ATI Wah Chang Zircadyne® Alloy Zr 702 price 2054 per MT

Physical Properties
Density
6.50 g/cc
Vapor Pressure
1.20 bar @Temperature 3600 °C

Mechanical Properties
Tensile Strength, Ultimate
157 MPa @Temperature 371 °C
Tensile Strength, Ultimate
198 MPa @Temperature 316 °C
Tensile Strength, Ultimate
201 MPa @Temperature 260 °C
Tensile Strength, Ultimate
230 MPa @Temperature 204 °C
Tensile Strength, Ultimate
305 MPa @Temperature 149 °C
Tensile Strength, Ultimate
364 MPa @Temperature 93.0 °C
Tensile Strength, Ultimate
468 MPa @Temperature 23.0 °C
Tensile Strength, Yield
82.0 MPa @Temperature 371 °C
Tensile Strength, Yield
97.2 MPa @Temperature 316 °C
Tensile Strength, Yield
129 MPa @Temperature 260 °C
Tensile Strength, Yield
139 MPa @Temperature 204 °C
Tensile Strength, Yield
196 MPa @Temperature 149 °C
Tensile Strength, Yield
268 MPa @Temperature 93.0 °C
Tensile Strength, Yield
321 MPa @Temperature 23.0 °C
Elongation at Break
28.9 % @Temperature 23.0 °C
Elongation at Break
31.5 % @Temperature 93.0 °C
Elongation at Break
40.1 % @Temperature 316 °C
Elongation at Break
42.5 % @Temperature 149 °C
Elongation at Break
44.1 % @Temperature 371 °C
Elongation at Break
49 % @Temperature 204 °C
Elongation at Break
49 % @Temperature 260 °C
Modulus of Elasticity
64.1 GPa @Temperature 371 °C
Modulus of Elasticity
69.6 GPa @Temperature 316 °C
Modulus of Elasticity
75.2 GPa @Temperature 260 °C
Modulus of Elasticity
80.7 GPa @Temperature 204 °C
Modulus of Elasticity
86.9 GPa @Temperature 149 °C
Modulus of Elasticity
93.1 GPa @Temperature 93.0 °C
Modulus of Elasticity
98.6 GPa @Temperature 38.0 °C
Modulus of Elasticity
99.2 GPa @Temperature 23.0 °C
Poissons Ratio
0.35
Shear Modulus
36.2 GPa @Temperature 23.0 °C

Thermal Properties
Heat of Fusion
252.7 J/g
Heat of Vaporization
6490 J/g
CTE, linear
6.30 µm/m-°C @Temperature 149 °C
CTE, linear
7.02 µm/m-°C @Temperature 260 °C
CTE, linear
7.38 µm/m-°C @Temperature 371 °C
Melting Point
1852 °C

Component Elements Properties
Fe + Cr
<= 0.20 %
Hafnium, Hf
<= 4.5 %
Zirconium, Zr
>= 94.7 %

Alternative products

Hexcel® Redux® 810 Two-Part Epoxy Paste Adhesive accurate 99%

$ 2584/MT

Density: 1.02 g/cc @Temperature 25.0 °C
Density: 1.11 g/cc @Temperature 25.0 °C
Density: 1.15 g/cc @Temperature 25.0 °C
Viscosity: 4000 - 8000 cP @Temperature 25.0 °C
Viscosity: 80000 - 90000 cP @Temperature 25.0 °C

DuPont Teijin Films Mylar® A Polyester Film, 1200 Gauge accurate 99%

$ 1518/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Tensile Modulus: 3.50 GPa
Poissons Ratio: 0.38
Poissons Ratio: 0.58

DuPont Teijin Films Mylar® A Polyester Film, 200 Gauge accurate 99%

$ 1476/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Film Elongation at Break, MD: 135 %
Film Elongation at Break, TD: 110 %
Tensile Modulus: 3.50 GPa

DuPont Teijin Films Mylar® A Polyester Film, 500 Gauge accurate 99%

$ 2436/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Film Elongation at Break, MD: 140 %
Film Elongation at Break, TD: 115 %
Tensile Modulus: 3.50 GPa

Ampco Metal AMPCO® 15 Aluminum Bronze, Extruded Rod, 25.4 - 50.8 mm. accurate 99%

$ 2351/MT

Specific Gravity: 7.65 g/cc
Density: 7.64 g/cc
Hardness, Brinell: 170
Hardness, Rockwell B: 87
Tensile Strength, Ultimate: >= 586 MPa

Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched accurate 99%

$ 1603/MT

Density: 8.20 g/cc
Hardness, Brinell: 190
Hardness, Knoop: 211
Hardness, Vickers: 199
Tensile Strength, Ultimate: 767 MPa

Haynes Multimet® alloy, GTAW, 6.35 mm plate accurate 99%

$ 1486/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 768 MPa
Elongation at Break: 21 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction accurate 99%

$ 1593/MT

Density: 8.20 g/cc
Hardness, Brinell: 342
Hardness, Knoop: 371
Hardness, Rockwell C: 37
Hardness, Vickers: 358

Haynes Multimet® alloy, SMAW, 9.5 mm plate accurate 99%

$ 1589/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 724 MPa
Elongation at Break: 28 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled accurate 99%

$ 1517/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for ATI Wah Chang Zircadyne® Alloy Zr 702

Seller from Khartoum – 2021-06-19:

Seller from Khartoum work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2304 per MT

Seller from Lahore – 2021-06-19:

Seller from Lahore work with company: Celanese Corporation, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2054 per MT

Seller from Lima – 2021-05-11:

Seller from Lima work with company: Celanese Corporation, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2330 per MT