ATI Allegheny Ludlum 316Ti Austenitic Stainless Steel price 2253 per MT

Physical Properties
Density
8.00 g/cc

Mechanical Properties
Hardness, Rockwell B
76
Tensile Strength, Ultimate
620 MPa
Tensile Strength, Ultimate
78.0 MPa @Temperature 982 °C
Tensile Strength, Ultimate
155 MPa @Temperature 871 °C
Tensile Strength, Ultimate
261 MPa @Temperature 760 °C
Tensile Strength, Ultimate
375 MPa @Temperature 649 °C
Tensile Strength, Ultimate
423 MPa @Temperature 538 °C
Tensile Strength, Ultimate
433 MPa @Temperature 427 °C
Tensile Strength, Ultimate
443 MPa @Temperature 316 °C
Tensile Strength, Ultimate
455 MPa @Temperature 204 °C
Tensile Strength, Ultimate
518 MPa @Temperature 93.0 °C
Tensile Strength, Yield
55.0 MPa @Temperature 982 °C
Tensile Strength, Yield
112 MPa @Temperature 871 °C
Tensile Strength, Yield
145 MPa @Temperature 538 °C
Tensile Strength, Yield
146 MPa @Temperature 649 °C
Tensile Strength, Yield
146 MPa @Temperature 760 °C
Tensile Strength, Yield
146 MPa @Temperature 427 °C
Tensile Strength, Yield
159 MPa @Temperature 316 °C
Tensile Strength, Yield
179 MPa @Temperature 204 °C
Tensile Strength, Yield
208 MPa @Temperature 93.0 °C
Tensile Strength, Yield
248 MPa @Strain 0.200 %
Elongation at Break
54 %
Elongation at Break
19.5 % @Temperature 649 °C
Elongation at Break
23 % @Temperature 760 °C
Elongation at Break
23 % @Temperature 538 °C
Elongation at Break
25 % @Temperature 427 °C
Elongation at Break
26 % @Temperature 316 °C
Elongation at Break
28 % @Temperature 204 °C
Elongation at Break
39.5 % @Temperature 93.0 °C
Elongation at Break
41 % @Temperature 982 °C
Elongation at Break
48 % @Temperature 871 °C

Thermal Properties
CTE, linear
16.5 µm/m-°C @Temperature 20.0 - 100 °C
CTE, linear
18.2 µm/m-°C @Temperature 20.0 - 500 °C
CTE, linear
19.5 µm/m-°C @Temperature 20.0 - 1000 °C
Thermal Conductivity
14.6 W/m-K @Temperature 100 °C
Melting Point
1345 - 1440 °C
Solidus
1345 °C
Liquidus
1440 °C

Component Elements Properties
Carbon, C
<= 0.080 %
Chromium, Cr
16 - 18 %
Iron, Fe
>= 61.295 %
Manganese, Mn
<= 2.0 %
Molybdenum, Mo
2.0 - 3.0 %
Nickel, Ni
10 - 14 %
Nitrogen, N
<= 0.10 %
Phosphorous, P
<= 0.045 %
Silicon, Si
<= 0.75 %
Sulfur, S
<= 0.030 %
Titanium, Ti
<= 0.70 %

Alternative products

ATI Allegheny Ludlum Type 317 Stainless Steel, UNS S31700 accurate 90%

$ 1550/MT

Density: 8.027 g/cc
Hardness, Brinell: <= 217
Hardness, Rockwell B: <= 95
Tensile Strength, Ultimate: >= 515 MPa
Tensile Strength, Yield: >= 205 MPa @Strain 0.200 %

Osprey Metals 317L Stainless Steel Powder (Grade 80% - 22) accurate 99%

$ 1796/MT

Particle Size: 12 µm
Carbon, C: 0.020 %
Carbon, C: <= 0.030 %
Chromium, Cr: 18 - 20 %
Iron, Fe: 62.53 %

Osprey Metals 317L Stainless Steel Powder (Grade 90% - 22) accurate 99%

$ 2269/MT

Particle Size: 10 µm
Carbon, C: 0.020 %
Carbon, C: <= 0.030 %
Chromium, Cr: 18 - 20 %
Iron, Fe: 62.53 %

ATI Allegheny Ludlum Type 316L Stainless Steel, UNS S31603 accurate 90%

$ 2179/MT

Density: 8.027 g/cc
Hardness, Brinell: <= 217
Hardness, Rockwell B: <= 95
Tensile Strength, Ultimate: >= 485 MPa
Tensile Strength, Yield: >= 170 MPa @Strain 0.200 %

Osprey Metals 317L Stainless Steel Powder (Grade 95% - 16) accurate 99%

$ 1539/MT

Particle Size: 6.7 µm
Carbon, C: 0.020 %
Carbon, C: <= 0.030 %
Chromium, Cr: 18 - 20 %
Iron, Fe: 62.53 %

Schmolz + Bickenbach UGIMA® 316/316L Stainless Steel Bar accurate 81%

$ 1865/MT

Density: 8.03 g/cc
Hardness, Brinell: 160 - 190 @Thickness >=25.4 mm
Hardness, Brinell: 190 - 220 @Thickness <=25.4 mm
Tensile Strength: 517 - 655 MPa @Thickness >=25.4 mm
Tensile Strength: 621 - 793 MPa @Thickness <=25.4 mm

Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 35% Cold Worked accurate 81%

$ 1550/MT

Density: 7.95 g/cc
Hardness, Brinell: 266
Hardness, Knoop: 289
Hardness, Rockwell C: 26
Hardness, Vickers: 280

AK Steel 316 Austenitic Stainless steel accurate 81%

$ 2224/MT

Density: 7.99 g/cc
Hardness, Rockwell B: 79
Tensile Strength, Ultimate: 579 MPa
Tensile Strength, Yield: 290 MPa @Strain 0.200 %
Elongation at Break: 50 %

ATI Allegheny Ludlum Type 316 Stainless Steel, UNS S31600 accurate 90%

$ 1482/MT

Density: 8.027 g/cc
Hardness, Brinell: <= 217
Hardness, Rockwell B: <= 95
Tensile Strength, Ultimate: >= 515 MPa
Tensile Strength, Yield: >= 205 MPa @Strain 0.200 %

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for ATI Allegheny Ludlum 316Ti Austenitic Stainless Steel

Seller from Los Angeles – 2021-05-17:

Seller from Los Angeles work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2496 per MT

Seller from Ho Chi Minh City – 2021-06-18:

Seller from Ho Chi Minh City work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2280 per MT

Seller from Baghdad – 2021-05-12:

Seller from Baghdad work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2253 per MT