-°C @Temperature 20.0 °C
- Vicat Softening Point: 115 °C
$ 2274/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 4.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1582/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 13 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 2086/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 1611/MT
- Density: 1.44 g/cc
- Water Absorption: 0.28 %
- Moisture Absorption at Equilibrium: 0.11 %
- Water Absorption at Saturation: 0.28 %
- Melt Flow: 4.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1503/MT
- Density: 1.35 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1761/MT
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Thickness 2.00 mm
$ 1979/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 65
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1447/MT
- Density: 0.970 g/cc
- Density: 1.15 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 43
- Tensile Strength at Break: 50.0 MPa
$ 1621/MT
- Density: 1.21 g/cc
- Water Absorption: 1.1 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 1.1 %
- Hardness, Shore A: 86
$ 1585/MT
- Density: 1.13 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1957/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 2201/MT
- Density: 1.23 g/cc
- Hardness, Shore D: 59
- Elongation at Break: >= 50 %
- Compression Set: 30 %
- Compression Set: 60 % @Temperature 70.0 °C
- CTE, linear, Parallel to Flow: 181 µm/m-°C @Temperature 20.0 °C
$ 2207/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 9.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1867/MT
- Density: 1.18 g/cc
- Density: 1.01 g/cc @Temperature 240 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 240 °C
$ 1882/MT
- Density: 1.15 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1665/MT
- Density: 1.215 g/cc
- Melt Flow: 19 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 100 %
$ 1597/MT
- Density: 1.22 g/cc
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.16 %
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 265 °C
- Tensile Strength, Yield: 48.0 MPa
$ 1488/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2178/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1558/MT
- Density: 1.15 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 2059/MT
- Density: 1.15 g/cc
- Density: 0.980 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 2095/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1596/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 32
- Abrasion: 30
- Compression Set: 25 % @Temperature 23.0 °C
$ 2263/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 1618/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Elongation at Break: >= 50 %
- Compression Set: 30 %
- Compression Set: 55 % @Temperature 70.0 °C
$ 1831/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 150000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm
$ 1663/MT
- Density: 1.10 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 1765/MT
- Density: 1.18 g/cc
- Density: 0.995 g/cc @Temperature 240 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 19 g/10 min @Load 5.00 kg, Temperature 240 °C
$ 1720/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 1455/MT
- Density: 1.25 g/cc
- Density: 1.07 g/cc @Temperature 260 °C
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1571/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1548/MT
- Density: 1.14 g/cc
- Density: 0.970 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 7.8 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1754/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 9.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1888/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1472/MT
- Density: 1.15 g/cc
- Density: 0.980 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1734/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1524/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1479/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 63.0 MPa
$ 1777/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1541/MT
- Density: 1.16 g/cc
- Melt Flow: 31 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Yield: 4.9 %
- Tensile Modulus: 2.45 GPa
$ 2451/MT
- Density: 1.21 g/cc
- Tensile Strength, Yield: 12.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 131 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 98.0 °C
$ 1606/MT
- Density: 1.19 g/cc
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Charpy Impact Unnotched: NB @Temperature 23.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 130 °C
- Deflection Temperature at 1.8 MPa (264 psi): 118 °C
$ 2238/MT
- Density: 1.19 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1468/MT
- Density: 1.22 g/cc
- Hardness, Shore D: 55
- Tensile Strength at Break: 58.0 MPa
- Tensile Strength, Yield: 58.0 MPa
- Tensile Strength, Yield: 14.0 MPa @Strain 100 %
$ 1467/MT
- Density: 1.02 g/cc @Temperature 260 °C
- Melt Flow: 19 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 5.0 %
$ 2015/MT
- Density: 1.18 g/cc
- CTE, linear, Parallel to Flow: 90.0 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 68.0 °C
- Deflection Temperature at 1.8 MPa (264 psi): 45.0 °C
- Vicat Softening Point: 140 °C
$ 1649/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.40 %
- Linear Mold Shrinkage, Flow: 0.0075 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0075 cm/cm @Thickness 2.00 mm
$ 1474/MT
- Density: 1.17 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 31 g/10 min @Load 2.16 kg, Temperature 330 °C
- Tensile Strength, Yield: 71.0 MPa
$ 1689/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 1.0 %
- Viscosity: 210000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0065 - 0.0085 cm/cm @Thickness 3.00 mm
$ 2188/MT
- Density: 1.27 g/cc
- Density: 1.08 g/cc @Temperature 300 °C
- Water Absorption: 0.26 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 2011/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 1794/MT
- Density: 1.31 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 18.5 g/10 min @Load 1.20 kg, Temperature 300 °C
- Elongation at Break: >= 50 %
$ 1607/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 1789/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 310 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1487/MT
- Density: 1.29 g/cc
- Water Absorption: 0.16 %
- Water Absorption at Saturation: 0.34 %
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 20 - 30 g/10 min @Load 5.00 kg, Temperature 265 °C
$ 1951/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1826/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Melt Flow: 13 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1470/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 2084/MT
- Viscosity: 275000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Tensile Strength at Break: 58.0 MPa
- Tensile Strength, Yield: 56.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 5.0 %
$ 1620/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 90
- Tensile Strength at Break: 26.0 MPa
- Tensile Strength, Yield: 26.0 MPa
- Tensile Strength, Yield: 6.30 MPa @Strain 100 %
$ 1474/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 2598/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 72
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1653/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1735/MT
- Density: 0.980 g/cc
- Density: 1.15 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 42
- Abrasion: 20
$ 1575/MT
- Density: 1.15 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 19 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1457/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 68
- Tensile Strength at Break: 67.0 MPa
- Tensile Strength, Yield: 67.0 MPa
$ 1744/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
$ 1736/MT
- Density: 1.35 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2090/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Melt Flow: 29 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: >= 50 %
$ 1704/MT
- Density: 1.09 g/cc
- Hardness, Shore A: 74
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 25.0 MPa
- Tensile Strength, Yield: 3.30 MPa @Strain 100 %
$ 1546/MT
- Density: 1.14 g/cc
- Density: 0.970 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 7.8 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 2068/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
$ 1719/MT
- Density: 1.15 g/cc
- Tensile Strength, Yield: 8.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 224 µm/m-°C @Temperature 20.0 °C
- Vicat Softening Point: 128 °C
$ 1863/MT
- Density: 1.22 g/cc
- Tensile Strength, Yield: 19.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 181 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 60.0 °C
$ 1581/MT
- Density: 1.20 g/cc
- Tensile Strength, Yield: 5.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 150 µm/m-°C @Temperature 20.0 °C
- Vicat Softening Point: 91.0 °C
$ 1951/MT
- Density: 1.13 g/cc
- Tensile Strength, Yield: 5.00 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- Vicat Softening Point: 106 °C
- Glass Transition Temp, Tg: -44.0 °C
$ 1491/MT
- Density: 1.24 g/cc
- Tensile Strength, Yield: 28.0 MPa @Strain 50.0 %
- Elongation at Break: >= 50 %
- CTE, linear, Parallel to Flow: 140 µm/m-°C @Temperature 20.0 °C
- Deflection Temperature at 0.46 MPa (66 psi): 46.0 °C
$ 1830/MT
- Density: 1.20 g/cc
- Transmission, Visible: 90 %
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1794/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1470/MT
- Density: 1.27 g/cc
- Density: 1.08 g/cc @Temperature 300 °C
- Water Absorption: 0.26 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1557/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 9.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1946/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 9.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2429/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 9.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2149/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1719/MT
- Density: 1.11 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 34
- Abrasion: 84
- Compression Set: 28 % @Temperature 23.0 °C
$ 1785/MT
- Density: 1.15 g/cc
- Density: 0.980 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1481/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 91
- Hardness, Shore D: 36
- Abrasion: 27
- Compression Set: 20 % @Temperature 23.0 °C
$ 1455/MT
- Density: 1.30 g/cc
- Density: 1.11 g/cc @Temperature 260 °C
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1549/MT
- Density: 1.02 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 40
- Abrasion: 25
$ 2190/MT
- Density: 1.21 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1571/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 1876/MT
- Density: 0.900 g/cc
- Density: 1.06 g/cc
- Hardness, Shore A: 70
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 1464/MT
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.50 %
- Viscosity: 380000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0050 cm/cm @Thickness 3.00 mm
$ 1501/MT
- Density: 1.41 g/cc
- Water Absorption: 0.20 %
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1559/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1843/MT
- Density: 1.15 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1911/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1643/MT
- Density: 1.22 g/cc
- Hardness, Shore D: 65
- Tensile Strength at Break: 55.0 MPa
- Tensile Strength, Yield: 55.0 MPa
- Tensile Strength, Yield: 20.0 MPa @Strain 100 %
$ 2409/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 53
- Tensile Strength at Break: 65.0 MPa
- Tensile Strength, Yield: 65.0 MPa
$ 1468/MT
- Density: 1.04 g/cc
- Density: 1.22 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 53
- Abrasion: 25
$ 1481/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 85
- Hardness, Shore D: 33
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Yield: 50.0 MPa
$ 1910/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 290 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1676/MT
- Density: 1.14 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Viscosity: 190000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm @Thickness 3.00 mm
$ 2061/MT
- Density: 1.10 g/cc
- Density: 0.935 g/cc @Temperature 260 °C
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1853/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 44
- Tensile Strength at Break: 38.0 MPa
- Tensile Strength, Yield: 38.0 MPa
$ 1583/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm
- Tensile Strength at Break: 54.0 MPa
- Tensile Strength, Yield: 70.0 MPa
$ 1836/MT
- Density: 1.12 g/cc
- Density: 0.960 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 4.8 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1884/MT
- Density: 1.25 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 1447/MT
- Density: 1.02 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 92
- Abrasion: 60
- Compression Set: 24 % @Temperature 23.0 °C
$ 1484/MT
- Density: 1.27 g/cc
- Density: 1.08 g/cc @Temperature 300 °C
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
$ 1478/MT
- Density: 1.18 g/cc
- Density: 1.01 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 1498/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 52
- Abrasion: 29
- Compression Set: 25 % @Temperature 23.0 °C
$ 1643/MT
- Density: 1.35 g/cc
- Tensile Modulus: 4.20 GPa
- CTE, linear, Parallel to Flow: 50.0 µm/m-°C
- CTE, linear, Transverse to Flow: 50.0 µm/m-°C
- Deflection Temperature at 0.46 MPa (66 psi): 130 °C
$ 2144/MT
- Bulk Density: 0.660 g/cc
- Density: 1.19 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Water Vapor Transmission: 15.0 g/m²/day @Thickness 0.100 mm
$ 1859/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 310 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1479/MT
- Density: 1.01 g/cc
- Density: 1.15 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 46
- Abrasion: 30
$ 1454/MT
- Density: 1.04 g/cc
- Density: 1.21 g/cc
- Hardness, Shore A: 80
- Abrasion: 35
- Compression Set: 22 % @Temperature 23.0 °C
$ 1538/MT
- Density: 1.17 g/cc
- Density: 0.995 g/cc @Temperature 330 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 330 °C
$ 2441/MT
- Bulk Density: 0.660 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 1448/MT
- Density: 1.23 g/cc
- Availability: Europe
- Availability: Near East/Africa
- Availability: North America
- Availability: South and Central America
$ 2221/MT
- Density: 1.20 g/cc
- Melt Flow: 13 g/10 min @Load 1.20 kg, Temperature 300 °C
- Deflection Temperature at 0.46 MPa (66 psi): 139 °C
- Deflection Temperature at 1.8 MPa (264 psi): 124 °C
- Vicat Softening Point: 147 °C @Load 5.10 kg
$ 1936/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1775/MT
- Density: 1.20 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 50.0 MPa
$ 1650/MT
- Density: 1.15 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.60 %
- Viscosity: 255000 cP @Shear Rate 1000 1/s, Temperature 260 °C
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm @Thickness 3.00 mm
$ 1461/MT
- Density: 1.22 g/cc
- Water Absorption: 0.96 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.96 %
- Hardness, Shore A: 97
$ 1832/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 9.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2043/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1917/MT
- Density: 1.19 g/cc
- Water Absorption: 0.70 %
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
$ 1449/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 61
- Tensile Strength at Break: 22.0 MPa
- Tensile Strength, Yield: 22.0 MPa
- Tensile Strength, Yield: 2.50 MPa @Strain 100 %
$ 2495/MT
- Density: 1.23 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Water Absorption: 0.60 %
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 95.0 MPa
$ 1910/MT
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.0075 cm/cm @Thickness 2.00 mm
$ 1976/MT
- Bulk Density: 0.640 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Thickness 2.00 mm
$ 1550/MT
- Density: 1.21 g/cc
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Break: 90 %
$ 2078/MT
- Density: 1.02 g/cc
- Density: 1.22 g/cc
- Hardness, Shore A: 86
- Hardness, Shore D: 33
- Tensile Strength at Break: 46.0 MPa
$ 1627/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 300 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 2158/MT
- Density: 1.02 g/cc
- Density: 1.20 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 40
- Abrasion: 25
$ 2174/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 260 °C
- Melt Flow: 29 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: >= 50 %
$ 2022/MT
- Density: 1.20 g/cc
- Water Absorption: 0.35 %
- Moisture Absorption at Equilibrium: 0.15 %
- Water Absorption at Saturation: 0.35 %
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1510/MT
- Density: 1.17 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 66
- Abrasion: 30
- Compression Set: 73 % @Temperature 23.0 °C
$ 1818/MT
- Density: 0.925 g/cc
- Density: 1.08 g/cc
- Hardness, Shore A: 66
- Abrasion: 150
- Compression Set: 16 % @Temperature 23.0 °C
$ 1616/MT
- Density: 1.02 g/cc
- Density: 1.23 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 62
- Abrasion: 23
$ 2392/MT
- Density: 0.980 g/cc
- Density: 1.12 g/cc
- Hardness, Shore A: 86
- Hardness, Shore D: 35
- Abrasion: 25
$ 2309/MT
- Density: 1.19 g/cc
- Density: 1.01 g/cc @Temperature 260 °C
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 19 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1919/MT
- Density: 1.20 g/cc
- Density: 1.02 g/cc @Temperature 280 °C
- Water Absorption: 0.30 %
- Moisture Absorption at Equilibrium: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
Delivery Thermoplastic Covestro
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.