AK Steel TRAN-COR® H-2 CARLITE® DR® Grain Oriented Electrical Steel price 1497 per MT

Physical Properties
Density
7.65 g/cc
Thickness
270 - 310 microns
Thickness
300 microns

Mechanical Properties
Knoop Microhardness
173
Hardness, Rockwell B
83
Tensile Strength, Ultimate
359 MPa
Tensile Strength, Yield
345 MPa
Elongation at Break
11 %
Modulus of Elasticity
113.8 GPa
Modulus of Elasticity
138 GPa
Modulus of Elasticity
203 GPa
Modulus of Elasticity
241 GPa
Modulus of Elasticity
276 GPa

Electrical Properties
Exciting Power (RMS)
0.00171 RMS AT/cm @Magnetic Field 0.100 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.00215 RMS AT/cm @Magnetic Field 0.100 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.00601 RMS AT/cm @Magnetic Field 0.200 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.00772 RMS AT/cm @Magnetic Field 0.200 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.0126 RMS AT/cm @Magnetic Field 0.300 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.0163 RMS AT/cm @Magnetic Field 0.300 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.0212 RMS AT/cm @Magnetic Field 0.400 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.0274 RMS AT/cm @Magnetic Field 0.400 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.0314 RMS AT/cm @Magnetic Field 0.500 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.0407 RMS AT/cm @Magnetic Field 0.500 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.0433 RMS AT/cm @Magnetic Field 0.600 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.0562 RMS AT/cm @Magnetic Field 0.600 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.0568 RMS AT/cm @Magnetic Field 0.700 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.07219 RMS AT/cm @Magnetic Field 0.800 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.07390 RMS AT/cm @Magnetic Field 0.700 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.08972 RMS AT/cm @Magnetic Field 0.900 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.09377 RMS AT/cm @Magnetic Field 0.800 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.1102 RMS AT/cm @Magnetic Field 1.00 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.1165 RMS AT/cm @Magnetic Field 0.900 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.1340 RMS AT/cm @Magnetic Field 1.10 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.1432 RMS AT/cm @Magnetic Field 1.00 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.1619 RMS AT/cm @Magnetic Field 1.20 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.174 RMS AT/cm @Magnetic Field 1.10 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.1953 RMS AT/cm @Magnetic Field 1.30 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.2099 RMS AT/cm @Magnetic Field 1.20 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.2352 RMS AT/cm @Magnetic Field 1.40 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.2522 RMS AT/cm @Magnetic Field 1.30 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.2856 RMS AT/cm @Magnetic Field 1.50 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.3028 RMS AT/cm @Magnetic Field 1.40 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.3549 RMS AT/cm @Magnetic Field 1.60 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.3655 RMS AT/cm @Magnetic Field 1.50 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.4504 RMS AT/cm @Magnetic Field 1.60 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.4702 RMS AT/cm @Magnetic Field 1.70 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.5895 RMS AT/cm @Magnetic Field 1.70 T, Frequency 60.0 Hz
Exciting Power (RMS)
0.77651 RMS AT/cm @Magnetic Field 1.80 T, Frequency 50.0 Hz
Exciting Power (RMS)
0.95190 RMS AT/cm @Magnetic Field 1.80 T, Frequency 60.0 Hz
Exciting Power (RMS)
2.8414 RMS AT/cm @Magnetic Field 1.90 T, Frequency 50.0 Hz
Exciting Power (RMS)
3.5230 RMS AT/cm @Magnetic Field 1.90 T, Frequency 60.0 Hz
Electrical Resistivity
0.0000500 ohm-cm

Magnetic Properties
Core Loss
0.00361 W/kg @Magnetic Field 0.100 T, Frequency 50.0 Hz
Core Loss
0.00487 W/kg @Magnetic Field 0.100 T, Frequency 60.0 Hz
Core Loss
0.01382 W/kg @Magnetic Field 0.200 T, Frequency 50.0 Hz
Core Loss
0.01871 W/kg @Magnetic Field 0.200 T, Frequency 60.0 Hz
Core Loss
0.0305 W/kg @Magnetic Field 0.300 T, Frequency 50.0 Hz
Core Loss
0.0413 W/kg @Magnetic Field 0.300 T, Frequency 60.0 Hz
Core Loss
0.0533 W/kg @Magnetic Field 0.400 T, Frequency 50.0 Hz
Core Loss
0.0720 W/kg @Magnetic Field 0.400 T, Frequency 60.0 Hz
Core Loss
0.0818 W/kg @Magnetic Field 0.500 T, Frequency 50.0 Hz
Core Loss
0.1103 W/kg @Magnetic Field 0.500 T, Frequency 60.0 Hz
Core Loss
0.1159 W/kg @Magnetic Field 0.600 T, Frequency 50.0 Hz

Alternative products

Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet accurate 74%

$ 1741/MT

Density: 8.387 g/cc
Hardness, Brinell: 102 @Temperature 871 °C
Hardness, Brinell: 167 @Temperature 760 °C
Hardness, Brinell: 203 @Temperature 649 °C
Hardness, Brinell: 226 @Temperature 538 °C

AK Steel TRAN-COR® H-1 CARLITE® DR® Grain Oriented Electrical Steel accurate 99%

$ 1593/MT

Density: 7.65 g/cc
Thickness: 240 - 280 microns
Thickness: 270 microns
Knoop Microhardness: 173
Hardness, Rockwell B: 83

Carpenter Custom 455® Stainless Steel, Condition H900 (Age Hardened 482°C) accurate 74%

$ 2460/MT

Density: 7.76 g/cc
Hardness, Brinell: 472
Hardness, Knoop: 519
Hardness, Rockwell C: 49
Hardness, Vickers: 496

AK Steel TRAN-COR® H-0 CARLITE® DR® Grain Oriented Electrical Steel accurate 99%

$ 1781/MT

Density: 7.65 g/cc
Thickness: 200 - 240 microns
Thickness: 230 microns
Knoop Microhardness: 173
Hardness, Rockwell B: 83

Latrobe Lescalloy® 4330+V VAC-ARC High Strength Alloy Steel accurate 74%

$ 2253/MT

Density: 7.83 g/cc
Hardness, Rockwell C: 47
Hardness, Rockwell C: 50
Tensile Strength, Ultimate: 1550 MPa
Tensile Strength, Ultimate: 1620 MPa

AK Steel TRAN-COR® H-0 CARLITE® Grain Oriented Electrical Steel accurate 99%

$ 1513/MT

Density: 7.65 g/cc
Thickness: 200 - 240 microns
Thickness: 230 microns
Knoop Microhardness: 173
Hardness, Rockwell B: 83

AK Steel TRAN-COR® H-1 CARLITE® Grain Oriented Electrical Steel accurate 99%

$ 1638/MT

Density: 7.65 g/cc
Thickness: 240 - 280 microns
Thickness: 270 microns
Knoop Microhardness: 173
Hardness, Rockwell B: 83

AK Steel TRAN-COR® H-2 CARLITE® Grain Oriented Electrical Steel accurate 99%

$ 1675/MT

Density: 7.65 g/cc
Thickness: 270 - 310 microns
Thickness: 300 microns
Knoop Microhardness: 173
Hardness, Rockwell B: 83

Carpenter Kovar® Alloy (Glass and Ceramic Sealing Alloy) accurate 74%

$ 1895/MT

Density: 8.36 g/cc
Hardness, Brinell: 120
Hardness, Rockwell B: 68
Tensile Strength, Ultimate: 517 MPa
Tensile Strength, Yield: 345 MPa

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for AK Steel TRAN-COR® H-2 CARLITE® DR® Grain Oriented Electrical Steel

Seller from Chicago – 2021-03-01:

Seller from Chicago work with company: 3M, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2064 per MT

Seller from Montréal – 2021-08-03:

Seller from Montréal work with company: PolyOne Corporation, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1857 per MT

Seller from Kolkata – 2021-04-29:

Seller from Kolkata work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1497 per MT