BASF Ultrason® E 2010 HC PESU price 1627 per MT

Physical Properties
Bulk Density
0.700 - 0.800 g/cc
Density
1.37 g/cc
Water Absorption
2.2 %
Moisture Absorption at Equilibrium
0.80 %
Viscosity Measurement
56
Linear Mold Shrinkage, Flow
0.0082 cm/cm
Linear Mold Shrinkage, Transverse
0.0086 cm/cm
Melt Flow
95.9 g/10 min @Load 10.0 kg, Temperature 360 °C

Mechanical Properties
Ball Indentation Hardness
154 MPa @Load 36.5 kg, Time 30.0 sec
Tensile Strength, Yield
90.0 MPa
Elongation at Yield
6.7 %
Tensile Modulus
2.70 GPa
Izod Impact, Notched (ISO)
6.50 kJ/m² @Temperature 23.0 °C
Izod Impact, Notched (ISO)
7.00 kJ/m² @Temperature -30.0 °C
Charpy Impact Unnotched
NB @Temperature -30.0 °C
Charpy Impact Unnotched
NB @Temperature 23.0 °C
Charpy Impact, Notched
0.650 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.700 J/cm² @Temperature -30.0 °C
Tensile Creep Modulus, 1000 hours
2700 MPa @Strain <=0.500 %

Thermal Properties
CTE, linear, Parallel to Flow
52.0 µm/m-°C @Temperature 23.0 - 80.0 °C
CTE, linear, Parallel to Flow
59.0 µm/m-°C @Temperature 180 °C
Maximum Service Temperature, Air
180 °C
Maximum Service Temperature, Air
220 °C
Deflection Temperature at 1.8 MPa (264 psi)
205 °C
Glass Transition Temp, Tg
225 °C
Decomposition Temperature
>= 400 °C
Flammability, UL94
V-0 @Thickness 1.60 mm

Optical Properties
Refractive Index
1.63 @Thickness 1.00 mm
Transmission, Visible
88 % @Thickness 2.00 mm

Electrical Properties
Volume Resistivity
>= 1.00e+13 ohm-cm
Dielectric Constant
3.8 @Frequency 1.00e+6 Hz
Dielectric Constant
3.9 @Frequency 100 Hz
Dielectric Strength
35.0 kV/mm
Dissipation Factor
0.0017 @Frequency 100 Hz
Dissipation Factor
0.014 @Frequency 1.00e+6 Hz
Comparative Tracking Index
100 V
Comparative Tracking Index
100 V

Processing Properties
Processing Temperature
80.0 °C
Zone 1
340 °C
Zone 2
350 °C
Zone 3
360 °C
Zone 4
360 °C
Melt Temperature
360 °C
Melt Temperature
340 - 390 °C
Mold Temperature
140 - 180 °C
Mold Temperature
160 °C
Drying Temperature
140 °C
Dry Time
4 hour

Descriptive Properties
Color
Light Yellow to Brownish
Commercial Status
Europe
Ignition Temperature
580-600°C
Primary Processing Technique
Injection molding, Extrusion and Blow molding

Alternative products

BASF Ultrason® E 2010 SW Q31 10088 PESU accurate 46%

$ 1696/MT

Bulk Density: 0.700 - 0.800 g/cc
Density: 1.37 g/cc
Water Absorption: 2.2 %
Moisture Absorption at Equilibrium: 0.80 %
Viscosity Measurement: 56

Covestro Apec® 1700 Polycarbonate (discontinued **) accurate 36%

$ 1866/MT

Density: 0.995 g/cc
Density: 1.17 g/cc
Water Absorption: 0.40 %
Moisture Absorption at Equilibrium: 0.20 %
Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 330 °C

BASF Ultrason® E 2010 MR SW 10111 PESU accurate 88%

$ 1612/MT

Bulk Density: 0.700 - 0.800 g/cc
Density: 1.37 g/cc
Water Absorption: 2.2 %
Moisture Absorption at Equilibrium: 0.80 %
Viscosity Measurement: 56

BASF Ultrason E 2010 PES accurate 41%

$ 1669/MT

Density: 1.37 g/cc
Water Absorption: 2.2 %
Moisture Absorption at Equilibrium: 0.80 %
Viscosity Test: 56 cm³/g
Linear Mold Shrinkage, Flow: 0.0082 cm/cm

Covestro Apec® 1803 Polycarbonate accurate 36%

$ 1576/MT

Density: 1.15 g/cc
Density: 0.980 g/cc @Temperature 330 °C
Water Absorption: 0.30 %
Moisture Absorption at Equilibrium: 0.12 %
Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 330 °C

BASF Ultrason® E 2010 MR HP PESU accurate 36%

$ 1627/MT

Bulk Density: 0.700 - 0.800 g/cc
Density: 1.33 g/cc
Water Absorption: 1.7 %
Moisture Absorption at Equilibrium: 0.50 %
Viscosity Measurement: 56

SABIC Innovative Plastics Valox® 357X PBT (Europe-Africa-Middle East) accurate 36%

$ 2005/MT

Specific Gravity: 1.34 g/cc
Density: 1.34 g/cc
Moisture Absorption: 0.150 %
Water Absorption at Saturation: 0.50 %
Viscosity: 310000 cP

BASF Ultrason® E 3010 MR UN PESU accurate 62%

$ 1684/MT

Bulk Density: 0.700 - 0.800 g/cc
Density: 1.37 g/cc
Water Absorption: 2.2 %
Moisture Absorption at Equilibrium: 0.80 %
Viscosity Measurement: 66

Covestro Apec® 2095 Polycarbonate accurate 36%

$ 1546/MT

Density: 1.14 g/cc
Density: 0.970 g/cc @Temperature 330 °C
Water Absorption: 0.30 %
Moisture Absorption at Equilibrium: 0.12 %
Melt Flow: 7.8 g/10 min @Load 2.16 kg, Temperature 330 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale ru. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for BASF Ultrason® E 2010 HC PESU

Seller from Madrid – 2021-03-23:

Seller from Madrid work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2151 per MT

Seller from Tianjin – 2021-03-11:

Seller from Tianjin work with company: Techmer ES, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1627 per MT

Seller from Boston – 2021-04-16:

Seller from Boston work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1958 per MT

Seller from Abidjan – 2021-07-23:

Seller from Abidjan work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2115 per MT