ATI Allegheny Ludlum AL 468™ Dual Stabilized- Low Titanium Stainless Steel price 1718 per MT

Mechanical Properties
Hardness, Rockwell B
75
Tensile Strength, Ultimate
461.9 MPa
Tensile Strength, Ultimate
34.5 MPa @Temperature 871 °C
Tensile Strength, Ultimate
89.6 MPa @Temperature 760 °C
Tensile Strength, Ultimate
206.8 MPa @Temperature 648 °C
Tensile Strength, Ultimate
282.7 MPa @Temperature 537 °C
Tensile Strength, Ultimate
324.1 MPa @Temperature 426 °C
Tensile Strength, Ultimate
386.1 MPa @Temperature 204 °C
Tensile Strength, Yield
27.6 MPa @Temperature 871 °C
Tensile Strength, Yield
62.1 MPa @Temperature 760 °C
Tensile Strength, Yield
117.2 MPa @Temperature 648 °C
Tensile Strength, Yield
165.5 MPa @Temperature 537 °C
Tensile Strength, Yield
186.2 MPa @Temperature 426 °C
Tensile Strength, Yield
220.6 MPa @Temperature 204 °C
Tensile Strength, Yield
289.6 MPa @Strain 0.200 %
Elongation at Break
32 %
Elongation at Break
17 % @Temperature 537 °C
Elongation at Break
18 % @Temperature 648 °C
Elongation at Break
20 % @Temperature 426 °C
Elongation at Break
26 % @Temperature 204 °C
Elongation at Break
30 % @Temperature 760 °C
Elongation at Break
55 % @Temperature 871 °C
Elongation at Break
70 % @Temperature 924 °C

Thermal Properties
CTE, linear
10.2 µm/m-°C @Temperature 20.0 - 100 °C
CTE, linear
11.6 µm/m-°C @Temperature 20.0 - 500 °C
CTE, linear
13.6 µm/m-°C @Temperature 20.0 - 1000 °C

Component Elements Properties
Aluminum, Al
0.030 %
Carbon, C
0.0090 %
Chromium, Cr
18.25 %
Iron, Fe
>= 80.15 %
Manganese, Mn
0.40 %
Nickel, Ni
0.22 %
Niobium, Nb (Columbium, Cb)
0.25 %
Nitrogen, N
0.016 %
Phosphorous, P
0.024 %
Silicon, Si
0.55 %
Sulfur, S
0.0010 %
Titanium, Ti
0.10 %

Descriptive Properties
Corrosion Rate mils per year
324
Corrosion Rate mils per year (base metal)
0.12
Corrosion Rate mils per year (base metal)
0.48
Corrosion Rate mils per year (base metal)
0.6
Corrosion Rate mils per year (base metal)
114 (ASTM A262, Practice C)
Corrosion Rate mils per year (base metal)
76.8
Corrosion Rate mils per year (base metal)
82.2 (ASTM A262, Practice B)
Corrosion Rate mils per year (base metal)
OK (ASTM A262 Practice E)
Corrosion Rate mils per year (weld)
0.12
Corrosion Rate mils per year (weld)
366
Corrosion Rate mils per year (weld)
687.6
Corrosion Rate mils per year (weld)
85.2 (ASTM A262, Practice B)
Corrosion Rate mils per year (weld)
90 (ASTM A262, Practice C)
Corrosion Rate mils per year (weld)
OK (ASTM A262 Practice E)

Alternative products

ATI Allegheny Ludlum AL 36™ Electrical Alloy (Cryogenic and Bimetal) UNS K93600 or UNS K93603 accurate 66%

$ 1688/MT

Density: 8.05 g/cc
Hardness, Rockwell B: 75
Tensile Strength, Ultimate: 462 MPa
Tensile Strength, Yield: 261 MPa @Strain 0.200 %
Elongation at Break: 32 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 95% - 16) accurate 66%

$ 1562/MT

Particle Size: 6.7 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 16) accurate 66%

$ 1714/MT

Particle Size: 8.4 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Haynes 242® alloy, cold rolled sheet, annealed and aged accurate 66%

$ 1668/MT

Density: 9.05 g/cc
Hardness, Brinell: 257
Hardness, Knoop: 286
Hardness, Rockwell C: 19
Hardness, Vickers: 78.0 @Temperature 870 °C

Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 746°C (1375°F)/8hr/AC to 621°C (1150°F)/8hr/AC accurate 66%

$ 1579/MT

Density: 8.40 g/cc
Hardness, Brinell: 369
Hardness, Knoop: 403
Hardness, Rockwell C: 40
Hardness, Vickers: 386

UBE 1022MT2 Nylon 6 Monofilament (Drawing Ratio=4.8) accurate 66%

$ 1471/MT

Fiber Count: 1510 dtex
Elongation at Break: 32 %
Elongation at Break: 32 %
Tenacity: 0.424 N/tex
Tenacity: 0.653 N/tex
Tenacity: 1.85 N/tex

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 80% - 22) accurate 66%

$ 1507/MT

Particle Size: 12 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

Osprey Metals 17-7 PH Stainless Steel Powder (Grade 90% - 22) accurate 66%

$ 1515/MT

Particle Size: 10 µm
Aluminum, Al: 0.75 - 1.5 %
Carbon, C: 0.014 %
Carbon, C: <= 0.090 %
Chromium, Cr: 16 - 18 %

AK Steel 409 ULTRA FORM® Stainless Steel accurate 66%

$ 1797/MT

Density: 7.74 g/cc
Hardness, Rockwell B: 66.9
Hardness, Rockwell B: 70
Hardness, Rockwell B: 85.3
Hardness, Rockwell B: 85.3

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale norway. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for ATI Allegheny Ludlum AL 468™ Dual Stabilized- Low Titanium Stainless Steel

Seller from Tehran – 2021-08-18:

Seller from Tehran work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1750 per MT

Seller from Hanoi – 2021-03-27:

Seller from Hanoi work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2484 per MT

Seller from Seoul – 2021-03-18:

Seller from Seoul work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1718 per MT