BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone

Seller in Riyadh price: $2187 per MT
Seller in Phoenix price: $2169 per MT
Seller in Manila price: $2448 per MT
Seller in Kolkata price: $2113 per MT

BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone in Polymer, Thermoplastic, Polyphenylsulfone (PPSU)

  • Physical Properties
  • Bulk Density
  • 0.700 - 0.800 g/cc
  • Density
  • 1.29 g/cc
  • Water Absorption
  • <= 1.2 %
  • Water Absorption
  • 0.56 % @Thickness 2.00 mm, Time 180000 sec
  • Water Absorption
  • 1.0 % @Thickness 2.00 mm, Time 360000 sec
  • Water Absorption
  • 1.15 % @Thickness 2.00 mm, Time 1.08e+6 sec
  • Water Absorption
  • 1.2 % @Thickness 2.00 mm, Time 1.80e+6 sec
  • Moisture Absorption at Equilibrium
  • 0.60 %
  • Water Vapor Transmission
  • 100 - 150 g/m²/day
  • Viscosity Measurement
  • 71
  • Linear Mold Shrinkage, Flow
  • 0.0090 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.010 cm/cm
  • Melt Flow
  • >= 45.15 g/10 min @Load 10.0 kg, Temperature 360 °C
  • Mechanical Properties
  • Ball Indentation Hardness
  • 124 MPa @Load 36.5 kg, Time 30.0 sec
  • Tensile Strength at Break
  • 74.0 MPa
  • Tensile Stress
  • 30.0 MPa @Temperature 160 °C
  • Tensile Stress
  • 35.0 MPa @Temperature 160 °C
  • Tensile Stress
  • 40.0 MPa @Temperature 23.0 °C
  • Tensile Stress
  • 60.0 MPa @Temperature 23.0 °C
  • Tensile Stress
  • 70.0 MPa @Temperature 23.0 °C
  • Tensile Strength, Yield
  • 74.0 MPa
  • Tensile Strength, Yield
  • 45.0 MPa @Temperature 140 °C
  • Tensile Strength, Yield
  • 55.0 MPa @Temperature 100 °C
  • Tensile Strength, Yield
  • 65.0 MPa @Temperature 60.0 °C
  • Tensile Strength, Yield
  • 75.0 MPa @Temperature 20.0 °C
  • Elongation at Break
  • 7.8 %
  • Elongation at Yield
  • 7.8 %
  • Elongation at Yield
  • 0.18 % @Time 36000 sec, Pressure 30.0 MPa
  • Elongation at Yield
  • 0.20 % @Time 3600 sec, Pressure 6.00 MPa
  • Elongation at Yield
  • 0.28 % @Time 36000 sec, Pressure 42.0 MPa
  • Elongation at Yield
  • 0.40 % @Time 3600 sec, Pressure 8.00 MPa
  • Elongation at Yield
  • 0.50 % @Pressure 6.00 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.50 % @Time 3600 sec, Pressure 10.0 MPa
  • Elongation at Yield
  • 0.51 % @Pressure 10.0 MPa, Time 36000 sec
  • Elongation at Yield
  • 0.52 % @Pressure 10.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 0.53 % @Pressure 10.0 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 0.90 % @Time 3600 sec, Pressure 12.0 MPa
  • Elongation at Yield
  • 1.0 % @Time 3600 sec, Pressure 14.0 MPa
  • Elongation at Yield
  • 1.0 % @Pressure 6.00 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 1.0 % @Pressure 8.00 MPa, Time 360000 sec
  • Elongation at Yield
  • 1.1 % @Time 3600 sec, Pressure 16.0 MPa
  • Elongation at Yield
  • 1.1 % @Time 3600 sec, Pressure 20.0 MPa
  • Elongation at Yield
  • 1.2 % @Time 36000 sec, Pressure 20.0 MPa
  • Elongation at Yield
  • 1.25 % @Pressure 20.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 1.28 % @Pressure 20.0 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 1.75 % @Time 3600 sec, Pressure 30.0 MPa
  • Elongation at Yield
  • 1.9 % @Pressure 8.00 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 1.9 % @Pressure 12.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 1.95 % @Pressure 30.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 2.1 % @Pressure 30.0 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 2.1 % @Pressure 14.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 2.5 % @Time 3600 sec, Pressure 40.0 MPa
  • Elongation at Yield
  • 2.6 % @Time 36000 sec, Pressure 40.0 MPa
  • Elongation at Yield
  • 2.7 % @Pressure 40.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 2.75 % @Time 3600 sec, Pressure 42.0 MPa
  • Elongation at Yield
  • 3.0 % @Pressure 16.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 3.0 % @Pressure 40.0 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 3.0 % @Pressure 42.0 MPa, Time 360000 sec
  • Elongation at Yield
  • 3.2 % @Pressure 42.0 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 3.5 % @Pressure 12.0 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 4.5 % @Pressure 14.0 MPa, Time 3.60e+6 sec
  • Elongation at Yield
  • 5.5 % @Pressure 16.0 MPa, Time 3.60e+6 sec
  • Creep Strength
  • 30.0 MPa @Time 3.60e+7 sec
  • Creep Strength
  • 33.0 MPa @Time 3.60e+6 sec
  • Creep Strength
  • 35.0 MPa @Time 360000 sec
  • Creep Strength
  • 37.0 MPa @Time 36000 sec
  • Modulus of Elasticity
  • 1.60 GPa @Temperature 140 °C
  • Modulus of Elasticity
  • 1.90 GPa @Temperature 100 °C
  • Modulus of Elasticity
  • 2.10 GPa @Temperature 60.0 °C
  • Modulus of Elasticity
  • 2.25 GPa @Temperature 20.0 °C
  • Tensile Modulus
  • >= 2.27 GPa
  • Tensile Modulus
  • >= 1.60 GPa @Temperature 140 °C
  • Tensile Modulus
  • >= 1.90 GPa @Temperature 100 °C
  • Tensile Modulus
  • >= 2.10 GPa @Temperature 60.0 °C
  • Tensile Modulus
  • >= 2.25 GPa @Temperature 20.0 °C
  • Shear Modulus
  • 0.200 GPa @Temperature 225 °C
  • Shear Modulus
  • 0.700 GPa @Temperature 200 °C
  • Shear Modulus
  • 0.750 GPa @Temperature 150 °C
  • Shear Modulus
  • 0.775 GPa @Temperature 100 °C
  • Shear Modulus
  • 0.800 GPa @Temperature 50.0 °C

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone

Seller from Riyadh – 2021-06-23:

Seller from Riyadh work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2187 per MT

Seller from Phoenix – 2021-03-27:

Seller from Phoenix work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2169 per MT

Seller from Manila – 2021-05-24:

Seller from Manila work with company: 3M, Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics)

Price: $2448 per MT

Seller from Kolkata – 2021-07-27:

Seller from Kolkata work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2113 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Executive suite rental agency in Singapore open-nearme.com