Physical Properties
Density
6.64 g/cc

Mechanical Properties
Tensile Strength, Ultimate
281 MPa @Temperature 371 °C
Tensile Strength, Ultimate
300 MPa @Temperature 316 °C
Tensile Strength, Ultimate
326 MPa @Temperature 260 °C
Tensile Strength, Ultimate
370 MPa @Temperature 204 °C
Tensile Strength, Ultimate
389 MPa @Temperature 149 °C
Tensile Strength, Ultimate
495 MPa @Temperature 93.0 °C
Tensile Strength, Ultimate
615 MPa @Temperature 23.0 °C
Tensile Strength, Yield
173 MPa @Temperature 371 °C
Tensile Strength, Yield
190 MPa @Temperature 316 °C
Tensile Strength, Yield
196 MPa @Temperature 260 °C
Tensile Strength, Yield
262 MPa @Temperature 204 °C
Tensile Strength, Yield
272 MPa @Temperature 149 °C
Tensile Strength, Yield
391 MPa @Temperature 93.0 °C
Tensile Strength, Yield
506 MPa @Temperature 23.0 °C
Elongation at Break
18.8 % @Temperature 23.0 °C
Elongation at Break
27.8 % @Temperature 371 °C
Elongation at Break
28.9 % @Temperature 260 °C
Elongation at Break
29 % @Temperature 316 °C
Elongation at Break
30.5 % @Temperature 93.0 °C
Elongation at Break
31.7 % @Temperature 149 °C
Elongation at Break
33 % @Temperature 204 °C
Modulus of Elasticity
74.6 GPa @Temperature 371 °C
Modulus of Elasticity
77.8 GPa @Temperature 316 °C
Modulus of Elasticity
81.0 GPa @Temperature 260 °C
Modulus of Elasticity
84.2 GPa @Temperature 204 °C
Modulus of Elasticity
87.3 GPa @Temperature 149 °C
Modulus of Elasticity
90.5 GPa @Temperature 93.0 °C
Modulus of Elasticity
93.8 GPa @Temperature 38.0 °C
Modulus of Elasticity
94.7 GPa @Temperature 23.0 °C
Poissons Ratio
0.33
Fatigue Strength
55.2 MPa
Fatigue Strength
290 MPa @# of Cycles 1.00e+7
Shear Modulus
34.5 GPa @Temperature 23.0 °C

Thermal Properties
CTE, linear
4.86 µm/m-°C @Temperature 149 °C
CTE, linear
5.58 µm/m-°C @Temperature 260 °C
CTE, linear
5.94 µm/m-°C @Temperature 371 °C
Melting Point
1840 °C

Component Elements Properties
Fe + Cr
<= 0.20 %
Hafnium, Hf
<= 4.5 %
Niobium, Nb (Columbium, Cb)
2.0 - 3.0 %
Zirconium, Zr
>= 91 %

Alternative products

Hexcel® Redux® 810 Two-Part Epoxy Paste Adhesive accurate 99%

$ 2584/MT

Density: 1.02 g/cc @Temperature 25.0 °C
Density: 1.11 g/cc @Temperature 25.0 °C
Density: 1.15 g/cc @Temperature 25.0 °C
Viscosity: 4000 - 8000 cP @Temperature 25.0 °C
Viscosity: 80000 - 90000 cP @Temperature 25.0 °C

DuPont Teijin Films Mylar® A Polyester Film, 1200 Gauge accurate 99%

$ 1518/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Tensile Modulus: 3.50 GPa
Poissons Ratio: 0.38
Poissons Ratio: 0.58

DuPont Teijin Films Mylar® A Polyester Film, 200 Gauge accurate 99%

$ 1476/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Film Elongation at Break, MD: 135 %
Film Elongation at Break, TD: 110 %
Tensile Modulus: 3.50 GPa

DuPont Teijin Films Mylar® A Polyester Film, 500 Gauge accurate 99%

$ 2436/MT

Density: 1.39 g/cc
Viscosity Measurement: 0.56
Film Elongation at Break, MD: 140 %
Film Elongation at Break, TD: 115 %
Tensile Modulus: 3.50 GPa

Ampco Metal AMPCO® 15 Aluminum Bronze, Extruded Rod, 25.4 - 50.8 mm. accurate 99%

$ 2351/MT

Specific Gravity: 7.65 g/cc
Density: 7.64 g/cc
Hardness, Brinell: 170
Hardness, Rockwell B: 87
Tensile Strength, Ultimate: >= 586 MPa

Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched accurate 99%

$ 1603/MT

Density: 8.20 g/cc
Hardness, Brinell: 190
Hardness, Knoop: 211
Hardness, Vickers: 199
Tensile Strength, Ultimate: 767 MPa

Haynes Multimet® alloy, GTAW, 6.35 mm plate accurate 99%

$ 1486/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 768 MPa
Elongation at Break: 21 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction accurate 99%

$ 1593/MT

Density: 8.20 g/cc
Hardness, Brinell: 342
Hardness, Knoop: 371
Hardness, Rockwell C: 37
Hardness, Vickers: 358

Haynes Multimet® alloy, SMAW, 9.5 mm plate accurate 99%

$ 1589/MT

Density: 8.20 g/cc
Tensile Strength, Ultimate: 724 MPa
Elongation at Break: 28 %
Poissons Ratio: 0.298
Poissons Ratio: 0.315 @Temperature 426 °C

Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled accurate 99%

$ 1517/MT

Density: 8.20 g/cc
Hardness, Brinell: 159
Hardness, Knoop: 176
Hardness, Rockwell B: 92
Hardness, Vickers: 201

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ship oil tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for ATI Wah Chang Zircadyne® Alloy Zr 705

Seller from Paris – 2021-04-28:

Seller from Paris work with company: Celanese Corporation, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $1991 per MT

Seller from Taipei – 2021-04-24:

Seller from Taipei work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1961 per MT

Seller from New York – 2021-03-19:

Seller from New York work with company: 3M, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2576 per MT