$ 1470/MT
- Density: 8.06 g/cc
- Tensile Strength, Ultimate: 1120 MPa
- Tensile Strength, Yield: 1010 MPa @Strain 0.200 %
- Elongation at Break: 8.0 %
- CTE, linear: 15.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 1806/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 910 MPa
- Tensile Strength, Yield: 824 MPa
- Elongation at Break: 18 %
$ 1685/MT
- Density: 7.74 g/cc
- Hardness, Rockwell C: 54
- Tensile Strength, Ultimate: 2022 MPa
- Tensile Strength, Yield: 1579 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 2157/MT
- Density: 7.72 g/cc
- Hardness, Rockwell B: 90
- Tensile Strength, Ultimate: 595 MPa
- Tensile Strength, Yield: 396 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 2253/MT
- Density: 8.00 g/cc
- Hardness, Rockwell B: 76
- Tensile Strength, Ultimate: 620 MPa
- Tensile Strength, Ultimate: 78.0 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 155 MPa @Temperature 871 °C
$ 1823/MT
- Density: 7.73 g/cc
- Hardness, Rockwell B: 88
- Hardness, Rockwell C: 56 - 59
- Tensile Strength, Ultimate: 600 MPa
- Tensile Strength, Yield: 310 MPa @Strain 0.200 %
$ 2144/MT
- Density: 7.76 g/cc
- Hardness, Rockwell B: 94
- Tensile Strength, Ultimate: 631 MPa
- Tensile Strength, Yield: 629 MPa @Strain 0.200 %
- Elongation at Break: 3.0 %
$ 1620/MT
- Density: 7.96 g/cc
- Hardness, Brinell: <= 201
- Hardness, Rockwell B: <= 92
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa @Strain 0.200 %
$ 1678/MT
- Density: 7.80 g/cc
- Hardness, Rockwell B: 79
- Tensile Strength, Ultimate: 286 MPa @Temperature 649 °C
- Tensile Strength, Ultimate: 401 MPa @Temperature 204 °C
- Tensile Strength, Ultimate: 492 MPa @Temperature 23.0 °C
$ 1550/MT
- Density: 8.027 g/cc
- Hardness, Brinell: <= 217
- Hardness, Rockwell B: <= 95
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa @Strain 0.200 %
$ 2312/MT
- Density: 7.90 g/cc
- Hardness, Brinell: 150
- Hardness, Rockwell B: 70 - 90
- Tensile Strength, Ultimate: >= 490 MPa
- Tensile Strength, Ultimate: 605 MPa
$ 1640/MT
- Density: 8.03 g/cc
- Hardness, Brinell: 382
- Hardness, Rockwell C: 41
- Tensile Strength, Ultimate: >= 1276 MPa
- Tensile Strength, Yield: >= 965 MPa @Strain 0.200 %
$ 1611/MT
- Density: 7.76 g/cc
- Hardness, Rockwell B: 93
- Tensile Strength, Ultimate: 591 MPa
- Tensile Strength, Yield: 577 MPa @Strain 0.200 %
- Elongation at Break: 4.5 %
$ 2107/MT
- Density: 7.64 g/cc
- Hardness, Brinell: 202
- Hardness, Rockwell B: 100
- Tensile Strength, Ultimate: 683 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 517 MPa @Strain 0.200 %
$ 1515/MT
- Density: 7.70 g/cc
- Tensile Strength, Ultimate: 818 MPa
- Tensile Strength, Yield: 795 MPa
- Elongation at Break: 3.2 %
- Modulus of Elasticity: 200 GPa
$ 1883/MT
- Density: 7.81 g/cc
- Hardness, Rockwell B: 100
- Tensile Strength, Ultimate: 1175 MPa
- Tensile Strength, Yield: 485 MPa @Strain 0.200 %
- Elongation at Break: 30 %
$ 1597/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 1282 MPa
- Tensile Strength, Yield: 1027 MPa
- Elongation at Break: 3.0 %
$ 1862/MT
- Specific Gravity: 7.70 g/cc
- Density: 7.70 g/cc
- Hardness, Rockwell B: 75 - 83 @Thickness 1.02 - 2.92 mm
- Hardness, Rockwell 30T: 62 - 70 @Thickness 0.508 - 1.52 mm
- Tensile Strength, Ultimate: 455 - 538 MPa @Thickness 1.02 - 2.92 mm
$ 1485/MT
- Density: 7.74 g/cc
- Hardness, Rockwell C: 53
- Tensile Strength, Ultimate: 1881 MPa
- Tensile Strength, Yield: 1610 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1609/MT
- Specific Gravity: 7.65 g/cc
- Density: 7.64 g/cc
- Hardness, Rockwell B: 82
- Hardness, Rockwell B: 98
- Hardness, Rockwell C: 35
$ 1914/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 34.5 @Temperature 23.0 °C
- Hardness, Rockwell C: 34.5 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1044 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1045 MPa @Temperature 23.0 °C
$ 2401/MT
- Density: 7.64 g/cc
- Hardness, Brinell: 260
- Hardness, Rockwell C: 26
- Tensile Strength, Ultimate: 931 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 758 MPa @Strain 0.200 %
$ 1458/MT
- Density: 7.64 g/cc
- Hardness, Rockwell B: <= 96
- Hardness, Rockwell B: 93 - 100
- Tensile Strength, Ultimate: >= 483 MPa
- Tensile Strength, Ultimate: >= 689 MPa
$ 1556/MT
- Density: 7.90 g/cc
- Hardness, Brinell: <= 201
- Hardness, Rockwell B: <= 92
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa
$ 1847/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 45.5 @Temperature 23.0 °C
- Hardness, Rockwell C: 45.5 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1495 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1522 MPa @Temperature 23.0 °C
$ 1473/MT
- Density: 7.711 g/cc
- Hardness, Rockwell B: 84
- Tensile Strength, Ultimate: 510 MPa
- Tensile Strength, Yield: 331 MPa
- Elongation at Break: 29 %
$ 1488/MT
- Density: 7.73 g/cc
- Hardness, Rockwell B: 85
- Tensile Strength, Ultimate: 592 MPa
- Tensile Strength, Yield: 355 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 2428/MT
- Density: 7.72 g/cc
- Hardness, Rockwell C: 29
- Tensile Strength, Ultimate: 936 MPa
- Tensile Strength, Yield: 743 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1586/MT
- Density: 8.06 g/cc
- Tensile Strength, Ultimate: 1210 MPa
- Tensile Strength, Yield: 1110 MPa @Strain 0.200 %
- Elongation at Break: 4.0 %
- CTE, linear: 15.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 2148/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 1103 MPa
- Tensile Strength, Yield: 986 MPa
- Elongation at Break: 5.0 %
$ 1583/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 88
- Tensile Strength, Ultimate: 862 MPa
- Tensile Strength, Yield: 758 MPa
- Elongation at Break: 22 %
$ 1583/MT
- Density: 7.76 g/cc
- Hardness, Rockwell C: 33
- Tensile Strength, Ultimate: 1030 MPa
- Tensile Strength, Yield: 760 MPa @Strain 0.200 %
- Elongation at Break: 8.0 %
$ 1465/MT
- Density: 7.65 g/cc
- Hardness, Rockwell C: 41
- Tensile Strength, Ultimate: 1300 MPa
- Tensile Strength, Yield: 916 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1660/MT
- Density: 8.08 g/cc
- Hardness, Rockwell B: 84.5 - 86.5
- Tensile Strength, Ultimate: 90.0 - 96.0 MPa
- Tensile Strength, Yield: 47.0 - 56.0 MPa
- Elongation at Break: 35 - 40 %
$ 1735/MT
- Density: 7.72 g/cc
- Hardness, Rockwell C: 53
- Tensile Strength, Ultimate: 1759 MPa
- Tensile Strength, Yield: 1452 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 2026/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 572 MPa
- Tensile Strength, Yield: 290 MPa
- Elongation at Break: 50 %
$ 1989/MT
- Density: 7.88 g/cc
- Hardness, Rockwell C: 27
- Tensile Strength, Ultimate: 860 MPa
- Tensile Strength, Yield: 585 MPa @Strain 0.200 %
- Elongation at Break: 30 %
$ 2073/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 88
- Tensile Strength, Ultimate: 1124 MPa
- Tensile Strength, Yield: 972 MPa
- Elongation at Break: 3.0 %
$ 1814/MT
- Density: 7.74 g/cc
- Hardness, Rockwell C: 53
- Tensile Strength, Ultimate: 1883 MPa
- Tensile Strength, Yield: 1531 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1832/MT
- Density: 7.72 g/cc
- Hardness, Rockwell C: 53
- Tensile Strength, Ultimate: 1868 MPa
- Tensile Strength, Yield: 1385 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1486/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 38 @Temperature 23.0 °C
- Hardness, Rockwell C: 38 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1123 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1140 MPa @Temperature 23.0 °C
$ 1669/MT
- Density: 7.76 g/cc
- Tensile Strength, Ultimate: 1276 MPa
- Tensile Strength, Yield: 1207 MPa @Strain 0.200 %
- Elongation at Break: 11 %
- Reduction of Area: 45 %
$ 1844/MT
- Density: 7.65 g/cc
- Hardness, Rockwell B: 81
- Tensile Strength, Ultimate: 554 MPa
- Tensile Strength, Yield: 313 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1860/MT
- Density: 7.88 g/cc
- Hardness, Brinell: 235
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Yield: 515 MPa @Strain 0.200 %
- Elongation at Break: 35 %
$ 1535/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 1014 MPa
- Tensile Strength, Yield: 931 MPa
- Elongation at Break: 10 %
$ 2316/MT
- Density: 7.70 g/cc
- Tensile Strength, Ultimate: 680 MPa
- Tensile Strength, Yield: 635 MPa
- Elongation at Break: 5.0 %
- Modulus of Elasticity: 200 GPa
$ 1685/MT
- Density: 7.65 g/cc
- Hardness, Rockwell C: 40
- Tensile Strength, Ultimate: 1289 MPa
- Tensile Strength, Yield: 1022 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1598/MT
- Density: 8.06 g/cc
- Tensile Strength, Ultimate: 1010 MPa
- Tensile Strength, Yield: 900 MPa @Strain 0.200 %
- Elongation at Break: 15 %
- CTE, linear: 15.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 1586/MT
- Density: 7.64 g/cc
- Hardness, Brinell: 235
- Hardness, Rockwell C: 21
- Tensile Strength, Ultimate: 738 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 565 MPa @Strain 0.200 %
$ 1520/MT
- Density: 8.03 g/cc
- Creep Strength: 20.0 MPa @Temperature 788 °C, Time 3.60e+7 sec
- Creep Strength: 138 MPa @Temperature 593 °C, Time 3.60e+7 sec
- Rupture Strength: 20.0 MPa @Temperature 899 °C, Time 3.60e+7 sec
- Rupture Strength: 138 MPa @Temperature 593 °C, Time 3.60e+7 sec
$ 1718/MT
- Hardness, Rockwell B: 75
- Tensile Strength, Ultimate: 461.9 MPa
- Tensile Strength, Ultimate: 34.5 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 89.6 MPa @Temperature 760 °C
- Tensile Strength, Ultimate: 206.8 MPa @Temperature 648 °C
$ 1619/MT
- Density: 8.03 g/cc
- Hardness, Brinell: 255
- Hardness, Rockwell C: 25
- Tensile Strength, Ultimate: >= 862 MPa
- Tensile Strength, Yield: >= 517 MPa @Strain 0.200 %
$ 2202/MT
- Density: 8.00 g/cc
- Hardness, Brinell: <= 217
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa
- Elongation at Break: >= 40 %
$ 1599/MT
- Density: 7.76 g/cc
- Hardness, Rockwell C: 45
- Tensile Strength, Ultimate: 1413 MPa
- Tensile Strength, Yield: 1310 MPa @Strain 0.200 %
- Elongation at Break: 10 %
$ 1727/MT
- Density: 7.80 g/cc
- Tensile Strength, Ultimate: 464 MPa
- Tensile Strength, Ultimate: 441 MPa @Temperature 93.3 °C
- Tensile Strength, Yield: 292 MPa
- Tensile Strength, Yield: 259 MPa @Temperature 93.3 °C
$ 1468/MT
- Density: 7.76 g/cc
- Hardness, Rockwell B: 70
- Tensile Strength, Ultimate: 419 MPa
- Tensile Strength, Yield: 225 MPa @Strain 0.200 %
- Elongation at Break: 35.3 %
$ 1713/MT
- Density: 7.76 g/cc
- Hardness, Rockwell C: 35
- Tensile Strength, Ultimate: 1034 MPa
- Tensile Strength, Yield: 931 MPa @Strain 0.200 %
- Elongation at Break: 14 %
$ 1615/MT
- Density: 7.90 g/cc
- Hardness, Brinell: <= 183
- Hardness, Rockwell B: <= 88
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa
$ 1850/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 655 MPa
- Tensile Strength, Yield: 290 MPa
- Elongation at Break: 60 %
$ 1884/MT
- Density: 7.857 g/cc
- Tensile Strength, Ultimate: 685 MPa @Temperature 70.0 °C
- Tensile Strength, Yield: 320 MPa @Temperature 70.0 °C
- Elongation at Break: 56 % @Temperature 70.0 °C
- Izod Impact: 208 J
$ 2103/MT
- Density: 7.73 g/cc
- Hardness, Rockwell C: 23
- Tensile Strength, Ultimate: 838 MPa
- Tensile Strength, Yield: 652 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1523/MT
- Density: 7.76 g/cc
- Hardness, Rockwell B: 71
- Tensile Strength, Ultimate: 434 MPa
- Tensile Strength, Yield: 241 MPa @Strain 0.200 %
- Elongation at Break: 33 % @Thickness 50.8 mm
$ 1551/MT
- Specific Gravity: 7.73 g/cc
- Density: 7.68 g/cc
- Hardness, Rockwell B: 85
- Hardness, Rockwell B: 87
- Hardness, Rockwell C: 23
$ 1459/MT
- Density: 7.76 g/cc
- Hardness, Rockwell C: 33
- Tensile Strength, Ultimate: 931 MPa
- Tensile Strength, Yield: 621 MPa @Strain 0.200 %
- Elongation at Break: 14 %
$ 1543/MT
- Carbon, C: 0.010 %
- Chromium, Cr: 16.25 %
- Iron, Fe: >= 68.685 %
- Manganese, Mn: 1.7 %
- Nickel, Ni: 10.15 %
$ 1850/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 49 @Temperature 23.0 °C
- Hardness, Rockwell C: 49 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1762 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1766 MPa @Temperature 23.0 °C
$ 1961/MT
- Density: 7.70 g/cc
- Hardness, Rockwell B: 78
- Tensile Strength, Ultimate: 455 MPa
- Tensile Strength, Yield: 290 MPa
- Elongation at Break: 34 %
$ 2100/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 88
- Tensile Strength, Ultimate: 745 MPa
- Tensile Strength, Yield: 641 MPa
- Elongation at Break: 33 %
$ 1797/MT
- Density: 7.65 g/cc
- Hardness, Rockwell B: 83
- Hardness, Rockwell C: 45 - 52
- Tensile Strength, Ultimate: 538 MPa
- Tensile Strength, Yield: 290 MPa @Strain 0.200 %
$ 1486/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Yield: 517 MPa
- Elongation at Break: 36 %
$ 1530/MT
- Density: 7.65 g/cc
- Hardness, Rockwell C: 41
- Tensile Strength, Ultimate: 1298 MPa
- Tensile Strength, Yield: 845 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1945/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 786 MPa
- Tensile Strength, Yield: 593 MPa
- Elongation at Break: 42 %
$ 1446/MT
- Density: 7.73 g/cc
- Hardness, Rockwell C: 44
- Tensile Strength, Ultimate: 1583 MPa
- Tensile Strength, Yield: 1213 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1863/MT
- Chromium, Cr: 29 %
- Iron, Fe: 65 %
- Molybdenum, Mo: 4.0 %
- Nickel, Ni: 2.0 %
$ 1651/MT
- Density: 7.73 g/cc
- Hardness, Rockwell B: 75
- Hardness, Rockwell B: <= 89
- Tensile Strength, Ultimate: >= 415 MPa
- Tensile Strength, Ultimate: 444 MPa
$ 1798/MT
- Density: 7.76 g/cc
- Hardness, Rockwell C: 47
- Tensile Strength, Ultimate: 1517 MPa
- Tensile Strength, Yield: 1413 MPa @Strain 0.200 %
- Elongation at Break: 10 %
$ 2179/MT
- Density: 8.027 g/cc
- Hardness, Brinell: <= 217
- Hardness, Rockwell B: <= 95
- Tensile Strength, Ultimate: >= 485 MPa
- Tensile Strength, Yield: >= 170 MPa @Strain 0.200 %
$ 1741/MT
- Density: 7.76 g/cc
- Hardness, Rockwell B: 89
- Tensile Strength, Ultimate: 480 MPa
- Tensile Strength, Yield: 470 MPa @Strain 0.200 %
- Elongation at Break: 12 %
$ 2092/MT
- Density: 8.06 g/cc
- Tensile Strength, Ultimate: 1320 MPa
- Tensile Strength, Yield: 1180 MPa @Strain 0.200 %
- Elongation at Break: 2.0 %
- CTE, linear: 15.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 1450/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 42.5 @Temperature 23.0 °C
- Hardness, Rockwell C: 42.5 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1264 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1300 MPa @Temperature 23.0 °C
$ 1838/MT
- Hardness, Rockwell B: 87
- Tensile Strength, Ultimate: 565 MPa
- Tensile Strength, Yield: 414 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- Charpy Impact: 67.8 J @Temperature -73.3 °C
$ 2083/MT
- Density: 7.86 g/cc
- Hardness, Rockwell B: 99.5 @Temperature 23.0 °C
- Hardness, Rockwell B: 99.5 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 783 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 814 MPa @Temperature 23.0 °C
$ 1943/MT
- Density: 7.857 g/cc
- Tensile Strength, Ultimate: 673 MPa @Temperature 70.0 °C
- Tensile Strength, Yield: 321 MPa @Temperature 70.0 °C
- Elongation at Break: 59 % @Temperature 70.0 °C
- Izod Impact: 184 J
$ 1863/MT
- Density: 8.03 g/cc
- Tensile Strength, Ultimate: 670 MPa
- Tensile Strength, Ultimate: 74.0 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 142 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 248 MPa @Temperature 760 °C
$ 1681/MT
- Density: 7.48 g/cc
- Hardness, Rockwell B: 88
- Tensile Strength, Ultimate: 519 MPa
- Tensile Strength, Ultimate: 524 MPa
- Tensile Strength, Ultimate: 538 MPa
$ 1629/MT
- Density: 8.03 g/cc
- Hardness, Rockwell B: 82
- Tensile Strength, Ultimate: 572.4 MPa
- Tensile Strength, Ultimate: 103.4 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 469 MPa @Temperature 538 °C
$ 1566/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 676 MPa
- Tensile Strength, Yield: 517 MPa
- Elongation at Break: 36 %
$ 2335/MT
- Density: 7.74 g/cc
- Hardness, Rockwell C: 31
- Tensile Strength, Ultimate: 933 MPa
- Tensile Strength, Yield: 727 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1598/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 88
- Tensile Strength, Ultimate: 1076 MPa
- Tensile Strength, Yield: 931 MPa
- Elongation at Break: 5.0 %
$ 1653/MT
- Density: 8.03 g/cc
- Creep Strength: 24.0 MPa @Temperature 788 °C, Time 3.60e+7 sec
- Creep Strength: 83.0 MPa @Temperature 593 °C, Time 3.60e+7 sec
- Rupture Strength: 17.0 MPa @Temperature 899 °C, Time 3.60e+7 sec
- Rupture Strength: 83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec
$ 1500/MT
- Density: 7.34 g/cc
- Hardness, Rockwell B: 89
- Tensile Strength, Ultimate: 554 MPa
- Tensile Strength, Yield: 412 MPa
- Elongation at Break: 28 %
$ 2061/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 48.5 @Temperature 23.0 °C
- Hardness, Rockwell C: 48.5 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1625 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1631 MPa @Temperature 23.0 °C
$ 2532/MT
- Chromium, Cr: 15.5 %
- Iron, Fe: 76.5 %
- Manganese, Mn: 0.95 %
- Molybdenum, Mo: 2.75 %
- Nickel, Ni: 4.3 %
$ 1917/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 88
- Tensile Strength, Ultimate: 648 MPa
- Tensile Strength, Yield: 517 MPa
- Elongation at Break: 45 %
$ 2342/MT
- Density: 8.03 g/cc
- Tensile Strength, Ultimate: 617 MPa
- Tensile Strength, Ultimate: 48.0 MPa @Temperature 1093 °C
- Tensile Strength, Ultimate: 76.0 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 209 MPa @Temperature 816 °C
$ 2076/MT
- Density: 8.00 g/cc
- Hardness, Rockwell B: 90
- Tensile Strength, Ultimate: 903 MPa
- Tensile Strength, Ultimate: 630 MPa @Temperature 300 °C
- Tensile Strength, Ultimate: 725 MPa @Temperature 100 °C
$ 1936/MT
- Density: 7.723 g/cc
- Hardness, Rockwell C: 20
- Tensile Strength, Ultimate: 725 MPa
- Tensile Strength, Ultimate: 745 MPa
- Tensile Strength, Ultimate: 917 MPa
$ 2284/MT
- Density: 7.78 g/cc
- Hardness, Rockwell C: 33
- Tensile Strength, Ultimate: 1035 MPa
- Tensile Strength, Yield: 760 MPa @Strain 0.200 %
- Elongation at Break: 10 %
$ 1691/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 39 @Temperature 23.0 °C
- Hardness, Rockwell C: 39 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1214 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1224 MPa @Temperature 23.0 °C
$ 1629/MT
- Density: 7.64 g/cc
- Hardness, Brinell: 385
- Hardness, Rockwell C: 42
- Tensile Strength, Ultimate: 1187 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 952 MPa @Strain 0.200 %
$ 2341/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 88
- Tensile Strength, Ultimate: 979 MPa
- Tensile Strength, Yield: 855 MPa
- Elongation at Break: 14 %
$ 1722/MT
- Density: 7.73 g/cc
- Hardness, Rockwell C: 36
- Tensile Strength, Ultimate: 1093 MPa
- Tensile Strength, Yield: 951 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1723/MT
- Carbon, C: 0.020 %
- Chromium, Cr: 21.8 %
- Copper, Cu: 0.20 %
- Iron, Fe: >= 45.069 %
- Manganese, Mn: 0.30 %
$ 1693/MT
- Density: 8.06 g/cc
- Tensile Strength, Ultimate: 1280 MPa
- Tensile Strength, Yield: 1140 MPa @Strain 0.200 %
- Elongation at Break: 3.0 %
- CTE, linear: 15.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 1658/MT
- Density: 8.03 g/cc
- Tensile Strength, Ultimate: 624 MPa
- Tensile Strength, Ultimate: 44.0 MPa @Temperature 1093 °C
- Tensile Strength, Ultimate: 81.0 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 155 MPa @Temperature 871 °C
$ 1549/MT
- Density: 8.03 g/cc
- Creep Strength: 20.0 MPa @Temperature 788 °C, Time 3.60e+7 sec
- Creep Strength: 138 MPa @Temperature 593 °C, Time 3.60e+7 sec
- Rupture Strength: 20.0 MPa @Temperature 899 °C, Time 3.60e+7 sec
- Rupture Strength: 138 MPa @Temperature 593 °C, Time 3.60e+7 sec
$ 1911/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 1103 MPa
- Tensile Strength, Yield: 986 MPa
- Elongation at Break: 5.0 %
$ 1781/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Yield: 690 MPa
- Elongation at Break: 26 %
$ 1460/MT
- Density: 7.857 g/cc
- Tensile Strength, Ultimate: 669 MPa @Temperature 70.0 °C
- Tensile Strength, Yield: 343 MPa @Temperature 70.0 °C
- Elongation at Break: 56.5 % @Temperature 70.0 °C
- Izod Impact: 154 J
$ 1791/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 1282 MPa
- Tensile Strength, Yield: 1027 MPa
- Elongation at Break: 3.0 %
$ 1613/MT
- Density: 8.03 g/cc
- Hardness, Brinell: 342
- Hardness, Rockwell C: 37
- Tensile Strength, Ultimate: >= 1207 MPa
- Tensile Strength, Yield: >= 931 MPa @Strain 0.200 %
$ 1854/MT
- Density: 7.674 g/cc
- Hardness, Rockwell B: 86
- Tensile Strength, Ultimate: 710 MPa
- Tensile Strength, Yield: 323 MPa @Strain 0.200 %
- Elongation at Break: 58 %
$ 2006/MT
- Density: 7.61 g/cc
- Hardness, Rockwell B: 78
- Tensile Strength, Ultimate: 470 MPa
- Tensile Strength, Ultimate: 20.0 MPa @Temperature 1093 °C
- Tensile Strength, Ultimate: 33.0 MPa @Temperature 871 °C
$ 2552/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 31 @Temperature 23.0 °C
- Hardness, Rockwell C: 31 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 938 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 957 MPa @Temperature 23.0 °C
$ 2051/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 1014 MPa
- Tensile Strength, Yield: 931 MPa
- Elongation at Break: 10 %
$ 2124/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 889 MPa
- Tensile Strength, Yield: 745 MPa
- Elongation at Break: 30 %
$ 1952/MT
- Density: 7.73 g/cc
- Hardness, Rockwell C: 46
- Tensile Strength, Ultimate: 1606 MPa
- Tensile Strength, Yield: 1236 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1640/MT
- Density: 8.03 g/cc
- Tensile Strength, Ultimate: 621 MPa
- Tensile Strength, Ultimate: 69.0 MPa @Temperature 982 °C
- Tensile Strength, Ultimate: 145 MPa @Temperature 871 °C
- Tensile Strength, Ultimate: 248 MPa @Temperature 760 °C
$ 1797/MT
- Density: 7.73 g/cc
- Hardness, Rockwell C: 46
- Tensile Strength, Ultimate: 1627 MPa
- Tensile Strength, Yield: 1280 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 2444/MT
- Density: 7.67 g/cc
- Hardness, Rockwell B: 90
- Tensile Strength, Ultimate: 655 MPa
- Tensile Strength, Yield: 520 MPa @Strain 0.200 %
- Elongation at Break: 22 %
$ 2245/MT
- Density: 7.95 g/cc
- Hardness, Brinell: <= 212
- Tensile Strength, Ultimate: >= 552 MPa
- Tensile Strength, Yield: >= 241 MPa @Strain 0.200 %
- Elongation at Break: >= 30 %
$ 1761/MT
- Density: 7.65 g/cc
- Hardness, Rockwell C: 40
- Tensile Strength, Ultimate: 1283 MPa
- Tensile Strength, Yield: 1026 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1523/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 1089 MPa
- Tensile Strength, Yield: 931 MPa
- Elongation at Break: 14 %
$ 1495/MT
- Carbon, C: 0.010 %
- Chromium, Cr: 18.25 %
- Iron, Fe: >= 69.825 %
- Manganese, Mn: 1.7 %
- Nickel, Ni: 9.5 %
$ 1528/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 793 MPa
- Tensile Strength, Yield: 690 MPa
- Elongation at Break: 26 %
$ 1596/MT
- Density: 7.72 g/cc
- Hardness, Rockwell C: 43
- Tensile Strength, Ultimate: 1434 MPa
- Tensile Strength, Yield: 1218 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1529/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 88
- Tensile Strength, Ultimate: 565 MPa
- Tensile Strength, Yield: 276 MPa
- Elongation at Break: 58 %
$ 1769/MT
- Hardness, Brinell: <= 217
- Hardness, Rockwell B: <= 95
- Tensile Strength, Ultimate: >= 517.1 MPa
- Tensile Strength, Yield: >= 206.9 MPa
- Elongation at Break: >= 40 %
$ 2064/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 41 @Temperature 23.0 °C
- Hardness, Rockwell C: 41 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1228 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1253 MPa @Temperature 23.0 °C
$ 1534/MT
- Density: 7.74 g/cc
- Hardness, Rockwell C: 52
- Tensile Strength, Ultimate: 1858 MPa
- Tensile Strength, Yield: 1466 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1666/MT
- Density: 7.65 g/cc
- Hardness, Rockwell C: 43
- Tensile Strength, Ultimate: 1399 MPa
- Tensile Strength, Yield: 1076 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 2099/MT
- Density: 7.81 g/cc
- Hardness, Rockwell B: 85
- Tensile Strength, Ultimate: 830 MPa
- Tensile Strength, Yield: 345 MPa @Strain 0.200 %
- Elongation at Break: 35 %
$ 1936/MT
- Chromium, Cr: 29 %
- Iron, Fe: 67 %
- Molybdenum, Mo: 4.0 %
$ 1574/MT
- Density: 7.65 g/cc
- Hardness, Rockwell B: 98
- Tensile Strength, Ultimate: 767 MPa
- Tensile Strength, Yield: 589 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1574/MT
- Density: 8.06 g/cc
- Tensile Strength, Ultimate: 1370 MPa
- Tensile Strength, Yield: 1240 MPa @Strain 0.200 %
- Elongation at Break: 2.0 %
- CTE, linear: 15.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 1958/MT
- Density: 7.76 g/cc
- Hardness, Rockwell B: 84
- Tensile Strength, Ultimate: 467 MPa
- Tensile Strength, Yield: 422 MPa @Strain 0.200 %
- Elongation at Break: 24.8 %
$ 1482/MT
- Density: 8.027 g/cc
- Hardness, Brinell: <= 217
- Hardness, Rockwell B: <= 95
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa @Strain 0.200 %
$ 1663/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 47 @Temperature 23.0 °C
- Hardness, Rockwell C: 47 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1701 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1742 MPa @Temperature 23.0 °C
$ 2391/MT
- Density: 7.90 g/cc
- Hardness, Brinell: <= 201
- Hardness, Rockwell B: <= 92
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa
$ 1982/MT
- Density: 7.589 g/cc
- Hardness, Rockwell B: 91
- Tensile Strength, Ultimate: 710 MPa
- Tensile Strength, Yield: 52.2 MPa @Strain 0.200 %
- Elongation at Break: 63 %
$ 1568/MT
- Density: 7.87 g/cc
- Hardness, Rockwell C: 25
- Tensile Strength, Ultimate: 895 MPa
- Tensile Strength, Yield: 725 MPa @Strain 0.200 %
- Elongation at Break: 15 %
$ 1641/MT
- Density: 7.64 g/cc
- Hardness, Brinell: 248
- Hardness, Rockwell C: 24
- Tensile Strength, Ultimate: 814 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 676 MPa @Strain 0.200 %
$ 2577/MT
- Density: 7.74 g/cc
- Hardness, Rockwell C: 41
- Tensile Strength, Ultimate: 1224 MPa
- Tensile Strength, Yield: 1013 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1723/MT
- Density: 7.75 g/cc
- Hardness, Rockwell B: 80
- Tensile Strength, Ultimate: 517 MPa
- Tensile Strength, Yield: 345 MPa @Strain 0.200 %
- Elongation at Break: 30 %
$ 1645/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 993 MPa
- Tensile Strength, Yield: 841 MPa
- Elongation at Break: 20 %
$ 2149/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 28.5 @Temperature 23.0 °C
- Hardness, Rockwell C: 28.5 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 856 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 902 MPa @Temperature 23.0 °C
$ 1499/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 572 MPa
- Tensile Strength, Yield: 290 MPa
- Elongation at Break: 50 %
$ 1838/MT
- Density: 7.70 g/cc
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Yield: 742 MPa
- Elongation at Break: 3.5 %
- Modulus of Elasticity: 200 GPa
$ 1508/MT
- Density: 8.06 g/cc
- Tensile Strength, Ultimate: 900 MPa
- Tensile Strength, Yield: 700 MPa @Strain 0.200 %
- Elongation at Break: 24 %
- CTE, linear: 15.3 µm/m-°C @Temperature 20.0 - 100 °C
$ 1543/MT
- Density: 8.08 g/cc
- Hardness, Brinell: 200 - 220
- Tensile Strength, Ultimate: 85.0 - 95.0 MPa
- Tensile Strength, Yield: 50.0 - 60.0 MPa
- Elongation at Break: 35 - 45 %
$ 1758/MT
- Density: 7.86 g/cc
- Hardness, Rockwell B: 93 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 785 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 396 MPa @Temperature 23.0 °C
- Elongation at Break: 56 % @Temperature 23.0 °C
$ 2227/MT
- Density: 7.86 g/cc
- Hardness, Rockwell B: 76
- Tensile Strength, Ultimate: 500 MPa
- Tensile Strength, Yield: 260 MPa
- Elongation at Break: 46 %
$ 2042/MT
- Density: 7.74 g/cc
- Hardness, Rockwell B: 94
- Tensile Strength, Ultimate: 747 MPa
- Tensile Strength, Yield: 354 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 2249/MT
- Density: 7.74 g/cc
- Hardness, Rockwell B: 94
- Tensile Strength, Ultimate: 747 MPa
- Tensile Strength, Yield: 354 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1669/MT
- Density: 7.73 g/cc
- Hardness, Rockwell C: 45
- Tensile Strength, Ultimate: 1606 MPa
- Tensile Strength, Yield: 1234 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1503/MT
- Density: 7.728 g/cc
- Hardness, Brinell: <= 302
- Hardness, Rockwell C: <= 32
- Tensile Strength, Ultimate: >= 758 MPa
- Tensile Strength, Yield: >= 552 MPa @Strain 0.200 %
$ 2192/MT
- Density: 7.76 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 576 MPa
- Tensile Strength, Yield: 560 MPa @Strain 0.200 %
- Elongation at Break: 5.5 %
$ 2169/MT
- Density: 7.96 g/cc
- Hardness, Brinell: <= 201
- Hardness, Rockwell B: <= 92
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa @Strain 0.200 %
$ 1453/MT
- Density: 7.72 g/cc
- Hardness, Rockwell C: 50
- Tensile Strength, Ultimate: 1729 MPa
- Tensile Strength, Yield: 1360 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1508/MT
- Carbon, C: 1.0 %
- Chromium, Cr: 16.5 %
- Iron, Fe: 82.5 %
$ 2086/MT
- Density: 7.76 g/cc
- Hardness, Rockwell C: 43
- Tensile Strength, Ultimate: 1207 MPa
- Tensile Strength, Yield: 1138 MPa @Strain 0.200 %
- Elongation at Break: 12 %
$ 1585/MT
- Density: 8.00 g/cc
- Tensile Strength, Ultimate: >= 550 MPa
- Tensile Strength, Yield: >= 240 MPa
- Elongation at Break: >= 40 %
- Modulus of Elasticity: 200 GPa
$ 2514/MT
- Density: 7.76 g/cc
- Hardness, Rockwell B: 97.5
- Tensile Strength, Ultimate: 737 MPa
- Tensile Strength, Yield: 721 MPa @Strain 0.200 %
- Elongation at Break: 1.8 %
$ 1448/MT
- Density: 7.86 g/cc
- Hardness, Rockwell C: 44.5 @Temperature 23.0 °C
- Hardness, Rockwell C: 44.5 @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1467 MPa @Temperature 23.0 °C
- Tensile Strength, Ultimate: 1499 MPa @Temperature 23.0 °C
$ 2207/MT
- Density: 7.90 g/cc
- Hardness, Brinell: <= 201
- Hardness, Rockwell B: <= 92
- Tensile Strength, Ultimate: >= 485 MPa
- Tensile Strength, Yield: >= 170 MPa
$ 1913/MT
- Density: 7.73 g/cc
- Hardness, Rockwell C: 48
- Tensile Strength, Ultimate: 1759 MPa
- Tensile Strength, Yield: 1311 MPa @Strain 0.200 %
- Modulus of Elasticity: 200 GPa
$ 1686/MT
- Density: 7.92 g/cc
- Hardness, Rockwell B: 85
- Tensile Strength, Ultimate: 620 MPa
- Tensile Strength, Yield: 275 MPa
- Elongation at Break: 40 %
$ 1696/MT
- Density: 7.64 g/cc
- Hardness, Brinell: 180
- Hardness, Rockwell B: 96
- Tensile Strength, Ultimate: 565 MPa @Temperature 23.0 °C
- Tensile Strength, Yield: 407 MPa @Strain 0.200 %
$ 1529/MT
- Density: 8.03 g/cc
- Hardness, Brinell: 297
- Hardness, Rockwell C: 32
- Tensile Strength, Ultimate: >= 1034 MPa
- Tensile Strength, Yield: >= 758 MPa @Strain 0.200 %
$ 1499/MT
- Density: 8.03 g/cc
- Hardness, Brinell: 165
- Hardness, Rockwell B: 85
- Tensile Strength, Ultimate: >= 515 MPa
- Tensile Strength, Yield: >= 205 MPa @Strain 0.200 %
$ 1873/MT
- Density: 8.06 g/cc
- Hardness, Brinell: 185
- Hardness, Rockwell B: 90
- Tensile Strength, Ultimate: 760 MPa
- Tensile Strength, Yield: 380 MPa
$ 1796/MT
- Density: 7.90 g/cc
- Hardness, Rockwell B: 92
- Tensile Strength, Ultimate: 1179 MPa
- Tensile Strength, Yield: 1007 MPa
- Elongation at Break: 10 %
Delivery Stainless Steel ATI Allegheny Ludlum
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
commercial ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.