BASF Ultrason E 2010 G6 30% Glass Filled PES

Seller in Ahmadābād price: $2334 per MT

BASF Ultrason E 2010 G6 30% Glass Filled PES in Polymer, Thermoplastic, Polyethersulfone (PES), 30%Glass Fiber Filled

  • Physical Properties
  • Density
  • 1.60 g/cc
  • Water Absorption
  • 1.6 %
  • Moisture Absorption at Equilibrium
  • 0.60 %
  • Viscosity Test
  • 56 cm³/g
  • Linear Mold Shrinkage, Flow
  • 0.0028 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0058 cm/cm
  • Melt Flow
  • 25 g/10 min @Load 10.0 kg, Temperature 360 °C
  • Mechanical Properties
  • Ball Indentation Hardness
  • 224 MPa
  • Tensile Strength at Break
  • 140 MPa
  • Tensile Strength at Break
  • 100 MPa @Temperature 140 °C
  • Tensile Strength at Break
  • 125 MPa @Temperature 100 °C
  • Tensile Strength at Break
  • 135 MPa @Temperature 60.0 °C
  • Tensile Strength at Break
  • 150 MPa @Temperature 20.0 °C
  • Tensile Stress
  • 31.0 MPa @# of Cycles 1.00e+7 , Temperature 180 °C
  • Tensile Stress
  • 38.0 MPa @# of Cycles 1.00e+6 , Temperature 180 °C
  • Tensile Stress
  • 43.0 MPa @# of Cycles 100000 , Temperature 180 °C
  • Tensile Stress
  • 50.0 MPa @Strain 0.600 %, Temperature 160 °C
  • Tensile Stress
  • 50.0 MPa @Strain 0.500 %, Temperature 23.0 °C
  • Tensile Stress
  • 75.0 MPa @Strain 1.00 %, Temperature 160 °C
  • Tensile Stress
  • 80.0 MPa @Strain 1.40 %, Temperature 160 °C
  • Tensile Stress
  • 80.0 MPa @Strain 1.00 %, Temperature 23.0 °C
  • Tensile Stress
  • 125 MPa @Strain 1.50 %, Temperature 23.0 °C
  • Tensile Strength, Yield
  • 140 MPa
  • Elongation at Break
  • 1.9 %
  • Elongation at Yield
  • 1.9 %
  • Elongation at Yield
  • 0.189 % @Time 3600 sec, Pressure 15.0 MPa
  • Elongation at Yield
  • 0.19 % @Pressure 15.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.20 % @Pressure 15.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 0.20 % @Pressure 10.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.20 % @Time 3600 sec, Pressure 10.0 MPa
  • Elongation at Yield
  • 0.25 % @Pressure 10.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 0.30 % @Time 3600 sec, Pressure 20.0 MPa
  • Elongation at Yield
  • 0.30 % @Pressure 20.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.30 % @Time 3600 sec, Pressure 30.0 MPa
  • Elongation at Yield
  • 0.35 % @Time 3600 sec, Pressure 30.0 MPa
  • Elongation at Yield
  • 0.38 % @Pressure 30.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.40 % @Pressure 30.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 0.40 % @Time 3600 sec, Pressure 40.0 MPa
  • Elongation at Yield
  • 0.40 % @Pressure 20.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 0.40 % @Pressure 30.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.50 % @Pressure 40.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.50 % @Time 3600 sec, Pressure 50.0 MPa
  • Elongation at Yield
  • 0.55 % @Time 3600 sec, Pressure 45.0 MPa
  • Elongation at Yield
  • 0.60 % @Pressure 45.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.78 % @Time 3600 sec, Pressure 60.0 MPa
  • Elongation at Yield
  • 0.80 % @Pressure 60.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.80 % @Pressure 50.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.90 % @Pressure 30.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 0.90 % @Pressure 60.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 0.99 % @Time 3600 sec, Pressure 75.0 MPa
  • Elongation at Yield
  • 1.1 % @Pressure 75.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 1.23 % @Pressure 75.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 1.5 % @Pressure 40.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 2.5 % @Pressure 50.0 MPa, Time 3.60e+7 sec
  • Elongation at Yield
  • 6.1 % @Pressure 45.0 MPa, Time 3.60e+7 sec
  • Creep Strength
  • 22.0 MPa @Time 3.60e+7 sec
  • Creep Strength
  • 30.0 MPa @Time 3.60e+6 sec
  • Creep Strength
  • 41.0 MPa @Time 360000 sec
  • Creep Strength
  • 55.0 MPa @Time 36000 sec
  • Modulus of Elasticity
  • 9.80 GPa @Temperature 160 °C
  • Modulus of Elasticity
  • 9.85 GPa @Temperature 60.0 °C
  • Modulus of Elasticity
  • 9.90 GPa @Temperature 20.0 °C
  • Modulus of Elasticity
  • 10.0 GPa @Temperature 120 °C
  • Tensile Modulus
  • 10.0 GPa
  • Fatigue Strength
  • 43.0 MPa @# of Cycles 1.00e+7
  • Fatigue Strength
  • 52.0 MPa @# of Cycles 1.00e+6
  • Fatigue Strength
  • 65.0 MPa @# of Cycles 100000
  • Shear Modulus
  • 0.200 GPa @Temperature 225 °C
  • Shear Modulus
  • 0.900 GPa @Temperature 200 °C
  • Shear Modulus
  • 0.950 GPa @Temperature 100 °C
  • Shear Modulus
  • 1.00 GPa @Temperature 50.0 °C
  • Izod Impact, Notched (ISO)
  • 8.00 kJ/m²
  • Izod Impact, Notched (ISO)
  • 8.00 kJ/m² @Temperature -30.0 °C
  • Izod Impact, Unnotched (ISO)
  • 42.0 kJ/m² @Temperature 120 °C
  • Izod Impact, Unnotched (ISO)
  • 50.0 kJ/m² @Temperature 25.0 °C
  • Izod Impact, Unnotched (ISO)
  • 57.0 kJ/m² @Temperature -25.0 °C
  • Izod Impact, Unnotched (ISO)
  • 59.0 kJ/m² @Temperature 0.000 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, seychelle yacht for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for BASF Ultrason E 2010 G6 30% Glass Filled PES

Seller from Ahmadābād – 2021-07-08:

Seller from Ahmadābād work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2334 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell BASF Ultrason E 2010 G6 30% Glass Filled PES?