3M HDT Heat Shrink Tubing price 2555 per MT

Physical Properties
Density
1.28 g/cc
Water Absorption
0.020 %

Mechanical Properties
Tensile Strength at Break
10.3 MPa
Tensile Strength at Break
16.5 MPa
Elongation at Break
475 %
Elongation at Break
225 % @Temperature 175 °C, Time 1.21e+6 sec
2% Secant Modulus
0.0965 GPa

Electrical Properties
Volume Resistivity
1.00e+14 ohm-cm
Dielectric Strength
7.87 kV/mm
Dielectric Strength
19.7 kV/mm

Alternative products

3M Dyneon™ PVDF 32008/0009 Polyvinylidene Fluoride accurate 44%

$ 1885/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

Seals Eastern 7202 Nitrile Rubber accurate 44%

$ 2495/MT

Specific Gravity: 1.19 g/cc
Hardness, Shore A: >= 65
Hardness, Shore A: 70
Hardness, Shore A: 71 @Temperature 100 °C, Time 252000 sec
Hardness, Shore A: 73 @Temperature 100 °C, Time 605000 sec

3M Dyneon™ PVDF 32008/0003 Polyvinylidene Fluoride (discontinued **) accurate 44%

$ 1928/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

3M Dyneon™ PVDF 31008/0009 Polyvinylidene Fluoride (discontinued **) accurate 44%

$ 2259/MT

Density: 1.78 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

3M MDT Tubing accurate 99%

$ 1576/MT

Density: 1.28 g/cc
Water Absorption: 0.20 %
Tensile Strength at Break: 10.3 MPa
Tensile Strength at Break: 16.5 MPa
Elongation at Break: 475 %

3M Dyneon™ PVDF 31508/0009 Polyvinylidene Fluoride accurate 44%

$ 2453/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced (Unverified Data**) accurate 44%

$ 1642/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc

3M Dyneon™ PVDF 31508/0001 Polyvinylidene Fluoride (discontinued **) accurate 44%

$ 2289/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

3M Dyneon™ PVDF 32008/0000 Polyvinylidene Fluoride (discontinued **) accurate 44%

$ 2401/MT

Density: 1.76 g/cc
Water Absorption: <= 0.040 %
Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 230 °C
Tensile Strength at Break: 22.0 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, bulk carrier large for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for 3M HDT Heat Shrink Tubing

Seller from Miami – 2021-03-03:

Seller from Miami work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2555 per MT