3M Dyneon™ PVDF 31508/0009 Polyvinylidene Fluoride price 2453 per MT

Physical Properties
Density
1.76 g/cc
Water Absorption
<= 0.040 %
Melt Index of Compound
5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound
15 g/10 min @Load 5.00 kg, Temperature 230 °C

Mechanical Properties
Tensile Strength at Break
22.0 MPa
Elongation at Break
475 %
Flexural Modulus
0.425 GPa

Thermal Properties
Melting Point
169 °C
Brittleness Temperature
-37.0 °C
Flammability, UL94
V-0
Oxygen Index
>= 100 % @Thickness 3.00 mm

Electrical Properties
Volume Resistivity
>= 1.00e+14 ohm-cm
Surface Resistivity per Square
>= 1.00e+14 ohm
Dielectric Constant
7.0 @Frequency 1e+6 Hz

Descriptive Properties
Form
Pellets

Alternative products

3M Dyneon™ PVDF 32008/0009 Polyvinylidene Fluoride accurate 99%

$ 1885/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

3M Dyneon™ PVDF 32008/0003 Polyvinylidene Fluoride (discontinued **) accurate 99%

$ 1928/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

3M Dyneon™ PVDF 31008/0009 Polyvinylidene Fluoride (discontinued **) accurate 99%

$ 2259/MT

Density: 1.78 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

3M Dyneon™ PVDF 11008/0003 Polyvinylidene Fluoride accurate 70%

$ 1539/MT

Density: 1.78 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 24 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 52.0 MPa

3M HDT Heat Shrink Tubing accurate 70%

$ 2555/MT

Density: 1.28 g/cc
Water Absorption: 0.020 %
Tensile Strength at Break: 10.3 MPa
Tensile Strength at Break: 16.5 MPa
Elongation at Break: 475 %

Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite accurate 70%

$ 2111/MT

Density: 0.920 g/cc
Density: 0.920 g/cc
Water Absorption: <= 0.10 %
Water Absorption: <= 0.10 %
Water Absorption: <= 0.10 %

3M Dyneon™ PVDF 31508/0001 Polyvinylidene Fluoride (discontinued **) accurate 99%

$ 2289/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

3M Dyneon™ PVDF 31008/0003 Polyvinylidene Fluoride (discontinued **) accurate 70%

$ 1756/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 56.0 MPa

3M Dyneon™ PVDF 32008/0000 Polyvinylidene Fluoride (discontinued **) accurate 99%

$ 2401/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale online. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for 3M Dyneon™ PVDF 31508/0009 Polyvinylidene Fluoride

Seller from Ōsaka – 2021-07-04:

Seller from Ōsaka work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2453 per MT